Petrographic and Mechanical Analysis of Lightweight Polymer Concrete Subjected to Acidic Solution
Publication: Journal of Materials in Civil Engineering
Volume 35, Issue 1
Abstract
This study aims to compare the microstructural and mechanical properties of lightweight polymer concrete (LPC) and lightweight ordinary cement concrete (OCC) before and after exposure to a corrosive acidic environment. In this regard, LPC mixes were prepared with five different unsaturated polyester resin contents (15%–27%) and combinations of lightweight expanded clay aggregate (LECA) and natural river sand. Thereafter, specimens were exposed to sulfuric acid solution for up to 90 days. In addition to visual inspections, physical and mechanical properties [mass and volume changes, compression strength, and modulus of elasticity (MOE)], petrographic inspections, and scanning electron microscope investigations were carried out. Mechanical results showed that LPCs had by far better mechanical features compared with OCC, where at the optimum mix comprised of 24% polymer, reduction of 6% for compression, and 7% for MOE was observed, whereas these values were respectively 70% and 55% for OCC at the same conditions. Outcomes of microscopic observations indicated that increasing the polymer content resulted in strengthening the bond between binder and aggregates where pores were filled by resin. In addition, the impact of the acidic solution on the LPC mixes was less pronounced than for OCC mixes, and lamination of the matrix and affected polymer areas were reduced in LPC mixes with a resin content of 24% and 27%. After 90 days, a slight reduction in properties of LPC specimens and degradation was observed due to the reaction of the acid with the surface of LPC specimens.
Get full access to this article
View all available purchase options and get full access to this article.
Data Availability Statement
No data, models, or code were generated or used during the study.
References
Abdel-Jawad, Y. A., and W. S. Abdullah. 2002. “Design of maximum density aggregate grading.” Constr. Build. Mater. 16 (8): 495–508. https://doi.org/10.1016/S0950-0618(02)00032-6.
ACI (American Concrete Institute). 2014. Guide for structural lightweight-aggregate concrete. ACI 213R-14. Farmington Hills, MI: ACI.
Ahn, N. 2004. “Effects of diacrylate monomers on the mechanical properties of polymer concrete made with wet aggregates.” J. Appl. Polym. Sci. 94 (3): 1077–1085. https://doi.org/10.1002/app.13407.
Alnahhal, M. F., U. J. Alengaram, M. Z. Jumaat, B. Alsubari, M. A. Alqedra, and K. H. Mo. 2018. “Effect of aggressive chemicals on durability and microstructure properties of concrete containing crushed new concrete aggregate and non-traditional supplementary cementitious materials.” Constr. Build. Mater. 163 (Feb): 482–495. https://doi.org/10.1016/j.conbuildmat.2017.12.106.
ASTM. 2004 Standard practice for petrographic examination of hardened concrete. ASTM C856. West Conshohocken, PA: ASTM.
ASTM. 2007. Standard test method for density, relative density (specific gravity), and absorption of fine aggregate. ASTM C128-07a. West Conshohocken, PA: ASTM.
ASTM. 2012a. Standard test method for density, relative density (specific gravity), and absorption of coarse aggregate. ASTM C127. West Conshohocken, PA: ASTM.
ASTM. 2012b. Standard test methods for compressive strength of chemical-resistant mortars, grouts, monolithic surfacings, and polymer concretes. ASTM C579. West Conshohocken, PA: ASTM.
ASTM. 2013. Standard test method for indentation hardness of rigid plastics by means of a Barcol impressor, American Society for Testing and Material. ASTM D2583. West Conshohocken, PA: ASTM.
ASTM. 2014. Standard test method for static modulus of elasticity and Poisson’s ratio of concrete in compression. ASTM C469/C469M-14. West Conshohocken, PA: ASTM.
Ataabadi, H. S., A. Sedaghatdoost, H. Rahmani, and A. Zare. 2021. “Microstructural characterization and mechanical properties of lightweight polymer concrete exposed to elevated temperatures.” Constr. Build. Mater. 311 (Dec): 125293. https://doi.org/10.1016/j.conbuildmat.2021.125293.
Aulia, T. B., and K. Deutschmann. 1999. “Effect of mechanical properties of aggregate on the ductility of high performance concrete.” Lacer 4 (Jan): 133–147.
Bărbuţă, M., M. Harja, and I. Baran. 2010. “Comparison of mechanical properties for polymer concrete with different types of filler.” J. Mater. Civ. Eng. 22 (7): 696–701. https://doi.org/10.1061/(ASCE)MT.1943-5533.0000069.
Bărbuţă, M., and I.-O. Toma. 2015. “Experimental evaluation of strength and elastic properties of polymer concrete with different volumes of volcanic tuff acting as filler.” J. Mater. Civ. Eng. 27 (6): 04014191. https://doi.org/10.1061/(ASCE)MT.1943-5533.0001155.
Chawla, K., B. Raju, D. B. Subbappa, K. B. Kancherla, and D. Roy Mahapatra. 2021. “Micromechanical effect of pores on elastic properties of polymer matrix composites.” Polym. Compos. 42 (3): 1497–1518. https://doi.org/10.1002/pc.25919.
Elalaoui, O., E. Ghorbel, V. Mignot, and M. B. Ouezdou. 2012. “Mechanical and physical properties of epoxy polymer concrete after exposure to temperatures up to 250 C.” Constr. Build. Mater. 27 (1): 415–424. https://doi.org/10.1016/j.conbuildmat.2011.07.027.
Ferdous, W., A. Manalo, H. S. Wong, R. Abousnina, O. S. AlAjarmeh, Y. Zhuge, and P. Schubel. 2020. “Optimal design for epoxy polymer concrete based on mechanical properties and durability aspects.” Constr. Build. Mater. 232 (Jan): 117229. https://doi.org/10.1016/j.conbuildmat.2019.117229.
Fowler, D. W. 2003. “Polymers in concrete: Where have we been and where are we going?” Spec. Publ. 214: 111–118.
Fuller, W. B., and S. E. Thompson. 1907. “The laws of proportioning concrete.” Trans. Am. Soc. Civ. Eng. 59 (2): 67–143. https://doi.org/10.1061/TACEAT.0001979.
Ghassemi, P., H. Rajabi, and V. Toufigh. 2020. “Fatigue performance of polymer and ordinary cement concrete under corrosive conditions: A comparative study.” Eng. Fail. Anal. 111 (Apr): 104493. https://doi.org/10.1016/j.engfailanal.2020.104493.
Gorninski, J., D. Dal Molin, and C. Kazmierczak. 2007. “Strength degradation of polymer concrete in acidic environments.” Cem. Concr. Compos. 29 (8): 637–645. https://doi.org/10.1016/j.cemconcomp.2007.04.001.
Gorninski, J. P., D. C. Dal Molin, and C. S. Kazmierczak. 2004. “Study of the modulus of elasticity of polymer concrete compounds and comparative assessment of polymer concrete and portland cement concrete.” Cem. Concr. Res. 34 (11): 2091–2095. https://doi.org/10.1016/j.cemconres.2004.03.012.
Haidar, M., E. Ghorbel, and H. Toutanji. 2011. “Optimization of the formulation of micro-polymer concretes.” Constr. Build. Mater. 25 (4): 1632–1644. https://doi.org/10.1016/j.conbuildmat.2010.10.010.
Hashemi, M., M. Jamshidi, and J. H. Aghdam. 2018. “Investigating fracture mechanics and flexural properties of unsaturated polyester polymer concrete (UP-PC).” Constr. Build. Mater. 163 (Feb): 767–775. https://doi.org/10.1016/j.conbuildmat.2017.12.115.
Hashemi, M. J., and M. Jamshidi. 2015. “Flexural behavior of polyester polymer concrete subjected to different chemicals.” Int. J. Eng. 28 (7): 978–983.
He, K., H. Yang, Z. Lu, F. Jia, E. Wang, and Q. Dong. 2014. “Effect of matrix modification on durability of cementitious composites in an acid rain environment.” J. Wuhan Univ. Technol. Mater. Sci. Ed. 29 (3): 498–503. https://doi.org/10.1007/s11595-014-0947-y.
Heidari-Rarani, M., M. Aliha, M. Shokrieh, and M. Ayatollahi. 2014. “Mechanical durability of an optimized polymer concrete under various thermal cyclic loadings–An experimental study.” Constr. Build. Mater. 64 (Aug): 308–315. https://doi.org/10.1016/j.conbuildmat.2014.04.031.
Heidarnezhad, F., K. Jafari, and T. Ozbakkaloglu. 2020. “Effect of polymer content and temperature on mechanical properties of lightweight polymer concrete.” Constr. Build. Mater. 260 (Nov): 119853. https://doi.org/10.1016/j.conbuildmat.2020.119853.
Hill, J., E. Byars, J. Sharp, C. Lynsdale, J. Cripps, and Q. Zhou. 2003. “An experimental study of combined acid and sulfate attack of concrete.” Cem. Concr. Compos. 25 (8): 997–1003. https://doi.org/10.1016/S0958-9465(03)00123-9.
Hong, S., H. Kim, and S.-K. Park. 2016. “Optimal mix and freeze-thaw durability of polysulfide polymer concrete.” Constr. Build. Mater. 127 (Nov): 539–545. https://doi.org/10.1016/j.conbuildmat.2016.10.056.
Huang, H., J. Hao, B. Zhao, X. Zhao, M. Li, J. Li, and J. Liu. 2017. “Experimental study on low temperature tensile properties of epoxy mortar in hydropower project.” Energy Procedia 105 (May): 1205–1210. https://doi.org/10.1016/j.egypro.2017.03.414.
Hwang, E. H., J. M. Kim, and J. H. Yeon. 2013. “Characteristics of polyester polymer concrete using spherical aggregates from industrial by-products.” J. Appl. Polym. Sci. 129 (5): 2905–2912. https://doi.org/10.1002/app.39025.
ISO. 1985. Plastics—Liquid resins—Determination of density by the pyknometer method. ISO 1675:1985. Geneva: ISO.
ISO. 2000. Plastics (polyester resins) and paints and varnishes (binders)—Determination of partial acid value and total acid value. ISO 2114:2000. Geneva: ISO.
ISO. 2008. Paints, varnishes and plastics—Determination of non-volatile-matter content. ISO 3251:2008. Geneva: ISO.
ISO. 2012. Plastics—Determination of tensile properties. ISO 527-1: 2012. Geneva: ISO.
ISO. 2013. Plastics—Determination of temperature of deflection under load—Part 1: General test method. ISO 75-1: 2013. Geneva: ISO.
Jackson, N., and K. Dir. 1996. Civil engineering materials. 5th ed. London: Macmillan.
Jamshidi, M., M. Alizadeh, M. Salar, and A. Hashemi. 2013. “Durability of polyester resin concrete in different chemical solutions.” In Proc., Advanced Materials Research, 150–154. Tehran, Iran: Trans Tech.
Jo, B.-W., S.-K. Park, and J.-C. Park. 2008. “Mechanical properties of polymer concrete made with recycled PET and recycled concrete aggregates.” Constr. Build. Mater. 22 (12): 2281–2291. https://doi.org/10.1016/j.conbuildmat.2007.10.009.
Kiliswa, M. W., K. L. Scrivener, and M. G. Alexander. 2019. “The corrosion rate and microstructure of portland cement and calcium aluminate cement-based concrete mixtures in outfall sewers: A comparative study.” Cem. Concr. Res. 124 (Oct): 105818. https://doi.org/10.1016/j.cemconres.2019.105818.
Kim, S.-S., J.-B. Lee, T.-J. Cho, and R. D. Hooton. 2014. “Determination of optimum glass transition temperature of acrylic acid ester copolymer to improve performance of cement matrixes.” ACI Mater. J. 111 (5): 521–530.
Lee, S. T., R. D. Hooton, H.-S. Jung, D.-H. Park, and C. S. Choi. 2008. “Effect of limestone filler on the deterioration of mortars and pastes exposed to sulfate solutions at ambient temperature.” Cem. Concr. Res. 38 (1): 68–76. https://doi.org/10.1016/j.cemconres.2007.08.003.
Liu, W., J. Wu, and H. Ge. 2016. “Influence of aggregate on the mechanical properties of UP polymer concrete.” In Proc., 2016 5th Int. Conf. on Advanced Materials and Computer Science (ICAMCS 2016). Beijing: Atlantis Press.
Mahmoodian, M., and A. M. Alani. 2017. “Effect of temperature and acidity of sulfuric acid on concrete properties.” J. Mater. Civ. Eng. 29 (10): 04017154. https://doi.org/10.1061/(ASCE)MT.1943-5533.0002002.
Monteny, J., N. De Belie, E. Vincke, W. Verstraete, and L. Taerwe. 2001. “Chemical and microbiological tests to simulate sulfuric acid corrosion of polymer-modified concrete.” Cem. Concr. Res. 31 (9): 1359–1365. https://doi.org/10.1016/S0008-8846(01)00565-8.
Muthukumar, M., and D. Mohan. 2005. “Studies on furan polymer concrete.” J. Polym. Res. 12 (3): 231–241. https://doi.org/10.1007/s10965-004-3206-7.
Neville, A. M. 1995. Properties of concrete. London: Longman.
Norwood, L. 1980. “Polyester resins in corrosive environments.” In Vol. 4 of Proc., Pipecon Int. Conf. on Large Diameter Glass Reinforced Plastic Pipes, 1–10. London: Springer.
Ohama, Y. 1997. “Recent progress in polymer mortar and concrete in Japan.” In Proc., 2nd East Asia Symp. on Polymers in Concrete (II-EASPIC), 21–30. Paris: RILEM.
Ong, F. S., E. K. Attiogbe, C. K. Nmai, and J. C. Smith. 2015. “Freezing-and-thawing behavior of cementitious systems with new polymeric microsphere-based admixture.” ACI Mater. J. 112 (6): 735–743. https://doi.org/10.14359/51687977.
Park, S., L. Castellano, M. A. Barlaz, and M. Pour-Ghaz. 2020. “Abrasion resistance of concrete exposed to organic acids.” J. Mater. Civ. Eng. 32 (8): 04020205. https://doi.org/10.1061/(ASCE)MT.1943-5533.0003251.
Rahmani, H., and A. Ramazanianpour. 2008. “Effect of binary cement replacement materials on sulfuric acid resistance of dense concretes.” Mag. Concr. Res. 60 (2): 145–155. https://doi.org/10.1680/macr.2008.60.2.145.
Reis, J. 2010. “Fracture assessment of polymer concrete in chemical degradation solutions.” Constr. Build. Mater. 24 (9): 1708–1712. https://doi.org/10.1016/j.conbuildmat.2010.02.020.
Reis, J., A. Carvalho, and H. da Costa Mattos. 2014. “Effects of displacement rate and temperature on the fracture properties of polymer mortars.” Constr. Build. Mater. 55 (Mar): 1–4. https://doi.org/10.1016/j.conbuildmat.2014.01.017.
Reis, J. M., and M. A. Jurumenh. 2011. “Experimental investigation on the effects of recycled aggregate on fracture behavior of polymer concrete.” Mater. Res. 14 (3): 326–330. https://doi.org/10.1590/S1516-14392011005000060.
Ribeiro, M., P. Nóvoa, A. Ferreira, and A. Marques. 2004. “Flexural performance of polyester and epoxy polymer mortars under severe thermal conditions.” Cem. Concr. Compos. 26 (7): 803–809. https://doi.org/10.1016/S0958-9465(03)00162-8.
Ries, J. M. L. 2009. “Mechanical characterization of polymer mortars exposed to degradation solutions.” Constr. Build. Mater. 23 (11): 3328–3331. https://doi.org/10.1016/j.conbuildmat.2009.06.047.
Sanaei Ataabadi, H., E. Mirzaei, and A. Sedaghatdoost. 2021a. “Effect of polypropylene and polyvinyl alcohol fibers on characteristics and microstructure of polymer composite.” Polym. Compos. 42 (4): 1782–1794. https://doi.org/10.1002/pc.25933.
Sanaei Ataabadi, H., A. Zare, H. Rahmani, A. Sedaghatdoost, and E. Mirzaei. 2021b. “Lightweight dense polymer concrete exposed to chemical condition and various temperatures: An experimental investigation.” J. Build. Eng. 34 (Feb): 101878. https://doi.org/10.1016/j.jobe.2020.101878.
Santhanam, M., M. D. Cohen, and J. Olek. 2002. “Mechanism of sulfate attack: A fresh look: Part 1: Summary of experimental results.” Cem. Concr. Res. 32 (6): 915–921. https://doi.org/10.1016/S0008-8846(02)00724-X.
Schmidt, T., B. Lothenbach, M. Romer, J. Neuenschwander, and K. Scrivener. 2009. “Physical and microstructural aspects of sulfate attack on ordinary and limestone blended portland cements.” Cem. Concr. Res. 39 (12): 1111–1121. https://doi.org/10.1016/j.cemconres.2009.08.005.
Shakhmenko, G., and J. Birsh. 1998. “Concrete mix design and optimization.” In Proc., 2nd Int. Symp. in Civil Engineering. Lausanne, Switzerland: International Federation for Structural Concrete.
Shen, Y., B. Liu, J. Lv, and M. Shen. 2019. “Mechanical properties and resistance to acid corrosion of polymer concrete incorporating ceramsite, fly ash and glass fibers.” Materials 12 (15): 2441. https://doi.org/10.3390/ma12152441.
Siad, H., M. Lachemi, M. Sahmaran, and K. M. A. Hossain. 2016. “Effect of glass powder on sulfuric acid resistance of cementitious materials.” Constr. Build. Mater. 113 (Jun): 163–173. https://doi.org/10.1016/j.conbuildmat.2016.03.049.
Siddique, R., J. Khatib, and I. Kaur. 2008. “Use of recycled plastic in concrete: A review.” Waste Manage. 28 (10): 1835–1852. https://doi.org/10.1016/j.wasman.2007.09.011.
Tasnim, S., and F. U. A. Shaikh. 2021. “Effect of chemical exposure on mechanical properties and microstructure of lightweight polymer composites containing solid waste fillers.” Constr. Build. Mater. 309 (Nov): 125192. https://doi.org/10.1016/j.conbuildmat.2021.125192.
Taylor, G. D. 1994. Materials in construction. London: Longman, Scientific & Technical.
Thomas, M. D. A., and K. J. Folliard. 2007. “Concrete aggregates and the durability of concrete.” In Durability of concrete and cement composites, edited by C. L. Page and M. M. Page, 247–281. Cambridge, UK: Woodhead.
Toufigh, V., M. J. Abyaneh, and K. Jafari. 2017. “Study of behavior of concrete under axial and triaxial compression.” ACI Mater. J. 114 (4): 619–629. https://doi.org/10.14359/51689716.
Tupý, M., K. Sotiriadis, I. Kusák, D. Štefková, M. Luňák, and V. Petránek. 2016. “Exposure of mortars modified with rubber aggregates and polymer admixtures to acid environments and elevated temperature conditions.” J. Mater. Civ. Eng. 28 (4): 04015171. https://doi.org/10.1061/(ASCE)MT.1943-5533.0001433.
Vaezi, M., A. Sedaghatdoost, M. N. Norouzifar, and H. Madani. 2021. “Petrographic investigation into the influence of chopped basalt fibers on the microstructure of portland cement mortars at elevated temperatures.” J. Mater. Civ. Eng. 33 (5): 04021078. https://doi.org/10.1061/(ASCE)MT.1943-5533.0003704.
Wang, J., Q. Dai, S. Guo, and R. Si. 2019. “Mechanical and durability performance evaluation of crumb rubber-modified epoxy polymer concrete overlays.” Constr. Build. Mater. 203 (Apr): 469–480. https://doi.org/10.1016/j.conbuildmat.2019.01.085.
Wang, X., and M. Petrů. 2019. “Freeze–thaw resistance of epoxy/concrete interface evaluated by a novel wedge splitting test.” Constr. Build. Mater. 210 (Jun): 434–441. https://doi.org/10.1016/j.conbuildmat.2019.03.139.
Wang, Y., B. Huang, Z. Mao, M. Deng, and H. Cao. 2020. “Effect of a boric acid corrosive environment on the microstructure and properties of concrete.” Materials 13 (21): 5036. https://doi.org/10.3390/ma13215036.
Yeon, K.-S., Y.-S. Choi, K.-K. Kim, and J. H. Yeon. 2017. “Flexural fatigue life analysis of unsaturated polyester-methyl methacrylate polymer concrete.” Constr. Build. Mater. 140 (Jun): 336–343. https://doi.org/10.1016/j.conbuildmat.2017.02.116.
Zhang, H., G. Zhang, F. Han, Z. Zhang, and W. Lv. 2018. “A lab study to develop a bridge deck pavement using bisphenol A unsaturated polyester resin modified asphalt mixture.” Constr. Build. Mater. 159 (Jan): 83–98. https://doi.org/10.1016/j.conbuildmat.2017.10.126.
Information & Authors
Information
Published In
Copyright
© 2022 American Society of Civil Engineers.
History
Received: Dec 9, 2021
Accepted: Apr 29, 2022
Published online: Oct 22, 2022
Published in print: Jan 1, 2023
Discussion open until: Mar 22, 2023
Authors
Metrics & Citations
Metrics
Citations
Download citation
If you have the appropriate software installed, you can download article citation data to the citation manager of your choice. Simply select your manager software from the list below and click Download.