Journal of Composites for Construction

Extensive research on fiber-reinforced polymer (FRP) confinement strengthening for concrete columns has led to a good understanding of, and accurate models for, circular columns subjected to axial load. This research is being extended to noncircular and eccentrically loaded columns, steel tubular, and concrete-filled steel tubular columns. A significant gap in our understanding of all these columns, however, is that the apparent FRP strain at failure is significantly lower than the ultimate strain in a flat coupon test. There may be many factors contributing to this complex phenomenon. This paper shows that one of these factors is the geometrical discontinuities at the ends of the FRP wrap. The significance of the effect of discontinuities on the strain concentrations in the FRP wrap and the bonding adhesive is explored through an elastic finite-element analysis.

In this study, 18 concrete cylinder specimens were tested either under uniaxial compression at different loading rates or exposed to sustained axial stresses after being jacketed externally with carbon-fiber-reinforced polymer (CFRP) sheets. The specimens were cast using medium strength concrete. All the specimens had identical dimensions and level of confinement. Loading rate and applied sustained stress level were the main test parameters. Applied loading rate varied between 0.0002 and 0.04 strain/min. Four stress levels between 0.52 and $0.85f_{\text{cc}}^{\prime }$ (0.90 and $1.46f_{\text{co}}^{\prime }$ ) were used in short-term creep tests. Test results showed that the stress-strain behavior of CFRP confined concrete was influenced by the change in loading rate, and CFRP confinement provided considerable increase in the creep performance of concrete. The strength enhancement was more pronounced for specimens loaded at higher strain rates, while specimens loaded at slower strain rates exhibited better deformability. Results obtained from short-term monotonic loading tests were also compared with the results of two analytical approaches originally developed for plain concrete. None of the specimens failed during the short-term creep tests. However, the lifetime of the specimen, which was subjected to $0.85f_{\text{cc}}^{\prime }$ $\left(1.46f_{\text{co}}^{\prime }\right)$ sustained axial stress, was predicted as 20 days. Results of residual strength tests showed that specimens did not have any strength loss due to sustained loading.

In this study, carbon fiber-reinforced polymer (CFRP) sheets were examined as a means to strengthening existing masonry walls allowing for efficient creation of doors, windows, and passage openings. The research reported here deals with eight masonry walls made with concrete blocks, subjected to three-point quasistatic loading. The parameters examined include the reinforcement configuration and their amount. While CFRP sheets were used as external reinforcement, companion studies were carried out with conventional steel rebars. Test results indicate an increase of 180% in shear strength of the reinforced walls as compared to reference unreinforced walls. Load-deflection relationships indicate that the combined plain masonry and CFRP laminate system possessed some nonlinear deformability. The use of CFRP laminates on the walls was found to have an influence on the mode of failure. Anchoring the CFRP laminates at both support regions helped in using a larger portion of the strength of the laminates. The reinforced walls exhibited diagonal shear cracks that developed at a much slower rate and were ultimately accompanied by the peeling off of the CFRP laminates.

The objective of this paper is to assess the out-of-plane flexural performance of masonry walls that are reinforced with glass fiber-reinforced polymers (GFRPs) rods, as an alternative for steel rebars. Eight $1\text{m}\times 3\text{m}$ full-scale walls were constructed using hollow concrete masonry units and tested in four-point bending with an effective span of 2.4 m between the supports. The walls were tested when subjected to increasing monotonic loads up to failure. The applied loads would represent out-of-plane loads arising from wind, soil pressure, or inertia force during earthquakes. One wall is unreinforced; another wall is reinforced with customary steel rebars; and the other six walls are reinforced with different amounts of GFRP reinforcement. Two of the GFRP-reinforced walls were grouted only in the cells where the rods were placed to investigate the effect of grouting the empty cells. The force-deformation relationship of the walls and the associated strains in the reinforcement were monitored throughout the tests. The relative performance of different walls is assessed to quantify the effect of different design variables. The range of GFRP reinforcement ratios covered in the experiments was used to propose a capacity diagram for the design of FRP-reinforced masonry walls similar to that of reinforced concrete elements.

Most existing models for evaluating the strength of fiber-reinforced polymer (FRP)-confined concrete columns are based in an early work. In this paper, a new model based on the Hoek-Brown failure criterion is proposed. The existing strength models for FRP-confined circular and square concrete columns are reviewed, evaluated, and compared with the proposed model. An updated database that includes a large number of test data are then used to evaluate the models. Comparisons between the models and the test results demonstrate the accuracy of the proposed model. Apart from this improved accuracy, the proposed model also has a unified form for both circular and square columns, and can be used to predict the strength of columns that have existing damage or cracks. Test data for FRP-repaired concrete columns are collected from the literature and used to evaluate and demonstrate the performance of the proposed model in predicting the strength of FRP-confined deficient columns.

Fiber-reinforced polymer (FRP) composite sheets have gained popularity as a viable strengthening technique for existing reinforced concrete structures. The efficiency of the strengthening system largely depends on adequate bond between FRP sheets and the concrete substrate. In recent years, techniques to anchor FRP sheets have been proposed in applications that have limited distance to develop FRP sheet strength. One promising technique consists of fabricating and bonding FRP anchors during the FRP sheet saturation and embedding them into predrilled holes in the concrete substrate. This paper presents experimental results highlighting the complex behavior between FRP sheets and anchors. The primary failure modes that the sheet-anchor system can experience are identified. The experiments identify the main variables that influence the FRP anchor-sheet system behavior. This research contributes to the needed experimental database that will aid in future development of design recommendations of this anchorage system.

Shear failure of exterior beam-column joints is identified as the principal cause of collapse of many moment-resisting frame buildings during recent earthquakes. Effective and economical strengthening techniques to upgrade joint shear resistance and ductility in existing structures are needed. In this paper, efficiency and effectiveness of carbon fiber-reinforced polymer (CFRP) sheets in upgrading the shear strength and ductility of seismically deficient exterior beam-column joints have been studied. Four as-built joints were constructed with nonoptimal design parameters (inadequate joint shear strength with no transverse reinforcement) representing preseismic code design construction practice of joints and encompassing most of existing beam-column connections. Out of these four as-built specimens, two specimens were used as baseline specimens (control specimens) and other two were strengthened with CFRP sheets under two different schemes (strengthened specimens). In the first scheme, CFRP sheets were epoxy bonded to joint, beams, and part of the column regions. In the second scheme, however, sheets were epoxy bonded to joint region only but they were effectively prevented against any possible debonding through mechanical anchorages. All of these four subassemblages were subjected to cyclic lateral load histories so as to provide the equivalent of severe earthquake damage. The damaged control specimens were then repaired by filling their cracks through epoxy and externally bonding them with CFRP sheets under the same above two schemes. These repaired specimens were subjected to the similar cyclic lateral load history and their response histories were obtained. Response histories of control, repaired, and strengthened specimens were then compared. The results were compared through hysteretic loops, load-displacement envelopes, column profiles, joint shear distortion, ductility, and stiffness degradation. The comparison shows that CFRP sheets are very effective in improving shear resistance and deformation capacity of the exterior beam-column joints and delaying their stiffness degradation.

Wet bond is a chemical bond developed to connect fiber-reinforced polymer (FRP) stay-in-place formwork to cast-in-place concrete for a composite action. Curing of chemical adhesive and fresh concrete occurs simultaneously in wet bond. Since FRP-concrete composite structure so designed is strongly dependent on the bond between FRP and concrete, a durable bond is of paramount importance. This paper presents a study on durability performance of wet bond exposed to sustained low temperature, freeze-thaw cycles, and wet-dry cycles. Single lap pull-off tests were conducted to evaluate the effect of exposure on bond. It was found that both first crack load and ultimate load of wet bond were reduced in comparison to dry bond. This reduction was more severe in first crack load than in ultimate capacity and was associated with voids, thickness, and surface of adhesive layer. The epoxy in wet bond had reached comparable degree of cure to dry bond and even gained a higher $T_{\text{g}}$ . Environmental exposures did not show more impact on wet bond than on dry bond.

The main objective of the research project reported here is to develop a new hybrid glulam beam that will increase the performance of timber structures and optimize the use of wood in such structures. The hybrid beam is made by combining glulam with ultrahigh-performance short fiber-reinforced concrete (UHPC-SFR) planks with or without internal reinforcement consisting of steel- or fiber-reinforced polymer reinforcement bars. This paper presents an experimental program of tests on eight large-scale hybrid beams under four-point bending. The results show that by combining wood and UHPC-SFR, it is possible to obtain a hybrid beam with greater bending stiffness and increased ultimate load capacity.

Because of the short construction season and cold winters in Alaska, the prestressed concrete decked bulb-tee bridge system is very popular. However, the concrete deck is an integral part of the bridge superstructure and cannot be easily replaced when it deteriorates. Obviously, there is merit in combining durable “premanufactured” fiber-reinforced polymer (FRP) composite deck with stiffer prestressed concrete girders in cold regions. However, the effects of long-term exposure to extreme temperature variations and various moisture conditions typical of cold regions on the performance of FRP composite materials are not fully understood. This paper summarizes the combined effect of low-temperature and deformation strain levels on the longitudinal modulus of glass fiber-reinforced polymer (GFRP) samples. The modulus of elasticity of GFRP laminate coupons was tested at various temperatures down to −31 °F $\left(-35°\text{C}\right)$ by temporarily subjecting the samples to three strain levels of 1,000, 2,000, or 3,000 microstrains. Both biaxial and uniaxial samples subjected to a deformation of 1,000 microstrains showed an increase in stiffness when tested at increasingly colder temperatures, and no noticeable change in stiffness was seen when the samples were retested after being equilibrated to room temperature. However, samples subjected to a predetermined elevated strain level did show significant stiffness degradation after room temperature equilibration. The degree of degradation was noticeably larger for samples subjected to the low temperatures than for control samples that were subjected to the equivalent number of cycles at room temperature. It was also noted that the degradation due to load cycles or temperature coupled with load cycles was noticeably less for uniaxial samples than for biaxial samples.

This paper presents the experimental and theoretical results of small and medium-scale concrete-filled fiber-reinforced polymer (FRP) tube (CFFT) columns. A total of 23 CFFT specimens were tested under axial compression load. Five different types of new FRP tubes were used as stay-in-place formwork for the columns. The effects of the following parameters were examined: the FRP-confinement ratio, the unconfined concrete compressive strength, the presence of longitudinal steel reinforcement, and the height-to-diameter ratio. Comparisons between the experimental test results and the theoretical prediction values by the three North American codes and design guidelines (ACI 440.2R-08, CSA-S6-06, and CSA-S806-02) are performed in terms of confined concrete strength and ultimate load carrying capacity. The results of this investigation indicate that the design equations of the ACI 440.2R-08, CAN/CSA-S6-06, and CAN/CSA-S806-02 overestimate the factored axial load capacity of the short CFFT columns as compared to the yield and crack load levels. Also, the CAN/CSA-S6-06 and CAN/CSA-S806-02 confinement models showed conservative predictions, while the ACI 440.2R-08 was slightly less conservative. A new confinement model is proposed for the confined concrete compressive strength of the CFFT cylinders. Also, the design equations are modified to accurately predict the ultimate and yield load capacities of internally reinforced and unreinforced short CFFT columns. Two new factors are introduced in the modified equations, $\left(k_{\text{cc}}\right)$ accounts for the in-place-strength of CFFT columns to CFFT cylinder strength, and $\left(k_{\text{cr}}\right)$ accounts for the initiation of the steel yielding and concrete cracking for the FRP-confined columns.

Due to increasing popularity of using fiber-reinforced polymer (FRP) for external strengthening of concrete structures, an urgent demand for understanding the structural behavior of FRP-strengthened structures has been emerging. Unlike conventional reinforced concrete (RC) structures, FRP-strengthened members can exhibit additional flexural capacity in the postyielding stage. This makes RC models for predicting deflection inapplicable in case of FRP-strengthened structures. Therefore, some models have been explicitly developed for evaluating deflection of the strengthened structures. However, most existing models are empirically based, verified with limited experimental results, and require in some cases sophisticated calculation procedures. Accordingly, there is still a demand for a rational and more convenient model for predicting deflection of FRP-strengthened beams. In the current paper, Bischoff’s model, originally proposed for RC and FRP reinforced structures, was extended. Consequently, the developed model is applicable to FRP-strengthened concrete beams besides its validity to both RC and FRP reinforced beams. Validation of the model with some available test data confirmed its accuracy.