Erratum for “New Model for Ductile Fracture of Metal Alloys. II: Reverse Loading” by Huajie Wen and Hussam Mahmoud

Note: CTF = cyclic to failure; C-PTF = cyclic then pulled to failure. The specimens are cycled between displacement limits and subjected to tension load at the incipient stages. The displacements history is described with the following examples: for CTF, ($-0.13:0.26$), [9,0.2] refers to specimen cycled between $-0.13$ and 0.26 mm until failure is observed on nine cycles at a 0.2-mm displacement; for C-PTF, 6($-0.13:0.25$), [0.6] refers to a specimen first subjected to six cycles with displacement limits of $-0.13$ and 0.25 mm and then pulled to failure at a 0.6-mm displacement.