Reinforced Concrete Degradation in the Harsh Climates of the Arabian Gulf: Field Study on 30-to-50-Year-Old Structures
Publication: Journal of Performance of Constructed Facilities
Volume 32, Issue 5
Abstract
This paper presents the results of a field study carried out on three reinforced concrete (RC) structures built in the 1960s, 1970s, and 1980s to determine the main load (environmental) and the resistance (for example, the concrete quality and clear cover) factors affecting the durability of the infrastructure in the harsh environmental conditions of the Arabian Gulf region. The effects of degradation, such as the carbonation depths and chloride concentration profiles, in the columns, beams and slabs were determined from concrete core samples. To determine the durability factors, the concrete resistivity to electrical charge, the rapid chloride permeability, and the sorpitivity were measured. Digital image processing was performed to estimate the cement contents and the proportions of other ingredients used in the concrete samples. In most of the structural members, the chloride threshold for steel depassivation had been surpassed and the carbonation had reached the steel surface. The spalling of the concrete cover was observed with severe corrosion damage to the reinforcing bars. It is expected that this study will help understand the degradation phenomena in RC structures in the Gulf region and similar hot, humid, and saline environments. The results will help to establish the input parameters for the chloride diffusion and carbonation models in aggressive environmental conditions. Because the concrete quality directly impacts the initiation of many deterioration processes such as corrosion of the steel reinforcement and carbonation, the results could be used to predict the remaining service life of existing RC structures with similar concrete properties.
Get full access to this article
View all available purchase options and get full access to this article.
Acknowledgments
The funding for this research was provided by the National Priorities Research Program of the Qatar National Research Fund (a member of the Qatar Foundation) under the award NPRP 7-410-2-169. The statements made herein are solely the responsibility of the authors and do not necessarily reflect the opinions of the sponsor.
References
AASHTO. 2011. Standard method of test for surface resistivity indication of concrete’s ability to resist chloride ion penetration. AASHTO TP 95. Washington, DC: AASHTO.
ACI (American Concrete Institute). 1981. ACI standard building code requirements for reinforced concrete. ACI 318-77. Farmington Hills, MI: ACI.
ACI (American Concrete Institute). 2017. Building code requirements for structural concrete (ACI 318-95) and commentary (ACI 318R-95). ACI-318. Farmington Hills, MI: ACI.
Al-Amoudi, O. S. B., Rasheeduzzafar, M. Maslehuddin. 1991. “Carbonation and corrosion of rebars in salt contaminated OPC/PFA concretes.” Cem. Concr. Res. 21 (1): 38–50. https://doi.org/10.1016/0008-8846(91)90029-H.
Al-Ansary, M., and S. R. Iyengar. 2013. “Physiochemical characterization of coarse aggregates in Qatar for construction industry.” Int. J. Sustainable Built Environ. 2 (1): 27–40. https://doi.org/10.1016/j.ijsbe.2013.07.003.
Al-Khaiat, H., B. Jones, and M. N. Haque. 2007. “Designing durable concrete structures in the Arabian Gulf: A draft code.” In Proc., 32nd Conf. on Our World in Concrete and Structures, Singapore: CI-Premier Conference Organization.
Al-Samarai, M. 2015 “Durability of concrete in the Arabian Gulf.” J. Mater. Sci. Eng. A 5 (11–12): 398–408. https://doi.org/10.17265/2161-6213/2015.11-12.003.
Al-Tayyib, A.-H. J., and A. I. Al-Mana. 1989. “Influences of the Arabian gulf environment on concrete durability.” In Durability of Structures. IABSE Symp., Lisbon (IABSE Rep. Volume 57/1), 955. Zurich, Switzerland: IABSE.
Al-Tayyib, A. J., M. M. Al-Zahrani, Rasheeduzzafar, G. J. Al-Sulaimani. 1988. “Effect of polypropylene fiber reinforcement on the properties of fresh and hardened concrete in the Arabian Gulf environment.” Cem. Concr. Res. 18 (4): 561–570. https://doi.org/10.1016/0008-8846(88)90049-X.
AS (Standard Australia). 2009. Concrete structures. AS 3600-2009. Sydney, Australia: AS.
ASTM. 2012. Standard test method for electrical indication of concrete’s ability to resist chloride ion penetration. ASTM C1202-12. West Conshohocken, PA: ASTM.
ASTM. 2013. Standard test method for measurement of rate of absorption of water by hydraulic-cement concretes. ASTM C1585-13. West Conshohocken, PA: ASTM.
Broomfield, J. P. 2006. Corrosion of steel in concrete: Understanding, investigation and repair. 2nd ed. Abingdon, UK: Taylor & Francis.
BSI (British Standards Institution). 1998. British Standard Testing concrete Part 124. Methods for analysis of hardened concrete. BS 1881. Part-124. London: BSI.
BSI (British Standards Institution). 2000. Concrete. Part 1: Specification, performance, production and conformity. EN 206-1. London: BSI.
BSI (British Standards Institution). 2006. Products and systems for the protection and repair of concrete structures—Test methods—Determination of carbonation depth in hardened concrete by the phenolphthalein method. BS 14630. London: BSI.
Cady, P. D., and Weyers, R. E. 1992. “Predicting service life of concrete bridge decks subject to reinforcement corrosion.” Corrosion forms and control for infrastructure, edited by V. Chaker. West Conshohocken, PA: ASTM.
Dakhi, F. H., and A. S. Al-Gahtani. 1984. “Deterioration of concrete structures in the environment of the Middle East.” ACI J. Proc. 81 (1): 13–20.
Dias, W. P. S. 2013. “Reduction of concrete sorptivity with age through carbonation.” Concr. Res. 30 (8): 1255–1261.
Funahashi, M. 1990. “Predicting corrosion-free service life of a concrete structure in a chloride environment.” ACI Mater. J. 87 (6): 581–587.
Gergely, J., J. E. Bledsoe, T. Q. Brett, and S. F. Iosif. 2006. Concrete diffusion coefficients and existing chloride exposure in North Carolina. Charlotte, NC: North Carolina Dept. of Transportation.
Glass, G. K., and N. R. Buenfeld 1997. “The presentation of the chloride threshold level for corrosion of steel in concrete.” Corros. Sci. 39 (5): 1001–1013. https://doi.org/10.1016/S0010-938X(97)00009-7.
Haque, M. N., and H. Al-Khaiat. 1997. “Carbonation of concrete structures in hot dry coastal regions.” Cem. Concr. Compos. 19 (2): 123–129. https://doi.org/10.1016/S0958-9465(96)00047-9.
ImageJ. 2009. “Downloads: ImageJ.” Accessed August 17, 2017. https://imagej.net/Downloads.
Kessler, R. J., R. G. Powers, and M. A. Paredes. 2005. “Resistivity measurements of water saturated concrete as an indicator of permeability.” In NACE Corrosion Conf. and Expo. Florida Gainesville, FL: Dept. of Transportation State Materials Office, Corrosion Research Laboratory.
Matta, Z. G. 1992. “Chlorides and corrosion in the Arabian Gulf environment.” Concr. Int. 14 (5): 47–48.
Matta, Z. G. Z. 1993. “Deterioration of concrete structures in the Arabian Gulf.” Concr. Int. 15 (7): 33–36.
Nagi, M., and D. Whiting. 2004. “Resistivity of concrete: State of the art.” In Corrosion 2014. Houston: NACE International.
Patel, V. N. 2009. Sorptivity testing to assess durability of concrete against freeze-thaw cycling. Montreal: Dept. of Civil Engineering and Applied Mechanics McGill Univ.
Polder, R., C. Andrade, B. Elsener, Ø. Vennesland, J. Gulikers, R. Weidert, and M. Raupach. 2000. “Test methods for on site measurement of resistivity of concrete.” Mater. Struct. Res. 33 (10): 603–611. https://doi.org/10.1007/BF02480599.
Qatalum. 2006. Environmental impact assessment. Doha, Qatar: Qatalum.
Smith, R. 2007. “The effects of corrosion on the performance of reinforced concrete beams.” Ph.D. thesis. Univ. of Michigan.
Sohail, M. G., S. Laurens, F. Deby, and J. P. Balayssac. 2015. “Significance of macrocell corrosion of reinforcing steel in partially carbonated concrete: Numerical and experimental investigation.” Mater. Struct. 48 (1–2): 217–233. https://doi.org/10.1617/s11527-013-0178-2.
Song, H., and V. Saraswathy. 2007. “Corrosion monitoring of reinforced concrete structures: A review.” Int. J. Electrochem Sci. 2 (1): 1–28.
Tuutti, K. 1982. “Corrosion of steel in concrete.” Stockholm.
Virmani, Y. P., K. C. Clear, and T. J. Pasko Jr. 1983. “Time to corrosion of reinforcing steel in concrete slabs.” Vol. 5 in Calcium Nitrite admixture and epoxy-coated reinforcing bars as corrosion protection systems. Springfield, VA: National Technical Information Service.
West, R. E., and W. G. Hime. 1985 “Chloride profiles in salty concrete.” Mater. Perform. (MP) 24 (7): 29–36.
Winter, N. B., and N. B. Winter. 2012. Scanning electron microscopy of cement and concrete. Woodbridge, ON, Canada: WHD Microanalysis.
Yuan, Y., Y. Ji, and S. P. Shah. 2007. “Comparison of two accelerated corrosion techniques for concrete structures.” ACI Struct. J. 104 (3): 344–347.
Zein Al-Abideen, H. M. 1998. “Concrete practices in the Arabian Peninsula and the Gulf.” Mater. Struct. 31 (4): 275–280. https://doi.org/10.1007/BF02480426.
Zhou, Y., B. Gencturk, K. Willam, and A. Attar. 2015. “Carbonation-induced and chloride-induced corrosion in reinforced concrete structures.” J. Mater. Civ. Eng. 27 (9): 4014245. https://doi.org/10.1061/(ASCE)MT.1943-5533.0001209.
Information & Authors
Information
Published In
Copyright
©2018 American Society of Civil Engineers.
History
Received: Sep 5, 2017
Accepted: Mar 20, 2018
Published online: Jun 26, 2018
Published in print: Oct 1, 2018
Discussion open until: Nov 26, 2018
Authors
Metrics & Citations
Metrics
Citations
Download citation
If you have the appropriate software installed, you can download article citation data to the citation manager of your choice. Simply select your manager software from the list below and click Download.