Journal of Composites for Construction

The bond behavior of reinforcing bars in concrete is a critical issue in the design of reinforced concrete structures. This study focuses on the bond strength of fiber reinforced polymer (FRP) rebars in normal strength concrete. Four different types of rebars were tested using the pullout method: aramid FRP (AFRP); carbon FRP (CFRP); glass FRP (GFRP), and steel. This involved a total of 151 specimens containing 6, 8, 10, 16, and $19\mathrm{mm}$ rebars embedded in a $203\mathrm{mm}$ concrete cube. The test embedment lengths were five, seven, and nine times the rebar diameter $\left(d_b\right)$ . For each rebar, the test results include the bond stress–slip response and the mode of failure. The test results showed that the bond strength of an FRP rebar is, on average, 40–100% the bond strength on a steel rebar for pullout failure mode. Based on this research, a proposal for the average bond strength of straight FRP rebars in normal strength concrete is made, which verifies an existing bond strength relationship (GFRP) and extends its application to AFRP and CFRP. It is an expression that is a function of the rebar diameter, and the concrete compressive strength.

This paper presents the peeling behavior and spalling resistant effect of bidirectional fiber reinforced polymer (FRP) sheets externally bonded to concrete surfaces. Experimental investigations are carried out through a series of newly designed punching-peeling tests. A wide range of variables, such as FRP sheet layers and fiber direction, plate constraint, concrete strength, adhesives, bond length of FRP sheets, diameter of indenter, and types of fibers, are considered in the experimental investigation. Theoretical study is also conducted for the specimens. Interfacial fracture energy is calculated analytically using a membrane-peeling method. It is realized that only two material parameters, i.e., the interfacial fracture energy of the FRP-concrete interface and the tensile stiffness of FRP sheets, are necessary to represent the interfacial spalling resistant behavior. Finally, the theoretical results are validated by comparing with experimental results. Comparison of theoretical to experimental results shows that the proposed theoretical model is satisfactory in reasonably and accurately predicting the peeling behavior and spalling resistant capacity of bidirectional FRP sheets bonded to concrete surface.

A new mathematical model for predicting the inelastic flexural response of corroded reinforced concrete (RC) beams repaired with fiber reinforced polymer (FRP) laminates is presented. The model accounts for the effect of the change in the bond strength at the steel-to-concrete interface due to corrosion and/or FRP wrapping on the beam load–deflection response. The effects of FRP strengthening and the reduction in the steel reinforcement area due to corrosion on the beam strength are predicted by the model. A computer program was coded to carry out the modeling procedure and the model’s predictions were compared with the results of an experimental study undertaken to investigate the model’s reliability. A comparison of the predicted and the experimental results showed that the model accurately predicted the load–deflection relationships for corroded RC beams repaired with FRP laminates.

The behavior of six 1:2.5-scale reinforced concrete cantilever wall specimens having an aspect ratio of 1.5, tested to failure and subsequently repaired and strengthened using fiber-reinforced polymer (FRP) sheets is investigated. Specimens were first repaired by removing heavily cracked concrete, lap splicing the fractured steel bars by welding new short bars, placing new hoops and horizontal web reinforcement, and finally casting nonshrink high-strength repair mortar. The specimens were then strengthened using FRP sheets and strips, with a view to increasing flexural as well as shear strength and ductility. In addition to different arrangements of steel and FRP reinforcement in the walls, a key parameter was the way carbon-FRP strips added for flexural strengthening were anchored; steel plates and steel angles were used to this effect. Steel plates were anchored using U-shaped glass-FRP (GFRP) strips or bonded metal anchors. Test results have shown that by using FRP reinforcement, the flexural and shear strength of the specimens can be increased. From the anchorage systems tested, metal plates combined with FRP strips appear to be quite efficient. The effectiveness of the bonded metal anchors used was generally less than that of the combination of plates and GFRP strips. In all cases, final failure of the FRP anchorage is brittle, but only occurs after the peak strength is attained and typically follows the fracture of steel reinforcement in critical areas, hence the overall behavior of the strengthened walls is moderately ductile.

An experimental investigation was conducted to develop an effective means of connecting glass fiber reinforced polymer (FRP) bridge decks to conventional reinforced concrete parapets. Six full-scale subassemblies were studied under quasi-static loading; two examined a prototype system installed in eastern Pennsylvania, two evaluated an improved connection detail, and two evaluated rehabilitation for the structural system after impact. Poor fabrication of the FRP on the first specimen led to brittle fracture of the deck at 20% of the expected capacity. Five properly fabricated FRP decks were subsequently tested and remained undamaged up to the ultimate capacity of the parapet. The results indicate: (1) reliance on reinforcement-to-resin anchorage transfer mechanisms result in brittle pullout failure of parapet reinforcement from the decks; (2) use of headed reinforcement anchored in the bottom deck flange enhances the ductility of the system; and (3) external steel brackets can provide adequate strength and deformation capability when rehabilitating damaged parapets.

Tech 21 is the third all-composite vehicular bridge installed in the United States. The deck has sandwich configuration with a center core made by bonding orthotropic fiberglass and polyester tubes. The three trapezoidal beams supporting the deck were fabricated using E-glass fibers with polyester resin. Each beam was fabricated as an integral unit with its deck section to facilitate transportation to the site, erection, and construction. The two-lane bridge is the first fully instrumented all-composite vehicular bridge, including an extensive health-monitoring system installed during its fabrication. A nearly four-year long continuous monitoring was carried out to demonstrate the performance of the bridge. Field monitored information was studied to evaluate the behavior and durability of composites in the harsh infrastructure environment. This evaluation determines the level of confidence in the long-term field benefits of composite materials and technology.

Concrete-filled fiber reinforced polymer (FRP) tubes (CFFT) have in the last decade been used as girders, beam columns, and piles. The focus of research, however, has been exclusively on their monotonic behavior, with little or no attention to the implications of using CFFT in seismic regions. A total of six CFFT specimens were tested as simple span beam columns under constant axial loading and quasi-static reverse lateral loading in four point flexure. Three of the tubes were made using centrifuge (spin) casting with $12.7\mathrm{mm}$ thickness with the majority of the fibers in the longitudinal direction, whereas the other three were filament wound with $5\mathrm{mm}$ thickness and $\pm 55°$ fiber orientation. One specimen for each type of tube had no internal reinforcement, whereas the other two incorporated approximately 1.7 and 2.5% steel reinforcement ratios, respectively. The two types of tubes represented two different failure modes; a brittle compression failure for the thick tubes with the majority of the fibers in the longitudinal direction, and a ductile tension failure for the thin tubes with off-axis fibers. The study showed that CFFT can be designed with ductility behavior comparable to reinforced concrete members. Significant ductility can stem from the fiber architecture and interlaminar shear in the FRP tube. Moderate amounts of internal steel reinforcement in the range of 1–2% may further improve the cyclic behavior of CFFT.

Conventional pile materials such as steel, concrete, and timber are prone to deterioration for many reasons. Fiber-reinforced polymer (FRP) concrete composites represent an alternative construction material for deep foundations that can eliminate many of the performance disadvantages of traditional piling materials. However, FRP composites present several difficulties related to constructability, and the lack of design tools for their implementation as a foundation element. This paper describes the results of an experimental study on frictional FRP/dense sand interface characteristics and the constructability of FRP–concrete composite piles. An innovative toe driving technique is developed to install the empty FRP shells in the soil and self-consolidating concrete is subsequently cast in them. The experimental program involves interface shear tests on small FRP samples and uplift load tests on large-scale model piles. Two different FRP pile materials with different roughness and a reference steel pile are examined. Static uplift load tests are conducted on different piles installed in soil samples subjected to different confining pressures in the pressure chamber. The results showed that the interface friction for FRP materials compared favorably with conventional steel material. It was shown that toe driving is suitable for installation of FRP piles in dense soils.

A fiber-reinforced polymer (FRP) deck-to-girder connection was evaluated for fatigue resistance and residual capacity in the transverse direction. The connection consisted of three shear studs cast into a trapezoidal cell of a FRP sandwich deck. Steel spirals were positioned around each shear stud to aid in grout confinement. Test fixturing consisted of multiple girders and tie downs to induce realistic loading of the connection due to wheel loads. The connection was fatigued according to AASHTO LRFD Specifications for $10.5\text{million}\text{cycles}$ ( $75\text{year}$ design life) and tested for residual capacity. The connection survived fatigue testing without failure. The haunch exhibited minimal debonding and cracking. Connection capacity after one lifetime of fatigue cycles exceeded strength limit state requirements.