The Impact of Particles on the Moisture Susceptibility and Fracture Toughness of HMA under Mixed-Mode I/II Loading and Various Crack Geometry and Temperatures
Publication: Journal of Materials in Civil Engineering
Volume 35, Issue 3
Abstract
In recent decades, some of the main goals of pavement engineers have been to increase bearing capacity, enhance tensile strength, and improve the moisture susceptibility of asphalt mixtures. Because moisture and frost intensify the damage caused by traffic loads on pavements in cold climates, the life and safety of asphalt pavements in this climate are reduced. Finally, cracking at low temperatures and moisture damage leads to a decrease in the serviceability of asphalt pavement in cold climates relative to temperate climates. Hence, a comprehensive and accurate program is necessary to estimate the fracture toughness and moisture susceptibility of asphalt mixtures in cold climates. In recent years, nanotechnology has become very popular due to its unique features in enhancing the operation of bitumen and asphalt mixtures. For this purpose, in this study, the impact of on pavement performance against cracking and moisture susceptibility is investigated. To achieve this objective, SCB specimens were fabricated with different ratios of (0.0% and 0.9%) and studied at the three temperatures of , , and under pure mode I, pure mode II, and four distinct mixed-mode (I/II) loading (, , , ) for various crack geometry, including vertical and angular cracks for which the crack angle is 45° in samples with angular cracks. In addition, the indirect tensile strength (ITS) test was employed to estimate the moisture susceptibility. The results indicated that modifying the asphalt mixture properties with 0.9% had a significant impact on the fracture behavior of the samples in both vertical and angular cracks under all temperatures. Additionally, with the application of and decreasing temperature, the fracture toughness of the samples increased. Furthermore, the findings displayed that the employment of 0.9% reduced the moisture susceptibility of asphalt mixtures by approximately 6%.
Get full access to this article
View all available purchase options and get full access to this article.
Data Availability Statement
All data, models, and code generated or used during the study appear in the published paper.
References
AASHTO. 1995. Resistance of compacted bituminous mixture to moisture induced damage. Standard specifications for transportation materials and methods of sampling and testing, part II Test. AASHTO T 283. Washington, DC: AASHTO.
AASHTO. 2002. Standard specification for performance-graded asphalt binder. AASHTO M 320. Washington, DC: AASHTO.
AASHTO. 2014. Standard method of test for sieve analysis of fine and coarse aggregates. AASHTO T 27. Washington, DC: AASHTO.
Adnan, A. M., X. Luo, C. Lü, J. Wang, and Z. Huang. 2020. “Improving mechanics behavior of hot mix asphalt using graphene-oxide.” Constr. Build. Mater. 254 (Sep): 119261. https://doi.org/10.1016/j.conbuildmat.2020.119261.
Aliha, M. R. M., H. Fazaeli, S. Aghajani, and F. Moghadas Nejad. 2015. “Effect of temperature and air void on mixed mode fracture toughness of modified asphalt mixtures.” Constr. Build. Mater. 95 (Oct): 545–555. https://doi.org/10.1016/j.conbuildmat.2015.07.165.
ASTM. 1997. Test method for resistance of plastic flow of bituminous mixtures using Marshall apparatus. ASTM D1559. West Conshohocken, PA: ASTM.
Azarhoosh, A., F. Moghaddas Nejad, and A. Khodaii. 2018. “Evaluation of the effect of on the adhesion between aggregate and asphalt binder in hot mix asphalt.” Eur. J. Environ. Civ. Eng. 22 (8): 946–961. https://doi.org/10.1080/19648189.2016.1229227.
Fakhri, M., S. Ali Siyadati, and M. R. M. Aliha. 2020. “Impact of freeze–thaw cycles on low temperature mixed mode I/II cracking properties of water saturated hot mix asphalt: An experimental study.” Constr. Build. Mater. 261 (Nov): 119939. https://doi.org/10.1016/j.conbuildmat.2020.119939.
Fakhri, M., and A. Rahimzadeh Mottahed. 2021. “Improving moisture and fracture resistance of warm mix asphalt containing RAP and nanoclay additive.” Constr. Build. Mater. 272 (Feb): 121900. https://doi.org/10.1016/j.conbuildmat.2020.121900.
Fakhri, M., and E. Shahryari. 2021. “The effects of nano zinc oxide (ZnO) and nano reduced graphene oxide (RGO) on moisture susceptibility property of stone mastic asphalt (SMA).” Case Stud. Constr. Mater. 15 (Dec): e00655. https://doi.org/10.1016/j.cscm.2021.e00655.
Fakhri, M., E. Shahryari, and T. Ahmadi. 2022. “Investigate the use of recycled polyvinyl chloride (PVC) particles in improving the mechanical properties of stone mastic asphalt (SMA).” Constr. Build. Mater. 326 (Apr): 126780. https://doi.org/10.1016/j.conbuildmat.2022.126780.
Günay, T., and P. Ahmedzade. 2020. “Physical and rheological properties of and nanocomposite modified bitumens.” Constr. Build. Mater. 243 (May): 118208. https://doi.org/10.1016/j.conbuildmat.2020.118208.
Haider, S., I. Hafeez, S. Bilal, A. Zaidi, M. Ali, and M. Rizwan. 2020a. “A pure case study on moisture sensitivity assessment using tests on both loose and compacted asphalt mixture.” Constr. Build. Mater. 239 (Apr): 117817. https://doi.org/10.1016/j.conbuildmat.2019.117817.
Haider, S., I. J. Hafeez, and R. Ullah. 2020b. “Sustainable use of waste plastic modifiers to strengthen the adhesion properties of asphalt mixtures.” Constr. Build. Mater. 235 (Feb): 117496. https://doi.org/10.1016/j.conbuildmat.2019.117496.
Hamedi, G. H. 2018. “Investigating the use of nano coating over the aggregate surface on moisture damage of asphalt mixtures.” Int. J. Civ. Eng. 16 (6): 659–669. https://doi.org/10.1007/s40999-016-0143-x.
Hu, J., and X. Yu. 2020. “Performance evaluation of solar-responsive asphalt mixture with thermochromic materials and scatterers.” Constr. Build. Mater. 247 (Jun): 118605. https://doi.org/10.1016/j.conbuildmat.2020.118605.
Liu, J., S. Zhao, L. Li, P. Li, and S. Saboundjian. 2017. “Low temperature cracking analysis of asphalt binders and mixtures.” Cold Reg. Sci. Technol. 141 (Sep): 78–85. https://doi.org/10.1016/j.coldregions.2017.06.001.
Luo, R., and H. Chen. 2019. “An improved method of characterizing fracture resistance of asphalt mixtures using modified Paris’ law: Part II—Establishment of index for fracture resistance.” Mech. Mater. 138 (Nov): 103168. https://doi.org/10.1016/j.mechmat.2019.103168.
Mamun, A. A., and M. Arifuzzaman. 2018. “Nano-scale moisture damage evaluation of carbon nanotube-modified asphalt.” Constr. Build. Mater. 193 (Dec): 268–275. https://doi.org/10.1016/j.conbuildmat.2018.10.155.
Naseri Yalghouzaghaj, M., A. Sarkar, G. H. Hamedi, and P. Hayati. 2021. “Application of the surface free energy method on the mechanism of low-temperature cracking of asphalt mixtures.” Constr. Build. Mater. 268 (Jan): 121194. https://doi.org/10.1016/j.conbuildmat.2020.121194.
Omar, H. A., N. I. M. Yusoff, M. Mubaraki, and H. Ceylan. 2020. “Effects of moisture damage on asphalt mixtures.” J. Traffic Transp. Eng. 7 (5): 600–628. https://doi.org/10.1016/j.jtte.2020.07.001.
Pirmohammad, S., and M. Khanpour. 2020. “Fracture strength of warm mix asphalt concretes modified with crumb rubber subjected to variable temperatures.” Supplement, Road Mater. Pavement Des. 21 (S1): S57–S75. https://doi.org/10.1080/14680629.2020.1724819.
Pirmohammad, S., Y. Majd Shokorlou, and B. Amani. 2020a. “Experimental investigation of fracture properties of asphalt mixtures modified with Nano and carbon nanotubes.” Road Mater. Pavement Des. 21 (8): 2321–2343. https://doi.org/10.1080/14680629.2019.1608289.
Pirmohammad, S., Y. Majd Shokorlou, and B. Amani. 2020b. “Laboratory investigations on fracture toughness of asphalt concretes reinforced with carbon and kenaf fibers.” Eng. Fract. Mech. 226 (Mar): 106875. https://doi.org/10.1016/j.engfracmech.2020.106875.
Razmi, A., and M. M. Mirsayar. 2018. “Fracture resistance of asphalt concrete modified with crumb rubber at low temperatures.” Int. J. Pavement Res. Technol. 11 (3): 265–273. https://doi.org/10.1016/j.ijprt.2017.10.003.
Sadeghnejad, M., and G. Shafabakhsh. 2017. “Use of Nano and Nano to improve the mechanical behaviour of stone mastic asphalt mixtures.” Constr. Build. Mater. 157 (Dec): 965–974. https://doi.org/10.1016/j.conbuildmat.2017.09.163.
Shafabakhsh, G., M. Sadeghnejad, and R. Ebrahimnia. 2021. “Fracture resistance of asphalt mixtures under mixed-mode I/II loading at low-temperature: Without and with nano .” Constr. Build. Mater. 266 (Jan): 120954. https://doi.org/10.1016/j.conbuildmat.2020.120954.
Shafabakhsh, G. A., M. Sadeghnejad, B. Ahoor, and E. Taheri. 2020. “Laboratory experiment on the effect of nano and on short and long-term aging behavior of bitumen.” Constr. Build. Mater. 237 (Mar): 117640. https://doi.org/10.1016/j.conbuildmat.2019.117640.
Sreedhar, S., E. Coleri, and S. S. Haddadi. 2018. “Selection of a performance test to assess the cracking resistance of asphalt concrete materials.” Constr. Build. Mater. 179 (Aug): 285–293. https://doi.org/10.1016/j.conbuildmat.2018.05.258.
Zhang, H. L., M. M. Su, S. F. Zhao, Y. P. Zhang, and Z. P. Zhang. 2016. “High and low temperature properties of nano-particles/polymer modified asphalt.” Constr. Build. Mater. 114 (Jul): 323–332. https://doi.org/10.1016/j.conbuildmat.2016.03.118.
Zhang, J., H. Tan, J. Pei, T. Qu, and W. Liu. 2019. “Evaluating crack resistance of asphalt mixture based on essential fracture energy and fracture toughness.” Int. J. Geomech. 19 (4): 06019005. https://doi.org/10.1061/(ASCE)GM.1943-5622.0001390.
Zhu, J., K. Zhang, K. Liu, and X. Shi. 2019. “Performance of hot and warm mix asphalt mixtures enhanced by nano-sized graphene oxide.” Constr. Build. Mater. 217 (Aug): 273–282. https://doi.org/10.1016/j.conbuildmat.2019.05.054.
Information & Authors
Information
Published In
Copyright
© 2022 American Society of Civil Engineers.
History
Received: Dec 19, 2021
Accepted: Jun 2, 2022
Published online: Dec 19, 2022
Published in print: Mar 1, 2023
Discussion open until: May 19, 2023
Authors
Metrics & Citations
Metrics
Citations
Download citation
If you have the appropriate software installed, you can download article citation data to the citation manager of your choice. Simply select your manager software from the list below and click Download.
Cited by
- Milad Keneshlou, Gholamali Shafabakhsh, Mostafa Sadeghnejad, Experimental and Statistical Investigation of the Effect of Nano on Asphalt Mixture Resistance against Low Temperature Cracking and Moisture Susceptibility, Journal of Materials in Civil Engineering, 10.1061/JMCEE7.MTENG-18054, 36, 9, (2024).