Degradation Behavior of Two Multilayered Textured White HDPE Geomembranes and Their Smooth Edges
Publication: Journal of Geotechnical and Geoenvironmental Engineering
Volume 149, Issue 5
Abstract
The longevity of two white multilayered textured geomembranes, manufactured with a smooth edge for welding, is examined when immersed in synthetic municipal solid waste leachate at five temperatures (40, 55, 65, 75, and 85°C) for 50 months. The textured and smooth parts of the geomembranes had similar initial chemical and physical properties, but the core of the smooth edge was thinner. It is shown that, depending on the relative effects of the difference in the core thickness and the surface area exposed to a solution, antioxidant depletion of the textured portion may be either faster or slower than the smooth edge. However, due to the lesser core thickness of the smooth edge of both geomembranes, the degradation in the tensile stress at break properties at 85°C is faster for the smooth edge than for the textured portion of the roll even when the antioxidant depletion was faster for the textured part. Thus, any assessment of the likely service life of the textured geomembrane requires consideration of both the smooth and textured portions of a multilayered textured geomembrane.
Get full access to this article
View all available purchase options and get full access to this article.
Data Availability Statement
Some or all data, models, or code that support the findings of this study are available from the corresponding author upon reasonable request.
Acknowledgments
The research presented in this paper was supported by the Natural Sciences and Engineering Council of Canada (NSERC) and Canadian Nuclear Laboratory (CNL). The equipment used was provided by funding from the Canada Foundation for Innovation (CFI) and the Government Ontario’s Ministry of Research and Innovation.
References
Abdelaal, F. B., M. S. Morsy, and R. K. Rowe. 2019. “Long-term performance of a HDPE geomembrane stabilized with HALS in chlorinated water.” Geotext. Geomembr. 47 (6): 815–830. https://doi.org/10.1016/j.geotexmem.2019.103497.
Abdelaal, F. B., and R. K. Rowe. 2014. “Effect of high temperatures on antioxidant depletion from different HDPE geomembranes.” Geotext. Geomembr. 42 (2): 284–301. https://doi.org/10.1016/j.geotexmem.2014.05.002.
Abdelaal, F. B., and R. K. Rowe. 2017. “Effect of high pH found in low-level radioactive waste leachates on the antioxidant depletion of a HDPE geomembrane.” J. Hazard. Toxic Radioact. Waste 21 (Dec): D4015001. https://doi.org/10.1061/(ASCE)HZ.2153-5515.0000262.
Abdelaal, F. B., R. K. Rowe, and R. W. I. Brachman. 2014a. “Brittle rupture of an aged HPDE geomembrane at local gravel indentations under simulated field conditions.” Geosynth. Int. 21 (1): 1–23. https://doi.org/10.1680/gein.13.00031.
Abdelaal, F. B., R. K. Rowe, and M. Z. Islam. 2014b. “Effect of leachate composition on the long-term performance of a HDPE geomembrane.” Geotext. Geomembr. 42 (Jun): 348–362. https://doi.org/10.1016/j.geotexmem.2014.06.001.
ASTM. 2013. Standard test method for melt flow rates of thermoplastics by extrusion plastometer. West Conshohocken, PA: ASTM.
ASTM. 2014. Standard test method for tensile properties of plastics. West Conshohocken, PA: ASTM.
ASTM. 2019. Standard test method for oxidative-induction time of polyolefins by differential scanning calorimetry. West Conshohocken, PA: ASTM.
ASTM. 2020a. Standard test method for determining tensile properties of nonreinforced polyethylene and nonreinforced flexible polypropylene geomembranes. West Conshohocken, PA: ASTM.
ASTM. 2020b. Standard test method for evaluation of stress crack resistance of polyolefin geomembranes using notched constant tensile load test. West Conshohocken, PA: ASTM.
ASTM. 2020c. Standard test method for oxidative induction time of polyolefin geosynthetics by high-pressure differential scanning calorimetry. West Conshohocken, PA: ASTM.
ASTM. 2021. Standard test method for oxidative induction time of polyolefin geosynthetics by differential scanning calorimetry. West Conshohocken, PA: ASTM.
Cadwallader, M. W. 1991. “Addressing the special concerns of landfill closures: VLDPE and textured geomembranes.” In Landfill closures. Amsterdam, Netherlands: Elsevier.
Erickson, R., R. Thiel, and J. Peters. 2008. “The ongoing quality issues regarding polyethylene geomembrane material manufacturing and installation.” In Proc., 1st Pan American Geosynthetics Conf. and Exhibition, 2–5. Roseville, MN: Advanced Textiles Association.
Ewais, A. M. R., and R. K. Rowe. 2014. “Effect of aging on the stress crack resistance of an HDPE geomembrane.” Polym. Degrad. Stab. 109 (6): 194–208. https://doi.org/10.1016/j.polymdegradstab.2014.06.013.
Ewais, A. M. R., R. K. Rowe, S. Rimal, and H. P. Sangam. 2018. “17-year elevated temperature study of HDPE geomembrane longevity in air, water and leachate.” Geosynth. Int. 25 (Sep): 525–544. https://doi.org/10.1680/jgein.18.00016.
Ewais, A. M. R., R. K. Rowe, and J. Scheirs. 2014. “Degradation behavior of HDPE geomembranes with high and low initial high-pressure oxidative induction time.” Geotext. Geomembr. 42 (Jun): 111–126. https://doi.org/10.1016/j.geotexmem.2014.01.004.
Francey, W., and R. K. Rowe. 2022. “Stress crack resistance of unaged high-density polyethylene geomembrane fusion seams.” Geosynth. Int. 2022 (1): 1–15. https://doi.org/10.1680/jgein.21.00027a.
Giroud, J., B. Tisseau, K. Soderman, and J. Beech. 1995. “Analysis of strain concentration next to geomembrane seams.” Geosynth. Int. 2 (6): 1049–1097. https://doi.org/10.1680/gein.2.0046.
GRI-GM13. 2021. Standard specification for test methods, test properties, and testing frequency for high density polyethylene (HDPE) smooth and textured geomembranes. Folsom, CA: Geosynthetic Research Institute.
Hsuan, Y., H. Schroeder, K. Rowe, W. Müller, J. Greenwood, D. Cazzuffi, and R. Koerner. 2008. “Long-term performance and lifetime prediction of geosynthetics.” In Proc., 4th European Conf. on Geosynthetics. Auxtin, TX: International Geosynthetics Society.
Hsuan, Y. G., and R. M. Koerner. 1998. “Antioxidant depletion lifetime in high density polyethylene geomembranes.” J. Geotech. Geoenviron. Eng. 124 (6): 532–541. https://doi.org/10.1061/(ASCE)1090-0241(1998)124:6(532).
Kavazanjian, E., J. Andresen, and A. Gutierrez. 2017. “Experimental evaluation of HDPE geomembrane seam strain concentrations.” Geosynth. Int. 24 (4): 333–342. https://doi.org/10.1680/jgein.17.00005.
Koerner, R. M., Y. H. Halse, and A. E. Lord. 1990. “Long-term durability and aging of geomembranes.” In Waste containment systems: Construction, regulation, and performance, 106–134. Reston, VA: ASCE.
Koerner, R. M., A. E. Lord, and Y. H. Hsuan. 1992. “Arrhenius modeling to predict geosynthetic degradation.” Geotext. Geomembr. 11 (92): 151–183. https://doi.org/10.1016/0266-1144(92)90042-9.
Kolbasuk, G. M. 1991. “Coextruded HDPE/VLDPE multilayer geomembranes.” In Landfill closures. Amsterdam, Netherlands: Elsevier.
Malík, J., A. Hrivík, and E. Tomová. 1992. “Diffusion of hindered amine light stabilizers in low density polyethylene and isotactic polypropylene.” Polym. Degrad. Stab. 35 (92): 61–66. https://doi.org/10.1016/0141-3910(92)90136-S.
Mar’in, A. P., V. Borzatta, M. Bonora, and L. Greci. 2000. “Diffusion of high molecular weight, sterically hindered amines in polypropylene.” J. Appl. Polym. Sci. 75 (Jun): 890–896. https://doi.org/10.1002/(SICI)1097-4628(20000214)75:7%3C890::AID-APP5%3E3.0.CO;2-K.
Morsy, M., and R. K. Rowe. 2019. “Effect of texturing on the longevity of HDPE geomembranes in municipal solid waste landfills.” Can. Geotech. J. 57 (1): 61–72. https://doi.org/10.1139/cgj-2019-0047(20000214)75:7%3C890::AID-APP5%3E3.0.CO;2-K.
Morsy, M. S., R. K. Rowe, and F. B. Abdelaal. 2020. “Longevity of 12 geomembranes in chlorinated water.” Can. Geotech. J. 58 (4): 479–495. https://doi.org/10.1139/cgj-2019-0520.
Mueller, W., and I. Jakob. 2003. “Oxidative resistance of high-density polyethylene geomembranes.” Polym. Degrad. Stab. 79 (2): 161–172. https://doi.org/10.1016/S0141-3910(02)00269-0.
Priyanto, D., B. Whitelaw, R. Rowe, F. Barone, F. Abdelaal, M. Zafari, and J. Buckley. 2019. “Implementation of research and development (R&D) results in the design of liner system for the near surface disposal facility (NSDF)–19089.” In Proc., WM2019 Conf., 3–7. Tempe, AZ: WM Symposia.
Rowe, R. K. 2020. “Protecting the environment with geosynthetics: 53rd Karl Terzaghi lecture.” J. Geotech. Geoenviron. Eng. 146 (9): 04020081. https://doi.org/10.1061/(ASCE)GT.1943-5606.0002239.
Rowe, R. K., and F. B. Abdelaal. 2016. “Antioxidant depletion in high-density polyethylene (HDPE) geomembrane with hindered amine light stabilizers (HALS) in low-pH heap leach environment.” Can. Geotech. J. 53 (6): 1612–1627. https://doi.org/10.1139/cgj-2016-0026.
Rowe, R. K., F. B. Abdelaal, and R. W. I. Brachman. 2013. “Antioxidant depletion of HDPE geomembrane with sand protection layer.” Geosynth. Int. 20 (2): 73–89. https://doi.org/10.1680/gein.13.00003.
Rowe, R. K., F. B. Abdelaal, M. Zafari, M. S. Morsy, and D. Priyanto. 2020. “An approach to HDPE geomembrane selection for challenging design requirements.” Can. Geotech. J. 57 (10): 1550–1565. https://doi.org/10.1139/cgj-2019-0572.
Rowe, R. K., and A. M. R. Ewais. 2014. “Antioxidant depletion from five geomembranes of same resin but of different thicknesses immersed in leachate.” Geotext. Geomembr. 42 (8): 540–554. https://doi.org/10.1016/j.geotexmem.2014.08.001.
Rowe, R. K., M. Z. Islam, and Y. G. Hsuan. 2008. “Leachate chemical composition effects on OIT depletion in an HDPE geomembrane.” Geosynth. Int. 15 (Feb): 136–151. https://doi.org/10.1680/gein.2008.15.2.136.
Rowe, R. K., M. S. Morsy, and A. M. R. Ewais. 2019. “Representative stress crack resistance of polyolefin geomembranes used in waste management.” Waste Manage. 100 (Dec): 18–27. https://doi.org/10.1016/j.wasman.2019.08.028.
Rowe, R. K., S. Rimal, and H. Sangam. 2009. “Aging of HDPE geomembrane exposed to air, water and leachate at different temperatures.” Geotext. Geomembr. 27 (2): 137–151. https://doi.org/10.1016/j.geotexmem.2008.09.007.
Rowe, R. K., and H. P. Sangam. 2002. “Durability of HDPE geomembranes.” Geotext. Geomembr. 20 (2): 77–95. https://doi.org/10.1016/S0266-1144(02)00005-5.
Rowe, R. K., and M. Shoaib. 2017a. “Effect of brine on long-term performance of four HDPE geomembranes.” Geosynth. Int. 24 (8): 508–523. https://doi.org/10.1680/jgein.17.00018.
Rowe, R. K., and M. Shoaib. 2017b. “Long-term performance HDPE geomembrane seams in MSW leachate.” Can. Geotech. J. 54 (12): 1623–1636. https://doi.org/10.1139/cgj-2017-0049.
Rowe, R. K., and M. Shoaib. 2018. “Durability of HDPE geomembrane seams immersed in brine for three years.” ASCE J. Geotech. Geoenviron. 144 (2): 04017114. https://doi.org/10.1061/(ASCE)GT.1943-5606.0001817.
Sangam, H. P., and R. K. Rowe. 2002. “Effects of exposure conditions on the depletion of antioxidants from high-density polyethylene (HDPE) geomembranes.” Can. Geotech. J. 39 (Jun): 1221–1230. https://doi.org/10.1139/t02-074.
Scheirs, J. 2009. A guide to polymeric geomembranes: A practical approach. New York: Wiley.
Scheirs, J., A. L. Marta, C. J. Armstrong, and R. Jotani. 2020. Rapid screening test for assessing durability of geomembranes in mining liquors. Rio De Janeiro, Brazil: GeoAmericas.
Tian, K., C. H. Benson, J. M. Tinjum, and T. B. Edil. 2017. “Antioxidant depletion and service life prediction for HDPE geomembranes exposed to low-level radioactive waste leachate.” J. Geotech. Geoenviron. Eng. 143 (6): 04017011. https://doi.org/10.1061/(ASCE)GT.1943-5606.0001643.
Information & Authors
Information
Published In
Copyright
© 2023 American Society of Civil Engineers.
History
Received: Jun 14, 2022
Accepted: Jan 4, 2023
Published online: Feb 25, 2023
Published in print: May 1, 2023
Discussion open until: Jul 25, 2023
Authors
Metrics & Citations
Metrics
Citations
Download citation
If you have the appropriate software installed, you can download article citation data to the citation manager of your choice. Simply select your manager software from the list below and click Download.