Effect of Cement and Bitumen Emulsion on the Drying and Film Formation of Bitumen Emulsion Paste
Publication: Journal of Materials in Civil Engineering
Volume 35, Issue 4
Abstract
To obtain a bitumen emulsion paste with a good bitumen film structure and rapid drying rate, the effect of cement content, cement type, and emulsion type on the drying and film formation of bitumen emulsion paste was studied. The drying and film formation mechanism of emulsion was employed to study the drying curve of bitumen emulsion paste. Results indicate that the drying and film formation process of bitumen emulsion paste can be divided into three stages. The solid volume fraction of the beginning of the final stage () and the maximum particle volume fraction () are proposed to evaluate the drying and film formation quality of bitumen emulsion paste. Higher values of and indicate a denser particle packing state and lower residual water content of the final stage, which are beneficial to the drying and film formation quality of bitumen emulsion paste. The and of bitumen emulsion paste differ slightly with the increasing content of ordinary portland cement. However, these quantitative indexes vary significantly with changing bitumen emulsions with different values of and . Compared with ordinary portland cement, sulfoaluminate cement can lead to a noticeable decrease in and ; thus, its addition is harmful to the film structure of bitumen emulsion paste. Overall, to obtain a bitumen emulsion paste with a good bitumen film structure and rapid drying rate, a bitumen emulsion with good drying and film formation quality is recommended.
Get full access to this article
View all available purchase options and get full access to this article.
Data Availability Statement
All data generated during the study appear in the published paper.
Acknowledgments
The authors are thankful for the research funds from National Natural Science Foundation of China (52178417), the Natural Science Foundation of Liaoning Province (2020-MS-116), and the Science Technology Innovation Project from Department of Transportation of Hunan Province (202004).
References
Asphalt Institute. 2008. A basic asphalt emulsion manual: Manual series no. 19 (MS-19). 4th ed. Lexington, KY: Asphalt Emulsion Manufactures Association.
Chevalier, Y., C. Pichot, C. Graillat, M. Joanicot, K. Wong, J. Maquet, P. Lindner, and B. Cabane. 1992. “Film formation with latex particles.” Colloid Polym. Sci. 270 (8): 806–821. https://doi.org/10.1007/BF00776153.
Croll, S. G. 1986. “Drying of latex paint.” J. Coat. Technol. 58 (734): 41–49.
Du Chesne, A., A. Bojkova, J. Gapinski, D. Seip, and P. Fischer. 2000. “Film formation and redispersion of waterborne latex coatings.” J. Colloid Interf. Sci. 224 (1): 91–98. https://doi.org/10.1006/jcis.1999.6645.
Fang, X., A. Garcia, F. Winnefeld, M. N. Partl, and P. Lura. 2016. “Impact of rapid-hardening cements on mechanical properties of cement bitumen emulsion asphalt.” Mater. Struct. 49 (1–2): 487–498. https://doi.org/10.1617/s11527-014-0512-3.
García, A., P. Lura, M. N. Partl, and I. Jerjen. 2013. “Influence of cement content and environmental humidity on asphalt emulsion and cement composites performance.” Mater. Struct. 46 (8): 1275–1289. https://doi.org/10.1617/s11527-012-9971-6.
Graziani, A., C. Godenzoni, F. Cardone, and M. Bocci. 2016. “Effect of curing on the physical and mechanical properties of cold-recycled bituminous mixtures.” Mater. Des. 95 (Jan): 358–369. https://doi.org/10.1016/j.matdes.2016.01.094.
Grilli, A., A. Graziani, E. Bocci, and M. Bocci. 2016. “Volumetric properties and influence of water content on the compactability of cold recycled mixtures.” Mater. Struct. 49 (10): 4349–4362. https://doi.org/10.1617/s11527-016-0792-x.
Keddie, J., and A. F. Routh. 2010. Fundamentals of latex film formation: Processes and properties. Berlin: Springer.
Meocci, M., A. Grilli, F. La Torre, and M. Bocci. 2017. “Evaluation of mechanical performance of cement–bitumen-treated materials through laboratory and in-situ testing.” Road Mater. Pavement Des. 18 (2): 376–389. https://doi.org/10.1080/14680629.2016.1213506.
Ministry of Communications of PR China. 2011. Standard test methods of bitumen and bituminous mixtures for highway engineering. [In Chinese.] JTG E20-2011. Beijing: China Communications Press.
Ouyang, J., P. Cao, Y. Meng, and T. Tang. 2021a. “Investigation on the drying and demulsification process of filler–bitumen emulsion paste.” Mater. Struct. 54 (1): 1–12. https://doi.org/10.1617/s11527-020-01600-x.
Ouyang, J., P. Cao, T. Tang, and Y. Meng. 2021b. “Investigation on maximum packing fraction of bitumen particles during emulsion drying.” Mater. Struct. 54 (5): 1–14. https://doi.org/10.1617/s11527-021-01784-w.
Ouyang, J., L. Hu, W. Yang, and B. Han. 2019a. “Strength improvement additives for cement bitumen emulsion mixture.” Constr. Build. Mater. 198 (5): 456–464. https://doi.org/10.1016/j.conbuildmat.2018.11.280.
Ouyang, J., Y. Meng, T. Tang, M. Miljković, and Y. Tan. 2021c. “Characterization of the drying behaviour of asphalt emulsion.” Constr. Build. Mater. 274 (Dec): 122090. https://doi.org/10.1016/j.conbuildmat.2020.122090.
Ouyang, J., B. Pan, W. Xu, and L. Hu. 2019b. “Effect of water content on volumetric and mechanical properties of cement asphalt emulsion mixture.” J. Mater. Civ. Eng. 31 (6): 04019085. https://doi.org/10.1061/(ASCE)MT.1943-5533.0002736.
Ouyang, J., W. Yang, J. Chen, and B. Han. 2020. “Effect of superplasticizer and wetting agent on the pavement properties of cold recycled mixture with bitumen emulsion and cement.” J. Mater. Civ. Eng. 32 (6): 04020136. https://doi.org/10.1061/(ASCE)MT.1943-5533.0003194.
Rabani, E., D. R. Reichman, P. L. Geissler, and L. E. Brus. 2003. “Drying-ediated self-assembly of nanoparticles.” Nature 426 (8): 271–274. https://doi.org/10.1038/nature02087.
Robati, M., A. Carter, and D. Perraton. 2015. “New conceptual model for filler stiffening effect on asphalt mastic of microsurfacing.” J. Mater. Civ. Eng. 27 (11): 04015033. https://doi.org/10.1061/(ASCE)MT.1943-5533.0001264.
Roulstone, B. J., M. C. Wilkinson, and J. Hearn. 1992. “Studies on polymer latex films: II. Effect of surfactants on the water vapour permeability of polymer latex films.” Polym. Int. 27 (1): 43–50. https://doi.org/10.1002/pi.4990270107.
Saadoon, T., B. Gómez-Meijide, and A. Garcia. 2018. “Prediction of water evaporation and stability of cold asphalt mixtures containing different types of cement.” Constr. Build. Mater. 186 (Jul): 751–761. https://doi.org/10.1016/j.conbuildmat.2018.07.218.
Talapin, D. V., E. V. Shevchenko, M. I. Bodnarchuk, X. C. Ye, J. Chen, and C. B. Murray. 2009. “Quasicrystalline order in self-assembled binary nanoparticle superlattices.” Nature 461 (42): 964–967. https://doi.org/10.1038/nature08439.
Toussaint, A., and M. D. Wilde. 1997. “A comprehensive model of sintering and coalescence of unpigmented latexes.” Prog. Org. Coat. 30 (3): 113–126. https://doi.org/10.1016/S0300-9440(96)00679-0.
Vanderhoff, J. W., E. B. Bradford, and W. K. Carrington. 1973. “The transport of water through latex films.” J. Polym. Sci. Polym. Symp. 41 (1): 155–174. https://doi.org/10.1002/polc.5070410116.
van Tent, A., and K. te Nijenhuis. 2000. “The film formation of polymer particles in drying thin films of aqueous acrylic latices: II. Coalescence, studied with transmission spectrophotometry.” J. Colloid Interf. Sci. 232 (2): 350–363. https://doi.org/10.1006/jcis.2000.7189.
Wang, F., Z. Liu, T. Wang, and S. Hu. 2008. “A novel method to evaluate the setting process of cement and asphalt emulsion in CA mortar.” Mater. Struct. 41 (4): 643–647. https://doi.org/10.1617/s11527-007-9270-9.
Wozniak, M., G. Derkachov, K. Kolwas, J. Archer, T. Wojciechowski, D. Jakubczyk, and M. Kolwas. 2015. “Formation of highly ordered spherical aggregates from drying microdroplets of colloidal suspension.” Langmuir 31 (28): 7860–7868. https://doi.org/10.1021/acs.langmuir.5b01621.
Xiao, J., W. Jiang, W. Ye, J. Shan, and Z. Wang. 2019. “Effect of cement and emulsified asphalt contents on the performance of cement-emulsified asphalt mixture.” Constr. Build. Mater. 220 (6): 577–586. https://doi.org/10.1016/j.conbuildmat.2019.06.051.
Yang, W., J. Ouyang, Y. Meng, B. Han, and Y. Sha. 2021. “Effect of curing and compaction on volumetric and mechanical properties of cold-recycled mixture with asphalt emulsion under different cement contents.” Constr. Build. Mater. 297 (21): 123699. https://doi.org/10.1016/j.conbuildmat.2021.123699.
Yao, X., L. Tan, and T. Xu. 2022a. “Preparation, properties and compound modification mechanism of waterborne epoxy resin/styrene butadiene rubber latex modified emulsified asphalt.” Constr. Build. Mater. 326 (Sep): 126860. https://doi.org/10.1016/j.conbuildmat.2021.126178.
Yao, X., H. Xu, and T. Xu. 2022b. “Syncretization mechanism between emulsified asphalt and aged asphalt in cold recycled asphalt mixture using developed demulsification-dehydration method.” Constr. Build. Mater. 318 (12): 126178. https://doi.org/10.1016/j.conbuildmat.2022.126860.
Zhu, C., H. Zhang, L. Huang, and C. Wei. 2020. “Long-term performance and microstructure of asphalt emulsion cold recycled mixture with different gradations.” J. Cleaner Prod. 215 (Jan): 944–951. https://doi.org/10.1016/j.jclepro.2019.01.103.
Information & Authors
Information
Published In
Copyright
© 2023 American Society of Civil Engineers.
History
Received: Jan 20, 2022
Accepted: Aug 4, 2022
Published online: Jan 30, 2023
Published in print: Apr 1, 2023
Discussion open until: Jun 30, 2023
Authors
Metrics & Citations
Metrics
Citations
Download citation
If you have the appropriate software installed, you can download article citation data to the citation manager of your choice. Simply select your manager software from the list below and click Download.