Laboratory Evaluation of Critical Properties and Attributes of Calcined Bauxite and Steel Slag Aggregates for Pavement Friction Surfacing
Publication: Journal of Materials in Civil Engineering
Volume 31, Issue 8
Abstract
The long-term friction performance of safety-focused friction surfacing, especially high-friction surface treatment (HFST), relies primarily on the properties of aggregate. Nevertheless, inconsistencies exist in the properties and attributes and requirements for aggregates across the country. A study was conducted to evaluate the properties of the calcined bauxite and steel slag aggregates selected for HFST. Differences were identified between the British Standard (BS) and AASHTO test methods for aggregate abrasion and polishing. Laboratory tests were conducted to determine the mechanical, physical, chemical, and geometric properties of the selected aggregates. It was found that the Micro-Deval abrasion (MDA) test is a repeatable test. A size effect existed in both the abrasion and polishing tests. It was concluded that steel slag may be used as an alternative aggregate for friction surfacing. The requirements for aggregates for HFST were established in terms of the critical property attributes, particularly the Los Angeles abrasion (LAA), MDA, and polish value PV-10, which can be readily implemented by state Departments of Transportation.
Get full access to this article
View all available purchase options and get full access to this article.
Acknowledgments
This work was supported by the Joint Transportation Research Program (JTRP) administered by Indiana Department of Transportation and Purdue University. The authors would like to thank the study advisory committee members, including Bill Tompkins, Tim Wells, Mike Holowaty, Matt Beeson, Mike Prather, Scott Chandler, Chris Moore, Ed Spahr, Enass Zayed, and Rick Drum for their guidance. Special thanks are extended to Bob Rees and Bart Williamson for their assistance in laboratory testing. The authors recognize the help from Frank Julian, David Merritt, Doug Fromm, Patrick Malfitano, Georgia Eusner, George Wang, and Mike Blackwell.
References
AASHTO. 2012a. Standard method of test for resistance of coarse aggregate to degradation by abrasion in the Micro-Deval apparatus. AASHTO T327. Washington, DC: AASHTO.
AASHTO. 2012b. Standard method of test for surface frictional properties using the British pendulum tester. AASHTO T278-90. Washington, DC: AASHTO.
AASHTO. 2014a. Standard method of test for accelerated polishing of aggregates using the British wheel. AASHTO T279. Washington, DC: AASHTO.
AASHTO. 2014b. Standard practice for high friction surface treatment for asphalt and concrete pavements. AASHTO PP79. Washington, DC: AASHTO.
AASHTO. 2015. Standard method of test for resistance to degradation of small-size coarse aggregate by abrasion and impact in the Los Angeles machine. AASHTO T96-02. Washington, DC: AASHTO.
AASHTO. 2017. Standard method of test for uncompacted void content of fine aggregate. AASHTO T304. Washington, DC: AASHTO.
AASHTO. 2018. Sweet sixteen high value research projects. Washington, DC: AASHTO.
Alexanderm, M., and S. Mindess. 2005. Aggregates in concrete. New York: Talyor & Francis Group.
ASTM. 2013. Standard test method for total evaporable moisture content of aggregate by drying. ASTM C566. West Conshohocken, PA: ASTM.
ASTM. 2015. Standard practice for accelerated polishing of aggregates or pavement surfaces using a small-wheel, circular track polishing machine. ASTM E660-90. West Conshohocken, PA: ASTM.
ASTM. 2017. Standard test methods for sampling and testing fly ash or natural pozzolans for use in portland-cement concrete. ASTM C311/C311M. West Conshohocken, PA: ASTM.
ATSSA (American Traffic Safety Services Association). 2016. “High friction surfacing.” Accessed October 12, 2015. http://www.atssa.com/Resources/HighFrictionSurfacing/StateSpecifications.aspx.
BSI (British Standards Institution). 2009. Tests for mechanical and physical properties of aggregates-determination of the polished stone value. BS EN 1097-8. London: BSI.
BSI (British Standards Institution). 2011. Road and airfield surface characteristics-test methods Part 4: Method for measurement of slip/skid resistance of a surface: The pendulum test. BS EN 13036-4. London: BSI.
Cuelho, E., R. Mokwa, K. Obert, and A. Miller. 2008. “Comparative analysis of micro-Deval, L.A. abrasion, and sulfate soundness tests.” In Proc., TRB 87th Annual Meeting Compendium of Papers DVD. Washington, DC: Transportation Research Board of the National Academies.
Denning, J. H. 1977. High-performance surface dressing: 1. Road experiments with new thermoplastic binders. Crowthorne, UK: Transport and Road Research Laboratory.
FHWA (Federal Highway Administration). 2012. Every day counts: High friction surface treatments. Washington, DC: FHWA.
FHWA (Federal Highway Administration). 2016. “Pavement friction.” Accessed October 18, 2016. https://safety.fhwa.dot.gov/roadway_dept/pavement_friction.
Fowler, D., and M. Rached. 2012. “Polish resistance of fine aggregates in portland cement concrete pavements.” Transp. Res. Rec. 2267 (1): 29–36. https://doi.org/10.3141/2267-03.
GLM (Great Lake Minerals). 2015. GRIPgrain RD-88 Chinese calcined bauxite for high friction surface treatment. Wurtland, KY: Great Lake Minerals.
Heitzman, M., P. Turner, and M. Greer. 2015. High friction surface treatment alternative aggregates study. Auburn, AL: National Center for Asphalt Technology.
Hosking, J. R., and L. W. Tubey. 1972. Aggregates for resin-bound skid-resistant road surfacings. Crowthorn, UK: Transport and Road Research Laboratory.
INDOT (Indiana Department of Transportation). 2016. Standard specifications. Indianapolis, IN: INDOT.
Izeppi, E., G. Flintsch, and K. McGee. 2010. Field performance of high friction surfaces. Richmond, VA: Virginia Transportation Research Council.
James, J. G. 1971. Trial of epoxy resin/calcined-bauxite surface dressing on A1, Sandy, Bedfordshire, 1968. Crowthorne, UK: Transport and Road Research Laboratory.
Kandhal, P. S., and F. Parker, Jr. 1998. Aggregate tests related to asphalt concrete performance in pavements. Washington, DC: TRB.
Lewis, D. W. 1982. “Properties and uses of iron and steel slags.” In Proc., Symp. on Slag. Pretoria, South Africa: National Institute for Transport and Road Research.
Li, S., P. L. Cong, D. M. Yu, R. Xiong, and Y. Jiang. 2018. Laboratory and field evaluation of single layer and double layer high friction surface treatments. Washington, DC: Transportation Research Record.
Merritt, D. K., C. A. Lyon, and B. N. Persaud. 2015. Evaluation of pavement safety performance. Austin, TX: Transtec Group.
NDRC (National Development and Reform Commission). 2005. Ferrous metallurgy industry standard: Bauxite clinker. [In Chinese.] YB/T 5179-2005. Beijing: NDRC.
NVDOT (Nevada Department of Transportation). 2015. Section 497 thin bonded multilayer overlay. Carson City, NV: NVDOT.
Rangaraju, P. R., and J. Edlinski. 2008. “Comparative evaluation of micro-Deval abrasion test with other toughness/abrasion resistance and soundness tests.” J. Mater. Civ. Eng. 20 (5): 343–351. https://doi.org/10.1061/(ASCE)0899-1561(2008)20:5(343).
Rogers, C. A., and S. A. Senior. 1994. “Recent development in physical testing of aggregates to ensure durable concrete.” In Proc., Engineering Foundation Conf.: Advances in Cement and Concrete, 338–361. Reston, VA: ASCE.
Senior, S. A., and C. A. Rogers. 1991. “Laboratory tests for predicting coarse aggregate performance in Ontario.” J. Transp. Res. Rec. 1301: 97–106.
Stock, A. F., C. Ibberson, and I. F. Taylor. 1996. “Skidding characteristics of pavement surfaces incorporating steel slag aggregates.” J. Transport. Res. Rec. 1545 (1): 35–40. https://doi.org/10.1177/0361198196154500105.
Yildirim, I. Z., and M. Prezzi. 2009. Use of steel slag in subgrade applications. West Lafayette, IN: Indiana Dept. of Transportation, Purdue Univ.
Zhong, X. C., and G. P. Li. 1981. “Sintering characteristics of Chinese bauxites.” Ceram. Int. 7 (2): 65–68. https://doi.org/10.1016/0272-8842(81)90016-X.
Information & Authors
Information
Published In
Copyright
©2019 American Society of Civil Engineers.
History
Received: Nov 13, 2018
Accepted: Mar 4, 2019
Published online: May 25, 2019
Published in print: Aug 1, 2019
Discussion open until: Oct 25, 2019
Authors
Metrics & Citations
Metrics
Citations
Download citation
If you have the appropriate software installed, you can download article citation data to the citation manager of your choice. Simply select your manager software from the list below and click Download.