Journal of Composites for Construction

Four large-scale reinforced concrete beams were constructed and tested to investigate the effectiveness of external poststrengthening with prestressed fiber reinforced polymer (FRP) sheets. One of the beams served as a control specimen, another was strengthened with nonprestressed carbon FRP sheets, and the remaining two were strengthened with prestressed carbon FRP sheets. Presented is a method of prestressing multiple layers of the carbon fiber sheets during the application process and the experimental and analytical behavior of the beams under quasi-static loading. Comparisons are made between the control beam, the beam reinforced with nonprestressed carbon FRP sheets, and the beams strengthened with prestressed sheets. Serviceability and ultimate conditions are considered in the theoretical prediction of beam behavior, including the effects of multiple layer prestressing and external loading. The bonding of prestressed FRP sheets to the tensile face of concrete beams improved both the serviceability and the ultimate behavior of the reinforced concrete beams.

Strengthening of RC cantilever slabs using bonded glass-fiber–reinforced plastic (GFRP) strips has recently been explored. That work led to the proposal that the GFRP strips should be anchored to the supporting wall using epoxy-mortar–filled horizontal slots and to the slab using fiber anchors, to prevent or limit debonding. This paper focuses on the strength of RC cantilever slabs strengthened using this method. Experimental work on model cantilever slabs with steel reinforcement of different amounts and different positions is presented. Because of the presence of fiber anchors, all strengthened slabs failed by tensile rupture of the fiber-reinforced plastic (FRP), although in some of the slabs partial debonding had appeared before the FRP rupture took place. Flexural strength equations based on the conventional plane section assumption are next described and shown to predict the test results well, even for slabs with partially debonded FRP strips. Finally, the effect of preloading on the strength of strengthened slabs is discussed.

An experimental program has been carried out to investigate the structural behavior of RC beams strengthened by carbon-fiber–reinforced polymer (CFRP) sheets and exposed to a corrosive environment. A total of eight specimens (120 × 175 × 2,000 mm) were tested. Six specimens were CFRP strengthened and corroded, one specimen was unstrengthened and corroded, and one specimen was neither strengthened nor corroded. Two different strengthening schemes were applied: (1) wrapping the specimen with CFRP sheets; and (2) both specimen wrapping and flexural strengthening. Three specimens were tested under monotonic loading and five specimens were tested in fatigue. The results showed that the use of CFRP sheets for strengthening RC beams that are experiencing steel reinforcement corrosion is an efficient technique that can maintain the structural integrity and enhance the structural behavior of such beams. The ultimate monotonic strength of the CFRP strengthened-corroded specimens increased to a level between 37 and 87% above the predicted strength of a similar unstrengthened-uncorroded (virgin) specimen. The fatigue life of the CFRP strengthened-corroded specimens was increased within a range of 2.5–6.0 times that of a similar unstrengthened-corroded specimen but was lower than that of the uncorroded (virgin) specimen.

This paper presents the results of an experimental investigation of the axial behavior of small-scale circular and square plain concrete specimens and large-scale circular and square reinforced concrete columns confined with fiber reinforced polymer (FRP) composite jackets, subject to monotonic, concentric axial loads. Improvements in the axial load-carrying and deformation capacities of FRP jacketed concrete members over unjacketed members are reported. Factors influencing the axial stress-strain behavior of FRP confined concrete, such as transverse dilation and effectively confined regions and their relationship to jacket properties, are identified and discussed. Factors necessary to calibrate in situ jacket behavior and reported or measured FRP material properties are proposed and their interrelationships discussed.

The objective of the presented study is to examine the effects of glass fiber reinforced polymer (GFRP) composite rehabilitation systems on the fatigue performance of reinforced concrete beams. Experiments were conducted on beams with and without GFRP composite sheets on their tensile surfaces. The specimens were 152 × 152 × 1,321 mm reinforced concrete beams with enough transverse reinforcement to avoid shear failure. The results of this study indicate that the fatigue life of reinforced concrete beams with the given geometry, subjected to the same cycling load, can be significantly extended through the use of externally bonded GFRP composite sheets. An interesting finding is that, although the fiber strengthening system increases the fatigue life of the beams, the failure mechanism, fatigue of the steel reinforcement, remains the same in both strengthened and nonstrengthened beams. Thus, it is possible to predict the fatigue life of a cyclically loaded beam using existing fatigue models.

Fiber-reinforced plastic (FRP) reinforcing bars are not prone to classical electrochemical corrosion. However, this material may suffer from other degradation mechanisms when exposed to moisture, alkaline, or acid solutions for a long period of time. In the present study, the absorption characteristic of aramid fiber-reinforced plastic (AFRP) prestressing rods with epoxy matrix was investigated in terms of weight gain or loss by immersing the rods in water, alkaline, and acid solutions for more than a year. The results showed that the weight of the 8 mm diameter AFRP rods immersed in water increased in weight marginally. The weight of the rods immersed in an alkaline or acid solution increased significantly. A scanning electron microscope photograph showed the penetration zone at the cross section of the rods when immersed in three different solutions. An electron probe microscope analyzer examination is useful to detect the presence of the ion Na⁺ from the NaOH solution where the rods were immersed. A Simplified Diffusion Model can predict the depth of penetration and was verified by a scanning electron microscope measurement.

Extensive testing has shown that externally bonded carbon fiber reinforced polymer (CFRP) laminates are particularly suited for improving the short-term behavior of deficient reinforced concrete beams. Accelerated fatigue tests conducted to date confirm that fatigue response is also improved. This paper describes an analytical model for simulating the static response and accelerated fatigue behavior of reinforced concrete beams strengthened with CFRP laminates. Static and fatigue calculations are carried out using a fiber section model that accounts for the nonlinear time-dependent behavior of concrete, steel yielding, and rupture of CFRP laminates. Analysis results are compared with experimental data from two sets of accelerated fatigue tests on CFRP strengthened beams and show good agreement. Cyclic fatigue causes a time-dependent redistribution of stresses, which leads to a mild increase in steel and CFRP laminate stresses as fatigue life is exhausted. Based on the findings, design considerations are suggested for the repair and/or strengthening of reinforced concrete beams using CFRP laminates.

This paper evaluates the shear strength, V_c, of intermediate length (2.5 < a/d < 6) simply supported concrete beams subjected to four-point monotonic loading and reinforced with deformed, glass fiber-reinforced polymer (GFRP) reinforcement bars. Six different overreinforced GFRP designs, ρ > ρ_b, were tested with three replicate beams per design. All samples failed as a result of diagonal-tension shear. Measured shear strengths at failure are compared with theoretical predictions calculated according to traditional steel-reinforced concrete procedures and recently published expressions intended for beams reinforced with GFRP. Recommendations are made regarding the adequacy of shear strength prediction equations for GFRP-reinforced members. The study concludes that shear capacity is significantly overestimated by the “Building Code Requirements for Structural Concrete and Commentary” (ACI 318-99) expression for, V_c, as a result of the large crack widths, small compression block, and reduced dowel action in GFRP-reinforced flexural members. Shear strength was found to be independent of the amount of longitudinal GFRP reinforcement. A simplified empirical equation for predicting the ultimate shear strength of concrete beams reinforced with GFRP is endorsed.