Long-Term Drying Shrinkage of GGBFS-Incorporated RCC under Various Temperature Exposures
Publication: Journal of Materials in Civil Engineering
Volume 33, Issue 6
Abstract
In this paper, the influence of different temperatures and ground-granulated blast-furnace slag (GGBFS) content on the compressive strength and shrinkage bahavior of roller-compacted concrete (RCC) was explored. For this purpose, four RCC mixes incorporating 0%, 20%, 40%, and 60% of GGBFS were prepared. The mixes were subjected to three temperatures, 25°C, 50°C, and 70°C. The results show that RCC gained strength more rapidly at higher curing temperatures. Shrinkage results showed that temperature had a direct impact on shrinkage strain development, with lower final shrinkage strain values at higher exposure temperatures. This was due to a loss of interlayer water at a faster rate in the early stages itself. Also, incorporation of GGBFS led to marginally higher shrinkage strain, which was compensated at higher exposure temperatures. Strength and shrinkage results were further confirmed at the microscopic level by scanning electron microscopy and thermogravimetry analyses. Based on the experimental results, a multivariable model incorporating the effect of temperature, time, and GGBFS percentage was developed for the prediction of shrinkage strain of RCC. The regression coefficient of the model was higher than 0.95 for all mixes, indicating that the proposed model can estimate shrinkage strain within 95% of the prediction band.
Get full access to this article
View all available purchase options and get full access to this article.
Data Availability Statement
All data, models, and code generated or used during the study appear in the published article.
Acknowledgments
Counto-Microfine Products Pvt. India is gratefully acknowledged for supplying the GGBFS for the study.
References
ACI (American Concrete Institute). 1992. Prediction of creep, shrinkage and temperature effects in concrete structures. Farmington Hills, MI: ACI.
ACI (American Concrete Institute). 2002. Guide for selecting proportions for no-slump concrete. Farmington Hills, MI: ACI.
Aghabaglou, A. M., and K. Ramyar. 2013. “Mechanical properties of high volume fly ash roller compacted concrete designed by maximum density method.” Constr. Build. Mater. 38 (Jan): 356–364. https://doi.org/10.1016/j.conbuildmat.2012.07.109.
Anoglu, N., Z. C. Girgin, and E. Anoglu. 2006. “Evaluation of ratio between splitting tensile strength and compressive strength for concretes upto 120 MPa and its application in strength criterion.” ACI Mater. J. 103 (1): 18–24.
ASTM. 2008. Standard practice for making roller compacted concrete in cylinder molds using a vibrating table. West Conshohocken, PA: ASTM.
Atis, C. D. 2005. “Strength properties of high-volume fly ash roller compacted and workable concrete and influence of curing condition.” Cem. Concr. Res. 35 (6): 1112–1121. https://doi.org/10.1016/j.cemconres.2004.07.037.
Atis, C. D., U. K. Sevim, F. Ozcan, C. Bilim, O. Karahan, A. H. Tanrikulu, and A. Eksi. 2004. “Strength properties of roller compacted concrete containing a non-standard high calcium fly ash.” Mater. Lett. 58 (9): 1446–1450. https://doi.org/10.1016/j.matlet.2003.10.007.
Barnett, S. J., M. N. Soutsos, S. G. Millard, and J. H. Bungey. 2006. “Strength development of mortars containing ground granulated blast furnace slag: Effect of curing temperature and determination of apparent activation energies.” Cem. Concr. Res. 36 (3): 434–440. https://doi.org/10.1016/j.cemconres.2005.11.002.
Bazant, Z. P., and S. Baweja. 1995. “Justification and refinement of model B3 for concrete creep and shrinkage 2. Updating and theoretical basis.” Mater. Struct. 28 (7): 488–495. https://doi.org/10.1007/BF02473171.
BIS (Bureau of Indian Standards). 1987. Specification for granulated slag for the manufacture of Portland slag cement. New Delhi, India: BIS.
BIS (Bureau of Indian Standards). 1989. Specification for 43 grade ordinary Portland cement. New Delhi, India: BIS.
Bouziadi, F., B. Boulekbache, and M. Hamrat. 2016. “The effects of fibres on the shrinkage of high strength concrete under various curing temperatures.” Constr. Build. Mater. 114 (Jul): 40–48. https://doi.org/10.1016/j.conbuildmat.2016.03.164.
Callaghan, P. W. O., and S. D. Probert. 1977. “Sol-air temperature.” Appl. Energy 3 (4): 307–311. https://doi.org/10.1016/0306-2619(77)90017-4.
Cao, C., W. Sun, and H. Qin. 2000. “The analysis on strength and fly ash effect of roller-compacted concrete with high volume fly ash.” Cem. Concr. Res. 30 (1): 71–75. https://doi.org/10.1016/S0008-8846(99)00203-3.
CEB (Comité Euro-International du Béton). 1990. CEB-FIP model code for concrete structures: Evaluation of the time dependent behaviour of concrete. Bulletin D'Information No. 199. Lausanne, Switzerland: International Federation for Structural Concrete.
Chu, I., S. H. Kwon, M. N. Amin, and J. K. Kim. 2012. “Estimation of temperature effects on autogenous shrinkage of concrete by a new prediction model.” Constr. Build. Mater. 35 (Oct): 171–182. https://doi.org/10.1016/j.conbuildmat.2012.03.005.
Collier, N. C. 2016. “Transition and decomposition temperatures of cement phases—A collection of thermal analysis data.” Ceram. Silik. 60 (4): 338–343. https://doi.org/10.13168/cs.2016.0050.
Gardner, N. J. 1990. “Effect of temperature on the early age properties of type I, type III and type I/fly ash concretes.” ACI Mater. J. 87 (1): 68–78.
Gardner, N. J., and M. J. Lockman. 2001. “Design provisions for drying shrinkage and creep of normal strength concrete.” ACI Mater. J. 98 (2): 159–167.
Hesami, S., A. Modarres, M. Soltaninejad, and H. Madani. 2016. “Mechanical properties of roller compacted concrete pavement containing coal waste and lime stone powder as partial replacement of cement.” Constr. Build. Mater. 111 (May): 625–636. https://doi.org/10.1016/j.conbuildmat.2016.02.116.
Jianyong, L., and Y. Yan. 2001. “A study on creep and drying shrinkage of high performance concrete.” Cem. Concr. Res. 31 (8): 1203–1206. https://doi.org/10.1016/S0008-8846(01)00539-7.
Junior, A. N., R. D. T. Filho, E. M. R. Fairbairn, and J. Dweck. 2012. “Early stages hydration of high initial strength Portland cement.” J. Therm. Anal. Calorim. 108 (2): 725–731. https://doi.org/10.1007/s10973-012-2256-z.
Khay, S. E. E., J. Neji, and A. Loulizi. 2010. “Shrinkage properties of compacted sand concrete used in pavements.” Constr. Build. Mater. 24 (9): 1790–1795. https://doi.org/10.1016/j.conbuildmat.2010.02.008.
Kjellsen, K. O., R. J. Detwiler, and O. E. Gjorv. 1991. “Development of microstructures in plain cement pastes hydrated at different temperatures.” Cem. Concr. Res. 21 (1): 179–189. https://doi.org/10.1016/0008-8846(91)90044-I.
Koenigsberger, O. H., T. G. Ingersoll, A. Mayhew, and S. V. Szokolay. 1974. Manual of tropical housing and building. Part 1: Climate design. London: Longman.
Kothari, C. R. 1990. Research methodology methods and techniques. 2nd ed. New Delhi, India: New Age International Publishers.
Lam, M. N. T., D. H. Le, and S. Jaritngam. 2018. “Compressive strength and durability properties of roller compacted concrete pavement containing electric arc furnace slag aggregate and fly ash.” Constr. Build. Mater. 191 (Dec): 912–922. https://doi.org/10.1016/j.conbuildmat.2018.10.080.
Lee, K. M., H. K. Lee, S. H. Lee, and G. Y. Kim. 2006. “Autogenous shrinkage of concrete containing granulated blast furnace slag.” Cem. Concr. Res. 36 (7): 1279–1285. https://doi.org/10.11016/j.cemconres.2006.01.005.
Lura, P., K. V. Breugel, and I. Maruyama. 2001. “Effect of curing temperature and type of cement on early age shrinkage of high performance concrete.” Cem. Concr. Res. 31 (12): 1867–1872. https://doi.org/S0008-8846(01)00601-9.
Mokarem, D. W., R. E. Weyer, and D. S. Lane. 2005. “Development of a shrinkage performance specifications and prediction model analysis for supplemental cementitious material concrete mixtures.” Cem. Concr. Res. 35 (5): 918–925. https://doi.org/10.1016/j.cemconres.2004.09.013.
Mounanga, P., V. Baroghel-Bouny, A. Loukili, and A. Khelidj. 2006. “Autogenous deformation of cement pastes: Part1. Temperature effects at early age and micro macro correlations.” Cem. Concr. Res. 36 (3): 110–122. https://doi.org/10.1016/j.cemconres.2004.10.019.
Naik, T. R., B. W. Ramme, and J. H. Tews. 1995. “Pavement construction with high volume class C and class F fly ash concrete.” ACI Mater. J. 92 (2): 200–211.
Oluokun, F. A. 1991. “Prediction of concrete tensile strength from its compressive strength evaluation relations for normal weight concrete.” ACI Mater. J. 88 (3): 302–309.
Petkova, V., V. Stoyanov, and Y. Pelovski. 2012. “TG-DTG-DTA in studying white self-compacting cement mortars.” J. Therm. Anal. Calorim. 109 (2): 797–806. https://doi.org/10.1007/s10973-012-2447-7.
Rao, S. K., P. Sravana, and T. C. Rao. 2016a. “Investigating the effect of M-sand on abrasion resistance of Fly Ash Roller Compacted Concrete.” Constr. Build. Mater. 118 (Aug): 352–363. https://doi.org/10.1016/j.conbuildmat.2016.05.017.
Rao, S. K., P. Sravana, and T. C. Rao. 2016b. “Abrasion resistance and mechanical properties of Roller Compacted Concrete with GGBS.” Constr. Build. Mater. 114 (Jul): 925–933. https://doi.org/10.1016/j.conbuildmat.2016.04.004.
Saluja, S., S. Goyal, and B. Bhattacharjee. 2019a. “Strength properties of roller compacted concrete containing GGBS as partial replacement of cement.” J. Eng. Res. 7 (1): 84–100.
Saluja, S., S. Goyal, and B. Bhattacharjee. 2019b. “Strength and abrasion resistance of roller compacted concrete incorporating GGBS and two types of coarse aggregates.” Adv. Concr. Constr. Int. J. 8 (2): 127–137. https://doi.org/10.12989/acc.2019.8.2.127.
Saluja, S., K. Kaur, S. Goyal, and B. Bhattacharjee. 2019c. “Assessing the effect of GGBS content and aggregate characteristics on drying shrinkage of roller compacted concrete.” Constr. Build. Mater. 201 (Mar): 72–80. https://doi.org/10.1016/j.conbuildmat.2018.12.179.
Shariq, M., J. Prasad, and H. Abbas. 2016. “Creep and drying shrinkage of concrete containing GGBFS.” Cem. Concr. Compos. 68 (Apr): 35–45. https://doi.org/10.1016/j.cemconcomp.2016.02.004.
Sharma, D., and S. Goyal. 2020. “Effect of accelerated carbonation curing on near surface properties of concrete.” Eur. J. Environ. Civ. Eng. 2020 (Jan): 1–22. https://doi.org/10.1080/19648189.2019.1707714.
Silva, A. S., A. Gameiro, J. Grilo, R. Veiga, and A. Velosa. 2014. “Long-term behavior of lime–metakaolin pastes at ambient temperature and humid curing condition.” Appl. Clay Sci. 88-89 (Feb): 49–55. https://doi.org/10.1016/j.clay.2013.12.016.
Tazawa, E., Y. Matsuoka, S. Miyazawa, and S. Okamoto. 1994. “Effect of autogenous shrinkage on self stress in hardening concrete.” In Proc., Int. Symp. on RILEM Symp: Thermal Cracking in Concrete at Early Ages, 221–228. London: E&FN Spon.
Turcry, P., A. Loukili, L. Barcelo, and J. M. Casabonne. 2002. “Can the maturity concept be used to separate the autogenous shrinkage and thermal deformation of a cement paste at early age?” Cem. Concr. Res. 32 (9): 1443–1450. https://doi.org/10.1016/S0008-8846(02)00800-1.
Turuallo, G. 2015. “Sustainable development of concrete using GGBS: Effect of curing temperature on the strength development of concrete.” Appl. Mech. Mater. 776 (5): 3–8. https://doi.org/10.4028/www.scientific.net/AMM.776.3.
Vahedifard, F., M. Nili, and C. L. Meehan. 2010. “Assessing the effect of supplementary cementitious materials on the performance of low-cement roller compacted concrete pavement.” Constr. Build. Mater. 24 (12): 2528–2535. https://doi.org/10.1016/j.conbuildmat.2010.06.003.
Verbeck, G. J., and R. A. Helmuth. 1968. “Structures and physical properties of cement paste.” In Proc., 5th Int. Congress Cement Chemistry, 1–32. New York: Wiley.
Videla, C., and C. Aguilar. 2006. “An updated look at drying shrinkage of Portland and blended Portland cement concretes.” Mag. Concr. Res. 58 (7): 459–476. https://doi.org/10.1680/macr.2006.58.7.459.
Vidya, B., and K. S. Rao. 2018. “Thermogravimetric analysis of concrete.” Int. J. Mod. Trends Eng. Res. 5 (4): 187–194.
Wang, P., N. Li, and L. Xu. 2017. “Hydration evolution and compressive strength of calcium sulphoaluminate cement constantly cured over the temperature range of 0 to 80 °C.” Cem. Concr. Res. 100 (Oct): 203–213. https://doi.org/10.1016/j.cemconres.2017.05.025.
Wongkeo, W., P. Thongsanitgarn, P. Chindaprasirt, and A. Chaipanich. 2013. “Thermogravimetry of ternary cement blends.” J. Therm. Anal. Calorim. 113 (3): 1079–1090. https://doi.org/10.1007/s10973-013-3017-3.
Yang, Y., M. Li, H. Deng, and Q. Liu. 2014. “Effects of temperature on drying shrinkage of concrete.” Appl. Mech. Mater. 584 (5): 1176–1181. https://doi.org/10.4028/www.scientific.net/AMM.584-586.1176.
Yazici, S., M. Tuyan, A. Mardani-Aghabaglou, and A. A. Ute. 2015. “Mechanical properties and impact resistance of roller compacted concrete containing polypropylene fibre.” Mag. Concr. Res. 67 (16): 867–875. https://doi.org/10.1680/macr.14.00242.
Yuan, B. J., W. Lindquist, D. Darwin, and J. Browning. 2015. “Effect of slag cement on drying shrinkage of concrete.” ACI Mater. J. 112 (2): 267–276.
Zollinger, D. 2016. Roller compacted concrete pavement. Washington, DC: DOT.
Information & Authors
Information
Published In
Copyright
© 2021 American Society of Civil Engineers.
History
Received: Jul 31, 2020
Accepted: Nov 9, 2020
Published online: Mar 29, 2021
Published in print: Jun 1, 2021
Discussion open until: Aug 29, 2021
Authors
Metrics & Citations
Metrics
Citations
Download citation
If you have the appropriate software installed, you can download article citation data to the citation manager of your choice. Simply select your manager software from the list below and click Download.