Effects of Concrete Composition on Resistance to Microbially Induced Corrosion
Publication: Journal of Environmental Engineering
Volume 143, Issue 6
Abstract
Microbially induced corrosion (MIC) is a process that can take place in concrete sewers, septic tanks, and transfer stations and can result in concrete deterioration. MIC is attributable to the microbial oxidation of hydrogen sulfide () to sulfuric acid () by a biofilm community that is established on a concrete surface. The rate and extent of this process will be influenced by the environment in which it takes place (e.g., temperature, concentration), as well as the composition of the concrete itself. Laboratory experiments were conducted to examine the effect of concrete composition and admixtures on MIC. The experiments were conducted in an isolated chamber where the climate was controlled, including the concentration. Concrete specimens representing 13 mixtures were inoculated with an aqueous suspension containing a mixture of four Acidothiobacillus spp. that have been associated with MIC in sewer systems. Results indicated that calcium aluminate cement (CAC) mortar, blended cement, and incorporation of a silane quaternary amine (SQA) antimicrobial agent can improve resistance to MIC under moderate exposure conditions (i.e., surface ). The rapid deterioration of specimens exposed to more aggressive conditions in the chamber indicated that degradation of concrete under the most severe MIC conditions (i.e., concrete surface ) was not prevented by simply manipulating concrete mixture proportions. A second set of experiments was conducted to quantify the effectiveness of SQA for the inactivation of pure cultures of planktonic bacteria. Results indicated that the antimicrobial agent performed well for the inactivation of pure cultures of Acidothiobacillus spp., except A. thiooxidans, which represent bacteria that are likely to be active under the most severe conditions (i.e., surface ).
Get full access to this article
View all available purchase options and get full access to this article.
Acknowledgments
This work was supported by Concrete Sealants, Inc. The authors wish to thank Chang Liao and Xuda Lin for their assistance.
References
Ahlström, B., Thompson, R., and Edebo, L. (1999). “Loss of bactericidal capacity of long-chain quaternary ammonium compounds with protein at lowered temperature.” APMIS, 107(1–6), 606–612.
Alexander, M., and Fourie, C. (2011). “Performance of sewer pipe concrete mixtures with portland and calcium aluminate cements subject to mineral and biogenic acid attack.” Mater. Struct., 44(1), 313–330.
Asamoto, S., Ohtsuka, A., Kuwahara, Y., and Miura, C. (2011). “Study on effects of solar radiation and rain on shrinkage, shrinkage cracking and creep of concrete.” Cem. Concr. Res., 41(6), 590–601.
ASTM. (2015a). “Standard specification for high solids content, cold liquid-applied elastomeric waterproofing membrane for use with separate wearing course.” ASTM C836, West Conshohocken, PA.
ASTM. (2015b). “Standard test method for resistance of concrete to rapid freezing and thawing.” ASTM C666, West Conshohocken, PA.
ASTM. (2016). “Standard test method for compressive strength of hydraulic cement mortars (using 2-in. or [50-mm] cube specimens).” ASTM C109, West Conshohocken, PA.
Blunden, J., Aneja, V. P., and Overton, J. H. (2008). “Modeling hydrogen sulfide emissions across the gas-liquid interface of an anaerobic swine waste treatment storage system.” Atmos. Environ., 42(22), 5602–5611.
Calas, M., Cordina, G., Bompart, J., Ben Bari, M., Jei, T., Ancelin, M. L., and Vial, H. (1997). “Antimalarial activity of molecules interfering with Plasmodium falciparum phospholipid metabolism. Structure-activity relationship analysis.” J. Med. Chem., 40(22), 3557–3566.
Dehkhoda, A. M., West, A. H., and Ellis, N. (2010). “Biochar based solid acid catalyst for biodiesel production.” Appl. Catalysis A: General, 382(2), 197–204.
Diercks, M., Sand, W., and Bock, E. (1991). “Microbial corrosion of concrete.” Experientia, 47(6), 514–516.
Ehrich, S., Helard, L., Letourneux, R., Willocq, J., and Bock, E. (1999). “Biogenic and chemical sulfuric acid corrosion of mortars.” J. Mater. Civ. Eng., 340–344.
Gu, J.-D., Ford, T. E., Berke, N. S., and Mitchell, R. (1998). “Biodeterioration of concrete by the fungus Fusarium.” Int. Biodeterior. Biodegrad., 41(2), 101–109.
Gutierrez-Padilla, M. G. D. (2007). “Activity of sulfur oxidizing microorganisms and impacts on concrete pipe corrosion.” Ph.D. thesis, Univ. of Colorado, Boulder, CO.
Hewayde, E., Nehdi, M., Allouche, E., and Nakhla, G. (2007). “Effect of mixture design parameters and wetting-drying cycles on resistance of concrete to sulfuric acid attack.” J. Mater. Civ. Eng., 155–163.
Hikita, H., Asai, S., and Takatsuka, T. (1976). “Absorption of carbon dioxide into aqueous sodium hydroxide and sodium carbonate-bicarbonate solutions.” Chem. Eng. J., 11(2), 131–141.
House, M., and Weiss, W. (2014). “Review of microbially induced corrosion and comments on needs related to testing procedures.” Proc., 4th Int. Conf. on the Durability of Concrete Structures, Purdue Univ., West Lafayette, IN.
House, M. W. (2013). “Using biological and physico-chemical test methods to assess the role of concrete mixture design in resistance to microbially induced corrosion.” M.S.C.E. thesis, Purdue Univ., West Lafayette, IN.
Irassar, E., Di Maio, A., and Batic, O. (1996). “Sulfate attack on concrete with mineral admixtures.” Cem. Concr. Res., 26(1), 113–123.
Islander, R. L., Devinny, J. S., Mansfeld, F., Postyn, A., and Shih, H. (1991). “Microbial ecology of crown corrosion in sewers.” J. Environ. Eng., 751–770.
Kosmatka, S. H., Kerkhoff, B., and Panarese, W. C. (2011). Design and control of concrete mixtures, Portland Cement Association, Skokie, IL.
Lange, F., Busch, P., and Thiele, K. (1989). “Quaternary ammonium compounds.” ⟨https://www.google.com/patents/US4874554⟩ (Nov. 10, 2015).
Lee, A. G. (2009). “Structural biology: Highly charged meetings.” Nature, 462(7272), 420–421.
Lin, J., Murthy, S. K., Olsen, B. D., Gleason, K. K., and Klibanov, A. M. (2003). “Making thin polymeric materials, including fabrics, microbicidal and also water-repellent.” Biotechnol. Lett., 25(19), 1661–1665.
Ling, A. L., et al. (2015). “High-resolution microbial community succession of microbially induced concrete corrosion in working sanitary manholes.” PloS One, 10(3), .
Lobos, J. H., Chisolm, T. E., Bopp, L. H., and Holmes, D. S. (1986). “Acidiphilium organovorum sp. nov., an acidophilic heterotroph isolated from a Thiobacillus ferrooxidans culture.” Int. J. Syst. Evol. Microbiol., 36(2), 139–144.
Mehta, P. (1985). “Studies on chemical resistance of low water/cement ratio concretes.” Cem. Concr. Res., 15(6), 969–978.
Milligan, A. J., Mioni, C. E., and Morel, F. M. (2009). “Response of cell surface pH to pCO2 and iron limitation in the marine diatom Thalassiosira weissflogii.” Mar. Chem., 114(1), 31–36.
Milović, N. M., Wang, J., Lewis, K., and Klibanov, A. M. (2005). “Immobilized N-alkylated polyethylenimine avidly kills bacteria by rupturing cell membranes with no resistance developed.” Biotechnol. Bioeng., 90(6), 715–722.
Monteny, J., et al. (2000). “Chemical, microbiological, and in situ test methods for biogenic sulfuric acid corrosion of concrete.” Cem. Concr. Res., 30(4), 623–634.
Okabe, S., Odagiri, M., Ito, T., and Satoh, H. (2007). “Succession of sulfur-oxidizing bacteria in the microbial community on corroding concrete in sewer systems.” Appl. Environ. Microbiol., 73(3), 971–980.
Parker, C. D. (1951). “Mechanics of corrosion of concrete sewers by hydrogen sulfide.” Sewage Ind. Wastes, 23, 1477–1485.
Portland Cement Association. (2002). “Concrete information: Types and causes of concrete deterioration.” Skokie, IL.
Roux, B., and MacKinnon, R. (1999). “The cavity and pore helices in the KcsA K+ channel: Electrostatic stabilization of monovalent cations.” Science, 285(5424), 100–102.
Sand, W., and Bock, E. (1984). “Concrete corrosion in the Hamburg sewer system.” Environ. Technol., 5(12), 517–528.
Saricimen, H., Shameem, M., Barry, M., Ibrahim, M., and Abbasi, T. (2003). “Durability of proprietary cementitious materials for use in wastewater transport systems.” Cem. Concr. Compos., 25(4), 421–427.
Senhadji, Y., Mouli, M., Khelafi, H., and Benosman, A. S. (2010). “Sulfate attack of Algerian cement-based material with crushed limestone filler cured at different temperatures.” Turk. J. Eng. Environ. Sci., 34(2), 131–143.
Song, H.-W., and Kwon, S.-J. (2007). “Permeability characteristics of carbonated concrete considering capillary pore structure.” Cem. Concr. Res., 37(6), 909–915.
Sunshine, R. A. (2009). “The budget and economic outlook: Fiscal years 2009 to 2019.” Testimony before the Committee on the Budget, U.S. Senate, Washington, DC.
Tian, B., and Cohen, M. D. (2000). “Does gypsum formation during sulfate attack on concrete lead to expansion?” Cem. Concr. Res., 30(1), 117–123.
Tiller, J. C., Liao, C.-J., Lewis, K., and Klibanov, A. M. (2001). “Designing surfaces that kill bacteria on contact.” Proc. Natl. Acad. Sci., 98(11), 5981–5985.
Yan, J., Moreno, L., and Neretnieks, I. (2000). “The long-term acid neutralizing capacity of steel slag.” Waste Manage., 20(2), 217–223.
Information & Authors
Information
Published In
Journal of Environmental Engineering
Volume 143 • Issue 6 • June 2017
Copyright
©2017 American Society of Civil Engineers.
History
Received: Mar 3, 2016
Accepted: Oct 28, 2016
Published online: Feb 23, 2017
Published in print: Jun 1, 2017
Discussion open until: Jul 23, 2017
Authors
Metrics & Citations
Metrics
Citations
Download citation
If you have the appropriate software installed, you can download article citation data to the citation manager of your choice. Simply select your manager software from the list below and click Download.