Fatigue Properties Investigation of Corroded High-Performance Steel Specimens
Publication: Journal of Materials in Civil Engineering
Volume 33, Issue 1
Abstract
Experiments were performed to investigate the fatigue properties of corroded high-performance steel (HPS). Ninety pieces of Q460D and 90 pieces of Q550E HPS specimens with five different corrosion levels were designed to investigate the effect of corrosion on their fatigue properties. Three-dimensional (3D) scanning and scanning electron microscope (SEM) were employed to observe the macroscopic and microscopic morphology. The curves in terms of various levels of corrosion damages were obtained, and the influences of different corrosion levels on the fatigue properties are discussed. The experimental results show that corrosion changes the characteristics of the fatigue crack source zone, crack development zone, critical transition zone, and instantaneous fracture zone. Compared with Q460D, the critical transition area of Q550E has a higher flatness. Progressing corrosion damage results in a linear decreasing fatigue life of the HPS specimens in the double logarithmic coordinate system. The fatigue life of steel specimens can be expressed as an exponential function of the cross-sectional corrosion loss level. The increasing stress level will aggravate the degradation of fatigue life.
Get full access to this article
View all available purchase options and get full access to this article.
Data Availability Statement
All data, models, and code generated or used during the study appear in the published article.
Acknowledgments
The study presented here was financially supported by the National Basic Research Program of China (973 Program, Grant No. 2015CB057701), the National Natural Science Foundation of China (Grant No. 51778068), and the Key Project of Hunan Provincial Education Department (18A136). This support is highly appreciated.
References
ASTM. 2003. Standard practice for preparing, cleaning, and evaluating corrosion test specimens. ASTM G1-03. West Conshohocken, PA: ASTM.
Austen, I. M., and P. McIntyre. 1979. “Corrosion fatigue of high-strength steel in low-pressure hydrogen gas.” Metal Sci. 13 (7): 420–428. https://doi.org/10.1179/msc.1979.13.7.420.
Bhandari, J., F. Khan, R. Abbassi, V. Garaniya, and R. Ojeda. 2015. “Modelling of pitting corrosion in marine and offshore steel structures—A technical review.” J. Loss Prev. Process Ind. 37 (Sep): 39–62. https://doi.org/10.1016/j.jlp.2015.06.008.
Dai, L., H. Bian, L. Wang, M. Potier-Ferry, and J. Zhang. 2020. “Prestress loss diagnostics in pretensioned concrete structures with corrosive cracking.” J. Struct. Eng. 146 (3): 04020013. https://doi.org/10.1061/(ASCE)ST.1943-541X.0002554.
Deng, L., W. Yan, and L. Nie. 2019. “A simple corrosion fatigue design method for bridges considering the coupled corrosion-overloading effect.” Eng. Struct. 178 (Jan): 309–317. https://doi.org/10.1016/j.engstruct.2018.10.028.
Dolley, E. J., B. Lee, and R. P. Wei. 2000. “The effect of pitting corrosion on fatigue life.” Fatigue Fract. Eng. Mater. 23 (7): 555–560. https://doi.org/10.1046/j.1460-2695.2000.00323.x.
El Maaddawy, T. A., and K. A. Soudki. 2003. “Effectiveness of impressed current technique to simulate corrosion of steel reinforcement in concrete.” J. Mater. Civ. Eng. 15 (1): 41–47. https://doi.org/10.1061/(ASCE)0899-1561(2003)15:1(41).
Feng, D. S. 2019. “Study on fatigue properties of Q345 steel after neutral salt spray corrosion.” [In Chinese.] Master thesis, China Univ. of Mining and Technology.
Heinilä, S., G. B. Marquis, and T. Björk. 2008. “Observations on fatigue crack paths in the corners of cold-formed high-strength steel tubes.” Eng. Fract. Mech. 75 (3): 833–844. https://doi.org/10.1016/j.engfracmech.2007.01.010.
Jiang, C., C. Wu, and X. Jiang. 2018. “Experimental study on fatigue performance of corroded high-strength steel wires used in bridges.” Constr. Build. Mater. 187 (Oct): 681–690. https://doi.org/10.1016/j.conbuildmat.2018.07.249.
Khurram, N., E. Sasaki, H. Kihira, H. Katsuchi, and H. Yamada. 2014. “Analytical demonstrations to assess residual bearing capacities of steel plate girder ends with stiffeners damaged by corrosion.” Struct. Infrastruct. Eng. 10 (1): 69–79. https://doi.org/10.1080/15732479.2012.697904.
Kim, I. T., M. J. Lee, J. H. Ahn, and S. Kainuma. 2013. “Experimental evaluation of shear buckling behaviors and strength of locally corroded web.” J. Constr. Steel Res. 83 (Apr): 75–89. https://doi.org/10.1016/j.jcsr.2012.12.015.
Langenberg, L. 2008. “Relation between design safety and Y/T ratio in application of welded high strength structural steels.” In Proc., Int. Symp. on Applications of High Strength Steels in Modern Constructions and Bridges-Relationship of Design Specifications. Beijing: China Steel Construction Society.
Li, S., Z. Zhang, E. Akiyama, K. Tsuzaki, and B. Zhang. 2010. “Evaluation of susceptibility of high strength steels to delayed fracture by using cyclic corrosion test and slow strain rate test.” Corros. Sci. 52 (5): 1660–1667. https://doi.org/10.1016/j.corsci.2010.02.005.
Martinez, L. L., A. Blom, H. Trogen, and T. Dahle. 1997. “Fatigue behavior of steels with strength levels between 350 and 900 MPa influence of post weld treatment under spectrum loading.” In Proc., North European Engineering and Science Conf. London: EMAS Publishing.
Miki, C., K. Homma, and T. Tominaga. 2002. “High strength and high performance steels and their use in bridge structures.” J. Constr. Steel Res. 58 (1): 3–20. https://doi.org/10.1016/S0143-974X(01)00028-1.
Mulligan, C. P., G. N. Vigilante, and J. J. Cannon. 2017. “Corrosion and fatigue behavior of high-strength steel treated with a Zn-alloy thermo-diffusion coating.” J. Mater. Eng. Perform. 26 (11): 5228–5236. https://doi.org/10.1007/s11665-017-2969-z.
Murtaza, G., and R. Akid. 2000. “Empirical corrosion fatigue life prediction models of a high strength steel.” Eng. Fract. Mech. 67 (5): 461–474. https://doi.org/10.1016/S0013-7944(00)00057-6.
Okayasu, M., K. Sato, K. Okada, S. Yoshifuji, and M. Mizuno. 2009. “Effects of atmospheric corrosion on fatigue properties of a medium carbon steel.” J. Mater. Sci. 44 (1): 306–315. https://doi.org/10.1007/s10853-008-3053-8.
Peng, J. X., L. F. Xiao, J. R. Zhang, C. S. Cai, and L. Wang. 2019. “Flexural behavior of corroded HPS beams.” Eng. Struct. 195: 274–287. https://doi.org/10.1016/j.engstruct.2019.06.006.
Pérez-Mora, R., T. Palin-Luc, C. Bathias, and P. C. Paris. 2015. “Very high cycle fatigue of a high strength steel under sea water corrosion: A strong corrosion and mechanical damage coupling.” Int. J. Fatigue 74 (May): 156–165. https://doi.org/10.1016/j.ijfatigue.2015.01.004.
Rahgozar, R., and Y. Sharifi. 2011. “Remaining fatigue life of corroded steel structural members.” Adv. Struct. Eng. 14 (5): 881–890. https://doi.org/10.1260/1369-4332.14.5.881.
Rusk, D. T., and W. Hoppe. 2009. “Fatigue life prediction of corrosion-damaged high-strength steel using an equivalent stress riser (ESR) model: Part I. Test development and results.” Int. J. Fatigue 31 (10): 1454–1463. https://doi.org/10.1016/j.ijfatigue.2009.05.006.
Rusk, D. T., W. Hoppe, W. Braisted, and N. Powar. 2009. “Fatigue life prediction of corrosion-damaged high-strength steel using an equivalent stress riser (ESR) model. Part II: Model development and results.” Int. J. Fatigue 31 (10): 1464–1475. https://doi.org/10.1016/j.ijfatigue.2009.06.008.
Schröter, F., and T. Lehnert. 2014. “Trends in the application of high-performance steel in European bridge building.” In Proc., 8th Int. Conf. Bridges in Danube Basin. Wiesbaden, Germany: Springer Fachmedien Wiesbaden.
Shi, G., H. Y. Ban, and Y. J. Shi. 2012. “Engineering application and recent research progress on high strength steel structures.” [In Chinese.] Ind. Constr. 42 (1): 1–164.
Shi, Y., and K. Xu. 2019. “Experimental and analytical study on local buckling behavior of high strength steel welded I-section beams.” Int. J. Steel Struct. 19 (4): 1171–1190. https://doi.org/10.1007/s13296-018-0196-6.
Shin, D. K., and K. Kim. 2019. “Flexural strength of composite HSB690 I-girders in negative moment.” Int. J. Steel Struct. 19 (6): 1875–1894. https://doi.org/10.1007/s13296-019-00251-1.
Standardization Administration of China. 2008. Metallic materials fatigue testing axial force controlled method. [In Chinese.] GB/T 3075-2008. Beijing: Standardization Administration of China.
Sun, Y., Y. Guo, Z. Chen, and W. Zhai. 2017. “Effect of differential ballast settlement on dynamic response of vehicle–track coupled systems.” Int. J. Struct. Stab. Dyn. 18 (07): 1850091. https://doi.org/10.1142/S0219455418500918.
Thomas, S. J., and C. J. Earls. 2003. “Cross-sectional compactness and bracing requirements for HPS483W girders.” J. Struct. Eng. 129 (12): 1569–1583. https://doi.org/10.1061/(ASCE)0733-9445(2003)129:12(1569).
Tohidi, S., and Y. Sharifi. 2016. “Load-carrying capacity of locally corroded steel plate girder ends using artificial neural network.” Thin Walled Struct. 100 (Mar): 48–61. https://doi.org/10.1016/j.tws.2015.12.007.
Wang, Y., G. Cheng, W. Wu, Q. Qiao, Y. Li, and X. Li. 2015. “Effect of pH and chloride on the micro-mechanism of pitting corrosion for high strength pipeline steel in aerated NaCl solutions.” Appl. Surf. Sci. 349 (Sep): 746–756. https://doi.org/10.1016/j.apsusc.2015.05.053.
Wu, Q., X. Chen, Z. Fan, D. Nie, and R. Wei. 2017. “Corrosion fatigue behavior of FV520B steel in water and salt-spray environments.” Eng. Fail. Anal. 79 (Sep): 422–430. https://doi.org/10.1016/j.engfailanal.2017.05.012.
Xiao, L. F., J. X. Peng, J. R. Zhang, and C. S. Cai. 2019. “Mechanical properties of corroded high performance steel specimens based on 3D scanning.” Adv. Steel Constr. 15 (2): 129–136. https://doi.org/10.18057/IJASC.2019.15.2.2.
Xiao, L. F., J. X. Peng, J. R. Zhang, Y. F. Ma, and C. S. Cai. 2020. “Comparative assessment of mechanical properties of HPS between electrochemical corrosion and spray corrosion.” Constr. Build. Mater. 237 (Mar): 117735. https://doi.org/10.1016/j.conbuildmat.2019.117735.
Xu, S. H., and Y. D. Wang. 2015. “Estimating the effects of corrosion pits on the fatigue life of steel plate based on the 3D profile.” Int. J. Fatigue 72 (Mar): 27–41. https://doi.org/10.1016/j.ijfatigue.2014.11.003.
Zhang, W. P., S. B. Li, X. L. Gu, and C. M. Zhu. 2009. “Experiment on axial tensile fatigue of naturally corroded steel bar.” [In Chinese.] China J. Highway Transp. 22 (2): 53–58.
Zheng, Y., and Y. Wang. 2019. “Damage evolution simulation and life prediction of high-strength steel wire under the coupling of corrosion and fatigue.” Corros. Sci. 164 (Mar): 108368. https://doi.org/10.1016/j.corsci.2019.108368.
Information & Authors
Information
Published In
Copyright
© 2020 American Society of Civil Engineers.
History
Received: Jan 3, 2020
Accepted: Jun 23, 2020
Published online: Oct 22, 2020
Published in print: Jan 1, 2021
Discussion open until: Mar 22, 2021
Authors
Metrics & Citations
Metrics
Citations
Download citation
If you have the appropriate software installed, you can download article citation data to the citation manager of your choice. Simply select your manager software from the list below and click Download.