Influence of Different Curing Regimes on the Performance and Microstructure of Alkali-Activated Slag Concrete
Publication: Journal of Materials in Civil Engineering
Volume 30, Issue 9
Abstract
This paper investigates the performance and microstructure of alkali-activated slag concrete (AASC) subjected to different 28-day curing regimes: air, intermittent water curing (7 days in water followed by 21 days in air), and continuous water curing. Three concrete mixes were prepared with fixed contents of slag, desert dune sand, and aggregate and activated by an alkaline solution consisting of sodium silicate and sodium hydroxide. The ratio of alkaline activator solution (AAS) to slag was varied between 0.45 and 0.55. Samples were tested to assess transport and mechanical properties. Test results showed that an AAS:slag ratio of 0.50 provided optimal performance. Intermittent water curing was found to be the most effective curing regime, resulting in a reduction in porosity and sorptivity, and an increase in bulk electrical resistivity, modulus of elasticity, and compressive strength. Differential scanning calorimetry, Fourier transform infrared spectroscopy, and scanning electron microscopy were used to characterize the microstructure. Calcium alumino-silicate hydrate gel was highlighted as the main reaction product, while sodium alumino-silicate hydrate gel was only detected in air cured counterparts.
Get full access to this article
View all available purchase options and get full access to this article.
Acknowledgments
Financial support for this study was provided by the United Arab Emirates University (UAEU) under Grant No. 31N258. The contributions of the UAEU lab staff and engineers are greatly appreciated.
References
Abdulkareem, O. A., A. M. Mustafa Al Bakri, H. Kamarudin, I. Khairul Nizar, and A. E. A. Saif. 2014. “Effects of elevated temperatures on the thermal behavior and mechanical performance of fly ash geopolymer paste, mortar and lightweight concrete.” Constr. Build. Mater. 50: 377–387. https://doi.org/10.1016/j.conbuildmat.2013.09.047.
ACI (American Concrete Institute). 1992. State of the art report on high-strength concrete. ACI 363. Farmington Hills, MI: ACI.
ACI (American Concrete Institute). 2014. Building code requirements for structural concrete and commentary. ACI 318. Farmington Hills, MI: ACI.
Al-Majidi, M. H., A. Lampropoulos, A. Cundy, and S. Meikle. 2016. “Development of geopolymer mortar under ambient temperature for in situ applications.” Constr. Build. Mater. 120: 198–211. https://doi.org/10.1016/j.conbuildmat.2016.05.085.
Al-Otaibi, S. 2008. “Durability of concrete incorporating GGBS activated by water-glass.” Constr. Build. Mater. 22 (10): 2059–2067. https://doi.org/10.1016/j.conbuildmat.2007.07.023.
AS (Standards Australia). 2009. Concrete structures. AS3600. Sydney, Australia: AS.
ASTM. 2012a. Standard test method for bulk electrical conductivity of hardened concrete. ASTM C1760. West Conshohocken, PA: ASTM.
ASTM. 2012b. Standard test method for electrical indication of concrete’s ability to resist chloride ion penetration. ASTM C1202. West Conshohocken, PA: ASTM.
ASTM. 2013a. Standard test method for density, absorption, and voids in hardened concrete. ASTM C642. West Conshohocken, PA: ASTM.
ASTM. 2013b. Standard test method for measurement of rate of absorption of water by hydraulic-cement concretes. ASTM C1585. West Conshohocken, PA: ASTM.
ASTM. 2014a. Standard test method for sieve analysis of fine and coarse aggregates. ASTM C136. West Conshohocken, PA: ASTM.
ASTM. 2014b. Standard test method for static modulus of elasticity and poisson’s ratio of concrete in compression. ASTM C469. West Conshohocken, PA: ASTM.
ASTM. 2014c. Standard test methods for specific gravity of soil solids by water pycnometer. ASTM D854. West Conshohocken, PA: ASTM.
ASTM. 2015. Standard test method for compressive strength of cylindrical concrete specimens. ASTM C39. West Conshohocken, PA: ASTM.
ASTM. 2017a. Standard practice for making and curing concrete test specimens in the field. ASTM C31. West Conshohocken, PA: ASTM.
ASTM. 2017b. Standard test method for bulk density (unit weight) and voids in aggregate. ASTM C29. West Conshohocken, PA: ASTM.
Aydın, S., and B. Baradan. 2012. “Mechanical and microstructural properties of heat cured alkali-activated slag mortars.” Mater. Des. 35: 374–383. https://doi.org/10.1016/j.matdes.2011.10.005.
Aydın, S., and B. Baradan. 2014. “Effect of activator type and content on properties of alkali-activated slag mortars.” Compos. Part B: Eng. 57: 166–172. https://doi.org/10.1016/j.compositesb.2013.10.001.
Bakharev, T., J. G. Sanjayan, and Y.-B. Cheng. 1999a. “Alkali activation of Australian slag cements.” Cem. Concr. Res. 29 (1): 113–120. https://doi.org/10.1016/S0008-8846(98)00170-7.
Bakharev, T., J. G. Sanjayan, and Y.-B. Cheng. 1999b. “Effect of elevated temperature curing on properties of alkali-activated slag concrete.” Cem. Concr. Res. 29 (10): 1619–1625. https://doi.org/10.1016/S0008-8846(99)00143-X.
Bakharev, T., J. G. Sanjayan, and Y.-B. Cheng. 2000. “Effect of admixtures on properties of alkali-activated slag concrete.” Cem. Concr. Res. 30 (9): 1367–1374. https://doi.org/10.1016/S0008-8846(00)00349-5.
Beglarigale, A., and H. Yazici. 2014. “Mitigation of detrimental effects of alkali-silica reaction in cement-based composites by combination of steel microfibers and ground-granulated blast-furnace slag.” J. Mater. Civ. Eng. 26 (12): 04014091. https://doi.org/10.1061/(ASCE)MT.1943-5533.0001005.
Behfarnia, K., and M. Rostami. 2017. “An assessment on parameters affecting the carbonation of alkali-activated slag concrete.” J. Cleaner Prod. 157: 1–9. https://doi.org/10.1016/j.jclepro.2017.04.097.
Ben Haha, M., B. Lothenbach, G. Le Saout, and F. Winnefeld. 2011. “Influence of slag chemistry on the hydration of alkali-activated blast-furnace slag. I: Effect of MgO.” Cem. Concr. Res. 41 (9): 955–963. https://doi.org/10.1016/j.cemconres.2011.05.002.
Ben Haha, M., B. Lothenbach, G. Le Saout, and F. Winnefeld. 2012. “Influence of slag chemistry on the hydration of alkali-activated blast-furnace slag. II: Effect of .” Cem. Concr. Res. 42 (1): 74–83. https://doi.org/10.1016/j.cemconres.2011.08.005.
Bernal, S. A., E. D. Rodríguez, R. Mejia de Gutiérrez, J. L. Provis, and S. Delvasto. 2012. “Activation of metakaolin/slag blends using alkaline solutions based on chemically modified silica fume and rice husk ash.” Waste Biomass Valorization 3 (1): 99–108. https://doi.org/10.1007/s12649-011-9093-3.
Brough, A. R., and A. Atkinson. 2002. “Sodium silicate-based, alkali-activated slag mortars. Part I: Strength, hydration and microstructure.” Cem. Concr. Res. 32 (6): 865–879. https://doi.org/10.1016/S0008-8846(02)00717-2.
CEB-FIB (International Federation for Structural Concrete). 1993. CEB-FIP model code 1990: Design code. London: Thomas Telford.
Chi, M., and R. Huang. 2013. “Binding mechanism and properties of alkali-activated fly ash/slag mortars.” Constr. Build. Mater. 40: 291–298. https://doi.org/10.1016/j.conbuildmat.2012.11.003.
Colella, C. 1999. “Use of thermal analysis in zeolite research and application.” In Characterization techniques of glasses and ceramics, edited by J. M. Rincon and M. Romero, 112–137. Berlin: Springer.
El-Hassan, H., and N. Ismail. 2018. “Effect of process parameters on the performance of fly ash/GGBS blended geopolymer composites.” J. Sustainable Cem. Based Mater. 7 (2): 122–140. https://doi.org/10.1080/21650373.2017.1411296.
Ferone, C., F. Colangelo, G. Roviello, D. Asprone, C. Menna, A. Balsamo, A. Prota, R. Cioffi, and G. Manfredi. 2013. “Application-oriented chemical optimization of a metakaolin based geopolymer.” Materials 6 (5): 1920–1939. https://doi.org/10.3390/ma6051920.
Gu, Y.-M., Y.-H. Fang, D. You, Y.-F. Gong, and C.-H. Zhu. 2015. “Properties and microstructure of alkali-activated slag cement cured at below- and about-normal temperature.” Constr. Build. Mater. 79: 1–8. https://doi.org/10.1016/j.conbuildmat.2014.12.068.
Ismail, I., S. A. Bernal, J. L. Provis, S. Hamdan, and J. S. J. van Deventer. 2013. “Microstructural changes in alkali activated fly ash/slag geopolymers with sulfate exposure.” Mater. Struct. 46 (3): 361–373. https://doi.org/10.1617/s11527-012-9906-2.
Ismail, I., S. A. Bernal, J. L. Provis, R. San Nicolas, S. Hamdan, and J. S. J. van Deventer. 2014. “Modification of phase evolution in alkali-activated blast furnace slag by the incorporation of fly ash.” Cem. Concr. Compos. 45: 125–135. https://doi.org/10.1016/j.cemconcomp.2013.09.006.
Izquierdo, M., X. Querol, J. Davidovits, D. Antenucci, H. Nugteren, and C. Fernández-Pereira. 2009. “Coal fly ash-slag-based geopolymers: Microstructure and metal leaching.” J. Hazard. Mater. 166 (1): 561–566. https://doi.org/10.1016/j.jhazmat.2008.11.063.
Jiang, M., X. Chen, F. Rajabipour, and C. T. Hendrickson. 2014. “Comparative life cycle assessment of conventional, glass powder, and alkali-activated slag concrete and mortar.” J. Infrastruct. Syst. 20 (4): 04014020. https://doi.org/10.1061/(ASCE)IS.1943-555X.0000211.
Juenger, M. C. G., F. Winnefeld, J. L. Provis, and J. H. Ideker. 2011. “Advances in alternative cementitious binders.” Cem. Concr. Res. 41 (12): 1232–1243. https://doi.org/10.1016/j.cemconres.2010.11.012.
Keeley, P. M., N. A. Rowson, T. P. Johnson, and D. E. Deegan. 2017. “The effect of the extent of polymerisation of a slag structure on the strength of alkali-activated slag binders.” Int. J. Min. Process. 164: 37–44. https://doi.org/10.1016/j.minpro.2017.05.007.
Laskar, S. M., and S. Talukdar. 2017. “Development of ultrafine slag-based geopolymer mortar for use as repairing mortar.” J. Mater. Civ. Eng. 29 (5): 04016292. https://doi.org/10.1061/(ASCE)MT.1943-5533.0001824.
López, T., P. Bosch, M. Asomoza, R. Gómez, and E. Ramos. 1997. “DTA-TGA and FTIR spectroscopies of sol-gel hydrotalcites: Aluminum source effect on physicochemical properties.” Mater. Lett. 31 (3): 311–316. https://doi.org/10.1016/S0167-577X(96)00296-0.
Majchrzak-Kucęba, I., and W. Nowak. 2004. “Thermal analysis of fly ash-based zeolites.” J. Therm. Anal. Calorim. 77 (1): 125–131. https://doi.org/10.1023/B:JTAN.0000033195.15101.4e.
Marjanović, N., M. Komljenović, Z. Baščarević, V. Nikolić, and R. Petrović. 2015. “Physical-mechanical and microstructural properties of alkali-activated fly ash-blast furnace slag blends.” Ceram. Int. 41 (1): 1421–1435. https://doi.org/10.1016/j.ceramint.2014.09.075.
Martys, N. S., and C. F. Ferraris. 1997. “Capillary transport in mortars and concrete.” Cem. Concr. Res. 27 (5): 747–760. https://doi.org/10.1016/S0008-8846(97)00052-5.
Nath, S. K., and S. Kumar. 2013. “Influence of iron making slags on strength and microstructure of fly ash geopolymer.” Constr. Build. Mater. 38: 924–930. https://doi.org/10.1016/j.conbuildmat.2012.09.070.
Noushini, A., and A. Castel. 2016. “The effect of heat-curing on transport properties of low-calcium fly ash-based geopolymer concrete.” Constr. Build. Mater. 112: 464–477. https://doi.org/10.1016/j.conbuildmat.2016.02.210.
Oh, S., and Y. C. Choi. 2018. “Superabsorbent polymers as internal curing agents in alkali activated slag mortars.” Constr. Build. Mater. 159: 1–8. https://doi.org/10.1016/j.conbuildmat.2017.10.121.
Palacios, M., and F. Puertas. 2005. “Effect of superplasticizer and shrinkage-reducing admixtures on alkali-activated slag pastes and mortars.” Cem. Concr. Res. 35 (7): 1358–1367. https://doi.org/10.1016/j.cemconres.2004.10.014.
Palomo, A., M. W. Grutzeck, and M. T. Blanco. 1999. “Alkali-activated fly ashes: A cement for the future.” Cem. Concr. Res. 29 (8): 1323–1329. https://doi.org/10.1016/S0008-8846(98)00243-9.
Puertas, F., and A. Fernandez-Jimenez. 2003. “Mineralogical and microstructural characterisation of alkali-activated fly ash/slag pastes.” Cem. Concr. Compos. 25 (3): 287–292. https://doi.org/10.1016/S0958-9465(02)00059-8.
Reig, L., M. M. Tashima, M. V. Borrachero, J. Monzó, C. R. Cheeseman, and J. Payá. 2013. “Properties and microstructure of alkali-activated red clay brick waste.” Constr. Build. Mater. 43: 98–106. https://doi.org/10.1016/j.conbuildmat.2013.01.031.
Richardson, I. G. 2008. “The calcium silicate hydrates.” Cem. Concr. Res. 38 (2): 137–158. https://doi.org/10.1016/j.cemconres.2007.11.005.
Saha, S., and C. Rajasekaran. 2017. “Enhancement of the properties of fly ash based geopolymer paste by incorporating ground granulated blast furnace slag.” Constr. Build. Mater. 146: 615–620. https://doi.org/10.1016/j.conbuildmat.2017.04.139.
Shi, C., A. F. Jiménez, and A. Palomo. 2011. “New cements for the 21st century: The pursuit of an alternative to portland cement.” Cem. Concr. Res. 41 (7): 750–763. https://doi.org/10.1016/j.cemconres.2011.03.016.
Thomas, R. J., H. Ye, A. Radlinska, and P. Sulapha. 2016. “Alkali-activated slag cement concrete.” Concr. Int. 38 (1): 33–38.
Wang, K., S. P. Shah, and A. Mishulovich. 2004. “Effects of curing temperature and NaOH addition on hydration and strength development of clinker-free CKD-fly ash binders.” Cem. Concr. Res. 34 (2): 299–309. https://doi.org/10.1016/j.cemconres.2003.08.003.
Wardhono, A., D. W. Law, and A. Strano. 2015. “The strength of alkali-activated slag/fly ash mortar blends at ambient temperature.” Procedia Eng. 125: 650–656. https://doi.org/10.1016/j.proeng.2015.11.095.
Yang, K.-H., J.-H. Mun, J.-I. Sim, and J.-K. Song. 2011. “Effect of water content on the properties of lightweight alkali-activated slag concrete.” J. Mater. Civ. Eng. 23 (6): 886–894. https://doi.org/10.1061/(ASCE)MT.1943-5533.0000244.
Yazici, H. 2012. “The effect of steel micro-fibers on ASR expansion and mechanical properties of mortars.” Constr. Build. Mater. 30: 607–615. https://doi.org/10.1016/j.
Information & Authors
Information
Published In
Journal of Materials in Civil Engineering
Volume 30 • Issue 9 • September 2018
Copyright
©2018 American Society of Civil Engineers.
History
Received: Dec 11, 2017
Accepted: Mar 21, 2018
Published online: Jul 3, 2018
Published in print: Sep 1, 2018
Discussion open until: Dec 3, 2018
Authors
Metrics & Citations
Metrics
Citations
Download citation
If you have the appropriate software installed, you can download article citation data to the citation manager of your choice. Simply select your manager software from the list below and click Download.