Preparation and Characterization of an Eco-Friendly Binder from Alkali-Activated Aluminosilicate Solid Industrial Wastes Containing CKD and GGBS
Publication: Journal of Materials in Civil Engineering
Volume 30, Issue 6
Abstract
This work aims to prepare an eco-friendly binder from alkali-activated aluminosilicate solid industrial wastes. Eco-friendly binders provide a solution to the present ecological problem of producing non-portland-cement binders. Cement kiln dust (CKD) and ground granulated blast-furnace slag (GGBS) by-products were used to prepare the binder from alkali-activated GGBS-CKD mixed with . The characteristics of the prepared binder were studied using different techniques such as FTIR, DTA/TGA, XRD, and SEM. The compressive strength and bulk density of alkali-activated GGBS-CKD binders increased with increasing CKD contents up to 20% mass (Mix D2), then decreased with the increase of CKD contents from 30 to 50% mass. The chemically combined water and combined slag content of activated GGBS-CKD increased with increasing CKD content up to 50% mass (Mix D4). Mix D2 (20% mass of CKD) is the optimum mix composition. (CH) and containing CKD disintegrated the aluminosilicate matrix of GGBS. CH acts as a ion source to accelerate the pozzolanic activity to form rigid spheres of the compact massive matrix of (N, C)–A–S–H gel having low porosity. In addition, CKD has higher alkali and content, which makes CKD an excellent activator to enhance the dissolution of GGBS to release silicate, aluminate, and/or aluminosilicate species and improve the alkali-activated network gel matrix formation.
Get full access to this article
View all available purchase options and get full access to this article.
Acknowledgments
The authors extend their sincere appreciation to the Deanship of Scientific Research at the Al Imam Mohammad Ibn Saud Islamic University (IMSIU), Riyadh, Kingdom of Saudi Arabia, for its funding of this research through Research Group Project No. 351216.
References
Abd-El-Eziz, M. A., and Heikal, M. (2009). “Hydration characteristics and durability of cements containing fly ash and limestone subjected to Qaron’s lake water.” Adv. Cem. Res., 21(3), 91–99.
Abdel-Fattah, W. I., and El-Didamony, H. (1981). “Thermal investigation on electrostatic precipitator kiln dust.” Thermochim. Acta, 51(2–3), 297–306.
Abo-El-Enein, S. A., Hekal, E. E., Gabr, N. A., and El-Barbary, M. (1994). “Blended cements containing cement kiln dust.” Silic. Ind., 59(9–10), 265–269.
Ahmari, S., and Zhang, L. (2013). “Utilization of cement kiln dust (CKD) to enhance mine tailings-based geopolymer bricks.” Constr. Build. Mater., 40(3), 1002–1011.
Aiad, I., El-Didamony, H., Heikal, M., and Al-Masry, S. (2013). “Effect of delaying addition time of synthesized SSPF condensate on the durability of sulphate resisting cement pastes incorporating micro-silica.” Constr. Build. Mater., 48(11), 1092–1103.
Allahverdi, A., and Škvára, F. (2001). “Nitric acid attack on hardened paste of geopolymeric cements: Part 1.” Ceram. Silik., 45(3), 81–88.
Altan, E., and Erdoğan, S. T. (2012). “Alkali activation of a slag at ambient and elevated temperatures.” Cem. Concr. Comp., 34(2), 131–139.
Amin, A. M., Ebied, E., and El–Didamony, H. (1995). “Activation of granulated slag with calcined cement kiln dust.” Silic. Ind., 60(3–4), 109–115.
Ashby, M. (2012). Materials and the environment, 2nd Ed., Elsevier, Burlington, MA.
ASTM. (1992). “Standard test method for compressive strength of hydraulic cement mortars.” ASTM 109-92, Philadelphia, 62.
Aydın, S., and Baradan, B. (2014). “Effect of activator type and content on properties of alkali-activated slag mortars.” Comp. Part B, 57(2), 166–172.
Barbosa, V. F., and MacKenzie, K. (2003). “Thermal behaviour of inorganic geopolymers and composites derived from sodium polysialate.” J. Mater. Res. Bull., 38(2), 319–331.
Buchwald, A., and Schultz, M. (2005). “Alkali-activated binders by use of industrial by-products.” Cem. Concr. Res., 35(5), 968–973.
Burciaga-Díaz, O., Magallanes-Rivera, R. X., and Escalante-García, J. I. (2013). “Alkali-activated slag-metakaolin pastes: Strength, structural, and microstructural characterization.” J. Sustainable Cem. Based Mater., 2(2), 111–127.
Chang, J. J. (2003). “A study on the setting characteristics of sodium silicate-activated slag pastes.” Cem. Concr. Res., 33(7), 1005–1011.
Chaunsali, P., and Peethamparan, S. (2011). “Evolution of strength, microstructure and mineralogical composition of a CKD-GGBFS binder.” Cem. Concr. Res., 41(2), 197–208.
Chaunsali, P., and Peethamparan, S. (2013). “Influence of the composition of cement kiln dust on its interaction with fly ash and slag.” Cem. Concr. Res., 54(12), 106–113.
Chi, M. C., Chang, J. J., and Huang, R. (2012). “Strength and drying shrinkage of alkali-activated slag paste and mortar.” Adv. Civ. Eng., 2012, 1–7.
Chithiraputhiran, S., and Neithalath, N. (2013). “Isothermal reaction kinetics and alkali activation of slag, fly ash, and their blends.” Constr. Build. Mater., 45(8), 233–242.
Damtoft, J. S., Lukasik, J., Herfort, D., Sorrentino, D., and Gartner, E. M. (2008). “Sustainable development and climate change initiatives.” Cem. Concr. Res., 38(2), 115–127.
Davidovits, J. (1991). “Geopolymers.” J. Therm. Anal. Calorim., 37(8), 1633–1656.
Davidovits, J. (1999). “Chemistry of geopolymeric systems: Terminology.” Proc., 2nd Int. Conf. on Geopolymer’99, Institut Géopolymère, Saint-Quentin, France, 9–39.
De Silva, P., Sagoe-Crenstil, K., and Sirivivatnanon, V. (2007). “Kinetics of geopolymerization: Role of Al2O3 and SiO2.” Cem. Concr. Res., 37(4), 512–518.
Duxson, P., Fernández-Jiménez, A., Provis, J. L., Lukey, G. C., Palomo, A., and Van Deventer, J. S. J. (2007a). “Geopolymer technology: The current state of the art.” J. Mater. Sci., 42(9), 2917–2933.
Duxson, P., Provis, J. L., Lukey, G. C., and Van Deventer, J. S. (2007b). “The role of inorganic polymer technology in the development of ‘green concrete’.” Cem. Concr. Res., 37(12), 1590–1597.
El-Didamony, H., Aiad, I., Heikal, M., and Al-Masry, S. (2014). “Impact of delayed addition time of SNF condensate on the fire resistance and durability of SRC-SF composite cement pastes.” Constr. Build. Mater., 50(1), 281–290.
Fernandez-Jimenez, A., Puertas, F., Sorbrados, I., and Sanz, J. (2003). “Structure of calcium silicate hydrates formed in alkaline activated slag: Influence of the type of alkaline activator.” J. Am. Ceram. Soc., 86(8), 1389–1394.
Fernández-Jiménez, A., Palomo, J. G., and Puertas, F. (1999). “Alkali-activated slag mortars: Mechanical strength behaviour.” Cem. Concr. Res., 29(8), 1313–1321.
Gadsden, A. (1975). Infrared spectra of minerals and related inorganic compounds, Butterworths, London.
Gartner, E. (2004). “Industrially interesting approaches to ‘low-CO2’ cements.” Cem. Concr. Res., 34(9), 1489–1498.
Guo, X., Shi, H., Chen, L., and Dick, W. A. (2010). “Alkali-activated complex binders from class C fly ash and Ca-containing admixtures.” J. Hazard. Mater., 173(1–3), 480–486.
Haha, M. B., Saout, G. L., Winnefeld, F., and Lothenbach, B. (2012). “Influence of activator type on hydration kinetics, hydrate assemblage and microstructural development of alkali activated blast furnace slags.” Cem. Concr. Res., 42(1), 74–83.
Hajimohammadi, A., Provis, J. L., and van Deventer, J. S. (2011). “The effect of silica availability on the mechanism of geopolymerisation.” Cem Concr Res., 41(3), 210–216.
Heikal, M., and Ibrahim, S. M. (2015). “Characteristics and durability of alkali activated slag-microsilica pastes subjected to sulphate and chloride ions attack.” Ceram. Silik., 59(2), 81–89.
Heikal, M., Morsy, M. S., El-Shimy, E., and Abo-El-Enein, S. A. (2004). “Hydrothermal reactivity of granulated slag and sand using a lime-rich industrial waste as an activator.” L’industria Italiana del Cemento, (iiC), 74(7–8), 614–625.
Heikal, M., Nassar, M. Y., El-Sayed, G., and Ibrahim, S. M. (2014). “Physico–chemical, mechanical, microstructure and durability characteristics of alkali activated Egyptian slag.” Constr. Build. Mater., 69(9), 60–72.
IEEE-IAS Cement Industry Committee, Adaska, W. S., and Taubert, D. H. (2008). “Beneficial uses of cement kiln dust.” IEEE/PCA 50th Cement Industry Technical Conf., Miami.
JCPDS-ICDD (Joint Committee on Powder Diffraction Standards-International Center for Diffraction Data). (2001). “Database of powder diffraction patterns.” Newtown Square, PA.
Jiang, M., Chen, X., Rajabipour, F., and Hendrickson, C. T. (2014). “Comparative life cycle assessment of conventional, glass powder, and alkali-activated slag concrete and mortar.” J. Infrast. Syst., 04014020.
Juenger, M., Winnefeld, F., Provis, J., and Ideker, J. (2011). “Advances in alternative cementitious binders.” Cem. Concr. Res., 41(12), 1232–1243.
Khater, H. M. (2012). “Effect of cement kiln dust on geopolymer composition and its resistance to sulphate attack.” Inter. J. Civ. Struct. Eng., 2(2), 749–762.
Khater, H. M., and Zedane, S. R. (2012). “Geopolymerization of industrial by-products and study of their stability upon firing treatment.” Greener. J. Phys. Sci., 2(1), 1–9.
Konsta-Gdoutos, M. S., and Shah, S. P. (2003). “Hydration and properties of novel blended cements based on cement kiln dust and blast furnace slag.” Cem. Concr. Res., 33(8), 1269–1276.
Lecomte, I., Henrist, C., Liegeois, M., Maseri, F., Rulmont, A., and Cloots, R. (2006). “(Micro)-structural comparison between geopolymers, alkali-activated slag cement and portland cement.” J. Eur. Ceram. Soc., 26(16), 3789–3797.
Martín-Sedeño, M. C., et al. (2010). “Aluminum-rich belite sulfoaluminate cements: Clinkering and early age hydration.” Cem. Concr. Res., 40(3), 359–369.
Provis, J. L., Palomo, A., and Shi, C. (2015). “Advances in understanding alkali-activated materials.” Cem. Concr. Res., 78(Part A), 110–125.
Puertas, F., Fernández-Jiménez, A., and Blanco-Varela, M. T. (2004). “Pore solution in alkali-activated slag cement pastes. Relation to the composition and structure of calcium silicate hydrate.” Cem. Concr. Res., 34(1), 139–148.
Ravikumar, D., and Neithalath, N. (2012). “Reaction kinetics in sodium silicate powder and liquid activated slag evaluated using isothermal calorimetry.” Thermochim. Acta, 546(Oct), 32–43.
Rees, C. A., Provis, J. L., Lukey, G. C., and van Deventer, J. S. (2007). “Attenuated total reflectance Fourier transform infrared analysis of fly ash geopolymer gel ageing.” J. Langmuir., 23(15), 8170–8179.
Sayed, M., and Zeedan, S. R. (2012). “Green binding material using alkali activated blast furnace slag with silica fume.” HBRC J., 8(3), 177–184.
Shi, C. (1996). “Strength, pore structure and permeability of alkali-activated slag mortars.” Cem. Concr. Res., 26(12), 1789–1799.
Shi, C., Krivenko, P. V., and Roy, D. (2006). “Alkali–activated cements and concretes.” Chapter 4, Hydration and microstructure of alkali-activated slag cements, Taylor & Francis, New York, 64–105.
Siddique, R. (2008). Waste materials and by-products in concrete, Springer, Berlin, 1–40.
Song, S., and Jennings, H. M. (1999). “Pore solution chemistry of alkali-activated ground granulated blast-furnace slag.” Cem. Concr. Res., 29(2), 159–170.
Stark, J., Ludwig, H. M., and Muller, A. (1991). “Determination of the degree of hydration of slag cements.” ZKG, 90(11), 557–560.
Tashima, M. M., Soriano, L., Borrachero, M. V., Monzó, J., and Payá, J. (2013). “Effect of curing time on microstructure and mechanical strength development of alkali activated binders based on vitreous calcium aluminosilicate (VCAS).” Bull. Mater. Sci., 36(2), 245–249.
Thomas, R. J., Ye, H., Radlińska, A., and Peethamparan, S. (2016). “Alkali-activated slag concrete: A closer look at sustainable alternatives to portland cement.” Concr. Int., 38(1), 33–38.
Wang, S-D, Scrivener, K. L., and Pratt, P. L. (1994). “Factors affecting the strength of alkali-activated slag.” Cem. Concr. Res., 24(6), 1033–1043.
Yip, C. K., and Van Deventer, J. S. J. (2003). “Microanalysis of calcium silicate hydrate gel formed within a geopolymeric binder.” J. Mater. Sci., 38(18), 3851–3860.
Zhang, Y. J., Wang, Y. C., Xu, D. L., and Li, S. (2010). “Mechanical performance and hydration mechanism of geopolymer composite reinforced by resin.” Mater. Sci. Eng., 527(24–25), 6574–6580.
Information & Authors
Information
Published In
Copyright
©2018 American Society of Civil Engineers.
History
Received: May 4, 2017
Accepted: Nov 21, 2017
Published online: Mar 28, 2018
Published in print: Jun 1, 2018
Discussion open until: Aug 28, 2018
Authors
Metrics & Citations
Metrics
Citations
Download citation
If you have the appropriate software installed, you can download article citation data to the citation manager of your choice. Simply select your manager software from the list below and click Download.