Abstract
Cross-laminated timber (CLT) panels have been adopted as main structural elements in the mass timber constructions that have recently caught the attention from different stakeholders. The enhanced mechanical performances allow the design of impressive structures like tall buildings. However, not so much is known about the performance of CLT panels under service life condition. In this context, the strain distribution taken from an experimental campaign carried out using Digital Image Correlation (DIC) is considered as a basis to investigate the stress distribution presented by CLT panels under cyclic moisture variations. Four CLT configurations promoting different moisture flow were conditioned in climatic chambers for 324 days at a constant temperature of 20°C, and with a humidity cycle varying every 21 days between 30% and 90%, getting constant at 65% after the first 142 days. Strains calculated through DIC, along with moduli of elasticity defined by ultrasound tests, were used to estimate strained and released stresses, respectively, before and after cutting specimens. Results show that sealing CLT panels play an insignificant role on distribution of stress induced by cyclic moisture, but peak stresses, both tension and compression resulted from wetting and drying cycles, respectively, were reduced in many specimens, especially when longitudinal faces were sealed. Moreover, as general recommendations to take in the design of CLT panels regarding moisture changes, it is possible to identify the need to limit the longitudinal length of panels, to use more thin layers rather than less thick ones, and to protect panels in the longitudinal direction, owing to high stress concentrated along this direction, particularly in the borders.
Get full access to this article
View all available purchase options and get full access to this article.
Data Availability Statement
All data, models, and code generated or used during the study appear in the published article.
References
Angst, V., and K. A. Malo. 2010. “Moisture induced stresses perpendicular to the grain in glulam: Review and evaluation of the relative importance of models and parameters.” Holzforschung 64 (5): 609–617. https://doi.org/10.1515/hf.2010.089.
Angst, V., and K. A. Malo. 2012. “The effect of climate variations on glulam—An experimental study.” Eur. J. Wood Wood Prod. 70 (5): 603–613. https://doi.org/10.1007/s00107-012-0594-y.
Angst, V., and K. A. Malo. 2013. “Moisture-induced stresses in glulam cross sections during wetting exposures.” Wood Sci. Technol. 47 (2): 227–241. https://doi.org/10.1007/s00226-012-0493-8.
BSI (British Standard Institution). 2003. Timber structures: Structural timber and glued laminated timber – Determination of some physical and mechanical properties. London: BSI.
CEN (European Committee for Standardization). 2002. Moisture content of a piece of sawn timber—Part 1: Determination by oven dry method. EN 13183-1:2002. Brussels, Belgium: CEN.
CEN (European Committee for Standardization). 2004. Design of timber structures. Part 1-1: General-common rules and rules for buildings. EN 1995-1-1:2004, Eurocode 5. Brussels, Belgium: CEN.
CEN (European Committee for Standardization). 2016. Structural timber—Determination of characteristic values of mechanical properties and density. EN 384. Brussels, Belgium: CEN.
Dietsch, P., S. Franke, B. Franke, A. Gamper, and S. Winter. 2015. “Methods to determine wood moisture content and their applicability in monitoring concepts.” J. Civ. Struct. Health Monit. 5 (2): 115–127. https://doi.org/10.1007/s13349-014-0082-7.
Dong, Y. L., and B. Pan. 2017. “A review of speckle pattern fabrication and assessment for digital image correlation.” Exp. Mech. 57 (8): 1161–1181. https://doi.org/10.1007/s11340-017-0283-1.
Fortino, S., P. Hradil, and G. Metelli. 2019. “Moisture-induced stresses in large glulam beams. Case study: Vihantasalmi Bridge.” Wood Mater. Sci. Eng. 14 (5): 366–380. https://doi.org/10.1080/17480272.2019.1638828.
Fragiacomo, M., S. Fortino, D. Tononi, I. Usardi, and T. Toratti. 2011. “Moisture-induced stresses perpendicular to grain in cross-sections of timber members exposed to different climates.” Eng. Struct. 33 (11): 3071–3078. https://doi.org/10.1016/j.engstruct.2011.06.018.
Gereke, T. 2009. “Moisture-induced stresses in cross-laminated wood panels. DISS. ETH No. 18427.” Doctoral dissertation, Dept. of Civil, Environmental and Geomatic Engineering, ETH Zurich. http://www.ifb.ethz.ch/wood%5Cnhttp://e-collection.library.ethz.ch/view/eth:201.
Gereke, T., P. J. Gustafsson, K. Persson, and P. Niemz. 2011. “The hygroscopic warping of cross-laminated timber.” In Delamination in wood, wood products and wood-based composites, 269–285. Dordrecht, Netherlands: Springer. https://doi.org/10.1007/978-90-481-9550-3_14.
Gereke, T., and P. Niemz. 2010. “Moisture-induced stresses in spruce cross-laminates.” Eng. Struct. 32 (2): 600–606. https://doi.org/10.1016/j.engstruct.2009.11.006.
Gereke, T., T. Schnider, A. Hurst, and P. Niemz. 2009. “Identification of moisture-induced stresses in cross-laminated wood panels from beech wood (Fagus sylvatica L.).” Wood Sci. Technol. 43 (3–4): 301–315. https://doi.org/10.1007/s00226-008-0218-1.
Gülzow, A., K. Richter, and R. Steiger. 2011. “Influence of wood moisture content on bending and shear stiffness of cross laminated timber panels.” Eur. J. Wood Wood Prod. 69 (2): 193–197. https://doi.org/10.1007/s00107-010-0416-z.
Jönsson, J. 2004. “Internal stresses in the cross-grain direction in glulam induced by climate variations.” Holzforschung 58 (2): 154–159. https://doi.org/10.1515/HF.2004.023.
KLH-Massivholzplatten. 2011. ETA-06/0138. Vienna, Austria: Austrian Institute of Construction Engineering/European Organisation for Technical Assessment.
Mirzaei, G., B. Mohebby, and G. Ebrahimi. 2017. “Glulam beam made from hydrothermally treated poplar wood with reduced moisture induced stresses.” Constr. Build. Mater. 135 (Mar): 386–393. https://doi.org/10.1016/j.conbuildmat.2016.12.178.
Nairn, J. A. 2019. “Predicting layer cracks in cross-laminated timber with evaluations of strategies for suppressing them.” Eur. J. Wood Wood Prod. 77 (3): 405–419. https://doi.org/10.1007/s00107-019-01399-7.
Pereira, J. L., J. Xavier, B. Ghiassi, J. Lousada, and J. Morais. 2018. “On the identification of earlywood and latewood radial elastic modulus of Pinus pinaster by digital image correlation: A parametric analysis.” J. Strain Anal. Eng. Des. 53 (8): 566–574. https://doi.org/10.1177/0309324718786351.
Schmidt, E. L., M. Riggio, A. R. Barbosa, and I. Mugabo. 2019. “Environmental response of a CLT floor panel: Lessons for moisture management and monitoring of mass timber buildings.” Build. Environ. 148 (Jan): 609–622. https://doi.org/10.1016/j.buildenv.2018.11.038.
Schreier, H., J. J. Orteu, and M. A. Sutton. 2009. Image correlation for shape, motion and deformation measurements: Basic concepts, theory and applications. Boston: Springer. https://doi.org/10.1007/978-0-387-78747-3.
Schwab, E., A. Steffen, and C. Korte. 1997. “In-plane swelling and shrinkage of wood-based panels.” Holz Roh Werkst. 55 (4): 227–233. https://doi.org/10.1007/BF02990553.
Silva, C., J. M. Branco, Z. Mehdipour, J. Xavier, A. S. Rebouças, and P. B. Lourenço. 2021. “Strain variation analysis of cross-laminated timber elements under cyclic moisture.” J. Build. Eng. 41 (Sep): 102373. https://doi.org/10.1016/j.jobe.2021.102373.
Silva, C., J. M. Branco, A. Ringhofer, P. B. Lourenço, and G. Schickhofer. 2016. “The influences of moisture content variation, number and width of gaps on the withdrawal resistance of self tapping screws inserted in cross laminated timber.” Constr. Build. Mater. 125 (Oct): 1205–1215. https://doi.org/10.1016/j.conbuildmat.2016.09.008.
Sjödin, J., and C. J. Johansson. 2007. “Influence of initial moisture induced stresses in multiple steel-to-timber dowel joints.” Holz Roh Werkst. 65 (1): 71–77. https://doi.org/10.1007/s00107-006-0136-6.
Sousa, H. S., J. M. Branco, and P. B. Lourenço. 2014. “Characterization of cross sections from old chestnut beams weakened by decay.” Int. J. Archit. Heritage 8 (3): 436–451. https://doi.org/10.1080/15583058.2013.826303.
Xavier, J., A. M. P. De Jesus, J. J. L. Morais, and J. M. T. Pinto. 2012. “Stereovision measurements on evaluating the modulus of elasticity of wood by compression tests parallel to the grain.” Constr. Build. Mater. 26 (1): 207–215. https://doi.org/10.1016/j.conbuildmat.2011.06.012.
Information & Authors
Information
Published In
Copyright
© 2022 American Society of Civil Engineers.
History
Received: Jun 15, 2021
Accepted: Dec 14, 2021
Published online: May 25, 2022
Published in print: Aug 1, 2022
Discussion open until: Oct 25, 2022
ASCE Technical Topics:
- Building materials
- Climates
- Engineering materials (by type)
- Environmental engineering
- Humidity
- Hydrologic engineering
- Hydrology
- Laminating
- Material mechanics
- Materials engineering
- Materials processing
- Meteorology
- Moisture
- Strain
- Stress (by type)
- Stress analysis
- Stress distribution
- Structural analysis
- Structural engineering
- Structural members
- Structural systems
- Water and water resources
- Wood and wood products
Authors
Metrics & Citations
Metrics
Citations
Download citation
If you have the appropriate software installed, you can download article citation data to the citation manager of your choice. Simply select your manager software from the list below and click Download.
Cited by
- Marcelo González-Retamal, Eric Forcael, Gerardo Saelzer-Fuica, Mauricio Vargas-Mosqueda, From Trees to Skyscrapers: Holistic Review of the Advances and Limitations of Multi-Storey Timber Buildings, Buildings, 10.3390/buildings12081263, 12, 8, (1263), (2022).
- Xi Zhang, Frédéric Dubois, Nicolas Sauvat, Mokhfi Takarli, Hybrid numerical method for the ultrasonic wave propagation velocity in orthotropic materials, Wood Science and Technology, 10.1007/s00226-022-01416-8, 56, 6, (1605-1630), (2022).