Flexural Response of Cross-Ply Flax Fiber–Reinforced Polymer Skinned Foam Cylinders
Publication: Journal of Composites for Construction
Volume 23, Issue 6
Abstract
The flexural response of 12 2-m-long and 152-mm-diameter fiber-reinforced polymer (FRP) skinned members with foam cores was investigated. Nine cylinders with various flax-FRP (FFRP) laminate arrangements and foam core densities were fabricated and tested in flexure; these were compared with three glass-FRP (GFRP) skinned specimens. Varying the foam density from 32 to was found to be insignificant in FFRP skinned beams because their failure was governed by fiber tensile rupture. However, increasing the foam density increased the capacity of the GFRP skinned members that failed in compression. The most effective ways to increase strength-to-weight and stiffness-to-weight ratios of FFRP skinned cylinders are to increase the number of longitudinal fiber layers and decrease the foam core density. A FFRP cylinder with five longitudinal and three transverse layers was able to develop over 80% the strength-to-weight and stiffness-to-weight ratios as a reference GFRP cylinder, substantially higher than the 30%–50% values seen in coupon tests. Although the FFRP cylinder performed fairly well, further work on the member axial, impact, and durability resistance is recommended.
Get full access to this article
View all available purchase options and get full access to this article.
Data Availability Statement
Experimental testing data generated and used during the study are available from the corresponding author by request.
References
Assarar, M., D. Scida, A. El Mahi, C. Poilane, and R. Ayad. 2011. “Influence of water ageing on mechanical properties and damage events of two reinforced composite materials: Flax-fibres and glass-fibres.” Mater. Des. 32 (2): 788–795. https://doi.org/10.1016/j.matdes.2010.07.024.
ASTM. 2014a. Standard test method for tensile properties of plastics. ASTM D638. West Conshohocken, PA: ASTM.
ASTM. 2014b. Standard test method for tensile properties of polymer matrix composite materials. ASTM D3039M. West Conshohocken, PA: ASTM.
Cicala, G., C. Giuseppe, G. Recca, and A. Latteri. 2010. Woven fabric engineering, edited by P. D. Dubrovski. Rijeka, Croatia: Sciyo.
Codyre, L. 2016. The effect of foam core density on the flexural and axial behaviour of sandwich panels of varying slenderness with natural flax-FRP and glass-FRP composite skins. M.A.Sc. thesis, Dept. of Civil Engineering, Queen’s Univ.
Composites Evolution. 2012. “Biotex flax unidirectional fabric technical data sheet.” Accessed February 15, 2019. http://www.jacomp.fi/wp-content/uploads/2014/04/Biotex-Flax-Unidirectional-TDS-March-2012.pdf.
Dammer, L., and L. Scholz. 2013. Market developments of and opportunities for biobased products and chemicals. Hürth, Germany: Nova-Institute for Ecology and Innovation.
Dittenber, D. B., and H. S. V. GangaRao. 2012. “Critical review of recent publications on use of natural composites in infrastructure.” Composites Part A 43 (8): 1419–1429. https://doi.org/10.1016/j.compositesa.2011.11.019.
Fam, A., and J.-K. Son. 2008. “Finite element modeling of hollow and concrete-filled fiber composite tubes in flexure: Optimization of partial filling and a design method for poles.” Eng. Struct 30 (10): 2667–2676. https://doi.org/10.1016/j.engstruct.2008.02.015.
Fyfe Company. 2012. “Tyfo SHE-51A composite using Tyfo® S epoxy.” Accessed February 15, 2019. http://www.fyfeco.com/Products/∼/media/Files/Fyfe/2013-Products/Tyfo%20SEH-51A%20Comp.ashx.
Holbery, J., and D. Houston. 2006. “Natural-fiber-reinforced polymer composites in automotive applications.” J. Miner. Met. Mater. Soc. 58 (11): 80–86. https://doi.org/10.1007/s11837-006-0234-2.
Ibrahim, S., D. Polyzois, and S. K. Hassan. 2000. “Development of glass fiber reinforced plastic poles for transmission and distribution lines.” Can. J. Civ. Eng. 27 (5): 850–858. https://doi.org/10.1139/l99-089.
Joshi, S. V., L. T. Drzal, S. K. Mohanty, and S. Arora. 2004. “Are natural fiber composites environmentally superior to glass fiber reinforced composites?” Composites Part A 35 (3): 371–376. https://doi.org/10.1016/j.compositesa.2003.09.016.
Ku, H., H. Wang, N. Pattarachaiyakoop, and M. Trada. 2011. “A review on the tensile properties of natural fiber reinforced polymer composites.” Composites Part B 42 (4): 856–873. https://doi.org/10.1016/j.compositesb.2011.01.010.
Li Loong, M., and D. Cree. 2017. “Enhancement of mechanical properties of bio-resin epoxy/flax fiber composites using acetic anhydride.” J. Polym. Environ. 26 (1): 224–234. https://doi.org/10.1007/s10924-017-0943-3.
Mak, K., A. Fam, and C. MacDougall. 2015. “Flexural behavior of sandwich panels with bio-FRP skins made of flax fibers and epoxidized pine-oil resin.” J. Compos. Constr. 19 (6): 04015005. https://doi.org/10.1061/(ASCE)CC.1943-5614.0000560.
Mak, K., A. Fam, and C. MacDougall. 2016. “The effects of long term exposure of flax fiber reinforced polymer to salt solution at high temperature on tensile properties.” Polym. Compos. 37 (11): 3234–3244. https://doi.org/10.1002/pc.23522.
Malkapuram, R., V. Kumar, and Y. S. Negi. 2008. “Recent development in natural fiber reinforced polypropylene composites.” J. Reinf. Plast. Compos. 28 (10): 1169–1189. https://doi.org/10.1177/0731684407087759.
Navon, R. 1995. “Economic benefits of lightweight versus conventional construction methods.” J. Constr. Eng. Manage. 121 (1): 27–36. https://doi.org/10.1061/(ASCE)0733-9364(1995)121:1(27).
O’Donnell, A., M. A. Dweib, R. P. Wool. 2004. “Natural fiber composites with plant oil-based resin.” Compos. Sci. Technol. 64: 1135–1145.
Oksman, K. 2001. “High quality flax fibre composites manufactured by the resin transfer moulding process.” J. Reinf. Plast. Compos. 20 (7): 621–627.
Poilâne, C., Z. E. Cherif, F. Richard, A. Vivet, and B. Doudou. 2014. “Polymer reinforced by flax fibers as a viscoelastoplastic material.” Compos. Struct. 112 (Jun): 100–112. https://doi.org/10.1016/j.compstruct.2014.01.043.
Rodríguez, E. S., V. A. Alvarez, and P. E. Montemartini. 2013. “Failure analysis of a GFRP pipe for oil transport.” Eng. Fail. Anal. 28 (Mar): 16–24. https://doi.org/10.1016/j.engfailanal.2012.07.025.
Saheb, D. N., and J. P. Jog. 1999. “Natural fiber polymer composites: A review.” Adv. Polym. Tech. 18 (4): 351–363. https://doi.org/10.1002/(SICI)1098-2329(199924)18:4%3C351::AID-ADV6%3E3.0.CO;2-X.
Taylor M., C. Tam, and D. Gielen. 2006. “Energy efficiency and emissions from the global cement industry.” In Proc., IEA-WBCSD Workshop: Energy Efficiency and CO2 Emission Reduction Potentials and Policies in the Cement Industry, 4–5. Paris: International Energy Agency.
Wambua, P., J. Ivens, and I. Verpoest. 2003. “Natural fibers: Can they replace glass in fiber reinforced plastics?” Compos. Sci. Technol. 63 (9): 1259–1264. https://doi.org/10.1016/S0266-3538(03)00096-4.
Yan, L., and N. Chouw. 2013a. “Compressive and flexural behaviour and theoretical analysis of flax fiber reinforced polymer tube encased coir fiber reinforced concrete composite.” Mater. Des. 52 (Dec): 801–811. https://doi.org/10.1016/j.matdes.2013.06.018.
Yan, L., and N. Chouw. 2013b. “Crashworthiness characteristics of flax fiber reinforced epoxy tubes for energy absorption application.” Mater. Des. 51 (Oct): 629–640. https://doi.org/10.1016/j.matdes.2013.04.014.
Yan, L., and N. Chouw. 2014. “Natural FRP tube confined fiber reinforced concrete under pure axial compression: A comparison with glass/carbon FRP.” Thin-Walled Struct. 82 (Sep): 159–169. https://doi.org/10.1016/j.tws.2014.04.013.
Yan, L., N. Chouw, and K. Jayaraman. 2014. “Effect of triggering and polyurethane foam-filler on axial crushing of natural flax/epoxy composite tubes.” Mater. Des. 56 (Apr): 528–541. https://doi.org/10.1016/j.matdes.2013.11.068.
Yan, L., N. Chouw, and K. Jayaraman. 2015. “Effect of UV and water spraying on the mechanical properties of flax fabric reinforced polymer composites used for civil engineering applications.” Mater. Des. 71 (Apr): 17–25. https://doi.org/10.1016/j.matdes.2015.01.003.
Yan, L., and L., Huang. 2015. “Effect of weathering conditions on durability of flax FRP composite used as concrete confinement material.” In Proc., 12th Int. Symp. on Fiber Reinforced Polymers for Reinforced Concrete Structures, 14–16. Nanjing, China. Kingston, Ontario, Canada: International Institute for FRP in Construction.
Information & Authors
Information
Published In
Copyright
©2019 American Society of Civil Engineers.
History
Received: Oct 30, 2018
Accepted: Apr 19, 2019
Published online: Sep 28, 2019
Published in print: Dec 1, 2019
Discussion open until: Feb 28, 2020
Authors
Metrics & Citations
Metrics
Citations
Download citation
If you have the appropriate software installed, you can download article citation data to the citation manager of your choice. Simply select your manager software from the list below and click Download.