Abstract
The purpose of this study is to understand the complex mechanisms through which the active ingredients of crystalline waterproofing agents change the microstructure of cement-based materials. Microstructural and phase characterization are carried out on cement pastes modified with waterproofing agents through thermogravimetric analysis, scanning electron microscope with energy-dispersive x-ray spectroscopy, and x-ray microcomputed tomography. Two types are investigated—one that is applied onto the surface of existing concrete and another that is incorporated as an admixture into the fresh mix. Samples treated with the waterproofing agents are compared with a sample cured in sodium carbonate solution, one of the key active ingredients. Results indicate that both types of waterproofing agents lead to formation of calcium carbonate. The surface treatment type forms a dense coating, with little penetration into the matrix, whereas the admixture type leads to a measurable decrease in porosity throughout. The sample cured in sodium carbonate solution leads to an increase in porosity due to decalcification shrinkage, which underscores the importance of controlling sodium carbonate content to avoid excessive carbonation.
Get full access to this article
View all available purchase options and get full access to this article.
Acknowledgments
The authors acknowledge RPM Belgium Vandex for financial support, materials, and technical consultation. Also, the authors acknowledge the technical support by the staff of Columbia University’s Carleton Laboratory and City University of New York’s Advanced Science Research Center (CUNY ASRC).
References
Aıtcin, P. C. 2003. “The durability characteristics of high performance concrete: A review.” Cem. Concr. Compos. 25 (4): 409–420. https://doi.org/10.1016/S0958-9465(02)00081-1.
Al-Kheetan, M. J., M. M. Rahman, and D. A. Chamberlain. 2017. “Influence of early water exposure on modified cementitious coating.” Constr. Build. Mater. 141 (Jun): 64–71. https://doi.org/10.1016/j.conbuildmat.2017.02.159.
Al-Kheetan, M. J., M. M. Rahman, and D. A. Chamberlain. 2018. “A novel approach of introducing crystalline protection material and curing agent in fresh concrete for enhancing hydrophobicity.” Constr. Build. Mater. 160 (Jan): 644–652. https://doi.org/10.1016/j.conbuildmat.2017.11.108.
ASTM. 2014. Standard practice for mechanical mixing of hydraulic cement pastes and mortars of plastic consistency. ASTM C305. West Conshohocken, PA: ASTM.
Basheer, L., J. Kropp, and D. J. Cleland. 2001. “Assessment of the durability of concrete from its permeation properties: A review.” Constr. Build. Mater. 15 (2): 93–103. https://doi.org/10.1016/S0950-0618(00)00058-1.
Bentz, D. P., D. A. Quenard, H. M. Kunzel, J. Baruchel, F. Peyrin, N. S. Martys, and E. J. Garboczi. 2000. “Microstructure and transport properties of porous building materials. Part II: Three-dimensional X-ray tomographic studies.” Mater. Struct. 33 (3): 147–153. https://doi.org/10.1007/BF02479408.
Bertolini, L., B. Elsener, P. Pedeferri, E. Redaelli, and R. B. Polder. 2013. Corrosion of steel in concrete: Prevention, diagnosis, repair. New York: Wiley.
Biparva, A. 2015. “Integral crystalline waterproofing.” Structure 52 (Feb): 52–53.
Chen, J. J., J. J. Thomas, and H. M. Jennings. 2006. “Decalcification shrinkage of cement paste.” Cem. Concr. Res. 36 (5): 801–809. https://doi.org/10.1016/j.cemconres.2005.11.003.
Du Plessis, A., B. J. Olawuyi, W. P. Boshoff, and S. G. Le Roux. 2016. “Simple and fast porosity analysis of concrete using X-ray computed tomography.” Mater. Struct. 49 (1–2): 553–562. https://doi.org/10.1617/s11527-014-0519-9.
Elkey, W., and E. J. Sellevold. 1995. Electrical resistivity of concrete, 11–13. Oslo, Norway: Norwegian Road Research Laboratory.
Hilsdorf, H., and J. Kropp. 2014. Performance criteria for concrete durability. Boca Raton, FL: CRC Press.
Lafhaj, Z., M. Goueygou, A. Djerbi, and M. Kaczmarek. 2006. “Correlation between porosity, permeability and ultrasonic parameters of mortar with variable water/cement ratio and water content.” Cem. Concr. Res. 36 (4): 625–633. https://doi.org/10.1016/j.cemconres.2005.11.009.
Lim, S., and P. Mondal. 2014. “Micro- and nano-scale characterization to study the thermal degradation of cement-based materials.” Mater. Charact. 92 (Jun): 15–25. https://doi.org/10.1016/j.matchar.2014.02.010.
Martys, N. S., and C. F. Ferraris. 1997. “Capillary transport in mortars and concrete.” Cem. Concr. Res. 27 (5): 747–760. https://doi.org/10.1016/S0008-8846(97)00052-5.
McCarter, W. J., M. Emerson, and H. Ezirim. 1995. “Properties of concrete in the cover zone: Developments in monitoring techniques.” Mag. Concr. Res. 47 (172): 243–251. https://doi.org/10.1680/macr.1995.47.172.243.
Moon, H. Y., D. G. Shin, and D. S. Choi. 2007. “Evaluation of the durability of mortar and concrete applied with inorganic coating material and surface treatment system.” Constr. Build. Mater. 21 (2): 362–369. https://doi.org/10.1016/j.conbuildmat.2005.08.012.
Neithalath, N. 2006. “Analysis of moisture transport in mortars and concrete using sorption-diffusion approach.” ACI Mater. J. 103 (3): 209–217.
Papadakis, V. G., A. P. Roumeliotis, M. N. Fardis, and C. G. Vagenas. 1996. “Mathematical modelling of chloride effect on concrete durability and protection measures.” In Proc., Int. Conf. on Concrete Repair, Rehabilitation and Protection. Scotland, UK: Univ. of Dundee.
Ramezanianpour, A. A., and V. M. Malhotra. 1995. “Effect of curing on the compressive strength, resistance to chloride-ion penetration and porosity of concretes incorporating slag, fly ash or silica fume.” Cem. Concr. Compos. 17 (2): 125–133. https://doi.org/10.1016/0958-9465(95)00005-W.
Ramezanianpour, A. A., A. Pilvar, M. Mahdikhani, and F. Moodi. 2011. “Practical evaluation of relationship between concrete resistivity, water penetration, rapid chloride penetration and compressive strength.” Constr. Build. Mater. 25 (5): 2472–2479. https://doi.org/10.1016/j.conbuildmat.2010.11.069.
Reiterman, P., and J. Pazderka. 2016. “Crystalline coating and its influence on the water transport in concrete.” Adv. Civ. Eng. 2016: 8. https://doi.org/10.1155/2016/2513514.
Roig-Flores, M., F. Pirritano, P. Serna, and L. Ferrara. 2016. “Effect of crystalline admixtures on the self-healing capability of early-age concrete studied by means of permeability and crack closing tests.” Constr. Build. Mater. 114 (Jul): 447–457. https://doi.org/10.1016/j.conbuildmat.2016.03.196.
Saleem, M., M. Shameem, S. E. Hussain, and M. Maslehuddin. 1996. “Effect of moisture, chloride and sulphate contamination on the electrical resistivity of portland cement concrete.” Constr. Build. Mater. 10 (3): 209–214. https://doi.org/10.1016/0950-0618(95)00078-X.
Salman, M., Ö. Cizer, Y. Pontikes, R. M. Santos, R. Snellings, L. Vandewalle, B. Blanpain, and K. Van Balen. 2014. “Effect of accelerated carbonation on AOD stainless steel slag for its valorisation as a CO2-sequestering construction material.” Chem. Eng. J. 246 (Apr): 39–52. https://doi.org/10.1016/j.cej.2014.02.051.
Song, H. W., and S. J. Kwon. 2007. “Permeability characteristics of carbonated concrete considering capillary pore structure.” Cem. Concr. Res. 37 (6): 909–915. https://doi.org/10.1016/j.cemconres.2007.03.011.
Teng, L. W., R. Huang, J. Chen, A. Cheng, and H. M. Hsu. 2014. “A study of crystalline mechanism of penetration sealer materials.” Materials 7 (1): 399–412. https://doi.org/10.3390/ma7010399.
Information & Authors
Information
Published In
Copyright
©2019 American Society of Civil Engineers.
History
Received: Jan 10, 2018
Accepted: Jan 14, 2019
Published online: Jun 17, 2019
Published in print: Sep 1, 2019
Discussion open until: Nov 17, 2019
Authors
Metrics & Citations
Metrics
Citations
Download citation
If you have the appropriate software installed, you can download article citation data to the citation manager of your choice. Simply select your manager software from the list below and click Download.