Shrinkage Characteristics of Alkali-Activated High-Volume Fly-Ash Pastes Incorporating Silica Fume
Publication: Journal of Materials in Civil Engineering
Volume 32, Issue 10
Abstract
The alkali-activation of high-volume fly ash (HVFA) produces a low-carbon sustainable cementitious binder with remarkable strength and chemical durability at room temperature. In this work, the influence of activator type (i.e., deionized water, NaOH, , solutions), silica fume incorporation, and curing duration on the phase assemblage and strength and shrinkage developments of HVFA is studied. The results show that -activated HVFA shows the highest strength achievement, followed by , NaOH, and water. Alkali incorporation in HVFA considerably increases the shrinkage magnitude and is mainly attributed to the detrimental effect of alkalis on the viscoelasticity and stiffness of cementitious solids. The HVFA activated by the NaOH solution shows the largest shrinkage, followed by and solutions, despite comparable moisture loss. The curing duration does not significantly affect the shrinkage development of alkali-activated HVFA without silica fume. However, with silica fume incorporation, extending curing duration considerably reduces the shrinkage of alkali-activated HVFA. The phase and molecular analysis suggest that silica fume noticeably retards the reaction of HVFA systems but tends to increase the level of silica polymerization in gel products, regardless of activator type.
Get full access to this article
View all available purchase options and get full access to this article.
Data Availability Statement
Some or all data, models, or code that support the findings of this study are available from the corresponding author upon reasonable request. The items include the raw datasets of XRD and FTIR spectra and TG/DTG curves.
Acknowledgments
The authors would like to thank the financial support from the National Natural Science Foundation of China (Grant No. 51808475) and Guangdong Natural Science Fund (Grant No. 1146). Any opinions, findings and conclusions or recommendations expressed in this material are those of the authors and do not necessarily reflect the views of the sponsors.
References
Alahrache, S., F. Winnefeld, J.-B. Champenois, F. Hesselbarth, and B. Lothenbach. 2016. “Chemical activation of hybrid binders based on siliceous fly ash and portland cement.” Cem. Concr. Compos. 66 (Feb): 10–23. https://doi.org/10.1016/j.cemconcomp.2015.11.003.
Atiş, C. D. 2002. “High volume fly ash abrasion resistant concrete.” J. Mater. Civ. Eng. 14 (3): 274–277. https://doi.org/10.1061/(ASCE)0899-1561(2002)14:3(274).
Atiş, C. D. 2003. “High-volume fly ash concrete with high strength and low drying shrinkage.” J. Mater. Civ. Eng. 15 (2): 153–156. https://doi.org/10.1061/(ASCE)0899-1561(2003)15:2(153).
Cartwright, C., F. Rajabipour, and A. Radlińska. 2014. “Shrinkage characteristics of alkali-activated slag cements.” J. Mater. Civ. Eng. 27 (7): B4014007. https://doi.org/10.1061/(ASCE)MT.1943-5533.0001058.
Donatello, S., A. Fernández-Jimenez, and A. Palomo. 2013. “Very high volume fly ash cements. Early age hydration study using as an activator.” J. Am. Ceram. Soc. 96 (3): 900–906. https://doi.org/10.1111/jace.12178.
Duran-Herrera, A., C. A. Juárez, P. Valdez, and D. P. Bentz. 2011. “Evaluation of sustainable high-volume fly ash concretes.” Cem. Concr. Compos. 33 (1): 39–45. https://doi.org/10.1016/j.cemconcomp.2010.09.020.
Garcia-Lodeiro, I., A. Fernández-Jiménez, and A. Palomo. 2013. “Variation in hybrid cements over time. Alkaline activation of fly ash–portland cement blends.” Cem. Concr. Res. 52 (Oct): 112–122. https://doi.org/10.1016/j.cemconres.2013.03.022.
Gartner, E. 2004. “Industrially interesting approaches to ‘low-CO2’ cements.” Cem. Concr. Res. 34 (9): 1489–1498. https://doi.org/10.1016/j.cemconres.2004.01.021.
Ghosh, S. N., and S. K. Handoo. 1980. “Infrared and Raman spectral studies in cement and concrete.” Cem. Concr. Res. 10 (6): 771–782. https://doi.org/10.1016/0008-8846(80)90005-8.
Ghrici, M., S. Kenai, and M. Said-Mansour. 2007. “Mechanical properties and durability of mortar and concrete containing natural pozzolana and limestone blended cements.” Cem. Concr. Compos. 29 (7): 542–549. https://doi.org/10.1016/j.cemconcomp.2007.04.009.
Hojati, M., and A. Radlińska. 2017. “Shrinkage and strength development of alkali-activated fly ash-slag binary cements.” Constr. Build. Mater. 150 (Sep): 808–816. https://doi.org/10.1016/j.conbuildmat.2017.06.040.
Hojati, M., F. Rajabipour, and A. Radlińska. 2019a. “Drying shrinkage of alkali-activated cements: Effect of humidity and curing temperature.” Mater. Struct. 52 (6): 118. https://doi.org/10.1617/s11527-019-1430-1.
Hojati, M., F. Rajabipour, and A. Radlińska. 2019b. “Effect of activator, curing and humidity on drying shrinkage of alkali-activated fly ash.” Green Mater. 7 (2): 71–83. https://doi.org/10.1680/jgrma.18.00069.
Hughes, T. L., C. M. Methven, T. G. J. Jones, S. E. Pelham, P. Fletcher, and C. Hall. 1995. “Determining cement composition by Fourier transform infrared spectroscopy.” Adv. Cem. Based Mater. 2 (3): 91–104. https://doi.org/10.1016/1065-7355(94)00031-X.
Joseph, S., R. Snellings, and Ö. Cizer. 2019. “Activation of portland cement blended with high volume of fly ash using .” Cem. Concr. Compos. 104 (Nov): 103417. https://doi.org/10.1016/j.cemconcomp.2019.103417.
Juenger, M. C. G., and H. M. Jennings. 2001. “Effects of high alkalinity on cement pastes.” ACI Mater. J. 98 (3): 251–255.
Juenger, M. C. G., F. Winnefeld, J. L. Provis, and J. H. Ideker. 2011. “Advances in alternative cementitious binders.” Cem. Concr. Res. 41 (12): 1232–1243. https://doi.org/10.1016/j.cemconres.2010.11.012.
Kovalchuk, O., R. Drochytka, and P. V. Krivenko. 2015. “Mix design of hybrid high-volume fly ash alkali activated cement.” Adv. Mater. Res. 1100: 36–43. https://doi.org/10.4028/www.scientific.net/AMR.1100.36.
Lodeiro, I. G., D. E. Macphee, A. Palomo, and A. Fernández-Jiménez. 2009. “Effect of alkalis on fresh C─ S─ H gels: FTIR analysis.” Cem. Concr. Res. 39 (3): 147–153. https://doi.org/10.1016/j.cemconres.2009.01.003.
Lothenbach, B., K. Scrivener, and R. D. Hooton. 2011. “Supplementary cementitious materials.” Cem. Concr. Res. 41 (12): 1244–1256. https://doi.org/10.1016/j.cemconres.2010.12.001.
Maas, A. J., J. H. Ideker, and M. C. G. Juenger. 2007. “Alkali silica reactivity of agglomerated silica fume.” Cem. Concr. Res. 37 (2): 166–174. https://doi.org/10.1016/j.cemconres.2006.10.011.
Malhotra, V. M., and P. K. Mehta. 2002. High-performance, high-volume fly ash concrete, 101. Ottawa: Supplementary Cementing Materials for Sustainable Development.
Marsh, B. K., and R. L. Day. 1988. “Pozzolanic and cementitious reactions of fly ash in blended cement pastes.” Cem. Concr. Res. 18 (2): 301–310. https://doi.org/10.1016/0008-8846(88)90014-2.
Martinez-Ramirez, S., and A. Palomo. 2001. “Microstructure studies on portland cement pastes obtained in highly alkaline environments.” Cem. Concr. Res. 31 (11): 1581–1585. https://doi.org/10.1016/S0008-8846(01)00603-2.
Mehta, P. K. 2004. “High-performance, high-volume fly ash concrete for sustainable development.” Proc., Int. Workshop on Sustainable Development and Concrete Technology, 3–14. Ames, IA: Iowa State Univ.
Mota, B., T. Matschei, and K. Scrivener. 2018. “Impact of NaOH and on the kinetics and microstructural development of white cement hydration.” Cem. Concr. Res. 108 (Jun): 172–185. https://doi.org/10.1016/j.cemconres.2018.03.017.
Nath, P., and P. K. Sarker. 2015. “Use of OPC to improve setting and early strength properties of low calcium fly ash geopolymer concrete cured at room temperature.” Cem. Concr. Compos. 55 (Jan): 205–214. https://doi.org/10.1016/j.cemconcomp.2014.08.008.
Pajares, I., S. Martínez-Ramírez, and M. T. Blanco-Varela. 2003. “Evolution of ettringite in presence of carbonate, and silicate ions.” Cem. Concr. Compos. 25 (8): 861–865. https://doi.org/10.1016/S0958-9465(03)00113-6.
Roychand, R., S. De Silva, and S. Setunge. 2018. “Nanosilica modified high-volume fly ash and slag cement composite: Environmentally friendly alternative to OPC.” J. Mater. Civ. Eng. 30 (4): 4018043. https://doi.org/10.1061/(ASCE)MT.1943-5533.0002220.
Scrivener, K. L., V. M. John, and E. M. Gartner. 2018. “Eco-efficient cements: Potential economically viable solutions for a low-CO2 cement-based materials industry.” Cem. Concr. Res. 114 (Dec): 2–26. https://doi.org/10.1016/j.cemconres.2018.03.015.
Tangpagasit, J., R. Cheerarot, C. Jaturapitakkul, and K. Kiattikomol. 2005. “Packing effect and pozzolanic reaction of fly ash in mortar.” Cem. Concr. Res. 35 (6): 1145–1151. https://doi.org/10.1016/j.cemconres.2004.09.030.
Velandia, D. F., C. J. Lynsdale, J. L. Provis, and F. Ramirez. 2018. “Effect of mix design inputs, curing and compressive strength on the durability of -activated high volume fly ash concretes.” Cem. Concr. Compos. 91 (Aug): 11–20. https://doi.org/10.1016/j.cemconcomp.2018.03.028.
Warren, C. J., and E. J. Reardon. 1994. “The solubility of ettringite at 25°C.” Cem. Concr. Res. 24 (8): 1515–1524. https://doi.org/10.1016/0008-8846(94)90166-X.
Wei, X., H. Zhu, G. Li, C. Zhang, and L. Xiao. 2007. “Properties of high volume fly ash concrete compensated by metakaolin or silica fume.” J. Wuhan Univ. Technol.-Mater. Sci. Ed. 22 (4): 728–732. https://doi.org/10.1007/s11595-006-4728-0.
Wongkeo, W., P. Thongsanitgarn, C.-S. Poon, and A. Chaipanich. 2019. “Heat of hydration of cement pastes containing high-volume fly ash and silica fume.” J. Therm. Anal. Calorim. 138 (3): 2065–2075. https://doi.org/10.1007/s10973-019-08641-7.
Ye, H., C. Cartwright, F. Rajabipour, and A. Radlińska. 2017a. “Understanding the drying shrinkage performance of alkali-activated slag mortars.” Cem. Concr. Compos. 76 (Feb): 13–24. https://doi.org/10.1016/j.cemconcomp.2016.11.010.
Ye, H., and Z. Chen. 2019. “Mechanisms of alkali-silica reaction in alkali-activated high-volume fly ash mortars.” J. Adv. Concr. Technol. 17 (6): 269–281. https://doi.org/10.3151/jact.17.269.
Ye, H., and A. Radlińska. 2016. “Shrinkage mechanisms of alkali-activated slag.” Cem. Concr. Res. 88 (Oct): 126–135. https://doi.org/10.1016/j.cemconres.2016.07.001.
Ye, H., and A. Radlińska. 2017. “Effect of alkalis on cementitious materials: Understanding the relationship between composition, structure, and volume change mechanism.” J. Adv. Concr. Technol. 15 (4): 165–177. https://doi.org/10.3151/jact.15.165.
Ye, H., A. Radlińska, and J. Neves. 2017b. “Drying and carbonation shrinkage of cement paste containing alkalis.” Mater. Struct. 50 (2): 132. https://doi.org/10.1617/s11527-017-1006-x.
Yu, P., R. J. Kirkpatrick, B. Poe, P. F. McMillan, and X. Cong. 1999. “Structure of calcium silicate hydrate (C-S-H): Near-, mid-, and far-infrared spectroscopy.” J. Am. Ceram. Soc. 82 (3): 742–748. https://doi.org/10.1111/j.1151-2916.1999.tb01826.x.
Information & Authors
Information
Published In
Copyright
© 2020 American Society of Civil Engineers.
History
Received: Oct 25, 2019
Accepted: Mar 26, 2020
Published online: Jul 31, 2020
Published in print: Oct 1, 2020
Discussion open until: Dec 31, 2020
Authors
Metrics & Citations
Metrics
Citations
Download citation
If you have the appropriate software installed, you can download article citation data to the citation manager of your choice. Simply select your manager software from the list below and click Download.