Mechanical and Durability Screening Test Methods for Cylindrical CFRP Prestressing Tendons
Publication: Journal of Composites for Construction
Volume 21, Issue 2
Abstract
Concrete prestressed with carbon fiber–reinforced polymer (CFRP) tendons beneficially utilizes the strain capacity and durability characteristics of the CFRP material. However, changes to CFRP tendon material formulations or production processes present a challenge when building up a body of knowledge to inform the long-term behavior of a prestressed concrete system. Initial qualification tests can help identify the potential for fiber–reinforced polymer (FRP) tendons to meet long-term mechanical and durability requirements. Protocols that can be undertaken on commercially produced cylindrical FRP pultrusions are particularly advantageous because the constituent materials and manufacturing processes are representative of the actual product. Selected mechanical and durability characterization approaches, and their suitability for adaptation for wet specimens with cylindrical geometries, were critically assessed. A series of qualification tests were then conducted on CFRP tendons with three different resin systems. Tendon samples were exposed to wet environments to evaluate the longer-term solution uptake and associated mechanical durability implications. While characterization measures such as the glass transition temperature, optical imaging, and moisture uptake provided comparative results, the correlation with mechanical properties obtained from uniaxial tension, double notch shear, and torsion tests was unclear. Using a subset of the mechanical test protocols, a retrospective analysis of CFRP tendons extracted from a prestressed concrete lighting pole under sustained load for 16.5 years was also reported.
Get full access to this article
View all available purchase options and get full access to this article.
Acknowledgments
The authors are very grateful to SACAC Ltd. for their technical advice and financial assistance. The work was supported by Swiss CTI-Project 8465.1 EPRP-IW. Funding from the Onassis Foundation for Eleni Toumpanaki is also appreciated.
References
ASTM. (2008a). “Standard test method for glass transition temperature (DMA Tg) of polymer matrix composites by dynamic mechanical analysis (DMA).” ASTM D7028-07, West Conshohocken, PA.
ASTM. (2008b). “Standard test method for shear modulus at room temperature.” ASTM E143-02, West Conshohocken, PA.
ASTM. (2009). “Standard test method for flexural properties of fiber reinforced pultruded plastic rods.” ASTM D4476-09, West Conshohocken, PA.
Bank, L. C., Gentry, T. R., Thompson, B. P., and Russell, J. S. (2003). “A model specification for FRP composites for civil engineering structures.” Constr. Build. Mater., 17(6-7), 405–437.
Bao, L. R., and Yee, A. F. (2002). “Moisture diffusion and hygrothermal aging in bismaleimide matrix carbon fiber composites—Part I: Uni-weave composites.” Compos. Sci. Technol., 62(16), 2099–2110.
Benmokrane, B., and Mohamed, H. M. (2013). “Durability issues of FRP for civil infrastructure.” 11th Int. Symp. on Fiber Reinforced Polymers for Reinforced Concrete Structures (FRPRCS-11), J. Barros and J. Sena-Cruz, eds., Universidade do Minho, Guimarães, Portugal.
Bowles, K. J., and Frimpong, S. (1992). “Void effects on the interlaminar shear strength of unidirectional graphite-fiber-reinforced composites.” J. Compos. Mater., 26(10), 1487–1509.
Bruggeling, A. S. G. (2001). “Übertragen der Vorspannung mittels Verbund [Prestress transfer by bond].” Beton und Stahlbetonbau [Concr. Reinf. Concr. Constr.], 96(3), 109–123 (in German).
Chen, Y., Davalos, J. F., Ray, I., and Kim, H.-Y. (2007). “Accelerated aging tests for evaluations of durability performance of FRP reinforcing bars for concrete structures.” Compos. Struct., 78(1), 101–111.
Costa, M. L., Rezende, M. C., and Almeida, S. F. M. (2004). “Strength of hygrothermally conditioned polymer composites with voids.” J. Compos. Mater., 39(21), 1943–1961.
Crank, J. (1975). The mathematics of diffusion, Clarendon Press, Oxford, U.K.
Davalos, J. F., Chen, Y., and Ray, I. (2008). “Effect of FRP bar degradation on interface bond with high strength concrete.” Cem. Concr. Compos., 30(8), 722–730.
DIN (Deutches Institut für Normung). (1986). “Standard: Prüfung von faserverstärkten Kunststoffen, Bestimmung der interlaminaren Scherfestigkeit im Zugversuch.” DIN 65148, Beuth Verlag GmbH, Berlin.
Empa (Eidgenössische Materialprüfanstalt). (2009). “New ways of increasing the prestress of filigree CFRP prestressed high performance concrete elements.”, Dübendorf, Switzerland.
Gentry, T. R. (2011). “Transverse shear of GFRP rods: Tests method development and potential for durability assessment.” 4th Int. Conf. on Durability and Sustainability of Fiber Reinforced Polymers (FRP) Composites for Construction and Rehabilitation, CDCC, 2011, Dept. of Civil Engineering, Faculty of Engineering, Université de Sherbrooke, Sherbrooke, Canada.
Giannakopoulos, G., Masania, K., and Taylor, A. C. (2011). “Toughening of epoxy using core-shell particles.” J. Mater. Sci., 46(2), 327–338.
Glaskova, T. I., Guedes, R. M., Morais, J. J., and Aniskevich, A. N. (2007). “A comparative analysis of moisture transport models as applied to an epoxy binder.” Mech. Compos. Mater., 43(4), 377–388.
Huntsman. (2004). “Advanced materials data sheet: Co-curing epoxy system based on Araldite LY 5052 / Aradur 5052.” Huntsman, Basel, Switzerland.
Keller, H. B., and Sachs, D. (1964). “Calculations of the conductivity of a medium containing cylindrical inclusions.” J. Appl. Phys., 35(3), 537–538.
Lees, J. M., and Burgoyne, C. J. (1999). “Experimental study of influence of bond on the flexural behavior of concrete beams pre-tensioned with AFRPs.” ACI Struct. J., 96(3), 377–385.
Mantell, C. L. (1968). Carbon and graphite handbook, Wiley, New York.
Micelli, F., and Nanni, A. (2004). “Durability of FRP rods for concrete structures.” Constr. Build. Mater., 18(7), 491–503.
Pettersson, K. B., and Neumeister, J. M. (2006). “A tensile setup for the IDNS composite shear test.” Compos. Part A: Appl. Sci. Manuf., 37(2), 229–242.
Scott, P., and Lees, J. M. (2012). “Effects of solution exposure on the combined axial-shear behaviour of unidirectional CFRP rods.” Compos. Part A: Appl. Sci. Manuf., 43(9), 1599–1611.
Shokrieh, M. M., and Lessard, L. B. (1998). “An assessment of the double-notch shear test for interlaminar shear characterization of a unidirectional graphite/epoxy under static and fatigue loading.” Appl. Compos. Mater., 5(5), 289–304.
Sims, G. D. (2007). “Review of composites standardisation status and activities.” National Composites Network, U.K.
Terrasi, G. P. (1998). “Mit Kohlenstoffasern vorgespannte Schleuderbetonrohre.” Ph.D. thesis, Eidgenössische Technische Hochschule (ETH), Zurich, Switzerland (in German).
Terrasi, G. P. (2013). “Prefabricated thin-walled structural elements made from high performance concrete prestressed with CFRP wires.” J. Mater. Sci. Res., 2(1), 1–14.
Terrasi, G. P., Affolter, C., and Barbezat, M. (2011a). “Numerical optimization of a compact and reusable pre-tensioning anchorage system for CFRP tendons.” J. Compos. Constr., 126–135.
Terrasi, G. P., Bisby, L., Barbezat, M., Affolter, C., and Hugi, E. (2012). “Fire behavior of thin CFRP pretensioned high-strength concrete slabs.” J. Compos. Constr., 381–394.
Terrasi, G. P., Broenimann, R., and Baettig, G. (2011b). “CFRP tendon prestress monitoring by resistance measurement in a high performance concrete powerline pylon.” Proc., SMAR 2011, 1st Middle East Conf. on Smart Monitoring, Assessment and Rehabilitation of Civil Structures, EMPA, Dübendorf, Swizterland.
Terrasi, G. P., Meier, U., and Affolter, C. (2014). “Long-term bending creep behavior of thin-walled CFRP tendon pretensioned spun concrete poles.” Polymers, 6(7), 2065–2081.
Toumpanaki, E., Lees, J. M., and Terrasi, G. P. (2013). “Effect of moisture uptake on the shear stiffness of CFRP tendons and the role of the manufacturing route.” FRPRCS11, 11th Int. Symp. on Fiber Reinforced Polymer for Reinforced Concrete Structures, J. Barros and J. Sena-Cruz, eds., Universidade do Minho, Guimarães, Portugal.
Toumpanaki, E., Lees, J. M., and Terrasi, G. P. (2015). “Shear modulus of cylindrical CFRP tendons exposed to moisture.” J. Compos. Constr., 04014059.
Uomoto, T. (2001). “Durability considerations for FRP reinforcements.” FRPRCS-5: Fibre-reinforced plastics for reinforced concrete structures, C. J. Burgoyne, ed., Thomas Telford, London, 17–32.
Vanlandingham, M. R., Eduljee, R. F., and Gillespie, J. W. (1999). “Relationships between stoichiometry, microstructure, and properties for amine-cured epoxies.” J. Appl. Polym. Sci., 71(5), 699–712.
Wright, W. W. (1981). “The effect of diffusion of water into epoxy resins and their carbon-fibre reinforced composites.” Composites, 12(3), 201–205.
Zhang, A. Y., Li, D. H., Zhang, D. X., Lu, H. B., Xiao, H. Y., and Jia, J. (2011). “Qualitative separation of the effect of voids on the static mechanical properties of hygrothermally conditioned carbon/epoxy composites.” Express Polym. Lett., 5(8), 708–716.
Information & Authors
Information
Published In
Copyright
©2016 American Society of Civil Engineers.
History
Received: Nov 3, 2015
Accepted: May 5, 2016
Published online: Aug 11, 2016
Discussion open until: Jan 11, 2017
Published in print: Apr 1, 2017
Authors
Metrics & Citations
Metrics
Citations
Download citation
If you have the appropriate software installed, you can download article citation data to the citation manager of your choice. Simply select your manager software from the list below and click Download.