Journal of Composites for Construction

This paper presents mechanical, microstructural, and physical characterization of glass fiber-reinforced polymer (GFRP) bars exposed to concrete environment. GFRP bars were embedded in concrete and exposed to tap water at 23, 40, and $50°\mathrm{C}$ to accelerate the effect of the concrete environment. The measured tensile strengths of the bars before and after exposure were considered as a measure of the durability performance of the specimens and were used for long-term properties prediction based on the Arrhenius theory. In addition, Fourier transform infrared spectroscopy, differential scanning calorimetry, and scanning electron microscopy were used to characterize the aging effect on the GFRP reinforcing bars. The results showed that the durability of mortar-wrapped GFRP bars and exposed to tap water was less affected by accelerated aging than the bars exposed to simulated pore-water solution. These results confirmed that the concerns about the durability of GFRP bars in concrete, based on simulated laboratory studies in alkaline solutions, do not properly correspond to the actual service life in concrete environments.

This study attempts to develop a semianalytical model for the mechanical behavior of reinforced concrete (RC) beams rehabilitated with externally prestressed carbon fiber-reinforced polymers (CFRP) laminates. The main significance of this study is the model of the process of degradation of RC beams until failure and its recovery through externally prestressed CFRP. Experiments have been carried out to observe the load–deflection behavior of fresh RC beams until the load resistance of the beam is exhausted. The beams have been rehabilitated with external CFRP laminates with varying levels of prestress. The rehabilitated beams have been reloaded until failure. The load–deflection behavior of the fresh and rehabilitated beams has been compared. A model for the load–deflection behavior of the fresh and rehabilitated beam has been proposed. The main import of the model is that it incorporates the effect of confinement of concrete. The model shows very good agreement with the experimental results.

Strengthening of concrete structures using fiber-reinforced polymer (FRP) systems has become a widely accepted technology in the construction industry over the past decade. Externally bonded FRP sheets are proven to be a feasible alternative to traditional methods for strengthening and stiffening deficient reinforced or prestressed concrete members. However, the delamination of FRP sheets from the concrete surface poses major concerns, as it usually leads to a brittle member failure. This paper reports on the development of FRP anchors to overcome delamination problems encountered in surface bonded FRP sheets. An experimental investigation was conducted on the performance of carbon FRP anchors that were embedded in normal- and high-strength concrete test specimens. A total of 81 anchors were tested under monotonic uniaxial loading. Test parameters included the length, diameter, and angle of inclination of the anchors and the compressive strength of the concrete. The experimental results indicate that FRP anchors can be designed to achieve high pullout capacities and hence can be used effectively to prevent or delay the delamination of externally bonded FRP sheets. The results also indicate that the diameter, length, and the angle of inclination of the anchors have a significant influence on the pullout capacity of FRP anchors.

Carbon fiber-reinforced polymers (CFRPs) have become increasingly important in recent years in bridge rehabilitation. Significant research has been done on the static behavior of CFRP-strengthened reinforced concrete (RC) structures; however, the fatigue behavior of such structures with interface defects subjected to harsh environmental conditions still needs to be investigated. Hence, an experimental program has been carried out to investigate the fatigue behavior, under a load range, which generates service load stress levels, of RC beams strengthened with CFRP fabrics. The effect of aggressive environments was studied by subjecting the test members to freeze–thaw, extreme temperature, ultraviolet light exposure, and relative humidity cycles. All beams survived 2 million fatigue cycles without showing significant bond degradation between composite and substrate. However, significant flexural stiffness degradation was observed in the conditioned specimens. The presence of defects also affected specimen stiffness; however, limited growth in defect size was observed due to fatigue cycling.

Steel-reinforced polymer (SRP) composite materials are very attractive due to their low weight and high strength. The ease of installation which significantly reduces repair time and expense is another major advantage. One of the main disadvantages of SRP materials is that the matrices used for their fabrication are typically organic and thus they are susceptible to fire. In this study, a newly developed retrofit system is being used. It consists of high strength steel fibers impregnated in a fireproof inorganic matrix. The objective of this study is to examine the effects of this hybrid rehabilitation system on the fatigue performance of strengthened reinforced concrete beams. Sixteen $100\mathrm{mm}\times 150\mathrm{mm}\times 1200\mathrm{mm}$ reinforced concrete beams with enough transverse reinforcement to avoid shear failure were used in this study. Nine beams were strengthened with steel fiber sheets on their tension faces. The results from the present study indicate that the fatigue life of reinforced concrete beams, subjected to the same cycling load, can be significantly extended using externally bonded sheets. A rather important finding is that although the strengthening system increases the fatigue life of the beams, the failure mechanism remains the same in both strengthened and nonstrengthened beams. Thus, it is possible to predict the fatigue life of a cyclically loaded beam using existing fatigue models. Furthermore, no delamination failures were observed due to fatigue loading.

Reinforced concrete columns usually have a minimum amount of transverse steel reinforcement this transverse reinforcement can have non negligible effects on the response of columns retrofitted with fiber-reinforced polymers (FRP). This paper presents a test program that was designed to study the behavior of small- and large-scale normal- and high-strength concrete circular columns confined with transverse steel reinforcement, FRP, and both transverse steel reinforcement and FRP under concentric loading. The effect of the main variables—such as the unconfined concrete strength, the volumetric ratio, the type and the yield strength of the transverse steel reinforcement, the concrete cover, and the number of FRP layers—are studied in this research program. The test results show that the enhancement of the confined concrete strength and strain is more pronounced in specimens with normal-strength concrete. It is also shown that the rupture of the FRP in the specimens with higher volumetric transverse steel reinforcement ratios corresponds to larger axial compressive strength and strain and that the postpeak behavior of these specimens is more ductile.

The aim of this paper is to study the properties of high-strength concrete (HSC) circular columns confined by aramid fiber-reinforced polymer (AFRP) sheets under axial compression. A total of 60 specimens were tested, considering the following parameters: the compressive strength of concrete, the number of AFRP layers, and the form of AFRP wrapping. In addition, an analytical model for predicting the stress–strain curves is proposed based on the experimental results. Meanwhile, a three-dimensional nonlinear finite-element model with a Drucker–Prager plasticity model for the concrete core and an elastic model for the AFRP is developed by using the finite-element code ANSYS. It is demonstrated that the strength and ductility of the columns with continuous AFRP wrapping are increased greatly; whereas the strength of the columns with discontinuous AFRP wrapping is also increased, but the ductility is not always increased notably. The analytical model and the finite-element model are validated against the experimental results.

This paper presents an experimental and nonlinear finite-element analysis (NLFEA) results of circular short reinforced concrete (RC) columns confined externally with carbon fiber-reinforced polymers (CFRP) subjected to pure axial loading. The experimental program involves the fabrication and testing of 55 specimens wrapped with different number and configuration of CFRP sheet layers in the transverse and longitudinal directions. In addition, the columns were modeled using NLFEA. After reasonable validation of NLFEA with the experimental test results of companion columns and available technical literature results, NLFEA was expanded to provide a parametric study of 96 columns that correlates the ultimate axial stress of CFRP-confined RC columns to unconfined strength of concrete $\left(f_{co}\right)$ , the volumetric ratio of CFRP $\left({\rho }_f\right)$ , and the size effect. Results indicated that the ultimate capacity and ductility increase with the increase in volumetric ratio of CFRP $\left({\rho }_f\right)$ and unconfined strength of concrete $\left(f_{co}\right)$ . In addition, the results indicated that size effect exists and the confinement effectiveness was more pronounced for columns with low $f_{co}$ and ${\rho }_f$ .

The problem of masonry columns subjected to structural deficiency under axial load was studied and reported in this paper. The results of an extensive experimental campaign are presented in order to show the behavior of columns built with clay or with calcareous blocks, commonly found in southern Italy, especially in historical buildings. Rectangular masonry columns were tested for a total of 33 specimens; uniaxial compression tests were conducted on columns taking into account the influence of several variables: different strengthening schemes (internal and/or external confinement), curvature radius of the corners, amount of fiber-reinforced polymer (FRP) reinforcement, cross-section aspect ratio, and material of masonry blocks. Materials characterization was preliminarily carried out including a mechanical test on plain masonry. For all cases the experimental results evidenced a significant increase in load carrying capacity and ductility after FRP strengthening, which identified the columns as ductile elements despite the brittle nature of the unconfined masonry. Differences in mechanical behavior, due to the geometry of the columns, to the nature of different materials, to different strengthening schemes, and to the amount of reinforcement, are presented and discussed in the paper. The calibration of design equations recently developed by Italian National Research Council, CNR was conducted to compare analytical prediction and experimental results. The same procedure was applied to calibrate an analytical model recently published, in which the existing coefficients are related only to clay. Here the model is applied to limestone for the first time. Thus, new important information is furnished to researchers and practitioners involved in structural assessment and strengthening of compressed elements in historical buildings.

The physical uncertainty associated with fiber-reinforced polymer composites has to be quantified and dealt with for their widespread use to be reliable. Developing probabilistic models based on experimental studies form an important part of this task. In the present paper, such models are developed for glass fiber-reinforced polymer (GFRP) composites based on an experimental study on panels obtained from Mondial House, a $32\text{year}$ old building demolished in 2006 in London. Having an average size of $1.5\mathrm{m}\times 1.7\mathrm{m}$ and made of chopped strand mat composites, these panels have been exposed to varying ambient conditions, protected only by a fire retardant gel coat for self-cleaning. Tensile and compressive tests are performed to quantify the variability in stiffness and strength properties of these panels. Intra- and interpanel effects and correlations between random variables are studied using statistical methods. A range of probability distributions is tested and suggestions are made with regard to their suitability for modeling different mechanical and geometric properties.