Preparation and Properties of Silicon-Modified Epoxy Grouting Material for Repairing Microcracks
Publication: Journal of Materials in Civil Engineering
Volume 34, Issue 3
Abstract
To improve the performance of epoxy grouting materials and achieve better repair of microcracks in cast-in-place concrete bridge deck pavements, polydimethylsiloxane (PDMS) and diluent were used to modify epoxy resin. The mechanical properties of silicon-modified epoxy grouting materials produced using different preparation processes were analyzed, and the best preparation process was optimized. The working performance of silicon-modified epoxy grouting material was determined, and the environmental adaptability before and after composite modification was explored. The results showed that the suitable reaction temperature, time, and PDMS content are 100°C, 3 min, and 8%, respectively. The higher the temperature, the better was the groutability and the shorter was the curing time. Therefore, the construction temperature should be at least 35°C. The impact resistance and strength of the grouting materials were improved significantly after the addition of PDMS. In addition, the strength essentially was formed after 5 days. This indicates that the curing age is 5 days. Silicon-based modified epoxy grouting materials have good environmental adaptability. After thermal shock, 30-day temperature variation treatment, and 30 freeze–thaw cycles, the flexibility and bonding properties of the materials were excellent, and were much higher than those of the unmodified materials. Although the tensile strength was slightly lower than that of the unmodified materials, it still remained at about 60 MPa.
Get full access to this article
View all available purchase options and get full access to this article.
Data Availability Statement
The data used to support the findings of this study are included within the article.
Acknowledgments
This research was sponsored by the Key Research and Development Project in Shaanxi Province (2021GY-206), the Fundamental Research Funds for the Central Universities (300102219314), and Science and Technology Projects of Shanxi Transportation Holdings Group (20-JKKJ-36).
References
Aghaeipour, A., and M. Madhkhan. 2020. “Effect of ground granulated blast furnace slag (GGBFS) on mechanical properties of roller-compacted concrete pavement.” J. Test. Eval. 48 (4): 2786–2802. https://doi.org/10.1520/JTE20170786.
Charles, A. D. M., and A. N. Rider. 2018. “Triblock copolymer toughening of a carbon fibre-reinforced epoxy composite for bonded repair.” Polymers 10 (8): 888. https://doi.org/10.3390/polym10080888.
Chen, Q., Y. F. Lu, C. H. Wang, B. Han, and H. Fu. 2020. “Effect of raw material composition on the working performance of waterborne epoxy resin for road.” Int. J. Pavement Eng. 2020 (10): 1–12. https://doi.org/10.1080/10298436.2020.1856842.
Chen Q., C. H. Wang, H. Fu, and G. L. Yang. 2021. “Optimization of construction method of waterborne epoxy asphalt cape seal based on performance evolution.” [In Chinese.] China J. Highway Transport 34 (7): 236–245. https://doi.org/10.19721/j.cnki.1001-7372.2021.07.019.
Chhetri, S., N. C. Adak, P. Samanta, P. K. Mallisetty, N. C. Murmu, and T. Kuila. 2018. “Interface engineering for the improvement of mechanical and thermal properties of covalent functionalized graphene/epoxy composites.” J. Appl. Polym. Sci. 135 (15): 46124. https://doi.org/10.1002/app.46124.
Code of China. 1993. Plastics—Determination of Charpy impact strength of rigid materials. [In Chinese.] GB/T 1043-1993. Beijing: The State Bureau of Technical Supervision, Standards Press of China.
Code of China. 1999. Determination for freeze-thaw resistance of film of building coatings. [In Chinese.] JG/T 25-1999. Beijing: Ministry of Urban and Rural Construction and Environmental Protection of the People’s Republic of China, China Architecture and Building Press.
Code of China. 2006. Epoxy resin flooring coating. [In Chinese.] JC/T 1015-2006. Beijing: National Development and Reform Commission of the People’s Republic of China, Standards Press of China.
Code of China. 2007. Epoxy grouting resin for concrete crack. [In Chinese.] JC/T 1041-2007. Beijing: National Development and Reform Commission, China Building Materials Press.
Code of China. 2008a. Test method for properties of resin casting body. [In Chinese.] GB/T 2567-2008. Beijing: General Administration of Quality Supervision, Inspection and Quarantine of the People’s Republic of China, Standardization Administration, Standards Press of China.
Code of China. 2008b. Test methods for building waterproofing coatings. [In Chinese.] GB/T 16777-2008. Beijing: General Administration of Quality Supervision, Inspection and Quarantine of the People’s Republic of China, Standardization Administration, Standards Press of China.
Code of China. 2013. Determination for viscosity of adhesives: Single-cylinder rotational viscometer method. [In Chinese.] GB/T 2794-2013. Beijing: General Administration of Quality Supervision, Inspection and Quarantine of the People’s Republic of China, Standardization Administration, Standards Press of China.
Editorial Department of China Journal of Highway and Transport. 2020. “Review on China’s pavement engineering research.” [In Chinese.] China J. Highway Transp. 33 (10): 1–66. https://doi.org/10.19721/j.cnki.1001-7372.2020.10.001.
Fathalla, E., Y. Tanaka, and K. Maekawa. 2019. “Effect of crack orientation on fatigue life of reinforced concrete bridge decks.” Appl. Sci. 9 (8): 1644. https://doi.org/10.3390/app9081644.
Fu, H., C. H. Wang, G. X. Yu, Q. Chen, and L. Q. Liu. 2021. “Design optimization and performance evaluation of the open-graded friction course with small particle size aggregate.” Adv. Civ. Eng. 2021 (Feb): 6668378. https://doi.org/10.1155/2021/6668378.
Guo, H. Y., J. Gu, Z. W. Ran, Y. Bao, and Q. H. Pu. 2020. “Flexural behaviors of full-scale prestressed high-performance concrete box girders.” Struct. Eng. Mech. 75 (5): 595–605. https://doi.org/10.12989/sem.2020.75.5.595.
Kaur, N. P., S. Majhi, N. K. Dhami, and A. Mukherjee. 2020. “Healing fine cracks in concrete with bacterial cement for an advanced non-destructive monitoring.” Constr. Build. Mater. 242 (May): 118151. https://doi.org/10.1016/j.conbuildmat.2020.118151.
Lee, B. J., and Y. Y. Kim. 2018. “Durability of latex modified concrete mixed with a shrinkage reducing agent for bridge deck pavement.” Int. J. Concr. Struct. Mater. 12 (1): 1–9. https://doi.org/10.1186/s40069-018-0261-8.
Li Y., J. F. Deng, S. Y. Yu, Z. Y. Sun, Q. H. Rao, and Z. Y. Mei. 2019. “Study on properties of epoxy resin modified with 669 diluent extended with urethane linkage.” [In Chinese.] Polym. Bull. 2019 (11): 33–39. https://doi.org/10.14028/j.cnki.1003-3726.2019.11.004.
Liu M. H., C. Li, and Z. Y. Liu. 2013. “Performance of epoxy resin/polyamide-amine curing agent system using epoxy cyclohexene as reactive diluents.” [In Chinese.] J. Central South Univ. (Sci. Technol.) 44 (2): 520–525.
Okumus, P., and M. D. Arancibia. 2020. “Sources, mitigation and implications of skew-related concrete deck cracks in girder bridges.” Struct. Infrastruct. Eng. 2020 (574): 1–14. https://doi.org/10.1080/15732479.2020.1818794.
Putri, P. Y., I. Ujike, N. Sandra, F. Rifwan, and T. Andayono. 2020. “Calcium carbonate in bio-based-material and factor affecting its precipitation rate for repairing concrete.” Crystals 10 (10): 883. https://doi.org/10.3390/cryst10100883.
Shim, C., and C. Lee. 2020. “Crack width control of precast deck loop joints for continuous steel-concrete composite girder bridges.” Adv. Concr. Constr. 10 (1): 21–34. https://doi.org/10.12989/acc.2020.10.1.021.
Su, H., R. Li, and M. Yang. 2020. “An experimental study of modified physical performance test of low-temperature epoxy grouting material for grouting joints with tenon and mortise.” J. Intell. Manuf. 32 (3): 667–677. https://doi.org/10.1007/s10845-020-01664-0.
Su, Z., Z. Wang, D. Zhang, and W. Tao. 2019. “Study on rheological behavior and surface properties of epoxy resin chemical grouting material considering time variation.” Materials 12 (20): 3277. https://doi.org/10.3390/ma12203277.
Sun, X., L. Miao, L. Wu, C. Wang, and R. Chen. 2020a. “The method of repairing microcracks based on microbiologically induced calcium carbonate precipitation.” Adv. Cem. Res. 32 (6): 262–272. https://doi.org/10.1680/jadcr.18.00121.
Sun, Y., G. X. Chen, Q. Z. Wu, and J. Y. Feng. 2020b. “Properties of epoxy resin modified by epoxy-terminated silicone.” J. Mater. Sci. Eng. 38 (5): 722–770. https://doi.org/10.14136/j.cnki.issn1673-2812.2020.05.006.
Wang, C., Q. Chen, T. Guo, and Q. Li. 2020. “Environmental effects and enhancement mechanism of graphene/tourmaline composites.” J. Cleaner Prod. 262 (Jul): 121313. https://doi.org/10.1016/j.jclepro.2020.121313.
Wang, C., Z. Fan, C. Li, H. Zhang, and X. Xiao. 2021a. “Preparation and engineering properties of low-viscosity epoxy grouting materials modified with silicone for microcrack repair.” Constr. Build. Mater. 290 (Jul): 123270. https://doi.org/10.1016/j.conbuildmat.2021.123270.
Wang, C., S. Wang, Z. Gao, and Z. Song. 2021b. “Effect evaluation of road piezoelectric micro-energy collection-storage system based on laboratory and on-site tests.” Appl. Energy 287 (Apr): 116581. https://doi.org/10.1016/j.apenergy.2021.116581.
Wang, C., X. Xiao, Y. Lu, C. Shu, and J. Guo. 2019. “Utilization and properties of modified epoxy resin for colorful anti-slip pavements.” Constr. Build. Mater. 227 (Dec): 116801. https://doi.org/10.1016/j.conbuildmat.2019.116801.
Wang, W., W. Zhao, J. Zhang, and J. Zhou. 2021c. “Epoxy-based grouting materials with super-low viscosities and improved toughness.” Constr. Build. Mater. 267 (18): 121104. https://doi.org/10.1016/j.conbuildmat.2020.121104.
Xiao X. D. 2020. Study on preparation and properties of grouting material with low viscosity for the micro cracks of the cast-in-situ concrete of pavement on deck bridge. [In Chinese.] Xi’an, China: Chang’an Univ.
Yang, G. L., C. H. Wang, H. Fu, and Z. B. Yan. 2019. “Waterborne epoxy resin–polyurethane–emulsified asphalt: Preparation and properties.” J. Mater. Civ. Eng. 31 (11): 04019265. https://doi.org/10.1061/(ASCE)MT.1943-5533.0002904.
Ying, W. B., H. S. Yang, D. S. Moon, M. W. Lee, N. Y. Ko, N. H. Kwak, B. Lee, J. Zhu, and R. Zhang. 2018. “Epoxy resins toughened with in situ azide–alkyne polymerized polysulfones.” J. Appl. Polym. Sci. 135 (5): 45790. https://doi.org/10.1002/app.45790.
You, X. Z., Y. G. Wang, J. Z. Zhao, M. Xia, and F. Tong. 2014. “Preparation and properties study of epoxy-modified silicone resin.” Inst. Mater. 47 (1): 66–68. https://doi.org/10.16790/j.cnki.1009-9239.im.2014.01.018.
Zhang, X., X. Lu, L. Qiao, L. Jiang, T. Cao, and Y. Zhang. 2019. “Developing an epoxy resin with high toughness for grouting material via co-polymerization method.” e-Polymers 19 (1): 489–498. https://doi.org/10.1515/epoly-2019-0052.
Zhang, Z. Y., C. H. Wang, L. Zhang, S. Wang, and W. Zeng. 2018. “Construction and assessment technology of green road in China.” [In Chinese.] J. Chang’an Univ. (Nat. Sci. Ed.) 38 (5): 76–86.
Zhao, X. Y., and S. F. Wang. 2018. “Thermal, mechanical properties and morphology of epoxy resins modified with light pyrolysis natural rubber.” Adv. Polym. Technol. 37 (7): 2541–2551. https://doi.org/10.1002/adv.21929.
Zhu, Y. X., Y. Cao, M. H. Wu, and Y. Wang. 2016. “Research and application of micro-cracks grouting material used on ballastless track of high speed railway.” J. Wuhan Univ. Technol. 38 (6): 32–38. https://doi.org/10.3963/j.issn.1671-4431.2016.06.006.
Information & Authors
Information
Published In
Copyright
© 2021 American Society of Civil Engineers.
History
Received: Feb 14, 2021
Accepted: Jul 20, 2021
Published online: Dec 24, 2021
Published in print: Mar 1, 2022
Discussion open until: May 24, 2022
Authors
Metrics & Citations
Metrics
Citations
Download citation
If you have the appropriate software installed, you can download article citation data to the citation manager of your choice. Simply select your manager software from the list below and click Download.
Cited by
- Jun Yao, Di Feng, Zhikui Wang, Chengcheng Peng, Yonggang Zhang, Lei Han, Experimental Study on Performance of Modified Cement-Based Building Materials under High-Water-Pressure Surrounding Rock Environment, Coatings, 10.3390/coatings13030501, 13, 3, (501), (2023).
- Dayang Xuan, Mingwei Zhang, Jian Li, Zebin Dong, Aimaiti Alimu, Jialin Xu, Experimental Study on the Diffusion Radius of Modified Slurry Used in Longwall Overburden Isolated Grouting, Geofluids, 10.1155/2023/7195779, 2023, (1-11), (2023).
- Zhentong Fan, Chaohui Wang, Haowen Xue, Ke Yi, SiTuo Liu, Rheological Properties of Epoxy-Grouting Materials for Early Cracks of Cast-In-Situ Concrete on Bridge Deck, Journal of Materials in Civil Engineering, 10.1061/JMCEE7.MTENG-15554, 35, 9, (2023).
- Penghui Wen, Chaohui Wang, Ming Chen, Zhi Chai, Engineering Property Evaluation and Multiobjective Parameter Optimization of Argillaceous Gangue–Filled Subgrade Based on Grey Relational Analysis, Journal of Materials in Civil Engineering, 10.1061/(ASCE)MT.1943-5533.0004674, 35, 4, (2023).
- Luqing Liu, Chaohui Wang, Qing Liang, Feng Chen, Xiaolei Zhou, A state-of-the-art review of rubber modified cement-based materials: Cement stabilized base, Journal of Cleaner Production, 10.1016/j.jclepro.2023.136270, 392, (136270), (2023).
- Lu Zhou, Dan Zhang, Xiaogang Li, Zhiwei Gao, Qian Chen, Chaohui Wang, Overview: Application of Resin Waterproof Adhesive Materials in Bridge Deck Pavement in China, Advances in Civil Engineering, 10.1155/2022/2320374, 2022, (1-15), (2022).
- Penghui Wen, Chaohui Wang, Xuan Gao, Ming Chen, Zhi Chai, Effect of environmental factors on mechanical properties and damage characteristics of mine overburden used in subgrade, International Journal of Pavement Engineering, 10.1080/10298436.2022.2032698, (1-14), (2022).
- Hao Fu, Chaohui Wang, Daotuan Wang, Qian Chen, Dan Zhang, Shuai Huang, Songyuan Tan, Durability evaluation of mechanical and bonding properties of polyurethane-modified waterborne epoxy resin for road, International Journal of Pavement Engineering, 10.1080/10298436.2022.2027419, (1-14), (2022).
- Luqing Liu, Chaohui Wang, Qing Liang, Preparation of a heat insulation bonding layer for roads and its heat insulation effect, Journal of Cleaner Production, 10.1016/j.jclepro.2022.132828, 365, (132828), (2022).
- Chaohui Wang, Kaixi Duan, Liang Song, Xiaoping Ji, Cheng Shu, Stability improvement technology of SBS/crumb rubber composite modified asphalt from Xinjiang China, Journal of Cleaner Production, 10.1016/j.jclepro.2022.132003, 359, (132003), (2022).
- See more