Functional Fatigue of Polycrystalline Cu-Al-Mn Superelastic Alloy Bars under Cyclic Tension
Publication: Journal of Materials in Civil Engineering
Volume 28, Issue 5
Abstract
This paper studies the response of Cu-Al-Mn superelastic alloy (SEA) bars to repeated tensile load at room temperature. The test specimens are three polycrystalline and one single crystal SEA bars of 11 mm diameter and 100 mm length. Strain-controlled tensile load is applied for 1,000 cycles with target strain amplitudes of 6–7%. In the test, variations are monitored in the stress-strain curve, recovery strain, elastic modulus, forward transformation stress, and damping ratio. All bars showed functional fatigue, or gradual loss of superelasticity, while they did not fracture by the end of the loading cycles. Full strain recovery was observed up to 50–100 cycles without any training beforehand, while a slight decrease of forward transformation stress was observed during these cycles. Then, a gradual loss of stress plateau and gradual increase of residual strain were observed up to 200–400 cycles. Afterward, a nearly linear response was observed. Microstructure and texture analyses suggest that both the grain sizes larger than the bar diameter and the uniform distribution of crystallographic orientations are possible reasons for avoiding premature fracture, which is often seen in polycrystalline Cu-based SEAs.
Get full access to this article
View all available purchase options and get full access to this article.
Acknowledgments
This research was supported by the A-STEP program (#AS2315014C) provided by Japan Science and Technology Agency (JST).
References
Araki, Y., et al. (2011). “Potential of superelastic Cu-Al-Mn alloy bars for seismic applications.” Earthquake Eng. Struct. Dyn., 40(1), 107–115.
Brown, L. C. (1979). “The fatigue of pseudoelastic single crystals of -CuAlNi.” Metallurg. Trans. A, 10A(2), 217–224.
Carreras, G., Casciati, F., Casciati, S., Isalgue, A., Marzi, A., and Torra, V. (2011). “Fatigue laboratory tests toward the design of SMA portico-braces.” Smart Struct. Syst., 7(1), 41–57.
Casciati, F., Casciati, S., and Faravelli, L. (2007). “Fatigue characterization of a Cu-based shape memory alloy.” Proc. Est. Acad. Sci. –Phys. Math., 56(2), 207–217.
Casciati, F., Casciati, S., Faravelli, L., and Marzi1, A. (2011). “Fatigue damage accumulation in a Cu-based shape memory alloy: Preliminary investigation.” Comput. Mater. Continua, 23(3), 287–306.
Casciati, S., and Marzi, A. (2010). “Experimental studies on the fatigue life of shape memory alloy bars.” Smart Struct. Syst., 6(1), 73–85.
Casciati, S., and Marzi, A. (2011). “Fatigue tests on SMA bars in span control.” Eng. Struct., 33(4), 1232–1239.
Chopra, A. (2011). Dynamics of structures, Prentice Hall, NJ.
Delville, R., Malard, B., Pilch, J., Sittner, P., and Schryvers, D. (2011). “Transmission electron microscopy investigation of dislocation slip during superelastic cycling of Ni-Ti wires.” Int. J. Plast., 27(2), 282–297.
DesRoches, R., McCormick, J., and Delemont, M. (2004). “Cyclic properties of superelastic shape memory alloy wires and bars.” J. Struct. Eng., 38–46.
DesRoches, R., and Smith, B. (2004). “Shape memory alloys in seismic resistant design and retrofit: A critical review of their potential and limitations.” J. Earthquake Eng., 7(3), 1–15.
Dolce, M., and Cardone, D. (2001). “Mechanical behaviour of shape memory alloys for seismic applications: 2. Austenite NiTi wires subjected to tension.” Int. J. Mech. Sci., 43(11), 2657–2677.
Eggeler, G., Hornbogen, E., Yawny, A., Heckmann, A., and Wagner, M. (2004). “Structural and functional fatigue of NiTi shape memory alloys.” Mater. Sci. Eng. A, 378(1–2), 24–33.
Gall, K., and Maier, H. (2002). “Cyclic deformation mechanisms in precipitated NiTi shape memory alloys.” Acta Mater., 50(18), 4643–4657.
Gall, K., Sehitoglu, H., Anderson, R., Karaman, I., Chumlyakov, Y., and Kireeva, I. V. (2001). “On the mechanical behavior of single crystal NiTi shape memory alloys and related polycrystalline phenomenon.” Mater. Sci. Eng. A, 317(1–2), 85–92.
Gencturk, B., Araki, Y., Kusama, T., Omori, T., Kainuma, R., and Medina, F. (2014). “Loading rate and temperature dependency of superelastic Cu-Al-Mn alloys.” Const. Build. Mater., 53, 555–560.
Graesser, E. J., and Cozzarelli, F. A. (1991). “Shape-memory alloys as new materials for aseismic isolation.” J. Eng. Mech., 2590–2608.
Janke, L., Czaderski, M., Motavalli, M., and Ruth, J. (2005). “Application of shape memory alloys in civil engineering structures—Overview, limits and new ideas.” Mater. Struct., 38(5), 578–592.
Kato, H., Ozu, T., Hashimoto, S., and Miura, S. (1999). “Cyclic stress-strain response of superelastic Cu-Al-Mn alloy single crystals.” Mater. Sci. Eng. A, 264(1–2), 245–253.
Malécot, P., Lexcellent, C., Foltête, E., and Collet, M. (2006). “Shape memory alloys cyclic behavior: Experimental study and modeling.” J. Eng. Mater. Tech., 128(3), 335–345.
Maletta, C., Sgambitterra, E., Furgiuele, F., Casati, R., and Tuissi, A. (2012). “Fatigue of pseudoelastic NiTi within the stress-induced transformation regime: A modified Coffin-Mason approach.” Smart Mater. Struct., 21(11), 112001.
Maletta, C., Sgambitterra, E., Furgiuele, F., Casati, R., and Tuissi, A. (2014). “Fatigue properties of a pseudoelastic NiTi alloy: Strain ratcheting and hysteresis under cyclic tensile loading.” Int. J. Fatigue, 66, 78–85.
McCormick, J., Tyber, J., DesRoches, R., Gall, K., and Maier, H. J. (2007). “Structural engineering with NiTi. II: Mechanical behavior and scaling.” J. Eng. Mech., 1019–1029.
Miyazaki, S., Imai, T., Igo, Y., and Otsuka, K. (1986). “Effect of cyclic deformation on the pseudoelasticity characteristics of Ti-Ni alloys.” Metallurg. Trans. A, 17(1), 115–120.
Omori, T., et al. (2013). “Abnormal grain growth induced by cyclic heat treatment.” Science, 341(6153), 1500–1502.
Omori, T., Sutou, Y., Kainuma, R., and Ishida, K. (2006). “Development of Cu-Al-Mn-based shape memory alloys.” Copper, J.-M. Welter, Wiley, Weinheim, Germany, 194–202.
Ozbulut, O. E., Hurlebaus, S., and Desroches, R. (2011). “Seismic response control using shape memory alloys: A review.” J. Intell. Mater. Syst. Struct., 22(14), 1531–1549.
Saadat, S., et al. (2002). “An overview of vibration and seismic application of NiTi shape memory alloy.” Smart Mater. Struct., 11(2), 218–229.
Sade, M., Bubani, F. C., Lovey, F. C., and Torra, V. (2014). “Effect of grain size on stress induced martensitic transformations in a Cu-Al–Be polycrystalline shape memory alloy. Pseudoelastic cycling effects and microstructural modifications.” Mater. Sci. Eng. A, 609, 300–309.
Sade, M., Damiani, C., Gastien, R., Lovey, F. C., Malarría, J., and Yawny, A. (2007). “Fatigue and martensitic transitions in Cu-Zn–Al and Cu-Al–Ni single crystals: Mechanical behaviour, defects and diffusive phenomena.” Smart Mater. Struct., 16(1), S126.
Sade, M., Rapaciol, R., and Ahlers, M. (1985). “Fatigue in Cu-Zn-Al single crystals.” Acta Mater., 33(3), 487–497.
Sakamoto, H., Shimizu, K., and Otsuka, K. (1981). “Fatigue properties associated with cyclic - transformation pseudoelasticity of Cu-Al-Ni alloy single crystals.” Trans. Jpn Inst. Metals, 22(8), 579–587.
Sehitoglu, H., Anderson, R., Karaman, I., Gall, K., and Chumlyakov, Y. (2001). “Cyclic deformation behavior of single crystal NiTi.” Mater. Sci. Eng. A, 314(1–2), 67–74.
Siredey, N., and Eberhardt, A. (2000). “Fatigue behavior of Cu-Al-Be shape memory single crystals.” Mater. Sci. Eng. A, 290(1–2), 171–179.
Song, M., Ma, N., and Li, H. N. (2006). “Applications of shape memory alloys in civil structures.” Eng. Struct., 28(9), 1266–1274.
Sutou, Y., Omori, T., Kainuma, R., and Ishida, K. (2003). “Effect of grain size and texture on superelasticity of Cu-Al–Mn-based shape memory alloys.” J De Physique IV, 112, 511–514.
Sutou, Y., Omori, T., Kainuma, R., and Ishida, K. (2013). “Grain size dependence of pseudoelasticity in polycrystalline Cu-Al–Mn-based shape memory sheets.” Acta Mater., 61(10), 3842–3850.
Sutou, Y., Omori, T., Yamauchi, K., Ono, N., Kainuma, R., and Ishida, K. (2005). “Effect of grain size and texture on pseudoelasticity in Cu-Al–Mn-based shape memory wire.” Acta Mater., 53(15), 4121–4133.
Tamai, H., and Kitagawa, Y. (2002). “Pseudoelastic behavior of shape memory alloy wire and its application to seismic resistance member for building.” Comput. Mater. Sci., 25(1–2), 218–227.
Tobushi, H., Shimeno, Y., Hachisuka, T., and Tanaka, K. (1998). “Influence of strain rate on superelastic properties of TiNi shape memory alloy.” Mech. Mater., 30(2), 141–150.
Torra, V., et al. (2009). “Damping in civil engineering using SMA. The fatigue behavior and stability of CuAlBe and NiTi alloys.” J. Mater. Eng. Perform., 18(5–6), 738–745.
Torra, V., Carreras, G., Casciati, S., and Terriault, P. (2014). “On the NiTi wires in dampers for stayed cables.” Smart Struct. Syst., 13(3), 353–374.
Tyber, J., et al. (2007). “Structural engineering with NiTi. I: Basic materials characterization.” J. Eng. Mech., 1009–1018.
Ueland, S. M., and Schur, C. A. (2012). “Superelasticity and fatigue in oligocrystalline shape memory alloy microwires.” Acta Mater., 60(1), 282–292.
Wilson, J. C., and Wesolowsky, M. J. (2005). “Shape memory alloys for seismic response modification: A state-of-the art review.” Earthquake Spectra, 21(2), 569–601.
Wollants, P., De Bonte, M., and Roos, J. R. (1979). “Thermodynamic analysis of the stress-induced martensitic transformation in a single-crystal.” Z. Metallk., 70(2), 113–117.
Zhang, Y., and Zhu, S. (2008). “Seismic response control of building structures with superelastic shape memory alloy wire dampers.” J. Eng. Mech., 240–251.
Information & Authors
Information
Published In
Copyright
© 2015 American Society of Civil Engineers.
History
Received: Nov 16, 2014
Accepted: Jul 6, 2015
Published online: Dec 14, 2015
Published in print: May 1, 2016
Discussion open until: May 14, 2016
Authors
Metrics & Citations
Metrics
Citations
Download citation
If you have the appropriate software installed, you can download article citation data to the citation manager of your choice. Simply select your manager software from the list below and click Download.