Microstructure and Mechanical Characterization of Alkali-Activated Palm Oil Fuel Ash
Publication: Journal of Materials in Civil Engineering
Volume 30, Issue 7
Abstract
Pastes and mortars of alkali-activated palm oil fuel ash (POFA) are synthesized with three types of alkaline solutions and are characterized for molecular functional groups by Fourier transform infrared (FTIR) spectroscopy, microstructure observation, and chemical composition by scanning electron microscopy with energy dispersive X-ray (SEM-EDX) and mechanical strength using a universal mechanical tester. The alkali activators chosen for this investigation are 12 M sodium hydroxide (NaOH), 3 M sodium silicate (), and a combination of both activators ( and NaOH) by mass ratio of . POFA with solution yields the highest compressive strength in comparison to the other activators. The main gel binder dominantly composed of silica with varying calcium/silica () ratios is analyzed by analytical techniques through FTIR and SEM-EDX.
Get full access to this article
View all available purchase options and get full access to this article.
Acknowledgments
The authors wish to thank Universiti Malaysia Sarawak and Ministry of Higher Education, Malaysia for research funding through Special Short Term Grant (No: F02/SpSTG/1389/16/31).
References
Abdullah, M. M. A., H. Kamarudin, M. Bnhussain, I. Khairul Nizar, A. R. Rafiza, and Y. Zarina. 2011. “The relationship of NaOH molarity, Na2SiO3/NaOH ratio, fly ash/alkaline activator ratio, and curing temperature to the strength of fly ash-based geopolymer.” Adv. Mater. Res. 328: 1475–1482.
Ariffin, M. A. M., M. A. R. Bhutta, M. W. Hussin, M. M. Tahir, and N. Aziah. 2013. “Sulfuric acid resistance of blended ash geopolymer concrete.” Constr. Build. Mater. 43: 80–86.
Ariffin, M. M. A., M. W. Hussin, and M. A. R. Bhutta. 2011. “Mix design and compressive strength of geopolymer concrete containing blended ash from agro-industrial wastes.” Adv. Mater. Res. 339: 452–457.
Awal, A. S. M. A., and M. W. Hussin. 2011. “Effect of palm oil fuel ash in controlling heat of hydration of concrete.” Procedia Eng. 14: 2650–2657.
Barbosa, V. F. F., K. J. D. MacKenzie, and C. Thaumaturgo. 2000. “Synthesis and characterisation of materials based on inorganic polymers of alumina and silica: Sodium polysialate polymers.” Int. J. Inorganic Mater. 2 (4): 309–317.
Bignozzi, M. C., S. Manzi, M. E. Natali, W. D. A. Rickard, and A. van Riessen. 2014. “Room temperature alkali activation of fly ash: The effect of Na2O/SiO2 ratio.” Constr. Build. Mater. 69: 262–270.
Chindaprasirt, P., S. Homwuttiwong, and C. Jaturapitakkul. 2007. “Strength and water permeability of concrete containing palm oil fuel ash and rice husk–bark ash.” Constr. Build. Mater. 21 (7): 1492–1499.
Davidovits, J. 1994. “Global warming impact on the cement and aggregates industries.” World Resour. Rev. 6 (2): 263–278.
Deepak, T. J., A. Elsayed, N. Hassan, N. Chakravarthy, Y. S. Tong, and B. M. Mithun. 2014. “Investigation on properties of concrete with palm oil fuel ash as cement replacement.” Int. J. Sci. Technol. Res. 3 (1): 138–142.
Duxson, P., J. L. Provis, G. C. Lukey, and J. S. J. van Deventer. 2007. “The role of inorganic polymer technology in the development of ‘green concrete’.” Cem. Concr. Res. 37 (12): 1590–1597.
Galiano, Y. L., C. F. Pereira, and J. Vale. 2011. “Stabilization/solidification of a municipal solid waste incineration residue using fly ash-based geopolymers.” J. Hazard. Mater. 185 (1): 373–381.
Görhan, G., and G. Kürklü. 2014. “The influence of the NaOH solution on the properties of the fly ash-based geopolymer mortar cured at different temperatures.” Compos. Part B Eng. 58: 371–377.
Hussin, M. W., and K. Abdullah. 2009. “Properties of palm oil fuel ash cement based aerated concrete panel subjected to different curing regimes.” Malaysian J. Civ. Eng. 21 (1): 17–31.
Ismail, I., S. A. Bernal, J. L. Provis, R. San Nicolas, S. Hamdan, and J. S. J. van Deventer. 2014. “Modification of phase evolution in alkali-activated blast furnace slag by the incorporation of fly ash.” Cem. Concr. Compos. 45: 125–135.
Khankhaje, E., M. Warid, J. Mirza, M. Ra, M. Razman, H. Chin, and M. N. M. Warid. 2016. “On blended cement and geopolymer concretes containing palm oil fuel ash.” Mater. Des. 89: 385–398.
Liu, M. Y. J., C. P. Chua, U. J. Alengaram, and M. Z. Jumaat. 2014. “Utilization of palm oil fuel ash as binder in lightweight oil palm shell geopolymer concrete.” Adv. Mater. Sci. Eng. 2014: 1–6.
Ma, Y. 2013. Microstructure and engineering properties of alkali activated fly ash as an environment friendly alternative to portland cement. Hubei, China: Wuhan Univ.
Mijarsh, M. J. A., M. A. Megat Johari, and Z. A. Ahmad. 2015. “Compressive strength of treated palm oil fuel ash based geopolymer mortar containing calcium hydroxide, aluminum hydroxide and silica fume as mineral additives.” Cem. Concr. Compos. 60: 65–81.
Nadziri, N., I. Ismail, and S. Hamdan. 2017. “Binding gel characterization of alkali-activated binders based on palm oil fuel ash (POFA) and fly ash.” J. Sustainable Cem. Based Mater. 7 (1): 1–14.
Palomo, A., M. W. Grutzeck, and M. T. Blanco. 1999. “Alkali-activated fly ashes: A cement for the future.” Cem. Concr. Res. 29 (8): 1323–1329.
Provis, J. L., P. Duxson, and J. S. J. van Deventer. 2011. “Alkali-activated binders to enhance the sustainability of concrete production.” In Proc., Asean Australian Engineering Congress 2011, 1–12. Kuching, Sarawak: Sarawak Development Institute.
Rattanasak, U., and P. Chindaprasirt. 2009. “Influence of NaOH solution on the synthesis of fly ash geopolymer.” Miner. Eng. 22 (12): 1073–1078.
Reddy, A. N., D. Anitha, and U. V. Tilak. 2014. “Performance of alkali activated slag and alkali activated slag + fly ash with various alkali activators.” Int. J. Eng. Tech. Res. 2 (1): 73–78.
Rivera, J. F., R. M. D. Gutierrez, J. M. Mejia, and M. Gordillo. 2014. “Hybrid cement based on the alkali activation of by-products of coal.” J. Constr. 13 (2): 31–39.
Rukzon, S., and P. Chindaprasirt. 2009. “Use of disposed waste ash from landfills to replace portland cement.” Waste Manage. Res. 27 (6): 588–594.
Salami, B. A., M. A. M. Johari, Z. A. Ahmad, and M. Maslehuddin. 2017. “Durability performance of palm oil fuel ash-based engineered alkaline-activated cementitious composite (POFA-EACC) mortar in sulfate environment.” Constr. Build. Mater. 131: 229–244.
Salih, M. A., A. A. Abang Ali, R. Demirboga, and M. Al Bakri. 2013. “Properties of fresh palm oil fuel ash based geopolymer material.” Adv. Environ. Biol. 7 (12): 3572–3579.
Salih, M. A., A. A. Abang Ali, and N. Farzadnia. 2014. “Characterization of mechanical and microstructural properties of palm oil fuel ash geopolymer cement paste.” Constr. Build. Mater. 65: 592–603.
Sata, V., C. Jaturapitakkul, and C. Rattanashotinunt. 2010. “Compressive strength and heat evolution of concretes containing palm oil fuel ash.” J. Mater. Civ. Eng. 22 (10): 1033–1038.
Sathonsaowaphak, A., P. Chindaprasirt, and K. Pimraksa. 2009. “Workability and strength of lignite bottom ash geopolymer mortar.” J. Hazard. Mater. 168 (1): 44–50.
Škvára, F., J. Šlosar, J. Bohunek, and A. Marková 2003. “Alkali-activated fly ash geopolymeric materials.” In Proc., Int. Congress on the Chemistry of Cement (ICCC), 1–10. Durban, South Africa: CD-ROM Proceedings.
Sulaiman, O., N. Salim, N. A. Nordin, R. Hashim, M. Ibrahim, and M. Sato. 2012. “The potential of oil palm trunk biomass as an alternative source for compressed wood.” BioResources 7 (2): 2688–2706.
Tempest, B., O. Sanusi, J. Gergely, V. Ogunro, and D. Weggel 2009. “Compressive strength and embodied energy optimization of fly ash based geopolymer concrete.” In Proc., 2009 World of Coal Ash (WOCA) Conf., 1–17. Lexington, KY: CD-ROM Proceedings.
Yong, M., J. Liu, U. J. Alengaram, M. Santhanam, M. Zamin, and K. Hung. 2016. “Microstructural investigations of palm oil fuel ash and fly ash based binders in lightweight aggregate foamed geopolymer concrete.” Constr. Build. Mater. 120: 112–122.
Zhang, Z., H. Wang, and J. L. Provis. 2012. “Quantitative study of the reactivity of fly ash in geopolymerization by FTIR.” J. Sustainable Cem. Based Mater. 1 (4): 154–166.
Information & Authors
Information
Published In
Copyright
©2018 American Society of Civil Engineers.
History
Received: Jun 19, 2017
Accepted: Dec 6, 2017
Published online: Apr 19, 2018
Published in print: Jul 1, 2018
Discussion open until: Sep 19, 2018
Authors
Metrics & Citations
Metrics
Citations
Download citation
If you have the appropriate software installed, you can download article citation data to the citation manager of your choice. Simply select your manager software from the list below and click Download.