Clay Content Assessment in Fine Aggregates Using Phenol Adsorption Method
Publication: Journal of Materials in Civil Engineering
Volume 34, Issue 5
Abstract
The scarcity of river sand is increasing due to worldwide fast-track urbanization and infrastructure development, which leads to high demand for fine aggregates. In recent years, the exploration and consumption of different types of fine aggregates other than natural sand in construction are growing across the globe. The existence of clay in alternative fine aggregates (AFA) is one of the formidable hurdles for their successful utilization in concrete and mortar. Clay content adversely affects the properties of concrete and mortar, such as strength, workability, and durability. Therefore, the objective of the present study represents the assessment of clay content in river sand and other types of alternative sands, such as recycled fine aggregate (RFA), crushed rock sand (CRS), and coal bottom ash (CBA), using an innovative phenol adsorption method. The activated clay effect on adsorption was also assessed. The phenol is adsorbed on the clay surface, resulting in an exothermic reaction that releases heat and causes an increase in the temperature of the solution. Standard correlation curves were developed to evaluate the clay content in different types of fine aggregates with the corresponding variation in temperature. The results were validated using a standard methylene blue value spot test, which was found in good agreement. Clay in different types of fine aggregates used in the present study was found to be less than 5%. Also found was that the activation process increases the phenol adsorption property of clay. The phenol adsorption method is relatively faster and more reliable than the methylene blue value spot test method for assessing clay content. The properties of mortar also indicated that workability and compressive strength decrease with an increase in the clay content in fine aggregates irrespective of activation. The phenol adsorption technique, which is novel, can be used to develop a sensor to evaluate the clay content in fine aggregates in the future by utilizing the exothermic property of clay.
Get full access to this article
View all available purchase options and get full access to this article.
Data Availability Statement
All data, models, and code generated or used during the study appear in the published article.
Acknowledgments
The authors thank M/s NBCC (India) Limited, New Delhi, for providing financial assistance under project GAP 0018 for “Characterization of Manufactured Sand and its Effective Utilization in Construction.”
References
AASHTO. 2015. Standard method of test for the qualitative detection of harmful clays. Washington, DC: AASHTO.
Aghamohammadi, N., A. A. Hamidi, I. M. Hasnain, A. A. Zinatizadeh, E. S. H. Nasr, and S. Ghafari. 2007. “Performance of a powdered activated carbon (PAC) augmented activated sludge process treating semi-aerobic Leachate.” Int. J. Environ. Res. 1 (5): 96–103.
Al-Jabri, K. S., A. H. Al-Saidy, and R. Taha. 2011. “Effect of copper slag as a fine aggregate on the properties of cement mortars and concrete.” Constr. Build. Mater. 25 (2): 933–938. https://doi.org/10.1016/j.conbuildmat.2010.06.090.
Amnon, K., and B. Hadassa. 2006. “Effect of high levels of fines content on concrete properties.” ACI Mater. J. 103 (6): 474–481.
Aringhieri, R., G. Pardini, M. Gispert, and A. Sole. 1992. “Testing a simple methylene blue method for surface area estimation in soils.” Agrochimica 36 (3): 224–232.
ASTM. 2002. Standard test method for compressive strength of hydraulic cement mortars (using 2-in. or [50 mm] cube specimens). West Conshohocken, PA: ASTM.
ASTM. 2018. Standard test method for drying shrinkage of mortar containing hydraulic cement. West Conshohocken, PA: ASTM.
Atkins, P., and J. D. Paula. 2006. Atkins physical chemistry. 8th ed., 916–918. Oxford, UK: Oxford University Press.
Behera, M., S. K. Bhattacharyya, A. K. Minocha, R. Deoliya, and S. Maiti. 2014. “Recycled aggregate from C&D waste & its use in concrete: A review.” Constr. Build. Mater. 68 (2): 501–516. https://doi.org/10.1016/j.conbuildmat.2014.07.003.
BIS (Bureau of Indian Standards). 1963. Method of tests for aggregates for concrete (Part I– Part VII). IS 2386 Part I-VII. New Delhi, India: BIS.
BIS (Bureau of Indian Standards). 1999a. Concrete admixtures—Specifications. New Delhi, India: BIS.
BIS (Bureau of Indian Standards). 1999b. Methods of sampling and analysis of concrete. New Delhi, India: BIS.
BIS (Bureau of Indian Standards). 1999c. Standard sand for testing cement—Specifications. New Delhi, India: BIS.
Chen, X., Y. Guo, B. Li, M. Zhou, B. Li, Z. Liu, and J. Zhou. 2020. “Coupled effects of the content and Methylene blue value (MBV) of micro fines on the performance of manufactured sand concrete.” Constr. Build. Mater. 240 (4): 117953. https://doi.org/10.1016/j.conbuildmat.2019.117953.
Cokca, E., and A. A. Birand. 1993. “Determination of cation exchange capacity of clayey soils by methylene blue test.” Geotech. Test. J. 16 (4): 518–524. https://doi.org/10.1520/GTJ10291J.
Dash, M. K., S. K. Patro, and A. K. Rath. 2016. “Sustainable use of industrial-waste as partial replacement of fine aggregate for preparation of concrete—A review.” Int. J. Sustainable Built Environ. 5 (2): 484–516.
Djebbar, M., F. Djafri, M. Bouchekara, and A. Djafri. 2012. “Adsorption of phenol on natural clay: A review.” Appl. Water Sci. 2 (3): 77–86. https://doi.org/10.1016/j.cis.2008.07.002.
Evangelista, L., and J. D. Brito. 2014. “Concrete with fine recycled aggregates: A review.” Eur. J. Environ. Civ. Eng. 18 (2): 129–172. https://doi.org/10.1080/19648189.2013.851038.
Hang, P. T., and G. W. Brindley. 1969. “Methylene blue absorption by clay minerals. Determination of surface areas and cation exchange capacity.” Clay Clay Miner. 18 (4): 203–212. https://doi.org/10.1346/CCMN.1970.0180404.
Hassani, A., S. Seif, A. H. Javid, and M. Borghei. 2008. “Comparison of adsorption process by GAC with novel formulation of coagulation—Flocculation for colour removal of textile wastewater.” Int. J. Environ. Res. 2 (3): 239–248.
Ilangovan, R., K. Nagamani, and K. Kumarasamy. 2006. “Studies on strength and behaviour of concrete by using crushed rock dust as fine aggregates.” Civ. Eng. Constr. Rev. 2006 (Oct): 924–932.
ISSA (International Sports Sciences Association). 1989. Test method for determination of Methylene blue adsorption value (MBV) of mineral aggregates fillers and fines. Phoenix: ISSA.
Jadhav, P. A., and D. K. Kulkarni. 2013. “Effect of replacement of natural sand by manufactured sand on the properties of cement mortar.” Int. J. Civ. Struct. Eng. 3 (3): 621–628.
Khalid, N., S. Ahmad, A. Toheed, and J. Ahmad. 2000. “Potential of rice husks for antimony removal.” Appl. Radiat. Isot. 52 (1): 31–38. https://doi.org/10.1016/s0969-8043(99)00115-3.
Kirthika, S. K., M. Surya, and S. K. Singh. 2019. “Effect of clay in alternative fine aggregates on performance of concrete.” Constr. Build. Mater. 228 (Dec): 116811. https://doi.org/10.1016/j.conbuildmat.2019.116811.
Kujawski, W., A. Warszawski, W. Ratajczak, T. Porebski, W. Capala, and I. Ostrowska. 2004. “Removal of phenol from wastewater by different separation techniques.” Desalination 163 (2): 287–296. https://doi.org/10.1016/S0011-9164(04)90202-0.
Morales, M. M., M. Zamorano, A. R. Moyano, and I. V. Espinosa. 2011. “Characterization of recycled aggregates construction and demolition waste for concrete production following the Spanish Structural Concrete Code EHE-08.” Constr. Build. Mater. 25 (2): 742–748. https://doi.org/10.1016/j.conbuildmat.2010.07.012.
Nanthagopalan, P., and M. Santhanam. 2011. “Fresh and Hardened properties of self-compacting concrete produced with manufactured sand.” Cem. Concr. Compos. 33 (Apr): 353–358. https://doi.org/10.1016/j.cemconcomp.2010.11.005.
Nataraja, M. C., S. Karthik, and A. N. Madhusudan. 2018. “Characterization of crushed fine aggregate for use in concrete based on methylene blue test.” Indian Concr. J. 92 (5): 18–25.
Pant, A., G. V. Ramana, M. Datta, and S. K. Gupta. 2019. “Coal combustion residue as structural fill material for reinforced soil structures.” J. Cleaner Prod. 232 (Sep): 417–426. https://doi.org/10.1016/j.jclepro.2019.05.354.
Passi, S., M. Picardo, and M. Nazzaro-porro. 1987. “Comparative cytotoxicity of phenols in vitro.” Biochem. J. 245 (2): 537–542. https://doi.org/10.1042/bj2450537.
Pitre, B. T. 2012. Application of the modified methylene blue test to detect clay minerals in coarse aggregate fines, 1–101. Austin, TX: Texas A&M Univ.
Raask, E. 1985. “Mineral impurities in coal combustion.” In Behaviour, problems and Remedial measures. New York: Hemisphere Publishing Corporation.
Rao, A., K. N. Jha, and S. Mishra. 2006. “A framework for use of construction and demolition waste as recycled aggregates in India.” Indian Concr. J. 80 (1): 12–19.
Rengaraj, S., S. M. Hyeon, and R. Sivabalan. 2002. “Agricultural solid waste for removal of organics: Adsorption of phenol from water and wastewater by palm seed coat activated carbon.” Waste Manage. 22 (5): 543–548. https://doi.org/10.1016/S0956-053X(01)00016-2.
Robert, M., and D. Tessier. 1974. “Method for preparation of soil clays for mineralogical investigations.” Ann. Agronomiques 25: 859–882.
Santamarina, J. C., K. A. Klein, Y. H. Wang, and E. Prencke. 2002. “Specific surface: Determination and relevance.” Can. Geotech. J. 39 (1): 233–241. https://doi.org/10.1139/t01-077.
Singh, S. K., and S. K. Kirthika. 2017. “Manufactured sand: A foreseeable alternative to river sand.” In Nirman Sarika—A newsletter of BMTPC special issue, 39–46. New Delhi, India: Building Materials and Technology Promotion Council.
Singh, S. K., S. K. Kirthika, and M. Surya. 2018. “Agenda for use of alternative sands in India.” Indian Concr. Inst. J. 19 (3): 1–11.
Sonawana, T. R., and S. S. Pimplikar. 2013. “Use of recycled aggregates in concrete.” Int. J. Eng. Res. Technol. 2 (1): 0181. https://doi.org/10.1680/macr.1987.39.141.214.
Tong, Z., Z. Qingxiang, H. Hui, L. Qin, and Z. Yi. 1997. “Removal of toxic phenol and 4-chlorophenol from waste water by horse radish peroxidase.” Chemosphere 34 (4): 893–903. https://doi.org/10.1016/S0045-6535(97)00015-5.
Wang, M. K., S. L. Wang, and W. M. Wang. 1996. “Rapid estimation of cation-exchange capacities of soil and clay with methylene blue exchange.” Soil Sci. Soc. Am. J. 60 (2): 138–141. https://doi.org/10.2136/sssaj1996.03615995006000010022x.
Yi, H., G. Xu, H. Cheng, J. Wang, Y. Wan, and H. Chen. 2012. “An overview of utilization of steel slag.” Procedia Environ. Sci. 16 (Jan): 791–801. https://doi.org/10.1016/j.proenv.2012.10.108.
Yool, A. I. G., T. P. Lees, and A. Fried. 1998. “Improvement to the methylene blue dye test for harmful clay in aggregates for concrete and mortar.” Cem. Concr. Res. 28 (10): 1417–1428. https://doi.org/10.1016/S0008-8846(98)00114-8.
Yukselen, Y., and A. Kaya. 2008. “Suitability of Methylene Blue test for surface area, Cation exchange capacity and swell potential determination of clayey soils.” Eng. Geol. 102 (1): 38–45. https://doi.org/10.1016/j.enggeo.2008.07.002.
Information & Authors
Information
Published In
Journal of Materials in Civil Engineering
Volume 34 • Issue 5 • May 2022
Copyright
© 2022 American Society of Civil Engineers.
History
Received: Jul 17, 2020
Accepted: Feb 4, 2021
Published online: Feb 17, 2022
Published in print: May 1, 2022
Discussion open until: Jul 17, 2022
Authors
Metrics & Citations
Metrics
Citations
Download citation
If you have the appropriate software installed, you can download article citation data to the citation manager of your choice. Simply select your manager software from the list below and click Download.