Role of Supplementary Cementitious Material Type in the Mitigation of Calcium Oxychloride Formation in Cementitious Pastes
Publication: Journal of Materials in Civil Engineering
Volume 30, Issue 10
Abstract
Premature deterioration has been observed at some joints in concrete pavements. This joint damage has been attributed, in part, to a deleterious chemical reaction between chloride-based deicing salts (e.g., calcium chloride) and calcium hydroxide from the cementitious matrix resulting in the formation of a compound referred to as calcium oxychloride. Calcium oxychloride formation can be mitigated in cementitious pastes through the replacement of cement with supplementary cementitious materials (SCMs) (e.g., fly ash or slag). Although various SCMs are beneficial in mitigating the formation of calcium oxychloride, little has been written to describe similarities or differences between the different types of SCMs relating to their ability to mitigate calcium oxychloride formation. This paper compares various SCM types. Cementitious pastes were prepared with between 0 and 60% of the cement being replaced (by volume) with SCMs for water-to-cementitious materials ratios () of 0.36 and 0.50, which are the lower and upper bounds of the w/cm typically used for pavements and sidewalks. Pastes were cured to develop a high degree of hydration, and subsequently ground to a fine powder for use in thermogravimetric analysis and low temperature differential scanning calorimetry testing to quantify the calcium hydroxide and calcium oxychloride amounts, respectively. The composition of the specific fly ash and slag used influences the calcium hydroxide and calcium oxychloride amounts. As the w/cm increases, calcium hydroxide and calcium oxychloride amounts increase; however, this amount was only between 4 and 30% for the calcium hydroxide and various SCMs. As the volume of supplementary cementitious materials replacing the cement increases, calcium hydroxide and calcium oxychloride amounts decrease. The supplementary cementitious materials reduce the calcium hydroxide and calcium oxychloride formed in the order calcined clay silica fume fly ash slag limestone. The contributions of the SCMs to reducing calcium hydroxide (CH) and calcium oxychloride (CAOXY) due to dilution and reaction are separated. The potential benefits of different SCMs in reducing calcium hydroxide amounts in paste can be predicted based on their pozzolanicity (determined from their response in pozzolanic tests based on isothermal calorimetry and thermogravimetric analysis).
Get full access to this article
View all available purchase options and get full access to this article.
Acknowledgments
The authors acknowledge funding from Indiana Department of Transportation (INDOT) as a part of the Joint Transportation Research Program (JTRP) through SPR 3864. Additional funding from the Portland Cement Association (PCA) Foundation and National Ready Mixed Concrete Association (NRMCA) Foundation is also acknowledged. The authors thank Mitchell Keys, Naomi Salgado, and Hunter Carolan for help in carrying out some of the experiments reported here.
References
ASTM. 2018. Standard specification for slag cement for concrete and mortars. ASTM C989. West Conshohocken, PA: ASTM.
Bentz, D. P., T. Sato, I. de la Varga, and W. J. Weiss. 2012. “Fine limestone additions to regulate setting in high volume fly ash mixtures.” Cem. Concr. Compos. 34 (1): 11–17. https://doi.org/10.1016/j.cemconcomp.2011.09.004.
Berodier, E., and K. Scrivener. 2014. “Understanding the filler effect on the nucleation and growth of C-S-H.” J. Am. Ceram. Soc. 97 (12): 3764–3773. https://doi.org/10.1111/jace.13177.
Chatterji, S. 1978. “Mechanism of the attack on portland cement concrete.” Cem. Concr. Res. 8 (4): 461–467. https://doi.org/10.1016/0008-8846(78)90026-1.
Collepardi, M., L. Coppola, and C. Pistolesi. 1994. “Durability of concrete structures exposed to based deicing salts.” In Proc., 3rd CANMENT/ACI Int. Conf. 107–120. Farmington Hills, MI: American Concrete Institute.
Durdzinski, P., et al. 2017. “Outcomes of the RILEM round robin on degree of reaction of slag and fly ash in blended cements.” Mater. Struct. 50 (2): 135. https://doi.org/10.1617/s11527-017-1002-1.
Farnam, Y., D. Bentz, A. Hampton, and W. J. Weiss. 2014. “Acoustic emission and low-temperature calorimetry study of freeze and thaw behavior in cementitious materials exposed to sodium chloride salt.” Transp. Res. Rec. 2441: 81–90. https://doi.org/10.3141/2441-11.
Farnam, Y., S. Dick, A. Wiese, J. Davis, D. Bentz, and W. J. Weiss. 2015. “The influence of calcium chloride deicing salt on phase changes and damage development in cementitious materials.” Cem. Concr. Compos. 64 (Nov): 1–15. https://doi.org/10.1016/j.cemconcomp.2015.09.006.
Galan, I., L. Perron, and F. P. Glasser. 2015. “Impact of chloride-rich environments on cement paste mineralogy.” Cem. Concr. Res. 68 (Feb): 174–183. https://doi.org/10.1016/j.cemconres.2014.10.017.
Gutteridge, W. A., and J. A. Dalziel. 1990. “Filler cement: The effect of the secondary component on the hydration of portland cement. I: A fine non-hydraulic filler.” Cem. Concr. Res. 20 (5): 778–782. https://doi.org/10.1016/0008-8846(90)90011-L.
Haynes, H., R. O’Neill, and P. K. Mehta. 1996. “Concrete deterioration from physical attack by salts.” Concr. Int. 18 (1): 63–68.
Jones, W., Y. Farnam, P. Imbrock, J. Spiro, C. Villani, M. Golias, J. Olek, and W. J. Weiss. 2013. An overview of joint deterioration in concrete pavement: Mechanisms, solution properties, and sealers. West Lafayette, IN: Purdue Univ.
Kim, T., and J. Olek. 2012. “Effects of sample preparation and interpretation of thermogravimetric curves on calcium hydroxide in hydrated pastes and mortars.” Transp. Res. Rec. 2290: 10–18. https://doi.org/10.3141/2290-02.
Lumley, J. S., R. S. Gollop, G. K. Moir, and H. F. W. Taylor. 1996. “Degrees of reaction of the slag in some blends with portland cements.” Cem. Concr. Res. 26 (1): 139–151. https://doi.org/10.1016/0008-8846(95)00190-5.
Monical, J., E. Unal, T. Barrett, Y. Farnam, and W. J. Weiss. 2016. “Reducing joint damage in concrete pavements: Quantifying calcium oxychloride formation.” Transp. Res. Rec. 2577: 17–24. https://doi.org/10.3141/2577-03.
Mori, H., R. Kuga, S. Ogawa, and Y. Kubo. 2013. “Chemical deterioration of hardened cement pastes immersed in calcium chloride solution.” In Proc., 3rd Int. Conf. on Sustainable Construction Materials and Technologies. Tokyo: Japan Concrete Institute.
Qiao, C., P. Suraneni, and J. Weiss. 2018. “Flexural strength reduction of cement pastes exposed to solutions.” Cem. Concr. Compos. 86 (Feb): 297–305. https://doi.org/10.1016/j.cemconcomp.2017.11.021.
Shi, X., et al. 2009. Evaluation of alternative anti-icing and deicing compounds using sodium chloride and magnesium chloride as baseline deicers: Phase I. Denver: Colorado Dept. of Transportation.
Suraneni, P., et al. 2016a. “Mitigation of deicer damage in concrete pavements caused by calcium oxychloride formation—Use of ground lightweight aggregates.” In Proc., Int. RILEM Conf. on Materials, Systems and Structures in Civil Engineering. Paris: RILEM Publications.
Suraneni, P., V. J. Azad, O. B. Isgor, and W. J. Weiss. 2016b. “Calcium oxychloride formation in pastes containing supplementary cementitious materials: Thoughts on the role of cement and supplementary cementitious materials reactivity.” RILEM Tech. Lett. 1 (May): 24–30. https://doi.org/10.21809/rilemtechlett.2016.7.
Suraneni, P., V. J. Azad, O. B. Isgor, and W. J. Weiss. 2016c. “Deicing salts and durability of concrete pavements and joints: Mitigating calcium oxychloride formation.” Concr. Int. 38 (4): 48–54.
Suraneni, P., V. J. Azad, O. B. Isgor, and W. J. Weiss. 2017a. “Use of fly ash to minimize deicing salt damage in concrete pavements.” Transp. Res. Rec. 2629: 24–32. https://doi.org/10.3141/2629-05.
Suraneni, P., T. Fu, V. J. Azad, O. B. Isgor, and J. Weiss. 2018. “Pozzolanicity of finely ground lightweight aggregates.” Cem. Concr. Compos. 88 (Apr): 115–120. https://doi.org/10.1016/j.cemconcomp.2018.01.005.
Suraneni, P., J. Monical, E. Unal, Y. Farnam, and W. J. Weiss. 2017b. “Calcium oxychloride formation potential in cementitious pastes exposed to blends of deicing salt.” ACI Mater. J. 114 (4): 631–641. https://doi.org/10.14359/51689607.
Suraneni, P., and J. Weiss. 2017. “Examining the pozzolanicity of supplementary cementitious materials using isothermal calorimetry and thermogravimetric analysis.” Cem. Concr. Compos. 83 (Oct): 273–278. https://doi.org/10.1016/j.cemconcomp.2017.07.009.
Valenza, J. J., II, and G. W. Scherer. 2006. “Mechanism for salt scaling.” J. Am. Ceram. Soc. 89 (4): 1161–1179. https://doi.org/10.1111/j.1551-2916.2006.00913.x.
Vu, K. A. T., and M. G. Stewart. 2000. “Structural reliability of concrete bridges including improved chloride-induced corrosion models.” Struct. Saf. 22 (4): 313–333. https://doi.org/10.1016/S0167-4730(00)00018-7.
Zeng, Q., K. Li, T. Fen-chong, and P. Dangla. 2012. “Determination of cement hydration and pozzolanic reaction extents for fly-ash cement pastes.” Constr. Build. Mater. 27 (1): 560–569. https://doi.org/10.1016/j.conbuildmat.2011.07.007.
Information & Authors
Information
Published In
Copyright
©2018 American Society of Civil Engineers.
History
Received: Aug 15, 2017
Accepted: Mar 19, 2018
Published online: Jul 14, 2018
Published in print: Oct 1, 2018
Discussion open until: Dec 14, 2018
Authors
Metrics & Citations
Metrics
Citations
Download citation
If you have the appropriate software installed, you can download article citation data to the citation manager of your choice. Simply select your manager software from the list below and click Download.