Fatigue Performance of Tension Steel Plates Strengthened with Prestressed CFRP Laminates
Publication: Journal of Composites for Construction
Volume 14, Issue 5
Abstract
An experimental and analytical study was conducted to investigate the fatigue behavior of tension steel plates strengthened with prestressed carbon-fiber-reinforced polymer (CFRP) laminates. A simple fracture mechanics model was proposed to predict the fatigue life of reinforced specimens. Double-edge-notched specimens were precracked by fatigue loading and then strengthened by CFRP laminates at different prestressing levels. The effects of the applied stress range, CFRP stiffness, and prestressing level on the crack growth were investigated. Experimental results show that the increase of the prestressing level extends the fatigue life of a damaged steel plate to a large amount. The CFRP with the highest prestressing level performed best, prolonging fatigue life by as much as four times under 25% higher fatigue loading. Theoretically, predicted results were in a reasonable agreement with the experimental results. A parametric analysis was also performed to investigate the effects of the applied stress range and the prestressing level on the debonding behavior of the adhesive and on the secondary crack propagation.
Get full access to this article
View all available purchase options and get full access to this article.
References
Bassetti, A. (2001). “Lamelles Precontraintes en Fibres Carbone pour le Renforcement de Ponts Rivetes Endommaees par Fatigue.” Ph.D. thesis, Swiss Federal Institute of Technology, EPFL, Lausanne, Switzerland (in French).
Chen, J. F., and Teng, J. G. (2001). “Anchorage strength models for FRP and steel plates bonded to concrete.” J. Struct. Eng., 127(7), 784–791.
Colombi, P., Bassetti, A., and Nussbaumer, A. (2003a). “Analysis of cracked steel members reinforced by pre-stress composite patch.” Fatigue Fract. Eng. Mater. Struct., 26(5), 429–438.
Colombi, P., Bassetti, A., and Nussbaumer, A. (2003b). “Delamination effects on cracked steel members reinforced by prestressed composite patch.” Theor. Appl. Fract. Mech., 39(1), 61–71.
Elber, W. (1970). “Fatigue crack closure under cyclic tension.” Eng. Fract. Mech., 2, 37–45.
European Committee for Standardization (CEN). (2005). “Design of steel structures, part 1–9: Fatigue.” Eurocode 3, Brussels.
Hull, D. (1999). Fractography: Observing, measuring, and interpreting fracture surface topography, Cambridge University Press, Cambridge, U.K.
Jones, S. C., and Civjan, S. A. (2003). “Application of fiber reinforced polymer overlays to extend steel fatigue life.” J. Compos. Constr., 7(4), 331–338.
Newman, J. R. (1982). “Prediction fatigue crack growth under variable amplitude and spectrum loading using a closure model.” Design of fatigue and fracture resistant structure, ASTM STP 761, P. R. Abelkis and C. M. Hudson, eds., ASTM, West Conshohocken, Pa., 255–277.
Schijve, J. (1988). “Fatigue crack closure: Observations and technical significance: Mechanics of fatigue crack closure.” ASTM STP982, ASTM, West Conshohocken, Pa., 5–34.
Täljsten, B. et al. (2009). “Strengthening of old metallic structures in fatigue with prestressed and non-prestressed CFRP laminates.” Constr. Build. Mater., 23(4), 1665–1677.
Tavakkolizadeh, M., and Saadatmanesh, H. (2003). “Fatigue strength of steel girders strengthened with carbon fiber reinforced polymer patch.” J. Struct. Eng., 129(2), 186–196.
Information & Authors
Information
Published In
Copyright
© 2010 ASCE.
History
Received: Aug 21, 2009
Accepted: Jan 29, 2010
Published online: Feb 3, 2010
Published in print: Oct 2010
Authors
Metrics & Citations
Metrics
Citations
Download citation
If you have the appropriate software installed, you can download article citation data to the citation manager of your choice. Simply select your manager software from the list below and click Download.