Investigation of Corrosion Resistance and Interfacial Bonding Properties of Zn/Zn–Al Multilayer Coating/Steel Substrate System
Publication: Journal of Materials in Civil Engineering
Volume 33, Issue 1
Abstract
As an important mechanical property index, the interfacial bonding properties between coating and substrate are key factors in determining the corrosion resistance and reliability of the system. In this paper, the corrosion resistance performance and interfacial bonding properties of the Zn/Zn–Al multilayer coating/steel substrate system were studied. Neutral salt spray tests and electrochemical tests were conducted to evaluate the corrosion resistance of the coatings. Meanwhile, the three-point bending test with the acoustic emission (AE) technique was used to study the interfacial bonding properties of the multilayer coating/substrate systems. As a comparison, these tests were carried out on a Zn monolayer coating/substrate system and a Zn–Al monolayer coating/substrate system. The corrosion test results showed that the superposition of the Zn/Zn–Al coating/substrate system with different grain sizes hinders the transport path of corrosive ions, resulting in rust spots appearing later in the multilayer coating/substrate system than in the monolayer coating/substrate system. Given the increase in coating thickness, the defects, porosity, and corrosion through the holes of the coating increase, which aids in the corrosion process and reduces the corrosion resistance of the coating. The interfacial bonding strength of the system was analyzed using fracture toughness. The test results showed that the extent of the depreciation of the fracture toughness of the multilayer coating/substrate system before and after corrosion is lower than that of the monolayer coating/substrate systems. The interfacial bonding properties of the multilayer coating/substrate system are better than that of the monolayer coating/substrate systems because of the good material matching and dislocation effect between the multilayer coatings.
Get full access to this article
View all available purchase options and get full access to this article.
Data Availability Statement
Some or all of the data, models, or code that support the findings of this study are available from the corresponding author on reasonable request. The available items are as follows:
1.
Tafel curves of specimens;
2.
Elastic modulus of specimens; and
3.
Fracture toughness of specimens.
References
Barranco, V., S. Feliu Jr., and S. Feliu. 2004a. “EIS study of the corrosion behaviour of zinc-based coatings on steel in quiescent 3% NaCl solution. Part 1: Directly exposed coatings.” Corros. Sci. 46 (9): 2203–2220. https://doi.org/10.1016/j.corsci.2003.09.032.
Barranco, V., S. Feliu Jr., and S. Feliu. 2004b. “EIS study of the corrosion behaviour of zinc-based coatings on steel in quiescent 3% NaCl solution. Part 2: Coatings covered with an inhibitor-containing lacquer.” Corros. Sci. 46 (9): 2221–2240. https://doi.org/10.1016/j.corsci.2003.09.033.
Barton, S. C., G. W. Vermaas, P. F. Duby, A. C. West, and R. Betti. 2000. “Accelerated corrosion and embrittlement of high-strength bridge wire.” J. Mater. Civ. Eng. 12 (1): 33–38. https://doi.org/10.1061/(ASCE)0899-1561(2000)12:1(33).
Cheng, S., K. L. Wang, and G. M. Zhao. 2002. “Tribological properties of Ni/nano-SiC composite coatings.” J. Tsinghua Univ. 42 (4): 516–519.
Cheung, M. S., and W. C. Li. 2001. “Serviceability reliability of corroded steel bridges.” Can. J. Civ. Eng. 28 (3): 419–424. https://doi.org/10.1139/l01-007.
Djerourou, S., H. Lahmar, N. Bouhellal, and Y. Mebdoua. 2013. “Study of twin wire arc sprayed zinc/aluminum coating on low carbon steel substrate: Application to corrosion protection.” In Vol. 685 of Advanced materials research, 271–276. Zürich, Switzerland: Trans Tech Publications.
Esfahani, E. A., H. Salimijazi, M. A. Golozar, J. Mostaghimi, and L. Pershin. 2012. “Study of corrosion behavior of arc sprayed aluminum coating on mild steel.” J. Therm. Spray Technol. 21 (6): 1195–1202. https://doi.org/10.1007/s11666-012-9810-x.
Foley, R. T. 1986. “Localized corrosion of aluminum alloys—A review.” Corrosion 42 (5): 277–288. https://doi.org/10.5006/1.3584905.
Galvele, J. R. 2005. “Tafel’s law in pitting corrosion and crevice corrosion susceptibility.” Corros. Sci. 47 (12): 3053–3067. https://doi.org/10.1016/j.corsci.2005.05.043.
Guo, J., C. Shang, S. Yang, H. Guo, X. Wang, and X. He. 2009. “Weather resistance of low carbon high performance bridge steel.” Mater. Des. 30 (1): 129–134. https://doi.org/10.1016/j.matdes.2008.04.038.
Hou, B. R. 2007. “Corrosion behavior of iron and steel facilities in sea spray splash area and new coating protection technology.” [In Chinese.] Corros. Prot. 28 (4): 174–175.
Hwang, S. J. 1999. “The effect of grain size on the mechanical properties of NiAl produced by mechanical alloying.” J. Metastable Nanocryst. Mater. 2 (6): 581–586. https://doi.org/10.4028/www.scientific.net/JMNM.2-6.581.
Kim, H. S., Y. Estrin, and M. B. Bush. 2000. “Plastic deformation behavior of fine-grained materials.” Acta Mater. 48 (2): 493–504. https://doi.org/10.1016/S1359-6454(99)00353-5.
Liu, J. G., G. P. Gong, and C. W. Yan. 2005. “EIS study of corrosion behaviour of organic coating/Dacromet composite systems.” Electrochim. Acta 50 (16–17): 3320–3332.
Liu, W., L. M. Chang, and X. X. Ji. 2011. “Preparation and electrochemical performances of stainless steel-based lead dioxide-coated anodes.” [In Chinese.] Electroplating Finish. 30 (7): 1–4.
Maiti, S. K. 2015. “Fracture mechanics: Fundamentals and applications.” MRS Bull. 41 (8): 635–636.
Maledi, N. B., O. P. Oladijo, I. Botef, T. P. Ntsoane, A. Madiseng, and L. Moloisane. 2017. “Influence of cold spray parameters on the microstructures and residual stress of Zn coatings sprayed on mild steel.” Surf. Coat. Technol. 318 (May): 106–113. https://doi.org/10.1016/j.surfcoat.2017.03.062.
Mansfeld, F. 2005. “Tafel slopes and corrosion rates obtained in the pre-Tafel region of polarization curves.” Corros. Sci. 47 (12): 3178–3186. https://doi.org/10.1016/j.corsci.2005.04.012.
Markworth, A. J., and J. H. Saunders. 1995. “A model of structure optimization for a functionally graded material.” Mater. Lett. 22 (1): 103–107. https://doi.org/10.1016/0167-577X(94)00238-X.
McCafferty, E. 2005. “Validation of corrosion rates measured by the Tafel extrapolation method.” Corros. Sci. 47 (12): 3202–3215. https://doi.org/10.1016/j.corsci.2005.05.046.
Rahsepar, M., and M. E. Bahrololoom. 2009. “Study of surface roughness and corrosion performance of Ni/Zn–Fe and Zn–Fe/Ni compositionally modulated multilayer coatings.” Surf. Coat. Technol. 204 (5): 580–585. https://doi.org/10.1016/j.surfcoat.2009.08.036.
Sharifi, Y., and J. K. Paik. 2016. “Safety analysis of steel box girder bridges with pitting corrosion.” Adv. Steel Constr. 12 (4): 359–379.
Shu, C., B. Liu, and Y. Zhou. 2012. “Research on corrosion resistance of Zn–Al/rich-Al composite coatings in marine environment.” [In Chinese.] Surf. Technol. 41 (5): 56–59.
Sun, J. B., Y. Wang, and M. X. Lu. 2006. “Corrosion mechanism of arc spraying aluminum coatings in marine environment.” [In Chinese.] J. Univ. Sci. Technol. Beijing 28 (11): 1029–1033.
Tachibana, K., Y. Moriniga, and M. Mayuzumi. 2007. “Hot dip fine Zn and Zn–Al alloy double coating for corrosion resistance at coastal area.” Corros. Sci. 49 (1): 149–157. https://doi.org/10.1016/j.corsci.2006.05.015.
Tafreshi, M., S. R. Allahkaram, and H. Farhangi. 2016. “Comparative study on structure, corrosion properties and tribological behavior of pure Zn and different Zn-Ni alloy coatings.” Mater. Chem. Phys. 183 (Nov): 263–272. https://doi.org/10.1016/j.matchemphys.2016.08.026.
Voronin, N. A. 2010. “Composite, effective, and real hardnesses of thin coatings.” J. Frict. Wear 31 (4): 241–252. https://doi.org/10.3103/S106836661004001X.
Wang, Z. Y. 2010. “Experimental study of fracture toughness of rubber-steel bond interface.” [In Chinese.] Supplement, Chin. J. Solid Mech. 31 (S1): 204–208.
Xia, S. M., Y. F. Gao, A. F. Bower, L. C. Lev, and Y. T. Cheng. 2007. “Delamination mechanism maps for a strong elastic coating on an elastic–plastic substrate subjected to contact loading.” Int. J. Solids Struct. 44 (11–12): 3685–3699. https://doi.org/10.1016/j.ijsolstr.2006.10.009.
Xie, D., J. Hu, S. Tong, J. Wang, and J. Zhang. 2004. “Influence of zinc content and surface contamination on the electrochemical behaviors of epoxy zinc-rich primer.” [In Chinese.] Acta Metall. Sinica 40 (1): 103–108.
Yin, H. M., G. H. Paulino, and W. G. Buttlar. 2008. “An explicit elastic solution for a brittle coating with periodic cracks.” Int. J. Fract. 153 (1): 39–52. https://doi.org/10.1007/s10704-008-9286-3.
Zhang, G. P., Y. P. Li, and X. F. Zhu. 2009. “Deformation and fracture behavior of several metallic multilayers and mechanisms.” [In Chinese.] J. Nanjing Univ. 45 (2): 180–186.
Zhang, H., Q. Li, Y. Wang, M. Addae, B. T. Jibrin, and J. Yang. 2018a. “Mechanical properties of zinc-aluminum film on steel cable substrate in corrosion environment.” J. Constr. Steel Res. 150 (Nov): 288–297. https://doi.org/10.1016/j.jcsr.2018.08.013.
Zhang, H., J. Yang, J. Hu, X. Li, M. Li, and C. Wang. 2018b. “An experimental and simulation study of interface crack on zinc coating/304 stainless steel.” Constr. Build. Mater. 161 (Feb): 112–123. https://doi.org/10.1016/j.conbuildmat.2017.11.022.
Zhang, J. B., and X. G. Yang. 2011. “Application of multilayer petrolatum coated anti-corrosion technology to key parts of steel structure in a coastal power plant.” [In Chinese.] Corros. Prot. 32 (11): 896–899.
Zhang, X. Y., and J. Tan. 2015. “Mechanical and anti-corrosion properties of Ti/TiN multilayer films prepared by PVD.” Surf. Technol. 44 (12): 80–91. https://doi.org/10.1016/j.surfcoat.2015.08.005.
Zhao, Z. 2018. “Effects of tempering temperature on tensile properties and fracture behavior of 15Cr12MoVN steel.” [In Chinese.] Trans. Mater. Heat Treat. 39 (11): 74–79.
Zhou, W. J., L. K. Xu, and J. Wang. 2007. “Study on corrosion electrochemical behavior of silane coating with flaked.” [In Chinese.] Acta Metall. Sinica 43 (9): 983–988.
Information & Authors
Information
Published In
Copyright
© 2020 American Society of Civil Engineers.
History
Received: Nov 19, 2019
Accepted: Jun 23, 2020
Published online: Oct 21, 2020
Published in print: Jan 1, 2021
Discussion open until: Mar 21, 2021
Authors
Metrics & Citations
Metrics
Citations
Download citation
If you have the appropriate software installed, you can download article citation data to the citation manager of your choice. Simply select your manager software from the list below and click Download.