Low-Temperature Calcination of Belite-Calcium Sulphoaluminate Cement Clinker and the Hydration Process
Publication: Journal of Materials in Civil Engineering
Volume 33, Issue 12
Abstract
To reduce the calcination temperature of belite ()-calcium sulphoaluminate () cement clinker, hydrothermal curing was applied to mixed raw materials before calcination. The influences of calcination temperature on the mineralogical composition of cement clinker were investigated, and the optimum ratio was deduced. The phase and microstructure evolution of the hydrated paste were analyzed using X-ray diffraction (XRD) and scanning electron microscopy (SEM). The compressive strength development was also tested. The results showed that after hydrothermal curing at 95°C, the belite-calcium sulphoaluminate cement clinker can be prepared with a low-temperature calcination of 1,200°C. When the ratio reached 50%/50%, the cement pastes had the highest 3- and 28-day compressive strengths of 37.34 and 62.94 MPa, respectively. The main hydration product formed in the cement paste was ettringite.
Get full access to this article
View all available purchase options and get full access to this article.
Data Availability Statement
Some or all data, models, or code that support the findings of this study are available from the corresponding author upon reasonable request.
Acknowledgments
The authors are grateful for the financial support of the National Natural Science Foundation of China (Grant No. 51872252).
References
ANSI (American National Standards Institute). 2001. The standard consistency water consumption, setting time, and stability of cement. GB/T 1346-2001. New York: ANSI.
ANSI (American National Standards Institute). 2008a. Glycerol-anhydrous ethanol method. New York: ANSI.
ANSI (American National Standards Institute). 2008b. Methods for chemical analysis of cement. GB/T 176-2008. New York: ANSI.
ANSI (American National Standards Institute). 2008c. Testing method for specific surface of cement-blaine method. GB/T 8074-2008. New York: ANSI.
Beltagui, H., G. Jen, M. Whittaker, and M. S. Imbabi. 2017. “The influence of variable gypsum and water content on the strength and hydration of a belite-calcium sulphoaluminate cement.” Adv. Appl. Ceram. 116 (4): 199–206. https://doi.org/10.1080/17436753.2017.1289722.
Benhelal, E., G. Zahedi, E. Shamsaei, and A. Bahadori. 2013. “Global strategies and potentials to curb emissions in cement industry.” J. Cleaner Prod. 51 (Jul): 142–161. https://doi.org/10.1016/j.jclepro.2012.10.049.
Beretka, J., B. De Vito, L. Santoro, N. Sherman, and G. L. Valenti. 1993. “Hydraulic behaviour of calcium sulfoaluminate-based cements derived from industrial process wastes.” Cem. Concr. Res. 23 (5): 1205–1214. https://doi.org/10.1016/0008-8846(93)90181-8.
Berger, S., C. C. D. Coumes, P. Le Bescop, and D. Damidot. 2011. “Influence of a thermal cycle at early age on the hydration of calcium sulphoaluminate cements with variable gypsum contents.” Cem. Concr. Res. 41 (2): 149–160. https://doi.org/10.1016/j.cemconres.2010.10.001.
Chang, J., J. Li, J. Han, and T. Zhang. 2019. “Traces of CH in a hydration system.” Constr. Build. Mater. 197 (Feb): 641–651. https://doi.org/10.1016/j.conbuildmat.2018.11.226.
Chang, J., Y. Zhang, X. Shang, J. Zhao, and X. Yu. 2017. “Effects of amorphous phase on mechanical properties and hydration process of C4A3S–CS--CH-H2O system.” Constr. Build. Mater. 133 (Feb): 314–322. https://doi.org/10.1016/j.conbuildmat.2016.11.111.
Chatterjee, A. K. 1996. “High belite cements—Present status and future technological options. Part I.” Cem. Concr. Res. 26 (8): 1213–1225. https://doi.org/10.1016/0008-8846(96)00099-3.
Chen, I. A., and M. C. G. Juenger. 2011. “Synthesis and hydration of calcium sulfoaluminate-belite cements with varied phase compositions.” J. Mater. Sci. 46 (8): 2568–2577.
El-Alfi, E. A., and R. A. Gado. 2016. “Preparation of calcium sulfoaluminate-belite cement from marble sludge waste.” Constr. Build. Mater. 113 (Jun): 764–772. https://doi.org/10.1016/j.conbuildmat.2016.03.103.
Gallardo, M., J. M. Almanza, D. A. Cortés, J. C. Escobedo, and J. I. Escalante-García. 2014. “Synthesis and mechanical properties of a calcium sulphoaluminate cement made of industrial wastes.” Mater. Constr. 64 (315): e023. https://doi.org/10.3989/mc.2014.04513.
Gao, Y., Z. Li, J. Zhang, Q. Zhang, and Y. Wang. 2020. “Synergistic use of industrial solid wastes to prepare belite-rich sulphoaluminate cement and its feasibility use in repairing materials.” Constr. Build. Mater. 264 (Dec): 120201. https://doi.org/10.1016/j.conbuildmat.2020.120201.
Gartner, E. 2004. “Industrially interesting approaches to ‘low-’ cements.” Cem. Concr. Res. 34 (9): 1489–1498. https://doi.org/10.1016/j.cemconres.2004.01.021.
Gong, Y., and Y. Fang. 2016. “Preparation of belite cement from stockpiled high-carbon fly ash using granule-hydrothermal synthesis method.” Constr. Build. Mater. 111 (May): 175–181. https://doi.org/10.1016/j.conbuildmat.2016.02.043.
Huang, Z., T. Zhang, and Z. Wen. 2015. “Proportioning and characterization of portland cement-based ultra-lightweight foam concretes.” Constr. Build. Mater. 79 (Mar): 390–396. https://doi.org/10.1016/j.conbuildmat.2015.01.051.
Ishak, S. A., and H. Hashim. 2015. “Low carbon measures for cement plant a review.” J. Cleaner Prod. 103 (Sep): 260–274. https://doi.org/10.1016/j.jclepro.2014.11.003.
Kacimi, L., M. Cyr, and P. Clastres. 2010. “Synthesis of - cement from fly-ash using the hydrothermal method at low temperature and atmospheric pressure.” J. Hazard. Mater. 181 (1–3): 593–601. https://doi.org/10.1016/j.jhazmat.2010.05.054.
Kacimi, L., A. Simon-Masseron, S. Salem, A. Ghomari, and Z. Derriche. 2009. “Synthesis of belite cement clinker of high hydraulic reactivity.” Cem. Concr. Res. 39 (7): 559–565. https://doi.org/10.1016/j.cemconres.2009.02.004.
Kim, Y. M., and S. H. Hong. 2010. “Influence of minor ions on the stability and hydration rates of -dicalcium silicate.” J. Am. Ceram. Soc. 87 (5): 900–905. https://doi.org/10.1111/j.1551-2916.2004.00900.x.
Kramar, S., L. Žibret, E. Fidanchevska, V. Jovanov, B. Angjusheva, and V. Ducman. 2019. “Use of fly ash and phosphogypsum for the synthesis of belite-sulfoaluminate clinker.” Mater. Constr. 69 (333): 176. https://doi.org/10.3989/mc.2019.11617.
Li, J., and J. Chang. 2019. “Effect of crystal/amorphous ratio on mechanical properties in a hydration system with or without gypsum addition.” Constr. Build. Mater. 208 (May): 36–45.
Li, X., W. Xu, S. Wang, M. Tang, and X. Shen. 2014. “Effect of and MgO on Portland cement clinker: Formation of clinker phases and alite polymorphism.” Constr. Build. Mater. 58 (May): 182–192. https://doi.org/10.1016/j.conbuildmat.2014.02.029.
Liu, C., J. Luo, Q. Li, S. Gao, Z. Jin, S. Li, P. Zhang, and S. Chen. 2019. “Preparation and physical properties of high-belite sulphoaluminate cement-based foam concrete using an orthogonal test.” Materials 12 (6): 984. https://doi.org/10.3390/ma12060984.
Lu, L., P. Zhao, S. Wang, and Y. Chen. 2011. “Effects of calcium carbide residue and high-silicon limestone on synthesis of belite-barium calcium sulphoaluminate cement.” J. Inorg. Organomet. Polym. Mater. 21 (4): 900–905. https://doi.org/10.1007/s10904-011-9560-0.
Lu, X. L., Z. M. Ye, and S. X. Wang. 2018. “Study on the preparation and properties of belite-ye’elimite-alite cement.” Constr. Build. Mater. 182 (Sep): 399–405.
Martin, L. H., F. Winnefeld, C. J. Müller, and B. Lothenbach. 2015. “Contribution of limestone to the hydration of calcium sulfoaluminate cement.” Cem. Concr. Compos. 62 (Sep): 204–211. https://doi.org/10.1016/j.cemconcomp.2015.07.005.
Martin, L. H., F. Winnefeld, E. Tschopp, C. J. Müller, and B. Lothenbach. 2017. “Influence of fly ash on the hydration of calcium sulfoaluminate cement.” Cem. Concr. Res. 95 (May): 152–163. https://doi.org/10.1016/j.cemconres.2017.02.030.
Matschei, T., B. Lothenbach, and F. P. Glasser. 2007. “The AFm phase in portland cement.” Cem. Concr. Res. 37 (2): 118–130. https://doi.org/10.1016/j.cemconres.2006.10.010.
Mazouzi, W., L. Kacimi, M. Cyr, and P. Clastres. 2014. “Properties of low temperature belite cements made from aluminosilicate wastes by hydrothermal method.” Cem. Concr. Compos. 53 (Oct): 170–177. https://doi.org/10.1016/j.cemconcomp.2014.07.001.
Morin, V., P. Termkhajornkit, B. Huet, and G. Pham. 2017. “Impact of quantity of anhydrite, water to binder ratio, fineness on kinetics and phase assemblage of belite-ye’elimite-ferrite cement.” Cem. Concr. Res. 99 (Sep): 8–17. https://doi.org/10.1016/j.cemconres.2017.04.014.
Morsli, K., G. Angeles, M. Zahir, and M. A. Aranda. 2007. “Mineralogical phase analysis of alkali and sulfate bearing belite rich laboratory clinkers.” Cem. Concr. Res. 37 (5): 639–646. https://doi.org/10.1016/j.cemconres.2007.01.012.
Nidheesh, P. V., and M. S. Kumar. 2019. “An overview of environmental sustainability in cement and steel production.” J. Cleaner Prod. 231 (Sep): 856–871. https://doi.org/10.1016/j.jclepro.2019.05.251.
Quillin, K. 2001. “Performance of belite–sulfoaluminate cements.” Cem. Concr. Res. 31 (9): 1341–1349. https://doi.org/10.1016/S0008-8846(01)00543-9.
Ren, C., W. Wang, and G. Li. 2017. “Preparation of high-performance cementitious materials from industrial solid waste.” Constr. Build. Mater. 152 (Oct): 39–47. https://doi.org/10.1016/j.conbuildmat.2017.06.124.
Rungchet, A., P. Chindaprasirt, S. Wansom, and K. Pimraksa. 2016. “Hydrothermal synthesis of calcium sulfoaluminate–belite cement from industrial waste materials.” J. Cleaner Prod. 115 (Mar): 273–283. https://doi.org/10.1016/j.jclepro.2015.12.068.
Rungchet, A., C. S. Poon, P. Chindaprasirt, and K. Pimraksa. 2017. “Synthesis of low-temperature calcium sulfoaluminate-belite cements from industrial wastes and their hydration: Comparative studies between lignite fly ash and bottom ash.” Cem. Concr. Compos. 83 (Oct): 10–19. https://doi.org/10.1016/j.cemconcomp.2017.06.013.
Schneider, M., M. Romer, M. Tschudin, and H. Bolio. 2011. “Sustainable cement production—Present and future.” Cem. Concr. Res. 41 (7): 642–650. https://doi.org/10.1016/j.cemconres.2011.03.019.
Shen, Y., X. Li, X. Chen, W. Zhang, and D. Yang. 2018. “Synthesis and calorimetric study of hydration behavior of sulfate-rich belite sulfoaluminate cements with different phase compositions.” J. Therm. Anal. Calorim. 133 (3): 1281–1289. https://doi.org/10.1007/s10973-018-7251-6.
Shen, Y., J. Qian, J. Chai, and Y. Fan. 2014. “Calcium sulphoaluminate cements made with phosphogypsum: Production issues and material properties.” Cem. Concr. Compos. 48 (Apr): 67–74. https://doi.org/10.1016/j.cemconcomp.2014.01.009.
Shen, Y., J. Qian, Y. Huang, and D. Yang. 2015. “Synthesis of belite sulfoaluminate-ternesite cements with phosphogypsum.” Cem. Concr. Compos. 63 (Oct): 67–75. https://doi.org/10.1016/j.cemconcomp.2015.09.003.
Snellings, R., A. Bazzoni, and K. Scrivener. 2014. “The existence of amorphous phase in portland cements: Physical factors affecting Rietveld quantitative phase analysis.” Cem. Concr. Res. 59 (May): 139–146. https://doi.org/10.1016/j.cemconres.2014.03.002.
Song, F., Z. Yu, F. Yang, Y. Lu, and Y. Liu. 2015. “Microstructure of amorphous aluminum hydroxide in belite-calcium sulfoaluminate cement.” Cem. Concr. Res. 71 (May): 1–6.
Telesca, A., M. Marroccoli, and F. Winnefeld. 2019. “Synthesis and characterization of calcium sulfoaluminate cements produced by different chemical gypsums.” Adv. Cem. Res. 31 (3): 113–123. https://doi.org/10.1680/jadcr.18.00122.
Xue, P., A. Xu, D. He, Q. Yang, G. Liu, F. Engström, and B. Björkman. 2016. “Research on the sintering process and characteristics of belite sulphoaluminate cement produced by BOF slag.” Constr. Build. Mater. 122 (Sep): 567–576. https://doi.org/10.1016/j.conbuildmat.2016.06.098.
Information & Authors
Information
Published In
Copyright
© 2021 American Society of Civil Engineers.
History
Received: Sep 22, 2020
Accepted: Apr 16, 2021
Published online: Sep 27, 2021
Published in print: Dec 1, 2021
Discussion open until: Feb 27, 2022
Authors
Metrics & Citations
Metrics
Citations
Download citation
If you have the appropriate software installed, you can download article citation data to the citation manager of your choice. Simply select your manager software from the list below and click Download.
Cited by
- Jiangchuan Li, Jun Chang, Tian Zeng, Zhiqi Hu, Jiye Li, Characterization of Phase Microstructure with Different Ratios Based on Calcium Sulfoaluminate Cement, Journal of Materials in Civil Engineering, 10.1061/JMCEE7.MTENG-15150, 35, 7, (2023).
- Xiaodong Ma, Tingshu He, Yongqi Da, Renhe Yang, Yongdong Xu, Mingming Li, Potential of sulphoaluminate cement to solidify fluorine-containing sludge, Construction and Building Materials, 10.1016/j.conbuildmat.2022.128427, 346, (128427), (2022).