Acoustic Emission Monitoring of Reinforced Concrete under Accelerated Corrosion
Publication: Journal of Materials in Civil Engineering
Volume 25, Issue 8
Abstract
The development of techniques capable of evaluating the deterioration of reinforced concrete structures is instrumental to the advancement of structural health monitoring (SHM) techniques and service life estimate methodologies for constructed facilities. One of the main causes of degradation is the corrosion of steel reinforcement. This process can be modeled phenomenologically, whereas laboratory tests aimed at studying durability responses are typically accelerated to provide usable results within a realistic period of time. Numerous nondestructive methods have been recently studied. Acoustic emission (AE) is emerging as a nondestructive tool to detect the onset and progression of deterioration mechanisms associated with concrete cracking. In this paper, an accelerated corrosion and continuous AE monitoring test setup is presented, providing relevant information on the characteristics of the corrosion circuit, continuous measurement procedure, selection of AE sensors, and AE parameter setting for data acquisition. The effectiveness of AE in detecting and characterizing the initiation of the corrosion process is discussed on the basis of results from small-scale, precracked RC specimens that are representative of areas near the clear cover in typical RC members. The main outcome is a new approach of AE data interpretation based on time-driven parameters.
Get full access to this article
View all available purchase options and get full access to this article.
Acknowledgments
The authors are grateful for the financial support of the U.S. Department of Commerce, National Institute of Standards and Technology, Technology Innovation Program, Cooperative Agreement Number 70NANB9H9007. The authors would like also to thank Artistic Stones Inc. for their valuable collaboration.
References
Allen, R. T. L., Edwards, S. C., and Shaw, J. D. N. (1993). The repair of concrete structures, Chapman and Hall, London, 18–22.
American Concrete Institute (ACI). (2011). “Building code requirements for structural concrete and commentary.”, Farmington Hills, MI, 136.
Andrade, C., Alonso, C., and Molina, F. J. (1993). “Cover cracking as a function of bar corrosion. Part I: Experimental test.” Mater. Struct., 26(8), 453–464.
ASCE. (2009). Report card for America’s infrastructure, Reston, VA, 73–81.
ASTM. (2004). “Standard practice for calculation of corrosion rates and related information from electrochemical measurements.”, West Conshohocken, PA.
ASTM. (2006). “Standard practice for determining damage-based design criteria for fiberglass reinforced plastic (FRP) materials using acoustic emission.”, West Conshohocken, PA.
ASTM. (2009a). “Standard test method for conducting potentiodynamic polarization resistance measurements.”, West Conshohocken, PA.
ASTM. (2009b). “Standard test method for half-cell potentials of uncoated reinforcing steel in concrete.”, West Conshohocken, PA.
ASTM. (2010). “Standard terminology for nondestructive examinations.”, West Conshohocken, PA.
ASTM. (2012). “Standard test method for compressive strength of cylindrical concrete specimens.”, West Conshohocken, PA.
Ballim, Y., and Reid, J. C. (2003). “Reinforcement corrosion and the deflection of RC beams–an experimental critique of current test methods.” Cem. Concr. Compos., 25(6), 625–632.
Browne, R. D. (1980). “Mechanism of corrosion of steel in concrete in relation to design, inspection and repairs of offshore and coastal structures.” ACI Spec. Publ., 65(11), 169–204.
Darwin, D., Manning, D. G., Hognestad, E., Beeby, A. W., Rice, P. F., and Ghowrwal, A. Q. (1985). “Debate: Crack width, cover, and corrosion.” Concr. Int., 7(5), 20–35.
Fregonese, M., Idrissi, H., Mazille, H., Renaud, L., and Cètre, Y. (2001). “Monitoring pitting corrosion of 304L and 316L austenitic stainless steels by acoustic emission: Influence of the pit morphology.” Proc. European Corrosion Congress 99, H. J. Wernicke and G. E. R. Aachen, eds., Maney, London.
Gamry Instruments. (2011). “Potentiostat/Galvanostat/ZRA operator’s manual.” Reference 600, Warminster, PA.
Godínez-Azcuaga, V. F., Farmer, J., Ziehl, P. H., Giurgiutiu, V., Nanni, A., and Inman, D. J. (2012). “Status in the development of self-powered wireless sensor node for structural health monitoring and prognosis.” Proc. SPIE, Smart Structures and Materials/Nondestructive Evaluation and Health Monitoring, Society of Photo-optical Instrumentation Engineers, Bellingham, WA.
Han, S. H., Lee, W. J., Cho, H. D., and Kim, D. G. (2001). “Crack source location technique for plain concrete beam using acoustic emission.” J. Korean Concr. Inst., 13(2), 107–113.
Higgins, D. D. (1995). “The effect of some test variables on chloride profiles.” Proc., RILEM Int. Workshop on Chloride Penetration into Concrete, RILEM, Bagneux, France.
Hope, B., Page, J. A., and Ip, A. K. C. (1986). “Corrosion rates of steel in concrete.” Cem. Concr. Res., 16(5), 771–781.
Idrissi, H., and Liman, A. (2003). “Study and characterization by acoustic emission and electrochemical measurements of concrete deterioration caused by reinforcement steel corrosion.” NDT&E International, 36(8), 563–569.
Kim, Y. P., Fregonese, M., and Feron, D. (2003). “Ability of acoustic emission technique for detection and monitoring of crevice corrosion on 304L austenitic stainless steel.” NDT&E International, 36(8), 553–562.
Li, Z., Li, F., Zdunek, A., Landis, E., and Shah, S. (1998). “Application of acoustic emission to detection of reinforcing steel corrosion in concrete.” ACI Mater. J., 95(1), 68–76.
Loreto, G., Di Benedetti, M., and Nanni, A. (2011). “Durability of reinforced concrete in marine environmental: a simplified model for service life prediction.” Int. J. 3R, 2(2), 253–260.
Melchers, R. E., and Li, C. Q. (2006). “Phenomenological modeling of reinforcement corrosion in marine environments.” ACI Mater. J., 103(1), 25–32.
Ohtsu, M., and Tomoda, Y. (2008). “Phenomenological model of corrosion process in reinforced concrete identified by acoustic emission.” ACI Mater. J., 105(2), 194–199.
Otieno, M. B., Alexander, M. G., and Beushausen, H. D. (2010). “Corrosion in cracked and uncracked concrete: Influence of crack width, concrete quality and crack reopening.” Mag. Concr. Res., 62(6), 393–404.
Physical Acoustics. (2005). R6I-AST sensor, Princeton Junction, NJ.
Physical Acoustics. (2009). Sensor Highway II user’s manual, Princeton Junction, NJ, 22–23.
Proust, A., Mazille, H., Fleischmann, P., and Rothea, R. (2001). “Characterization by AE technique of emissive phenomena during stress corrosion cracking of stainless steels.” J. Acoust. Emiss., 19(1), 229–240.
Shalon, R., and Raphael, M. (1959). “Influence of sea water on corrosion of steel reinforcement.” J. Am. Concr. Inst., 55(1), 1251–1268.
Yoon, D. J., Weiss, W. J., and Shah, S. (2000). “Assessing damage in corroded reinforced concrete using acoustic emission.” J. Eng. Mech., 126(3), 273–283.
Yuyama, S., and Nishida, T. (2003). “Acoustic emission evaluation of corrosion damages in buried pipes of refinery.” J. Acoust. Emiss., 21(1), 187–196.
Ziehl, P. H., and Fowler, T. J. (2003). “Fiber reinforced polymer vessel design with a damage approach.” J. Compos. Struct., 61(4), 395–411.
Ziehl, P. H., Galati, N., Nanni, A., and Tumialan, J. G. (2008). “In situ evaluation of two concrete slab systems. II: Evaluation criteria and outcomes.” J. Perform. Constr. Facil., 22(4), 217–227.
Information & Authors
Information
Published In
Copyright
© 2013 American Society of Civil Engineers.
History
Received: Jan 11, 2012
Accepted: Aug 7, 2012
Published online: Aug 28, 2012
Discussion open until: Jan 28, 2013
Published in print: Aug 1, 2013
Authors
Metrics & Citations
Metrics
Citations
Download citation
If you have the appropriate software installed, you can download article citation data to the citation manager of your choice. Simply select your manager software from the list below and click Download.