Properties of High-Early-Strength Aerated Concrete Incorporating Metakaolin
Publication: Journal of Materials in Civil Engineering
Volume 31, Issue 10
Abstract
Conventional portland cement–based aerated concrete needs autoclaved curing in order to obtain high early-stage strength. Magnesium phosphate cement–based lightweight materials, such as aerated magnesium phosphate cement and magnesium phosphate cement–based foamed concrete can achieve the high early strength without thermal curing. In this study, metakaolin was introduced to enhance the performance of aerated magnesium phosphate cement, and the compressive strength, splitting tensile strength, thermal conductivity, foamability, strength retention coefficient after water immersion, sorptivity, and hygroscopicity were measured. Experimental results indicate that the presence of metakaolin has a slight influence on thermal insulation performance, and its strength and water resistance were improved significantly. The 3-h compressive strength of metakaolin-blended aerated magnesium phosphate cement can reach approximately 3 MPa. Metakaolin slightly slows down the gas-foaming process, and a larger amount of finer pores and smaller amount of capillary interconnected pores are produced. For this reason, the height of water migration in aerated magnesium phosphate cement with metakaolin is lower than that without metakaolin. Likewise, metakaolin decreases the hygroscopic moisture content of aerated magnesium phosphate cement, and the hygroscopicity, which can be described by several classical sorption isotherm models, reveals the typical characteristics of the hygroscopic property of portland cement–based porous materials.
Get full access to this article
View all available purchase options and get full access to this article.
Acknowledgments
This research work was financially supported by the National Natural Science Foundation of China, Grant No. 51808560.
References
Alexanderson, J. 1979. “Relations between structure and mechanical properties of autoclaved aerated concrete.” Cem. Concr. Res. 9 (4): 507–514. https://doi.org/10.1016/0008-8846(79)90049-8.
Almalkawi, A. T., W. Hong, S. Hamadna, P. Soroushian, and G. Al-Chaar. 2018a. “Behavior of a lightweight frame made with aerated slurry-infiltrated chicken mesh under cyclic lateral loading.” Constr. Build. Mater. 160 (Jan): 679–686. https://doi.org/10.1016/j.conbuildmat.2017.11.079.
Almalkawi, A. T., W. Hong, S. Hamadna, P. Soroushian, A. G. N. D. Darsanasiri, A. Balchandra, and G. Al-Chaar. 2018b. “Mechanical properties of aerated cement slurry-infiltrated chicken mesh.” Constr. Build. Mater. 166 (Mar): 966–973. https://doi.org/10.1016/j.conbuildmat.2018.01.101.
Almalkawi, A. T., T. Salem, S. Hamadna, A. G. N. D. Darsanasiri, P. Soroushian, A. Balchandra, and G. Al-Chaar. 2018c. “Physio-microstructural properties of aerated cement slurry for lightweight structures.” Material 11 (4): 597. https://doi.org/10.3390/ma11040597.
ASTM. 2017. Standard test method for steady-state thermal transmission properties by means of the heat flow meter apparatus. ASTM C518. West Conshohocken, PA: ASTM.
Chen, X., S. Wu, and J. Zhou. 2013. “Influence of porosity on compressive and tensile strength of cement mortar.” Constr. Build. Mater. 40 (Mar): 869–874. https://doi.org/10.1016/j.conbuildmat.2012.11.072.
Colinart, T., and P. Glouannec. 2017. “Temperature dependence of sorption isotherm of hygroscopic building materials. Part 1: Experimental evidence and modeling.” Energy Build. 139 (Mar): 360–370. https://doi.org/10.1016/j.enbuild.2016.12.082.
Ding, Z., and Z. J. Li. 2005. “High-early-strength magnesium phosphate cement with fly ash.” ACI Mater. J. 102 (6): 375.
Efavi, J. K., L. Damoah, D. Y. Bensah, D. D. Arhin, and D. Tetteh. 2012. “Development of porous ceramic bodies from kaolin deposits for industrial applications.” Appl. Clay Sci. 65 (Sep): 31–36. https://doi.org/10.1016/j.clay.2012.04.010.
Fu, X., Z. Lai, X. Lai, Z. Lu, and S. Lv. 2016. “Preparation and characteristics of magnesium phosphate cement based porous materials.” Constr. Build. Mater. 127 (Nov): 712–723. https://doi.org/10.1016/j.conbuildmat.2016.10.041.
Gao, Y., C. Ma, G. C. Long, B. Zhao, and Y. J. Xie. 2018. “Effects of metakaolin on a novel aerated magnesium phosphate cement with high early strength.” Constr. Build. Mater. 187 (Oct): 1130–1133. https://doi.org/10.1016/j.conbuildmat.2018.08.037.
Hartley, I. D., S. Wang, and Y. Zhang. 2007. “Water vapor sorption isotherm modeling of commercial oriented strand panel based on species groups and resin type.” Build. Environ. 42 (10): 3655–3659. https://doi.org/10.1016/j.buildenv.2006.10.002.
Hilal, A. A., N. H. Thom, and A. R. Dawson. 2015a. “On entrained pore size distribution of foamed concrete.” Constr. Build. Mater. 75 (Jan): 227–233. https://doi.org/10.1016/j.conbuildmat.2014.09.117.
Hilal, A. A., N. H. Thom, and A. R. Dawson. 2015b. “On void structure and strength of foamed concrete made without/with additives.” Constr. Build. Mater. 85: 157–164. https://doi.org/10.1016/j.conbuildmat.2015.03.093.
Hilal, A. A., N. H. Thom, and A. R. Dawson. 2016. “Failure mechanism of foamed concrete made with/without additives and lightweight aggregate.” J. Adv. Concr. Technol. 14 (9): 511–520. https://doi.org/10.3151/jact.14.511.
Holt, E., and P. Raivio. 2005. “Use of gasification residues in aerated autoclaved concrete.” Cem. Concr. Res. 35 (4): 796–802. https://doi.org/10.1016/j.cemconres.2004.05.005.
Ioannou, I., A. Hamilton, and C. Hall. 2008. “Capillary absorption of water and n-decane by autoclaved aerated concrete.” Cem. Concr. Res. 38 (6): 766–771. https://doi.org/10.1016/j.cemconres.2008.01.013.
ISO. 2013. Hygrothermal performance of building materials and products—Determination of hygroscopic sorption properties. ISO 12571. Geneva, Switzerland: ISO.
Jerman, M., and R. Černý. 2012. “Effect of moisture content on heat and moisture transport and storage properties of thermal insulation materials.” Energy Build. 53 (Oct): 39–46. https://doi.org/10.1016/j.enbuild.2012.07.002.
Jiang, C., K. Fan, F. Wu, and D. Chen. 2014. “Experimental study on the mechanical properties and microstructure of chopped basalt fibre reinforced concrete.” Mater. Des. 58: 187–193. https://doi.org/10.1016/j.matdes.2014.01.056.
Karagiannis, N., M. Karoglou, A. Bakolas, and A. Moropoulou. 2016. “Effect of temperature on water capillary rise coefficient of building materials.” Build. Environ. 106 (Sep): 402–408. https://doi.org/10.1016/j.buildenv.2016.07.008.
Le-Ping, L., C. Xue-Min, Q. Shu-Heng, Y. Jun-Li, and Z. Lin. 2010. “Preparation of phosphoric acid-based porous geopolymers.” Appl. Clay Sci. 50 (4): 600–603. https://doi.org/10.1016/j.clay.2010.10.004.
Le Rouzic, M., T. Chaussadent, G. Platret, and L. Stefan. 2017. “Mechanisms of k-struvite formation in magnesium phosphate cements.” Cem. Concr. Res. 91: 117–122. https://doi.org/10.1016/j.cemconres.2016.11.008.
Li, Y., and B. Chen. 2014. “New type of super-lightweight magnesium phosphate cement foamed concrete.” J. Mater. Civ. Eng. 27 (1): 04014112. https://doi.org/10.1061/(ASCE)MT.1943-5533.0001044.
Liu, M. Y. J., U. J. Alengaram, M. Z. Jumaat, and K. H. Mo. 2014. “Evaluation of thermal conductivity, mechanical and transport properties of lightweight aggregate foamed geopolymer concrete.” Energy Build. 72 (Apr): 238–245. https://doi.org/10.1016/j.enbuild.2013.12.029.
Lu, X., and B. Chen. 2016. “Experimental study of magnesium phosphate cements modified by metakaolin.” Constr. Build. Mater. 123 (Oct): 719–726. https://doi.org/10.1016/j.conbuildmat.2016.07.092.
Ma, C., and B. Chen. 2015. “Properties of a foamed concrete with soil as filler.” Constr. Build. Mater. 76 (Feb): 61–69. https://doi.org/10.1016/j.conbuildmat.2014.11.066.
Ma, C., and B. Chen. 2016. “Properties of magnesium phosphate cement containing redispersible polymer powder.” Constr. Build. Mater. 113 (Jun): 255–263. https://doi.org/10.1016/j.conbuildmat.2016.03.053.
Ma, C., and B. Chen. 2017. “Experimental study on the preparation and properties of a novel foamed concrete based on magnesium phosphate cement.” Constr. Build. Mater. 137 (Apr): 160–168. https://doi.org/10.1016/j.conbuildmat.2017.01.092.
Ma, C., Y. J. Xie, and G. C. Long. 2018. “A calculation model for compressive strength of cleaner earth-based construction with a high-efficiency stabilizer and fly ash.” J. Cleaner Prod. 183 (May): 292–303. https://doi.org/10.1016/j.jclepro.2018.02.153.
Masi, G., W. D. Rickard, L. Vickers, M. C. Bignozzi, and A. Van Riessen. 2014. “A comparison between different foaming methods for the synthesis of light weight geopolymers.” Ceram. Int. 40 (9): 13891–13902. https://doi.org/10.1016/j.ceramint.2014.05.108.
Nambiar, E. K., and K. Ramamurthy. 2007. “Sorption characteristics of foam concrete.” Cem. Concr. Res. 37 (9): 1341–1347. https://doi.org/10.1016/j.cemconres.2007.05.010.
Narayanan, N., and K. Ramamurthy. 2000. “Structure and properties of aerated concrete: A review.” Cem. Concr. Compos. 22 (5): 321–329. https://doi.org/10.1016/S0958-9465(00)00016-0.
Obada, D. O., D. Dodoo-Arhin, M. Dauda, F. O. Anafi, A. S. Ahmed, and O. A. Ajayi. 2017. “Physico-mechanical and gas permeability characteristics of kaolin based ceramic membranes prepared with a new pore-forming agent.” Appl. Clay Sci. 150 (Dec): 175–183. https://doi.org/10.1016/j.clay.2017.09.014.
Sanjuan, M. A., and R. Muñoz-Martialay. 1996. “Influence of the water/cement ratio on the air permeability of concrete.” J. Mater. Sci. 31 (11): 2829–2832. https://doi.org/10.1007/BF00355989.
Seehra, S. S., S. Gupta, and S. Kumar. 1993. “Rapid setting magnesium phosphate cement for quick repair of concrete pavements-characterisation and durability aspects.” Cem. Concr. Res. 23 (2): 254–266. https://doi.org/10.1016/0008-8846(93)90090-V.
Song, Y., B. Li, E. H. Yang, Y. Liu, and T. Ding. 2015. “Feasibility study on utilization of municipal solid waste incineration bottom ash as aerating agent for the production of autoclaved aerated concrete.” Cem. Concr. Compos. 56 (Feb): 51–58. https://doi.org/10.1016/j.cemconcomp.2014.11.006.
Wang, C. L., W. Ni, S. Q. Zhang, S. Wang, G. S. Gai, and W. K. Wang. 2016. “Preparation and properties of autoclaved aerated concrete using coal gangue and iron ore tailings.” Constr. Build. Mater. 104 (Feb): 109–115. https://doi.org/10.1016/j.conbuildmat.2015.12.041.
Yaseen, Z. M., R. C. Deo, A. Hilal, A. M. Abd, L. C. Bueno, S. Salcedo-Sanz, and M. L. Nehdi. 2018. “Predicting compressive strength of lightweight foamed concrete using extreme learning machine model.” Adv. Eng. Software 115 (Jan): 112–125. https://doi.org/10.1016/j.advengsoft.2017.09.004.
Zhang, Z., J. L. Provis, A. Reid, and H. Wang. 2015. “Mechanical, thermal insulation, thermal resistance and acoustic absorption properties of geopolymer foam concrete.” Cem. Concr. Compos. 62 (Sep): 97–105. https://doi.org/10.1016/j.cemconcomp.2015.03.013.
Information & Authors
Information
Published In
Copyright
©2019 American Society of Civil Engineers.
History
Received: Jul 31, 2018
Accepted: Mar 21, 2019
Published online: Jul 26, 2019
Published in print: Oct 1, 2019
Discussion open until: Dec 26, 2019
Authors
Metrics & Citations
Metrics
Citations
Download citation
If you have the appropriate software installed, you can download article citation data to the citation manager of your choice. Simply select your manager software from the list below and click Download.