Long-Term Corrosion Monitoring of Bacterially Healed Concrete Using Electrochemical and Ultrasonic Techniques
Publication: Journal of Materials in Civil Engineering
Volume 35, Issue 7
Abstract
Bacterial biocementation has been shown to have the unique capability of healing cracks in concrete. However, there is a concern that the materials used in biocement may cause corrosion. This paper reports the performance of bacterially healed reinforced concrete when exposed to chloride-induced reinforcement corrosion. Cracks in reinforced concrete specimens were healed using two different calcium sources. After healing, the samples were subjected to 3.5% sodium chloride exposure to salt water for 120 days. The state of corrosion was assessed through standard electrochemical techniques such as half-cell and linear polarization methods as well as ultrasonic-guided waves. After the exposure period, the bars were extracted from concrete, and mass loss and tensile tests were conducted. It was found that electrochemical measurements indicated corrosion activity in the cracked specimens, but the uncracked specimen did not indicate corrosion during the entire exposure period. The presence of electrolytes in the healing fluid seems to have influenced the electrochemical measurements and gave a misleading indication of corrosion. The ultrasonic-guided waves that assess both effects of corrosion, loss of metal and bar-concrete interfacial debonding, were found to realistically assess the state of corrosion in all the samples. The rate of corrosion had slowed down significantly as a result of healing.
Get full access to this article
View all available purchase options and get full access to this article.
Data Availability Statement
Some or all data, models, or code generated or used during the study are available from the corresponding author by request.
Acknowledgments
The authors would like to acknowledge the contribution of the Australian Government Research Training Program Scholarship in supporting this research. The authors also acknowledge the use of Curtin University’s Microscopy & Microanalysis Facility, whose instrumentation has been partially funded by the University, State, and Commonwealth Governments. This research is supported by the Australia Research Council Linkage Grant LP180100132 in partnership with industry partners ConBioCrete, Mainroads Western Australia, and Structural Specialities and Projects.
References
Achal, V., A. Mukherjee, D. Kumari, and Q. Zhang. 2015. “Biomineralization for sustainable construction—A review of processes and applications.” Earth Sci. Rev. 148 (Sep): 1–17. https://doi.org/10.1016/j.earscirev.2015.05.008.
Aggelis, D., and T. Shiotani. 2007. “Repair evaluation of concrete cracks using surface and through-transmission wave measurements.” Cem. Concr. Compos. 29 (9): 700–711. https://doi.org/10.1016/j.cemconcomp.2007.05.001.
Anagnostopoulos, C. A. 2014. “Effect of different superplasticisers on the physical and mechanical properties of cement grouts.” Constr. Build. Mater. 50 (Jun): 162–168. https://doi.org/10.1016/j.conbuildmat.2013.09.050.
Assouli, B., G. Ballivy, and P. Rivard. 2008. “Influence of environmental parameters on application of standard ASTM C876-91: Half cell potential measurements.” Corros. Eng. Sci. Technol. 43 (1): 93–96. https://doi.org/10.1179/174327807X214572.
Broomfield, J. 2003. Corrosion of steel in concrete: Understanding, investigation and repair. Boca Raton, FL: CRC Press.
De Belie, N., and J. Wang. 2016. “Bacteria-based repair and self-healing of concrete.” J. Sustainable Cem. Based Mater. 5 (1–2): 35–56. https://doi.org/10.1080/21650373.2015.1077754.
De Muynck, W., D. Debrouwer, N. De Belie, and W. Verstraete. 2008. “Bacterial carbonate precipitation improves the durability of cementitious materials.” Cem. Concr. Res. 38 (7): 1005–1014. https://doi.org/10.1016/j.cemconres.2008.03.005.
Dhami, N. K., M. S. Reddy, and A. Mukherjee. 2013. “Biomineralization of calcium carbonates and their engineered applications: A review.” Front Microbiol. 4 (Oct): 314. https://doi.org/10.3389/fmicb.2013.00314.
Dhami, N. K., S. M. Reddy, and A. Mukherjee. 2012. “Biofilm and microbial applications in biomineralized concrete.” In Advanced topics in biomineralization. London: InTech. https://doi.org/10.5772/31124.
Dubey, A. A., R. Murugan, K. Ravi, A. Mukherjee, and N. K. Dhami. 2022. “Investigation on the Impact of cementation media concentration on properties of biocement under stimulation and augmentation approaches.” J. Hazard. Toxic Radioact. Waste 26 (1): 04021050. https://doi.org/10.1061/(ASCE)HZ.2153-5515.0000662.
Ducasse-Lapeyrusse, J., R. Gagné, C. Lors, and D. Damidot. 2017. “Effect of calcium gluconate, calcium lactate, and urea on the kinetics of self-healing in mortars.” Constr. Build. Mater. 157 (Dec): 489–497. https://doi.org/10.1016/j.conbuildmat.2017.09.115.
Elsener, B. 2002. “Macrocell corrosion of steel in concrete–implications for corrosion monitoring.” Cem. Concr. Compos. 24 (1): 65–72. https://doi.org/10.1016/S0958-9465(01)00027-0.
Erşan, Y. Ç., E. Hernandez-Sanabria, N. Boon, and N. De Belie. 2016a. “Enhanced crack closure performance of microbial mortar through nitrate reduction.” Cem. Concr. Compos. 70 (Jul): 159–170. https://doi.org/10.1016/j.cemconcomp.2016.04.001.
Erşan, Y. Ç., H. Verbruggen, I. De Graeve, W. Verstraete, N. De Belie, and N. Boon. 2016b. “Nitrate reducing precipitating bacteria survive in mortar and inhibit steel corrosion.” Cem. Concr. Res. 83 (May): 19–30. https://doi.org/10.1016/j.cemconres.2016.01.009.
Farrugia, C., R. P. Borg, L. Ferrara, and J. Buhagiar. 2019. “The application of Lysinibacillus sphaericus for surface treatment and crack healing in mortar.” Front. Built Environ. 5 (May): 62. https://doi.org/10.3389/fbuil.2019.00062.
Jonkers, H. M., A. Thijssen, G. Muyzer, O. Copuroglu, and E. Schlangen. 2010. “Application of bacteria as self-healing agent for the development of sustainable concrete.” Ecol. Eng. 36 (2): 230–235. https://doi.org/10.1016/j.ecoleng.2008.12.036.
Kaur, N. P., S. Majhi, N. K. Dhami, and A. Mukherjee. 2020. “Healing fine cracks in concrete with bacterial cement for an advanced non-destructive monitoring.” Constr. Build. Mater. 242 (May): 118151. https://doi.org/10.1016/j.conbuildmat.2020.118151.
Kaur, N. P., J. K. Shah, S. Majhi, and A. Mukherjee. 2018. “Healing and simultaneous ultrasonic monitoring of cracks in concrete.” Mater. Today Commun. 18 (Mar): 87–99. https://doi.org/10.1016/j.mtcomm.2018.10.022.
Ling, H., and C. Qian. 2017. “Effects of self-healing cracks in bacterial concrete on the transmission of chloride during electromigration.” Constr. Build. Mater. 144 (Feb): 406–411. https://doi.org/10.1016/j.conbuildmat.2017.02.160.
Lu, Y., J. Li, L. Ye, and D. Wang. 2013. “Guided waves for damage detection in rebar-reinforced concrete beams.” Constr. Build. Mater. 47 (Oct): 370–378. https://doi.org/10.1016/j.conbuildmat.2013.05.016.
Majhi, S., A. Mukherjee, N. V. George, V. Karaganov, and B. Uy. 2021. “Corrosion monitoring in steel bars using laser ultrasonic guided waves and advanced signal processing.” Mech. Syst. Sig. Process. 149 (Feb): 107176. https://doi.org/10.1016/j.ymssp.2020.107176.
Montemor, M., A. Simoes, and M. Ferreira. 2003. “Chloride-induced corrosion on reinforcing steel: From the fundamentals to the monitoring techniques.” Cem. Concr. Compos. 25 (4–5): 491–502. https://doi.org/10.1016/S0958-9465(02)00089-6.
Neville, A. M. 1995. Properties of concrete. London: Longman.
Panasyuk, V., V. Marukha, and V. Sylovanyuk. 2014. Injection technologies for the repair of damaged concrete structures. New York: Springer Netherlands.
Popovics, S., J. L. Rose, and J. S. Popovics. 1990. “The behaviour of ultrasonic pulses in concrete.” Cem. Concr. Res. 20 (2): 259–270. https://doi.org/10.1016/0008-8846(90)90079-D.
Poursaee, A. 2016. “Corrosion of steel in concrete structures.” In Corrosion of steel in concrete structures, 19–33. Amsterdam, Netherlands: Elsevier.
Qian, C., H. Chen, L. Ren, and M. Luo. 2015. “Self-healing of early age cracks in cement-based materials by mineralization of carbonic anhydrase microorganism.” Front. Microbiol. 6 (Nov): 1225. https://doi.org/10.3389/fmicb.2015.01225.
Rodrigues, R., S. Gaboreau, J. Gance, I. Ignatiadis, and S. Betelu. 2020. “Reinforced concrete structures: A review of corrosion mechanisms and advances in electrical methods for corrosion monitoring.” Constr. Build. Mater. 269 (Feb): 121240. https://doi.org/10.1016/j.conbuildmat.2020.121240.
Shao-feng, Z., L. Chun-hua, and L. Rong-gui. 2011. “Experimental determination of chloride penetration in cracked concrete beams.” Procedia Eng. 24 (Jan): 380–384. https://doi.org/10.1016/j.proeng.2011.11.2661.
Sharma, A., S. Sharma, S. Sharma, and A. Mukherjee. 2015. “Ultrasonic guided waves for monitoring corrosion of FRP wrapped concrete structures.” Constr. Build. Mater. 96 (Oct): 690–702. https://doi.org/10.1016/j.conbuildmat.2015.08.084.
Sharma, S., and A. Mukherjee. 2010. “Longitudinal guided waves for monitoring chloride corrosion in reinforcing bars in concrete.” Struct. Health Monit. 9 (6): 555–567. https://doi.org/10.1177/1475921710365415.
Sharma, S., and A. Mukherjee. 2011. “Monitoring corrosion in oxide and chloride environments using ultrasonic guided waves.” J. Mater. Civ. Eng. 23 (2): 207–211. https://doi.org/10.1061/(ASCE)MT.1943-5533.0000144.
Sharma, S., and A. Mukherjee. 2013. “Nondestructive evaluation of corrosion in varying environments using guided waves.” Res. Nondestr. Eval. 24 (2): 63–88. https://doi.org/10.1080/09349847.2012.699609.
Sharma, S., and A. Mukherjee. 2014. “Ultrasonic guided waves for monitoring the setting process of concretes with varying workabilities.” Supplement, Constr. Build. Mater. 72 (SC): 358–366. https://doi.org/10.1016/j.conbuildmat.2014.09.018.
Sharma, S., and A. Mukherjee. 2015. “Ultrasonic guided waves for monitoring corrosion in submerged plates.” Struct. Control Health Monit. 22 (1): 19–35. https://doi.org/10.1002/stc.1657.
Shiotani, T., and D. G. Aggelis. 2009. “Wave propagation in cementitious material containing artificial distributed damage.” Mater. Struct. 42 (3): 377–384. https://doi.org/10.1617/s11527-008-9388-4.
Song, H.-W., and V. Saraswathy. 2007. “Corrosion monitoring of reinforced concrete structures—A review.” Int. J. Electrochem. Sci. 2 (1): 1–28.
Stocks-Fischer, S., J. K. Galinat, and S. S. Bang. 1999. “Microbiological precipitation of CaCO3.” Soil Biol. Biochem. 31 (11): 1563–1571. https://doi.org/10.1016/S0038-0717(99)00082-6.
Stratfull, R. F. 1968. “How chlorides affect concrete used with reinforcing steel.” Mater. Prot. 7 (3): 29–34.
Trtnik, G., and M. Gams. 2014. “Recent advances of ultrasonic testing of cement based materials at early ages.” Ultrasonics 54 (1): 66–75. https://doi.org/10.1016/j.ultras.2013.07.010.
Vijay, K., and M. Murmu. 2019. “Effect of calcium lactate on compressive strength and self-healing of cracks in microbial concrete.” Front. Struct. Civ. Eng. 13 (3): 515–525. https://doi.org/10.1007/s11709-018-0494-2.
Wang, J., Y. C. Ersan, N. Boon, and N. De Belie. 2016. “Application of microorganisms in concrete: A promising sustainable strategy to improve concrete durability.” Appl. Microbiol. Biotechnol. 100 (7): 2993–3007. https://doi.org/10.1007/s00253-016-7370-6.
Wang, J., H. Soens, W. Verstraete, and N. De Belie. 2014. “Self-healing concrete by use of microencapsulated bacterial spores.” Cem. Concr. Res. 56 (Aug): 139–152. https://doi.org/10.1016/j.cemconres.2013.11.009.
Xu, J., Y. Du, Z. Jiang, and A. She. 2015. “Effects of calcium source on biochemical properties of microbial CaCO3 precipitation.” Front. Microbiol. 6 (Dec): 1366. https://doi.org/10.3389/fmicb.2015.01366.
Yeih, W., and R. Huang. 1998. “Detection of the corrosion damage in reinforced concrete members by ultrasonic testing.” Cem. Concr. Res. 28 (7): 1071–1083. https://doi.org/10.1016/S0008-8846(98)00060-X.
Zheng, T., C. Qian, and Y. Su. 2020. “Influences of different calcium sources on the early age cracks of self-healing cementitious mortar.” Biochem. Eng. J. 166 (Feb): 107849. https://doi.org/10.1016/j.bej.2020.107849.
Information & Authors
Information
Published In
Copyright
© 2023 American Society of Civil Engineers.
History
Received: Jan 7, 2022
Accepted: Oct 7, 2022
Published online: Apr 26, 2023
Published in print: Jul 1, 2023
Discussion open until: Sep 26, 2023
Authors
Metrics & Citations
Metrics
Citations
Download citation
If you have the appropriate software installed, you can download article citation data to the citation manager of your choice. Simply select your manager software from the list below and click Download.
Cited by
- Qifang Liu, Guangda Pei, Lijie Chen, Kang Duan, Fengling Zhang, Ray Kai-Leung Su, Effects of Chloride, Humidity, and Concrete Mix on the Electrochemical Parameters of Steel Reinforcement Corrosion, Journal of Materials in Civil Engineering, 10.1061/JMCEE7.MTENG-17914, 36, 8, (2024).
- A. Thirumalaiselvi, Saptarshi Sasmal, Early Detection and Monitoring of Corrosion in Reinforced Concrete Structures Using Coupled Time-Frequency Analysis, Journal of Materials in Civil Engineering, 10.1061/JMCEE7.MTENG-17393, 36, 8, (2024).
- Bhavdeep Sharma, Shruti Sharma, M. Sudhakara Reddy, Nondestructive Monitoring of Bacterial Intrinsic Self-Healing in Cementitious Structures Using Ultrasonic Wave Propagation, Journal of Materials in Civil Engineering, 10.1061/JMCEE7.MTENG-17109, 36, 4, (2024).