Mechanical Behavior and Thermal Oxidative Aging of Anhydride-Cured Epoxy Asphalt with Different Asphalt Contents
Publication: Journal of Materials in Civil Engineering
Volume 34, Issue 10
Abstract
Anhydride-cured epoxy asphalt (AC-EA) is an asphalt/resin two-phase system, the properties of which are affected by the asphalt and resin contents. This study aims to investigate the effect of asphalt content on the tensile properties, hardness, dynamic mechanical parameters, chemical components, and microscopic structure of AC-EA through experimental methods. Thermal aging resistance and mechanism of AC-EA with the asphalt content of 25%, 35%, 45%, 55%, and 65% were also investigated. The results show that as the asphalt content increased from 25% to 65%, the tensile strength and hardness of AC-EA binder increased first and then decreased, the elongation decreased, the glass transition temperature () rose, and the carbonyl absorption band changed from a single peak to double peak. The absorption bands of aromatic ether and sulfoxide in AC-EA binder overlapped with each other. The carbonyl ester index (CEI) and sulfoxide index (SI) showed a good linear correlation with the asphalt content. Besides, phase inversion occurred in the AC-EA system when the asphalt content was between 45% and 55%. AC-EA binder with an asphalt content less than 45% is a resin-based composite, and that with the asphalt content higher than 45% is an asphalt-based composite. At the thermal aging process, AC-EA binders with asphalt content higher than 45% were more likely to cause significant changes in the tensile parameters, hardness, and modulus than those with asphalt content less than 45%, indicating that the existence of the resin network can reduce the sensitivity of AC-EA to oxidation. After aging, of resin-based composites increased, whereas that of asphalt-based composites decreased. The Fourier transform infrared (FTIR) and scanning electron microscope (SEM) analyses indicated that the AC-EA binder had both postcuring and oxidative degradation during thermal aging. The postcuring was dominant in the resin-based AC-EA composite, whereas the oxidative degradation was dominant in the asphalt-based composite.
Get full access to this article
View all available purchase options and get full access to this article.
Data Availability Statement
All data and models generated or used during the study appear in this article.
Acknowledgments
This study was supported by the National Key R&D Program of China (Grant No. 2018YFB1600100).
References
Apostolidis, P., X. Liu, S. Erkens, and A. Scarpas. 2019. “Evaluation of epoxy modification in bitumen.” Constr. Build. Mater. 208 (Mar): 361–368. https://doi.org/10.1016/j.conbuildmat.2019.03.013.
Apostolidis, P., X. Liu, S. Erkens, and T. Scarpas. 2020. “Oxidative aging of epoxy asphalt.” Int. J. Pavement Eng. 2020 (Aug): 1–11. https://doi.org/10.1080/10298436.2020.1806278.
ASTM. 2014. Standard test method for tensile properties of plastics. ASTM D638. West Conshohocken, PA: ASTM.
ASTM. 2018. Standard test method for assignment of the glass transition temperature by dynamic mechanical analysis. ASTM E1640. West Conshohocken, PA: ASTM.
ASTM. 2021. Standard test method for rubber property—Durometer hardness. ASTM D2240. West Conshohocken, PA: ASTM.
Cheng, L., J. Yu, Q. Zhao, J. Wu, and L. Zhang. 2020. “Chemical, rheological and aging characteristic properties of Xinjiang rock asphalt-modified bitumen.” Constr. Build. Mater. 240 (Dec): 117908. https://doi.org/10.1016/j.conbuildmat.2019.117908.
Cong, P., W. Luo, P. Xu, and Y. Zhang. 2019. “Chemical and physical properties of hot mixing epoxy asphalt binders.” Constr. Build. Mater. 198 (Dec): 1–9. https://doi.org/10.1016/j.conbuildmat.2018.11.275.
Dai, X., J. Xiao, J. Ceng, J. Liu, C. Yin, and Z. Liu. 2008. “Curing kinetics of epoxy resin for RFI process using isothermal DSC.” [In Chinese.] Acta Mater. Compos. Sin. 25 (4): 18–23. https://doi.org/10.13801/j.cnki.fhclxb.2008.04.003.
Delor-Jestin, F., D. Drouin, P. Cheval, and J. Lacoste. 2006. “Thermal and photochemical ageing of epoxy resin—Influence of curing agents.” Polym. Degrad. Stab. 91 (6): 1247–1255. https://doi.org/10.1016/j.polymdegradstab.2005.09.009.
Ge, D., S. Chen, Z. You, and X. Yang. 2019. “Correlation of DSR results and FTIR’s carbonyl and sulfoxide indexes: Effect of aging temperature on asphalt rheology.” J. Mater. Civ. Eng. 31 (7): 04019115. https://doi.org/10.1061/(ASCE)MT.1943-5533.0002781.
Glavchev, I., K. Petrova, and P. Devedjiev. 2002. “Determination of the activity of phosphorus containing compounds on the crosslinking of epoxy resins by acid anhydrides.” Polym. Test. 21 (3): 243–245. https://doi.org/10.1016/S0142-9418(01)00075-7.
Gong, Z. 2016. “Study on the erosion wear of modified epoxy and its composite.” [In Chinese.] Master dissertation, Dept. of Civil and Environmental Engineering, Lanzhou Jiaotong Univ.
Herrington, P., and D. Alabaster. 2008. “Epoxy modified open-graded porous asphalt.” Road Mater. Pavement Des. 9 (3): 481–498. https://doi.org/10.1080/14680629.2008.9690129.
Jamshidi, A., G. White, and K. Kurumisawa. 2021. “Rheological characteristics of epoxy asphalt binders and engineering properties of epoxy asphalt mixtures—State-of-the-art.” Road Mater. Pavement Des. 2021 (Aug): 1–24. https://doi.org/10.1080/14680629.2021.1963814.
Kang, Y., Z. Chen, Z. Jiao, and W. Huang. 2010. “Rubber-like thermosetting epoxy asphalt composites exhibiting atypical yielding behaviors.” J. Appl. Polym. Sci. 116 (3): 1678–1685. https://doi.org/10.1002/app.31563.
Kang, Y., R. Jin, Q. Wu, L. Pu, M. Song, J. Cheng, and P. Yu. 2016. “Anhydrides-cured bimodal rubber-like epoxy asphalt composites: From thermosetting to quasi-thermosetting.” Polymer 8 (4): 1042011. https://doi.org/10.3390/polym8040104.
Li, K., K. Wang, M. Zhan, and W. Xu. 2013. “The change of thermal-mechanical properties and chemical structure of ambient cured DGEBA/TEPA under accelerated thermo-oxidative aging.” Polym. Degrad. Stab. 98 (11): 2340–2346. https://doi.org/10.1016/j.polymdegradstab.2013.08.014.
Li, P., Z. Ding, Z. Zhang, and Z. Wang. 2008. “Research on behavior and mechanism of thermo aging without oxygen of asphalt.” [In Chinese.] New Build. Mater. 35 (7): 60–63. https://doi.org/10.3969/j.issn.1001-702X.2008.07.018.
Min Z. 2004. “Development and performance research of thermosetting epoxy asphalt and its mixture.” [In Chinese.] Doctoral dissertation, Dept. of Civil and Environmental Engineering, Southeast Univ.
Min, Z., L. Sun, Q. Wang, and Z. Yu. 2020. “Influence of aggregate packing on the performance of uncured and cured epoxy asphalt mixtures.” J. Mater. Civ. Eng. 32 (5): 04020103. https://doi.org/10.1061/(ASCE)MT.1943-5533.0003149.
Min, Z., Q. Wang, Y. Xie, J. Xie, and B. Zhang. 2021. “Influence of polyethylene glycol (PEG) chain on the performance of epoxy asphalt binder and mixture.” Constr. Build. Mater. 272 (Nov): 121614. https://doi.org/10.1016/j.conbuildmat.2020.121614.
Min, Z., L. Zhou, Q. Wang, and Y. Zhang. 2019. “Performance evaluation of epoxy-asphalt mixture blended with glass aggregate.” J. Mater. Civ. Eng. 31 (6): 04019083. https://doi.org/10.1061/(ASCE)MT.1943-5533.0002731.
Ollier-Dureault, V., and B. Gosse. 1998. “Photooxidation of anhydride-cured epoxies: FTIR study of the modifications of the chemical structure.” J. Appl. Polym. Sci. 70 (6): 1221–1237. https://doi.org/10.1002/(SICI)1097-4628(19981107)70:6%3C1221::AID-APP19%3E3.0.CO;2-1.
Singh, B., N. Saboo, and P. Kumar. 2017. “Effect of short-term aging on creep and recovery response of asphalt binders.” J. Transp. Eng., Part B 143 (4): 04017017. https://doi.org/10.1061/JPEODX.0000018.
Tan, X., J. Zhang, D. Guo, G. Sun, Y. Zhou, W. Zhang, and Y. Guan. 2020. “Preparation, characterization and repeated repair ability evaluation of asphalt-based crack sealant containing microencapsulated epoxy resin and curing agent.” Constr. Build. Mater. 256 (May): 119433. https://doi.org/10.1016/j.conbuildmat.2020.119433.
Wang, J., L. Yu, and S. Luo. 2015. “Service condition system and analysis of epoxy asphalt concrete pavement on Nanjing Second Yangtze River Bridge after thirteen years life.” [In Chinese.] Highway 60 (8): 37–40.
Wen, S. 2018. Fourier transform infrared spectroscopy analysis. Beijing: Chemical Industry Press.
Wu, J., P. Herrington, and D. Alabaster. 2019. “Long-term durability of epoxy modified open graded porous asphalt wearing course.” Int. J. Pavement Eng. 20 (8): 920–927. https://doi.org/10.1080/10298436.2017.1366764.
Wu, Q., C. Wang, R. Liang, Y. Liu, J. Cheng, and Y. Kang. 2018. “Fractional linear viscoelastic constitutive relations of anhydride-cured thermosetting rubber-like epoxy asphalt binders.” Constr. Build. Mater. 170 (Mar): 582–590. https://doi.org/10.1016/j.conbuildmat.2018.03.060.
Yang, Y., Z. Qian, and X. Song. 2015a. “A pothole patching material for epoxy asphalt pavement on steel bridges: Fatigue test and numerical analysis.” Constr. Build. Mater. 94 (Sep): 299–305. https://doi.org/10.1016/j.conbuildmat.2015.07.017.
Yang, Y., G. Xian, H. Li, and L. Sui. 2015b. “Thermal aging of an anhydride-cured epoxy resin.” Polym. Degrad. Stab. 118 (May): 111–119. https://doi.org/10.1016/j.polymdegradstab.2015.04.017.
Youtcheff, J., N. Gibson, A. Shenoy, and A. Al-Khateeb. 2006. “The evaluation of epoxy asphalt and epoxy asphalt mixtures.” In Proc., 51st Annual Conf. of the Canadian Technical Asphalt Association, 351–368. West Kelowna, Canada: Canadian Technical Asphalt Association.
Zeng, G., W. Xu, H. Huang, and X. Zhang. 2019. “SEM Study on the microstructure and properties of hot-mix epoxy asphalt.” Int. J. Pavement Res. Technol. 12 (2): 147–153. https://doi.org/10.1007/s42947-019-0019-y.
Information & Authors
Information
Published In
Copyright
© 2022 American Society of Civil Engineers.
History
Received: Oct 26, 2021
Accepted: Jan 27, 2022
Published online: Jul 19, 2022
Published in print: Oct 1, 2022
Discussion open until: Dec 19, 2022
Authors
Metrics & Citations
Metrics
Citations
Download citation
If you have the appropriate software installed, you can download article citation data to the citation manager of your choice. Simply select your manager software from the list below and click Download.
Cited by
- Qichang Wang, Zhaohui Min, Wei Huang, Zhiyong Shi, Investigation on the Photo-Oxidative Degradation of Amine-Based Epoxy Asphalt Binder, Journal of Materials in Civil Engineering, 10.1061/JMCEE7.MTENG-17804, 36, 9, (2024).
- Fei Chen, Zhaohui Min, Mingyue Li, Zhiyong Shi, Yingqin Zhao, Jiliang Feng, Preparation and Performance Evaluation of Warm-Mixed Epoxy Asphalt Ultrathin Overlay by Post-Doping Method, Journal of Materials in Civil Engineering, 10.1061/JMCEE7.MTENG-16527, 36, 6, (2024).
- Qichang Wang, Zhaohui Min, Yiik Diew Wong, Zhiyong Shi, Wei Huang, Aging degradation of anhydride-cured epoxy asphalt binder subjected to ultraviolet exposure, International Journal of Pavement Engineering, 10.1080/10298436.2023.2171037, 24, 1, (2023).
- Fenglei Zhang, Pengfei Yao, Xiaoxuan Guo, Lei Zhang, Kai Huang, Study on the Performance of Epoxy Asphalt with Different Matrix Asphalt Contents, Journal of Materials in Civil Engineering, 10.1061/JMCEE7.MTENG-15788, 35, 10, (2023).
- Zhaohui Min, Zhiyong Shi, Mingyue Li, Guofeng Lin, Wei Huang, Performance Evaluation of Epoxy Asphalt Mixtures Prepared with Basalt and Limestone Aggregate under Different Epoxy System Contents, Journal of Materials in Civil Engineering, 10.1061/JMCEE7.MTENG-15482, 35, 7, (2023).
- Jakub Szabelski, Robert Karpiński, Józef Jonak, Mariaenrica Frigione, Adhesive Joint Degradation Due to Hardener-to-Epoxy Ratio Inaccuracy under Varying Curing and Thermal Operating Conditions, Materials, 10.3390/ma15217765, 15, 21, (7765), (2022).