Environmental Fatigue and Static Behavior of RC Beams Strengthened with Carbon-Fiber-Reinforced Polymer

Many countries around the world have tremendous needs to repair and strengthen their transportation infrastructure. Almost everywhere, traffic loads have reached levels largely exceeding design expectations. Northern countries also experience severe winter conditions that are combined with an extensive use of deicing salts and accelerate structural deterioration. In Canada, the extent of deterioration has prompted many authorities, including the federal and provincial governments, to investigate the potential use of fiber-reinforced polymer products to extend the life of their existing structures. However, it is widely recognized that the large-scale implementation of these products is often impaired by the lack of data on their durability. This paper presents an experimental project undertaken in order to assess the durability of reinforced concrete beams externally strengthened with two types of carbon-fiber-reinforced polymer (CFRP). The beams were first exposed to either wet-dry cycles or continuous immersion in water and then were loaded in fatigue. Finally, they were tested quasi-statically under four-point bending up to failure. The test results presented here provide some insights on the potential long-term performance of CFRP-strengthened beams exposed to severe environmental conditions.