Durability of Commercially Available GFRP Reinforcement in Seawater-Mixed Concrete under Accelerated Aging Conditions
Publication: Journal of Composites for Construction
Volume 24, Issue 4
Abstract
The effect of seawater used as mixing water in concrete on the long-term properties of glass fiber–reinforced polymer (GFRP) bars is the focus of this work. The durability of GFRP bars embedded in seawater-mixed concrete was studied in terms of residual mechanical properties (i.e., tensile strength, horizontal and transverse shear strength, and GFRP–concrete bond strength) after immersion in seawater at 60°C for a period of 24 months. Benchmark specimens were also cast using conventional concrete. Results showed comparable performance in tensile and shear properties between the two sets of bars with some degradation of the mechanical properties in both cases. However, bond strength showed some differences between the two sets of bars. SEM was used to identify degradation mechanisms. Areas with large concentrations of voids near the bar edge, formed during manufacturing, may provide a pathway for moisture and alkalis, which could lead to the fiber disintegration and debonding between fibers and the resin. Over time, a greater number of fibers are affected, which leads to the formation of significant cracking near the edge. Results were qualitatively similar for embedded bars in seawater-mixed and conventional concrete, explaining a similar reduction in tensile properties, horizontal shear strength, and transverse shear strength seen in both sets of bars. However, the bond strength does not significantly decrease in these specimens over time for unclear reasons.
Get full access to this article
View all available purchase options and get full access to this article.
Acknowledgments
The authors would like to express their gratitude to Infravation for funding under Project No. 31109806.005-SEACON. Funding from ACI Foundation's Concrete Research Council is also acknowledged. The statements made herein are solely the responsibility of the authors.
References
Abbasi, A., and P. J. Hogg. 2005. “Temperature and environmental effects on glass fibre rebar: Modulus, strength and interfacial bond strength with concrete.” Composites Part B 36 (5): 394–404. https://doi.org/10.1016/j.compositesb.2005.01.006.
Almusallam, T. H., Y. A. Al-Salloum, S. H. Alsayed, S. El-Gamal, and M. Aqel. 2013. “Tensile properties degradation of glass fiber-reinforced polymer bars embedded in concrete under severe laboratory and field environmental conditions.” J. Compos. Mater. 47 (4): 393–407. https://doi.org/10.1177/0021998312440473.
ASTM. 2013. Standard test methods for density and specific gravity (relative density) of plastics by displacement. ASTM D792-13. West Conshohocken, PA: ASTM.
ASTM. 2014. Standard test method for bond strength of fiber-reinforced polymer matrix composite bars to concrete by pullout testing. ASTM D7913/D7913M-14. West Conshohocken, PA: ASTM.
ASTM. 2016a. Standard test method for apparent horizontal shear strength of pultruded reinforced plastic rods by the short-beam method. ASTM D4475-02. West Conshohocken, PA: ASTM.
ASTM. 2016b. Standard test method for tensile properties of fiber reinforced polymer matrix composite bars. ASTM D7205/D7205M-06 West Conshohocken, PA: ASTM.
ASTM. 2017a. Standard specification for solid round glass fiber reinforced polymer bars for concrete reinforcement. ASTM D7957/D7957M-17. West Conshohocken, PA: ASTM.
ASTM. 2017b. Standard test method for transverse shear strength of fiber-reinforced polymer matrix composite bars. ASTM D7617/D7617M-11. West Conshohocken, PA: ASTM.
ASTM. 2018a. Standard test method for assignment of the glass transition temperatures by differential scanning calorimetry. ASTM E1356-08. West Conshohocken, PA: ASTM.
ASTM. 2018b. Standard test method for heat of reaction of thermally reactive materials by differential scanning calorimetry. ASTM E2160-04. West Conshohocken, PA: ASTM.
ASTM. 2018c. Standard test method for ignition loss of cured reinforced resins. ASTM D2584-18. West Conshohocken, PA: ASTM.
ASTM. 2018d. Standard test method for water absorption of plastics. ASTM D570-98. West Conshohocken, PA: ASTM.
ASTM. 2019a. Standard specification for coal fly ash and raw or calcined natural pozzolan for use in concrete. ASTM C618-19. West Conshohocken, PA: ASTM.
ASTM. 2019b. Standard specification for portland cement. ASTM C150/C150M-19. West Conshohocken, PA: ASTM.
Bakis, C. E., T. E. Boothby, R. A. Schaut, and C. G. Pantano. 2005. “Tensile strength of GFRP bars under sustained loading in concrete beams.” In Vol. 2 of Proc., 7th Int. Symp. on Fiber Reinforced Polymer Reinforcement for Concrete Structures, ACI Special Publication 230, edited by C. K. Shield, J. P. Busel, S. L. Walkup, and D. D. Gremel, 1429–1446. Farmington Hills, MI: ACI.
Bank, L. C., T. R. Gentry, B. P. Thompson, and J. S. Russell. 2003. “A model specification for FRP composites for civil engineering structures.” Constr. Build. Mater. 17 (6–7): 405–437. https://doi.org/10.1016/S0950-0618(03)00041-2.
Bank, L. C., M. Puterman, and A. Katz. 1998. “The effect of material degradation on bond properties of fiber reinforced plastic reinforcing bars in concrete.” ACI Mater. J. 95 (3): 232–243.
Bazli, M., H. Ashrafi, and A. V. Oskouei. 2017. “Experiments and probabilistic models of bond strength between GFRP bar and different types of concrete under aggressive environments.” Constr. Build. Mater. 148: 429–443. https://doi.org/10.1016/j.conbuildmat.2017.05.046.
Byars, E. A., P. Waldron, V. Dejke, S. Demis, and S. Heddadin. 2003. “Durability of FRP in concrete—Deterioration mechanisms.” Int. J. Mater. Prod. Technol. 19 (1/2): 28–39. https://doi.org/10.1504/IJMPT.2003.003554.
Chen, Y., J. F. Davalos, I. Ray, and H.-Y. Kim. 2007. “Accelerated aging tests for evaluations of durability performance of FRP reinforcing bars for concrete structures.” Compos. Struct. 78 (1): 101–111. https://doi.org/10.1016/j.compstruct.2005.08.015.
CSA (Canadian Standards Association). 2019. Specification for fibre-reinforced polymers. CAN/CSA-S807. Rexdale, ON, Canada: CSA.
Davalos, J. F., Y. Chen, and I. Ray. 2008. “Effect of FRP bar degradation on interface bond with high strength concrete.” Cem. Concr. Compos. 30 (8): 722–730. https://doi.org/10.1016/j.cemconcomp.2008.05.006.
El-Hassan, H., T. El-Maaddawy, A. Al-Sallamin, and A. Al-Saidy. 2017. “Performance evaluation and microstructural characterization of GFRP bars in seawater-contaminated concrete.” Constr. Build. Mater. 147: 66–78. https://doi.org/10.1016/j.conbuildmat.2017.04.135.
El-Maaddawy, T., A. Al-Saidy, and A. Al-Sallamin. 2016. “Residual strength of glass fiber reinforced polymer bars in seawater-contaminated concrete.” In Proc., Int. Workshop on Seawater sea-Sand Concrete (SSC) Structures Reinforced with FRP Composites.
Fergani, H., M. Di Benedetti, C. Miàs Oller, C. Lynsdale, and M. Guadagnini. 2018. “Durability and degradation mechanisms of GFRP reinforcement subjected to severe environments and sustained stress.” Constr. Build. Mater. 170: 637–648. https://doi.org/10.1016/j.conbuildmat.2018.03.092.
Ghorab, H. Y., M. S. Hilal, and E. A. Kishar. 1989. “Effect of mixing and curing waters on the behaviour of cement pastes and concrete. Part 1: Microstructure of cement pastes.” Cem. Concr. Res. 19 (6): 868–878. https://doi.org/10.1016/0008-8846(89)90099-9.
Gooranorimi, O., and A. Nanni. 2017. “GFRP reinforcement in concrete after 15 years of service.” J. Compos. Constr. 21 (5): 04017024. https://doi.org/10.1061/(ASCE)CC.1943-5614.0000806.
Hao, Q., Y. Wang, Z. He, and J. Ou. 2009. “Bond strength of glass fiber reinforced polymer ribbed rebars in normal strength concrete.” Constr. Build. Mater. 23 (2): 865–871. https://doi.org/10.1016/j.conbuildmat.2008.04.011.
ICC-ES (International Code Council-Evaluation Services). 2015. Acceptance criteria for fiber-reinforced polymers (FRP) bars for internal reinforcement of concrete members. AC-454. Whittier, CA: ICC-ES.
Kampmann, R., F. De Caso, M. Roddenberry, and A. R. Emparanza. 2018. Performance evaluation of glass fiber reinforced polymer (GFRP) reinforcing bars embedded in concrete under aggressive environments. Final Rep. Tallahassee, FL: Florida Department of Transportation, Research Center.
Katsuki, F. 1995. “Prediction of deterioration of FRP rods due to alkali attack.” In Proc., 2nd Int. RILEM Symp.: Non-Metallic (FRP) Reinforcement for Concrete Structures, 82–89. Boca Raton, FL: CRC Press.
Khatibmasjedi, M., and A. Nanni. 2017. “Durability of GFRP reinforcement in SEACON.” In Proc., 5th Int. Conf.on Durability of Fiber Reinforced Polymer (FRP) Composites for Construction and Rehabilitation of Structures, 1–8. Quebec, Canada: Universite de Sherbrooke.
Khatibmasjedi, S., F. J. De Caso y Basalo, and A. Nanni. 2016. “SEACON: Redefining sustainable concrete.” In Proc., 4th Int. Conf. on Sustainable Construction Materials and Technologies, 1–10. UK: The International Committee of the SCMT conferences.
Micelli, F., and A. Nanni. 2004. “Durability of FRP rods for concrete structures.” Constr. Build. Mater. 18 (7): 491–503. https://doi.org/10.1016/j.conbuildmat.2004.04.012.
Mufti, A. A., N. Banthia, B. Benmokrane, M. Boulfiza, and J. P. Newhook. 2007. “Durability of GFRP composite rods.” Concr. Int. 29 (02): 37–42.
Mukherjee, A., and S. J. Arwikar. 2005. “Performance of glass fiber-reinforced polymer reinforcing bars in tropical environments. Part II: Microstructural tests.” ACI Struct. J. 102 (6): 816–822.
Murphy, K., S. Zhang, and V. Karbhari. 1999. “Effect of concrete based alkaline solutions on short term response of composites.” In Proc., 44th Int. SAMPE Symp. and Exhibition, edited by L. J. Cohen, J. L. Bauer, and W. E. Davis, 2222–2230. Long Beach, CA: Society for the Advancement of Material and Process Engineering.
Nanni, A., A. De Luca, and H. J. Zadeh. 2014. FRP reinforced concrete structures—Theory, design and practice. Boca Raton, FL: CRC Press.
Park, Y. 2012. “Long-term performance of GFRP reinforced concrete beams and bars subjected to aggressive environments.” Ph.D. thesis, Civil Engineering, University of Texas at Arlington.
Porter, M. L., J. Mehus, K. A. Young, E. F. O’Neil, and B. A. Barnes. 1997. “Aging for fiber reinforcement in concrete.” In Vol. 2 of 3rd Int. Symp. on Non-Metallic (FRP) Reinforcement for Concrete Structures, 59–66. Sapporo, Japan: Japan Concrete Institute.
Robert, M., and B. Benmokrane. 2010. “Effect of aging on bond of GFRP bars embedded in concrete.” Cem. Concr. Compos. 32 (6): 461–467. https://doi.org/10.1016/j.cemconcomp.2010.02.010.
Robert, M., and B. Benmokrane. 2013. “Combined effects of saline solution and moist concrete on long-term durability of GFRP reinforcing bars.” Constr. Build. Mater. 38: 274–284. https://doi.org/10.1016/j.conbuildmat.2012.08.021.
Robert, M., P. Cousin, and B. Benmokrane. 2009. “Durability of GFRP reinforcing bars embedded in moist concrete.” J. Compos. Constr. 13 (2): 66–73. https://doi.org/10.1061/(ASCE)1090-0268(2009)13:2(66).
Ruiz Emparanza, A., R. Kampmann, and F. J. De Caso y Basalo. 2017. “State-of-the-practice of FRP rebar global manufacturing.” In Proc., Composites and Advanced Materials Expo. Orlando, Florida, USA: The Composites and Advanced Materials Expo.
Wang, Z., X.-L. Zhao, G. Xian, G. Wu, R. K. Singh Raman, S. Al-Saadi, and A. Haque. 2017. “Long-term durability of basalt- and glass-fibre reinforced polymer (BFRP/GFRP) bars in seawater and sea sand concrete environment.” Constr. Build. Mater. 139: 467–489. https://doi.org/10.1016/j.conbuildmat.2017.02.038.
Zhou, J., X. Chen, and S. Chen. 2012. “Effect of different environments on bond strength of glass fiber-reinforced polymer and steel reinforcing bars.” KSCE J. Civ. Eng. 16 (6): 994–1002. https://doi.org/10.1007/s12205-012-1462-3.
Information & Authors
Information
Published In
Journal of Composites for Construction
Volume 24 • Issue 4 • August 2020
Copyright
© 2020 American Society of Civil Engineers.
History
Received: Dec 19, 2018
Accepted: Feb 5, 2020
Published online: Apr 24, 2020
Published in print: Aug 1, 2020
Discussion open until: Sep 24, 2020
Authors
Metrics & Citations
Metrics
Citations
Download citation
If you have the appropriate software installed, you can download article citation data to the citation manager of your choice. Simply select your manager software from the list below and click Download.