Chloride Transport in Interfacial Zone of New–Old Concrete Joints of Precast Prestressed Concrete Bridges under Fatigue Load
Publication: Journal of Materials in Civil Engineering
Volume 34, Issue 10
Abstract
The interfacial zone of new–old concrete in precast concrete structure is the natural weak part in durability, and fatigue stress and an aggressive medium will accelerate the durability degradation of the interfacial zone. To study the chloride transport behavior in the interfacial zone of new–old concrete joints of precast prestressed bridges under the combined action of fatigue load and chloride penetration, a set of long-term (90–360 days) and low-frequency (0.3 Hz) experiments was carried out in this paper, where three fatigue stress ranges and four exposure durations were set as the main variables. The results indicated that the chloride content in the interfacial zone is higher than that present elsewhere, which shows the interfacial zone effect (IZE). By introducing the index of IZE, the influence laws of fatigue stress range and exposure duration on the IZE are revealed, namely as the fatigue stress range increases, the IZE first increases and then decreases, and as the exposure duration increases, the IZE decreases invariably. Moreover, the influence mechanism of fatigue stress range and exposure duration on the distribution and evolution of chloride concentration in the interfacial zone is analyzed. Considering the heterogeneous distribution of mesocomposition and internal defects (pores) in the interfacial zone of new–old concrete, the model of the chloride diffusion coefficient is established. Based on the relationship between volume strain and porosity, and the relationship between strain and specific crack area, a revised model of the effective chloride diffusion coefficient in the interfacial zone under fatigue stress is proposed. The accuracy of the revised model was verified by physical experiments.
Get full access to this article
View all available purchase options and get full access to this article.
Data Availability Statement
Some or all data, models, or code that support the findings of this study are available from the corresponding author upon reasonable request.
Acknowledgments
Financial support from the National Natural Science Foundation of China (NSFC) with Grant No. 51878656 and the Key Project of Research and Development Program of Jiangsu Province, China, with Grant No. BE2018636 are gratefully acknowledged.
References
Anna, H. 2011. “Influence new-to-old concrete interface qualities on the behaviour of support zones of composite concrete beams.” Constr. Build. Mater. 25 (10): 4072–4078. https://doi.org/10.1016/j.conbuildmat.2011.04.045.
Chen, X., S. Wu, and J. Zhou. 2013. “Influence of porosity on compressive and tensile strength of cement mortar.” Constr. Build. Mater. 40 (Mar): 869–874. https://doi.org/10.1016/j.conbuildmat.2012.11.072.
Chen, Z. 2020. Study on inhomogeneity of the physical state in interfacial zones between the new and old concrete in assembly structure. Jiangsu, China: China Univ. of Mining and Technology.
Du, X., L. Jin, and G. Ma. 2014. “A meso-scale numerical method for the simulation of chloride diffusivity in concrete.” Finite Elem. Anal. Des. 85 (Aug): 87–100. https://doi.org/10.1016/j.finel.2014.03.002.
Fan, J., L. Wu, and B. Zhang. 2021. “Influence of old concrete age, interface roughness and freeze-thawing attack on new-to-old concrete structure.” Materials 14 (5): 1057. https://doi.org/10.3390/ma14051057.
Gan, Y., H. Zhang, Y. Zhang, Y. Xu, E. Schlangen, K. van Breugel, and B. Šavija. 2021. “Experimental study of flexural fatigue behaviour of cement paste at the microscale.” Int. J. Fatigue 151 (Oct): 106378. https://doi.org/10.1016/j.ijfatigue.2021.106378.
Gao, Y., J. Zhang, S. Zhang, and Y. Zhang. 2017. “Probability distribution of convection zone depth of chloride in concrete in a marine tidal environment.” Constr. Build. Mater. 140 (Jun): 485–495. https://doi.org/10.1016/j.conbuildmat.2017.02.134.
Garboczi, E. J., and D. P. Bentz. 1992. “Computer simulation of the diffusivity of cement-based materials.” J. Mater. Sci. 27 (8): 2083–2092. https://doi.org/10.1007/BF01117921.
Gontar, W. A., J. P. Martin, and J. S. Popovics. 2000. “Effects of cyclic loading on chloride permeability of plain concrete.” Condition Monit. Mater. Struct. 2000 (1): 95–109. https://doi.org/10.1061/40495(302)8.
Halamickova, P., R. J. Detwiler, D. P. Bentz, and E. J. Garboczi. 1995. “Water permeability and chloride ion diffusion in Portland cement mortars: Relationship to sand content and critical pore diameter.” Cem. Concr. Res. 25 (4): 790–802. https://doi.org/10.1016/0008-8846(95)00069-O.
Hong, K., and R. D. Hooton. 2000. “Effects of fresh water exposure on chloride contaminated concrete.” Cem. Concr. Res. 30 (8): 1199–1207. https://doi.org/10.1016/S0008-8846(00)00335-5.
Ingrao, C., A. Lo Giudice, C. Mbohwa, and M. T. Clasadonte. 2014. “Life cycle inventory analysis of a precast reinforced concrete shed for goods storage.” J. Cleaner Prod. 79 (Sep): 152–167. https://doi.org/10.1016/j.jclepro.2014.05.030.
Ishida, T., P. O. Iqbal, and H. T. L. Anh. 2009. “Modeling of chloride diffusivity coupled with non-linear binding capacity in sound and cracked concrete.” Cem. Concr. Res. 39 (10): 913–923. https://doi.org/10.1016/j.cemconres.2009.07.014.
Issa, M. A., A. T. Idriss, I. I. Kaspar, and S. Y. Khayyat. 1995. “Full depth precast and precast, prestressed concrete bridge deck panels.” PCI J. 40 (1): 59–80. https://doi.org/10.15554/pcij.01011995.59.80.
Jang, S. Y., B. S. Kim, and B. H. Oh. 2011. “Effect of crack width on chloride diffusion coefficients of concrete by steady-state migration tests.” Cem. Concr. Res. 41 (1): 9–19. https://doi.org/10.1016/j.cemconres.2010.08.018.
Jiang, L., C. Li, C. Zhu, Z. Song, and H. Chu. 2017. “The effect of tensile fatigue on chloride ion diffusion in concrete.” Constr. Build. Mater. 151 (6): 119–126. https://doi.org/10.1016/j.conbuildmat.2017.06.090.
Kim, J. K., and Y. Y. Kim. 1996. “Experimental study of the fatigue behavior of high strength concrete.” Cem. Concr. Res. 26 (10): 1513–1523. https://doi.org/10.1016/0008-8846(96)00151-2.
Kreijger, P. C. 1984. “The skin of concrete composition and properties.” Mater. Struct. 17 (4): 275–283. https:// doi/10.1007/bf02479083.
Li, F., and X. Luo. 2019. “Interfacial zone effects of chloride penetration in precast concrete member joints.” Adv. Cem. Res. 31 (6): 279–289. https://doi.org/10.1680/jadcr.17.00211.
Li, F., X. Luo, K. Wang, and Y. Ji. 2017. “Pitting damage characteristics on prestressing steel strands by combined action of fatigue load and chloride corrosion.” J. Bridge Eng. 7 (22): 04017023. https://doi.org/10.1061/(ASCE)BE.1943-5592.0001057.
Li, F., Y. Yuan, and C. Li. 2011. “Corrosion propagation of prestressing steel strands in concrete subject to chloride attack.” Constr. Build. Mater. 25 (10): 3878–3885. https://doi.org/10.1016/j.conbuildmat.2011.04.011.
Li, G., H. Hu, and C. Ren. 2016. “Resistance of segmental joints to chloride ions.” ACI Mater. J. 113 (4): 471–481. https://doi.org/10.14359/51688931.
Li, G., H. Xie, and G. Xiong. 2001. “Transition zone studies of new-to-old concrete with different binders.” Cem. Concr. Res. 23 (4): 381–387. https://doi.org/10.1016/S0958-9465(01)00002-6.
Liu, F., and J. Zhou. 2017. “Research on fatigue strain and fatigue modulus of concrete.” Adv. Civ. Eng. 2017 (1): 1–7. https://doi.org/10.1155/2017/6272906.
Long, G. C., K. L. Ma, and Y. J. Xie. 2010. “Water sorptivity and permability of new-old concrete composite system.” Adv. Mater. Res. 163–167 (11): 3311–3319. https://doi.org/10.4028/www.scientific.net/AMR.163-167.3311.
Loo, Y. H. 1995. “Propagation of microcracks in concrete under uniaxial compression.” Mag. Concr. Res. 47 (170): 83–91. https://doi.org/10.1680/macr.1995.47.170.83.
Mien, T. V., B. Stitmannaithum, and T. Nawa. 2011. “Prediction of chloride diffusion coefficient of concrete under flexural cyclic load.” Comput. Concr. 8 (3): 343–355. https://doi.org/10.12989/cac.2011.8.3.343.
Peng, Z., and J. M. Zhongguo. 2010. “Selection of durable closure pour materials for accelerated bridge construction.” J. Bridge Eng. 15 (6): 695–704. https://doi.org/10.1061/(ASCE)BE.1943-5592.0000106.
Petcherdchoo, A. 2013. “Time dependent models of apparent diffusion coefficient and surface chloride for chloride transport in fly ash concrete.” Constr. Build. Mater. 38 (Jan): 497–507. https://doi.org/10.1016/j.conbuildmat.2012.08.041.
Ren, Y., Q. Huang, Q. Y. Liu, J. Z. Sun, and X. L. Liu. 2015. “Chloride ion diffusion of structural concrete under the coupled effect of bending fatigue load and chloride.” Mater. Res. Innovation 19 (1): 181–184. https://doi.org/10.1179/1432891715Z.0000000001400.
Shakouri, M., and D. Trejo. 2017. “A time-variant model of surface chloride build-up for improved service life predictions.” Cem. Concr. Compos. 84 (8): 99–110. https://doi.org/10.1016/j.cemconcomp.2017.08.008.
Shen, Y., J. Liu, S. Zhou, and G. Li. 2019. “Experimental investigation on the freeze-thaw durability of concrete under compressive load and with joints.” Constr. Build. Mater. 229 (Dec): 116893. https://doi.org/10.1016/j.conbuildmat.2019.116893.
Song, Z., L. Jiang, W. Li, C. Xiong, and H. Chu. 2016. “Impact of compressive fatigue on chloride diffusion coefficient in OPC concrete: An analysis using EIS method.” Constr. Build. Mater. 113 (Jun): 712–720. https://doi.org/10.1016/j.conbuildmat.2016.03.108.
Straatman, R., and J. N. J. A. Vambersky. 2001. “Precast construction and environment.” Struct. Concr. 2 (2): 93–98. https://doi.org/10.1680/stco.2001.2.2.93.
Udaipurwala, S. A. Y. 2013. Corrosion activity in precast concrete elements and cementitious closure pours. Reston, VA: ASCE. https://doi.org/10.1061(ASCE)BE.1943-5592.0000757.
von der Haar, C., and S. Marx. 2018. “A strain model for fatigue-loaded concrete.” Struct. Concr. 19 (2): 463–471. https://doi.org/10.1002/suco.201700029.
Wang, R., G. Zhao, and Y. Song. 1991. “Study on the fatigue performance of concrete under compressive stress.” [In Chinese.] China Civ. Eng. J. 4 (5): 38–47.
Wang, X., and L. Zheng. 2019. “Effect of different pre-exposure loading on chloride penetration in reinforced concrete specimens.” Int. J. Civ. Eng. 17 (7): 1075–1094. https://doi.org/10.1007/s40999-018-0359-z.
Wang, Y., L. Wu, Y. Wang, C. Liu, and Q. Li. 2018. “Effects of coarse aggregates on chloride diffusion coefficients of concrete and interfacial transition zone under experimental drying-wetting cycles.” Constr. Build. Mater. 185 (7): 230–245. https://doi.org/10.1016/j.conbuildmat.2018.07.049.
Winslow, D. N., M. D. Cohen, D. P. Bentz, K. A. Snyder, and E. J. Garboczi. 1994. “Percolation and pore structure in mortars and concrete.” Cem. Concr. Res. 24 (1): 25–37. https://doi.org/10.1016/0008-8846(94)90079-5.
Won, J., H. Kim, S. Lee, and S. Choi. 2015. “Carbon reduction of precast concrete under the marine environment.” Constr. Build. Mater. 74 (9): 118–123. https://doi.org/10.1016/j.conbuildmat.2014.09.074.
Wu, J., J. Xu, B. Diao, L. Jin, and X. Du. 2021. “Fatigue life prediction for the reinforced concrete (RC) beams under the actions of chloride attack and fatigue.” Eng. Struct. 242 (Sep): 112543. https://doi.org/10.1016/j.engstruct.2021.112543.
Wu, L., W. Li, and X. Yu. 2017. “Time-dependent chloride penetration in concrete in marine environments.” Constr. Build. Mater. 152 (Oct): 406–413. https://doi.org/10.1016/j.conbuildmat.2017.07.016.
Xiang, T., and R. Zhao. 2007. “Reliability evaluation of chloride diffusion in fatigue damaged concrete.” Eng. Struct. 29 (7): 1539–1547. https://doi.org/10.1016/j.engstruct.2006.09.002.
Yadav, I. N., and K. B. Thapa. 2020. “Fatigue damage model of concrete materials.” Theor. Appl. Fract. Mech. 108 (Aug): 102578. https://doi.org/10.1016/j.tafmec.2020.102578.
Yang, C. C., and S. W. Cho. 2003. “Influence of aggregate content on the migration coefficient of concrete materials using electrochemical method.” Mater. Chem. Phys. 80 (3): 752–757. https://doi.org/10.1016/S0254-0584(03)00112-3.
Yang, C. C., and J. K. Su. 2002. “Approximate migration coefficient of interfacial transition zone and the effect of aggregate content on the migration coefficient of mortar.” Cem. Concr. Res. 32 (10): 1559–1565. https://doi.org/10.1016/S0008-8846(02)00832-3.
Yang, T., B. Guan, G. Liu, and Y. Jia. 2019. “Modeling of chloride ion diffusion in concrete under fatigue loading.” KSCE J. Civ. Eng. 23 (1): 287–294. https://doi.org/10.1007/s12205-018-0403-1.
Zhao, J., F. Li, and X. Luo. 2020. “Influence of compressive stress on chloride transport in the interfacial zone of precast and cast-in-place concrete.” Struct. Concr. 22 (5): 2624–2635. https://doi.org/10.1002/suco.201900147.
Zhou, J. H., Y. X. Zhang, X. H. Meng, and Y. Liu. 2011. “Research on residual strength of concrete under fatigue loading and corrosion of chloride.” Appl. Mech. Mater. 94–96 (1): 1369–1372. https://doi.org/10.4028/www.scientific.net/AMM.94-96.1369.
Zuo, S., J. Xiao, and Q. Yuan. 2020. “Comparative study on the new-old mortar interface deterioration after wet-dry cycles and heat-cool cycles.” Constr. Build. Mater. 244 (May): 118374. https://doi.org/10.1016/j.conbuildmat.2020.118374.
Information & Authors
Information
Published In
Copyright
© 2022 American Society of Civil Engineers.
History
Received: Aug 31, 2021
Accepted: Jan 31, 2022
Published online: Jul 22, 2022
Published in print: Oct 1, 2022
Discussion open until: Dec 22, 2022
Authors
Metrics & Citations
Metrics
Citations
Download citation
If you have the appropriate software installed, you can download article citation data to the citation manager of your choice. Simply select your manager software from the list below and click Download.