Mechanical Behavior and Permeability of Plastic Concrete Containing Natural Zeolite under Triaxial and Uniaxial Compression
Publication: Journal of Materials in Civil Engineering
Volume 34, Issue 2
Abstract
This paper represents a series of laboratory tests to illustrate the effects of natural zeolite and sulfate environment on the mechanical behavior, hydraulic properties, and microstructure of plastic concrete. Plastic concrete (Pl-C) is comprised of cement, water, aggregate, and bentonite. Because cement production is responsible for a significant amount of carbon dioxide emissions into the atmosphere, cement was replaced in five different percentages of 0%, 10%, 15%, 20%, and 25% by natural zeolite (Z). Moreover, all the specimens were cured in chambers simulating sulfate attack. The mechanical behavior of plastic concrete containing natural zeolite (Pl-CZ) was studied using a series of confined and unconfined compression tests. Hydraulic properties were evaluated using three different confining pressures of 200, 350, and 500 kPa. Scanning electron microscopy (SEM) images were utilized to explore the microstructure of Pl-CZ specimens. The test results show that, although increasing the zeolite content decreased the unconfined strength, peak strength, and the elastic modulus in the early ages, at the later ages, it increased the unconfined strength as well as the peak strength and the elastic modulus, while it decreased the permeability. As illustrated in SEM images, specimens cured in the sulfate environment indicated lower porosity which led to having higher unconfined strength, elastic modulus, and peak strength, along with lower permeability.
Get full access to this article
View all available purchase options and get full access to this article.
Data Availability Statement
Some or all data, models, or code that support the findings of this study are available from the corresponding author upon reasonable request.
References
Alós Shepherd, D., E. Kotan, and F. Dehn. 2020. “Plastic concrete for cut-off walls: A review.” Constr. Build. Mater. 255 (Sep): 119248. https://doi.org/10.1016/j.conbuildmat.2020.119248.
Amlashi, A. T., S. M. Abdollahi, S. Goodarzi, and A. R. Ghanizadeh. 2019. “Soft computing based formulations for slump, compressive strength, and elastic modulus of bentonite plastic concrete.” J. Cleaner Prod. 230 (Sep): 1197–1216. https://doi.org/10.1016/j.jclepro.2019.05.168.
ASTM. 1989. Test method for unconsolidated undrained compressive strength of cohesive soils in triaxial compression. ASTM D2850. West Conshohocken, PA: ASTM.
ASTM. 2005. Standard test method for compressive strength of cylindrical concrete specimens. ASTM C39. West Conshohocken, PA: ASTM.
ASTM. 2006. Standard test method for unconfined compressive strength of cohesive soil. ASTM D2166. West Conshohocken, PA: ASTM.
ASTM. 2011. Standard specification for portland cement. ASTM C150/ C150M–11. West Conshohocken, PA: ASTM.
ASTM. 2012. Standard test method for slump of hydraulic-cement concrete. ASTM C143. West Conshohocken, PA: ASTM.
Bagheri, A. R., M. Alibabaie, and M. Babaie. 2008. “Reduction in the permeability of plastic concrete for cut-off walls through utilization of silica fume.” Constr. Build. Mater. 22 (6): 1247–1252. https://doi.org/10.1016/j.conbuildmat.2007.01.024.
Barger, G. S., J. Bayles, B. Blair, D. Brown, H. Chen, T. Conway, and P. Hawkins. 2001. Vol. 2166 of Ettringite formation and the performance of concrete, 1–16. Skokie, IL: Portland Cement Association.
CRD (Concepts and Requirements Division). 1992. Test method for water permeability of concrete using triaxial cell. CRD-C 163-92. Washington, DC: USACE.
Damtoft, J. S., J. Lukasik, D. Herfort, D. Sorrentino, and E. M. Gartner. 2008. “Sustainable development and climate change initiatives.” Cem. Concr. Res. 38 (2): 115–127. https://doi.org/10.1016/j.cemconres.2007.09.008.
Day, R. L., and C. Shi. 1994. “Influence of the fineness of pozzolan on the strength of lime natural-pozzolan cement pastes.” Cem. Concr. Res. 24 (8): 1485–1491. https://doi.org/10.1016/0008-8846(94)90162-7.
Dembovska, L., D. Bajare, I. Pundiene, and L. Vitola. 2017. “Effect of pozzolanic additives on the strength development of high performance concrete.” Procedia Eng. 172 (Jan): 202–210. https://doi.org/10.1016/j.proeng.2017.02.050.
Fernández-Jiménez, A., and A. Palomo. 2011. “New cements for the 21st century: The pursuit of an alternative to portland cement.” Cem. Concr. Res. 41 (7): 750–763. https://doi.org/10.1016/j.cemconres.2011.03.016.
Gao, R., Q. Li, and S. Zhao. 2013. “Concrete deterioration mechanisms under combined sulfate attack and flexural loading.” J. Mater. Civ. Eng. 25 (1): 39–44. https://doi.org/10.1061/(ASCE)MT.1943-5533.0000538.
Gartner, E. 2004. “Industrially interesting approaches to ‘’ cements.” Cem. Concr. Res. 34 (9): 1489–1498. https://doi.org/10.1016/j.cemconres.2004.01.021.
Ghrici, M., S. Kenai, and E. Meziane. 2006. “Mechanical and durability properties of cement mortar with Algerian natural pozzolana.” J. Mater. Sci. 41 (21): 6965–6972. https://doi.org/10.1007/s10853-006-0227-0.
Gupta, N., and R. Siddique. 2020. “Sulfate resistance and drying shrinkage of self-compacting concrete incorporating copper slag.” J. Mater. Civ. Eng. 32 (12): 04020389. https://doi.org/10.1061/(ASCE)MT.1943-5533.0003501.
Hall, M. R., R. Lindsay, and M. Krayenhoff. 2012. Modern earth buildings: Materials, engineering, constructions and applications. Amsterdam, Netherlands: Elsevier.
Hartell, J. A., A. J. Boyd, and C. C. Ferraro. 2011. “Sulfate attack on concrete: Effect of partial immersion.” J. Mater. Civ. Eng. 23 (5): 572–579. https://doi.org/10.1061/(ASCE)MT.1943-5533.0000208.
He, K., C. Ye, Y. Deng, J. Zhou, B. Liao, R. Gong, Y. Bi, and W. Ji. 2020. “Study on the microscale structure and anti-seepage properties of plastic concrete for cut-off walls modified with silica fume: Experiment and modelling.” Constr. Build. Mater. 261 (Nov): 120489. https://doi.org/10.1016/j.conbuildmat.2020.120489.
Hinchberger, S., J. Weck, and T. Newson. 2010. “Mechanical and hydraulic characterization of plastic concrete for seepage cut-off walls.” Can. Geotech. J. 47 (4): 461–471. https://doi.org/10.1139/T09-103.
ICOLD (International Commission on Large Dams). 1985. Filling materials for watertight cut off walls. Paris: ICOLD.
Idorn, G. M. 1992. “Expansive mechanisms in concrete.” Cem. Concr. Res. 22 (6): 1039–1046. https://doi.org/10.1016/0008-8846(92)90034-S.
Ikumi, T., S. H. P. Cavalaro, and I. Segura. 2019. “The role of porosity in external sulphate attack.” Cem. Concr. Compos. 97 (Mar): 1–12. https://doi.org/10.1016/j.cemconcomp.2018.12.016.
Jafarzadeh, F., and S. H. Mousavi. 2012. “Effect of specimen’s age on mechanical properties of plastic concrete walls in dam foundations.” Electron. J. Geotech. Eng. 17 (Jan): 473–482.
Janotka, I., and L. Krajči. 2008. “Sulphate resistance and passivation ability of the mortar made from pozzolan cement with zeolite.” J. Therm. Anal. Calorim. 94 (1): 7–14. https://doi.org/10.1007/s10973-008-9180-2.
Juenger, M. C. G., and R. Siddique. 2015. “Recent advances in understanding the role of supplementary cementitious materials in concrete.” Cem. Concr. Res. 78 (Dec): 71–80. https://doi.org/10.1016/j.cemconres.2015.03.018.
Li, G.-Z., N.-Q. Feng, and X.-W. Zang. 1990. “High-strength and flowing concrete with a zeolitic mineral admixture.” Cem. Concr. Aggregates 12 (2): 61–69. https://doi.org/10.1520/CCA10273J.
Liu, K., D. Sun, A. Wang, G. Zhang, and J. Tang. 2018. “Long-term performance of blended cement paste containing fly ash against sodium sulfate attack.” J. Mater. Civ. Eng. 30 (12): 04018309. https://doi.org/10.1061/(ASCE)MT.1943-5533.0002516.
Liu, M., Y. Hu, Z. Lai, T. Yan, X. He, J. Wu, Z. Lu, and S. Lv. 2020. “Influence of various bentonites on the mechanical properties and impermeability of cement mortars.” Constr. Build. Mater. 241 (Apr): 118015. https://doi.org/10.1016/j.conbuildmat.2020.118015.
Mahboubi, A., and A. Ajorloo. 2005. “Experimental study of the mechanical behavior of plastic concrete in triaxial compression.” Cem. Concr. Res. 35 (2): 412–419. https://doi.org/10.1016/j.cemconres.2004.09.011.
Małolepszy, J., and E. Grabowska. 2015. “Sulphate attack resistance of cement with zeolite additive.” Procedia Eng. 108 (Jan): 170–176. https://doi.org/10.1016/j.proeng.2015.06.133.
Mehta, P. K., and P. J. M. Monteiro. 1997. Concrete: Structure, proper-ties and materials. Englewood Cliffs, NJ: Prentice Hall.
Mehta, P. K., and P. J. M. Monteiro. 2001. Concrete: Microstructure, properties and materials, 239. New York: McGraw-Hill.
Momayez, A., M. R. Ehsani, A. A. Ramezanianpour, and H. Rajaie. 2005. “Comparison of methods for evaluating bond strength between concrete substrate and repair materials.” Cem. Concr. Res. 35 (4): 748–757. https://doi.org/10.1016/j.cemconres.2004.05.027.
Nateghi, R., K. Goshtasbi, and H. R. Nejati. 2020. “Coupled effects of confining pressure and loading rate on the mechanical behavior of plastic concrete.” J. Mater. Civ. Eng. 32 (10): 04020292. https://doi.org/10.1061/(ASCE)MT.1943-5533.0003341.
Neville, A. 2004. “The confused world of sulfate attack on concrete.” Cem. Concr. Res. 34 (8): 1275–1296. https://doi.org/10.1016/j.cemconres.2004.04.004.
Pashang Pisheh, Y., and M. Mir Mohammad Hosseini. 2020. “Laboratory study on the cyclic and postcyclic behavior of plastic concrete used in cutoff walls of embankment dams.” J. Mater. Civ. Eng. 32 (5): 04020088. https://doi.org/10.1061/(ASCE)MT.1943-5533.0003172.
Pashang Pisheh, Y., and S. M. Mir Mohammad Hosseini. 2012. “Stress-strain behavior of plastic concrete using monotonic triaxial compression tests.” J. Cent. South Univ. Technol. 19 (4): 1125–1131. https://doi.org/10.1007/s11771-012-1118-y.
Perraki, T., G. Kakali, and F. Kontoleon. 2003. “The effect of natural zeolites on the early hydration of portland cement.” Microporous Mesoporous Mater. 61 (1–3): 205–212. https://doi.org/10.1016/S1387-1811(03)00369-X.
Ping, X., and J. J. Beaudoin. 1992. “Mechanism of sulphate expansion I. Thermodynamic principle of crystallization pressure.” Cem. Concr. Res. 22 (4): 631–640. https://doi.org/10.1016/0008-8846(92)90015-N.
Plecas, I., S. Dimovic, and I. Smiciklas. 2009. “Influence of bentonite and zeolite in cementation of dry radioactive evaporator concentrates.” Appl. Clay Sci. 43 (1): 9–12. https://doi.org/10.1016/j.clay.2008.07.003.
Poon, C. S., L. Lam, S. C. Kou, and Z. S. Lin. 1999. “A study on the hydration rate of natural zeolite blended cement pastes.” Constr. Build. Mater. 13 (8): 427–432. https://doi.org/10.1016/S0950-0618(99)00048-3.
Rahhal, V. F., Z. Pavlík, A. Tironi, C. C. Castellano, M. A. Trezza, R. Černý, and E. F. Irassar. 2017. “Effect of cement composition on the early hydration of blended cements with natural zeolite.” J. Therm. Anal. Calorim. 128 (2): 721–733. https://doi.org/10.1007/s10973-016-6007-4.
Ramesh, B. A., and B. Kondraivendhan. 2020. “Effect of accelerated carbonation on the performance of concrete containing natural zeolite.” J. Mater. Civ. Eng. 32 (4): 04020037. https://doi.org/10.1061/(ASCE)MT.1943-5533.0003050.
Ramezanianpour, A. A., A. Kazemian, M. Sarvari, and B. Ahmadi. 2013. “Use of natural zeolite to produce self-consolidating concrete with low portland cement content and high durability.” J. Mater. Civ. Eng. 25 (5): 589–596. https://doi.org/10.1061/(ASCE)MT.1943-5533.0000621.
Ramezanianpour, A. A., R. Mousavi, M. Kalhori, J. Sobhani, and M. Najimi. 2015. “Micro and macro level properties of natural zeolite contained concretes.” Constr. Build. Mater. 101 (Dec): 347–358. https://doi.org/10.1016/j.conbuildmat.2015.10.101.
Rasheeduzzafar, O. S. B., O. S. B. Al-Amoudi, S. N. Abduljauwad, and M. Maslehuddin. 1994. “Magnesium-sodium sulfate attack in plain and blended cements.” J. Mater. Civ. Eng. 6 (2): 201–222. https://doi.org/10.1061/(ASCE)0899-1561(1994)6:2(201).
Rodriguez-Camacho, R. E., and R. Uribe-Afif. 2002. “Importance of using the natural pozzolans on concrete durability.” Cem. Concr. Res. 32 (12): 1851–1858. https://doi.org/10.1016/S0008-8846(01)00714-1.
Shaheen, F., and B. Pradhan. 2020. “Role of chloride ion and cation type accompanied by sulfate ion on durability performance of concrete in conjoint chloride–sulfate environment.” J. Mater. Civ. Eng. 32 (9): 04020264. https://doi.org/10.1061/(ASCE)MT.1943-5533.0003319.
Süleyman Gökçe, H., O. Şimşek, and S. Korkmaz. 2013. “Reduction of alkali-silica reaction expansion of mortars by utilisation of pozzolans.” Mag. Concr. Res. 65 (7): 441–447. https://doi.org/10.1680/macr.12.00118.
Taha, A. S., and H. El-Didamony. 1982. “Studies on artificial pozzolanic cement: Compressive strength and sulfate attack.” Ton ind-ztg 106 (1): 64.
Toropovs, N., D. Bajare, G. Sahmenko, L. Krage, and A. Korjakins. 2014. “The formation of microstructure in high strength concrete containing micro and nanosilica.” Key Eng. Mater. 604 (Mar): 83–86. https://doi.org/10.4028/www.scientific.net/KEM.604.83.
Tumidajski, P. J., and M. L. Thomson. 1994. “Influence of cadmium on the hydration of .” Cem. Concr. Res. 24 (7): 1359–1372. https://doi.org/10.1016/0008-8846(94)90121-X.
Zhang, Z., J. Zhou, J. Yang, Y. Zou, and Z. Wang. 2020. “Understanding of the deterioration characteristic of concrete exposed to external sulfate attack: Insight into mesoscopic pore structures.” Constr. Build. Mater. 260 (Nov): 119932. https://doi.org/10.1016/j.conbuildmat.2020.119932.
Information & Authors
Information
Published In
Copyright
© 2021 American Society of Civil Engineers.
History
Received: Dec 24, 2020
Accepted: Jun 22, 2021
Published online: Nov 26, 2021
Published in print: Feb 1, 2022
Discussion open until: Apr 26, 2022
Authors
Metrics & Citations
Metrics
Citations
Download citation
If you have the appropriate software installed, you can download article citation data to the citation manager of your choice. Simply select your manager software from the list below and click Download.
Cited by
- Serkan Etli, Mechanical Properties of Self-Compacting Mortars Containing Rubber Waste Particles as Fine Aggregate in Freeze–Thaw Cycles, Journal of Materials in Civil Engineering, 10.1061/JMCEE7.MTENG-17647, 36, 9, (2024).
- Bhavdeep Sharma, Shruti Sharma, M. Sudhakara Reddy, Nondestructive Monitoring of Bacterial Intrinsic Self-Healing in Cementitious Structures Using Ultrasonic Wave Propagation, Journal of Materials in Civil Engineering, 10.1061/JMCEE7.MTENG-17109, 36, 4, (2024).
- Shun Kang, Haikuan Wu, Zhihao He, Rong Deng, Changwu Liu, Performance of Lightweight Peach-Shell Concrete with Optimal Substitution Ratio, Journal of Materials in Civil Engineering, 10.1061/JMCEE7.MTENG-17079, 36, 5, (2024).
- Yong Han, Shuchen Li, Jinglong Li, Xiuwei Wang, Chao Yuan, Luoning Li, Effects of Mix Proportion and Cyclic Loading on the Stress–Strain Behavior of a Flexible Thin Spray-On Liner under Uniaxial Compression, Journal of Materials in Civil Engineering, 10.1061/JMCEE7.MTENG-16882, 36, 5, (2024).
- Ahmed Salih Mohammed, Aso A. Abdalla, Rawaz Kurda, Warzer Sarwar Qadir, Wael Mahmood, Kawan Ghafor, Investigation of Hybrid Intelligence Models to Optimize Cement Kiln Content Based on the Failure Stress, Chemical Composition, and Loss on Ignition of Mortar, Journal of Materials in Civil Engineering, 10.1061/JMCEE7.MTENG-16718, 36, 3, (2024).
- Busra Akturk, Fracture behavior of alkali-activated basalt powder/slag systems reinforced with basalt and hybrid fibers, Materials and Structures, 10.1617/s11527-023-02139-3, 56, 2, (2023).
- Xiong Qian, Yunxing Ruan, Tariq Jamil, Chuanlin Hu, Fazhou Wang, Shuguang Hu, Yunpeng Liu, Sustainable cementitious material with ultra-high content partially calcined limestone-calcined clay, Construction and Building Materials, 10.1016/j.conbuildmat.2023.130891, 373, (130891), (2023).
- T.V. Muthukumarana, M.A.V.H.M. Arachchi, H.M.C.C. Somarathna, S.N. Raman, A review on the variation of mechanical properties of carbon fibre-reinforced concrete, Construction and Building Materials, 10.1016/j.conbuildmat.2022.130173, 366, (130173), (2023).
- Ali Akbarpour, Mahdi Mahdikhani, Effects of natural zeolite and sulfate environment on mechanical properties and permeability of cement–bentonite cutoff wall, European Journal of Environmental and Civil Engineering, 10.1080/19648189.2022.2075940, (1-14), (2022).