Development of Lightweight Rubberized Geopolymer Concrete by Using Polystyrene and Recycled Crumb-Rubber Aggregates
Publication: Journal of Materials in Civil Engineering
Volume 32, Issue 2
Abstract
An environmentally friendly concrete is of high interest to develop because the production of portland cement as the main binder of conventional concrete is associated with generating a large amount of carbon dioxide. As a green and eligible alternative to conventional concrete, geopolymer concrete (GC) has been invented and studied over the past 2 decades. This experimental study was aimed to take one step further by examining the possibility of developing lightweight, rubberized, and lightweight rubberized geopolymer concrete. In the first step, a control mix was established for GC suitable to be cured at ambient temperature as it is necessary to promote its usage in the construction industry. Afterward, lightweight geopolymer concrete (LWGC) was developed by replacing fine aggregates with expanded polystyrene beads (called BST) at 25%, 50%, 75%, and 100% ratios by volume. Then rubberized geopolymer concrete (RGC) was produced by 10% and 20% natural aggregate replacement by volume with crumb rubber (CR) aggregate, which is another pollution source to the global environment. Finally, the possibility of developing lightweight rubberized geopolymer concrete (LWRGC) was examined using BST and CR aggregates. The performance of developed GCs is discussed based on slump flow, density, compressive, tensile, and flexural strength at 7 and 28 days in this paper. The optimal mix design concluded from LWGC and RGC mixes is also introduced for LWRGC with two different CR sizes (2–5 mm and 5–10 mm). The proposed green mixes showing acceptable fresh and hardened mechanical properties are able to be used in appropriate construction projects and hence reduce the need for cement manufacture as well as disposal of end life tires.
Get full access to this article
View all available purchase options and get full access to this article.
Acknowledgments
This experimental study supported by the School of Engineering, University of Western Australia, Australia.
References
Aslani, F. 2016. “Mechanical properties of waste tire rubber concrete.” J. Mater. Civ. Eng. 28 (3): 04015152. https://doi.org/10.1061/(ASCE)MT.1943-5533.0001429.
Aslani, F., and Z. Asif. 2019. “Properties of ambient-cured normal and heavyweight geopolymer concrete exposed to high temperatures.” Materials 12 (5): 740. https://doi.org/10.3390/ma12050740.
Aslani, F., and R. Gedeon. 2019. “Experimental investigation into the properties of self-compacting rubberised concrete incorporating polypropylene and steel fibers.” Struct. Concr. 20 (1): 267–281. https://doi.org/10.1002/suco.201800182.
Aslani, F., and J. Kelin. 2018. “Assessment and development of high-performance fibre-reinforced lightweight self-compacting concrete including recycled crumb rubber aggregates exposed to elevated temperatures.” J. Clean. Prod. 200 (Nov): 1009–1025. https://doi.org/10.1016/j.jclepro.2018.07.323.
Aslani, F., and M. Khan. 2019. “Properties of high-performance self-compacting rubberized concrete exposed to high-temperatures.” J. Mater. Civ. Eng. 31 (5): 04019040. https://doi.org/10.1061/(ASCE)MT.1943-5533.0002672.
Aslani, F., and G. Ma. 2018. “Normal- and high-strength lightweight self-compacting concrete incorporating perlite, scoria, and polystyrene aggregates at elevated temperatures.” J. Mater. Civ. Eng. 30 (12): 04018328. https://doi.org/10.1061/(ASCE)MT.1943-5533.0002538.
Aslani, F., G. Ma, and G. Muselin. 2018a. “Development of high-performance self-compacting concrete using waste recycled concrete aggregates and rubber granules.” J. Clean. Prod. 182 (May): 553–566. https://doi.org/10.1016/j.jclepro.2018.02.074.
Aslani, F., G. Ma, D. L. Y. Wan, and V. X. T. Le. 2018b. “Experimental investigation into rubber granules and their effects on the fresh and hardened properties of self-compacting concrete.” J. Clean. Prod. 172 (Jan): 1835–1847. https://doi.org/10.1016/j.jclepro.2017.12.003.
AS/NZS (Australian/New Zealand Standard). 2016b. Supplementary cementitious materials, Part 1: Fly ash. AS/NZS 3582.1. Sydney, Australia: AS/NZS.
AS (Standards Australia). 2000a. Chemical admixtures for concrete, mortar and grout-admixtures for concrete. AS 1478.1. Sydney, Australia: AS.
AS (Standards Australia). 2000b. Methods of testing concrete-determination of the modulus of rupture. AS 1012.11. Sydney, Australia: AS.
AS (Standards Australia). 2006. Methods of testing Portland, blended and masonry cements. AS 2350.2. Sydney, Australia: AS.
AS (Standards Australia). 2009a. Aggregates and rock for engineering purposes, Part 1: Concrete aggregates. AS 2758. Sydney, Australia: AS.
AS (Standards Australia). 2009b. Methods for sampling and testing aggregates. AS 1141. Sydney, Australia: AS.
AS (Standards Australia). 2010. Methods of testing concrete-determination of indirect tensile strength of concrete cylinders (‘Brazil’ or splitting test). AS 1012.10. Sydney, Australia: AS.
AS (Standards Australia). 2014. Methods of testing concrete-compressive strength tests-concrete, mortar and grout specimens. AS 1012.9. Sydney, Australia: AS.
AS (Standards Australia). 2015. Methods of testing concrete: Determination of properties related to the consistency of concrete-slump flow, T500 and J-ring test. AS 1012.3.5. Sydney, Australia: AS.
AS (Standards Australia). 2016a. Methods of test for supplementary cementitious materials for use with portland and blended cement. AS 3583. Sydney, Australia: AS.
ASTM. 2014. Standard test method for sieve analysis of fine and coarse aggregates. ASTM C136. West Conshohocken, PA: ASTM.
ASTM. 2015. Standard test method for slump of hydraulic-cement concrete. ASTM C143. West Conshohocken, PA: ASTM.
ASTM. 2017a. Standard specification for chemical admixtures for concrete. ASTM C494. West Conshohocken, PA: ASTM.
ASTM. 2017b. Standard specification for lightweight aggregates for structural concrete. ASTM C330. West Conshohocken, PA: ASTM.
ASTM. 2017c. Standard test method for splitting tensile strength of cylindrical concrete specimens. ASTM C496. West Conshohocken, PA: ASTM.
ASTM. 2018a. Standard specification for slag cement for use in concrete and mortars. ASTM C989. West Conshohocken, PA: ASTM.
ASTM. 2018b. Standard test method for compressive strength of cylindrical concrete specimens. ASTM C39. West Conshohocken, PA: ASTM.
ASTM. 2018c. Standard test method for flexural strength of concrete (using simple beam with third-point loading). ASTM C78. West Conshohocken, PA: ASTM.
ASTM. 2019. Standard specification for coal fly ash and raw or calcined natural pozzolan for use in concrete. ASTM C618. West Conshohocken, PA: ASTM.
Azmi, A. A., M. M. A. B. Abdullah, C. M. R. Ghazali, A. Victor Sandu, and K. Hussin. 2016. “Effect of crumb rubber on compressive strength of fly ash based geopolymer concrete.” MATEC Web Conf. 78: 01063. https://doi.org/10.1051/matecconf/20167801063.
Babu, D. S., K. G. Babu, and W. Tiong-Huan. 2006. “Effect of polystyrene aggregate size on strength and moisture migration characteristics of lightweight concrete.” Cem. Concr. Compos. 28 (6): 520–527. https://doi.org/10.1016/j.cemconcomp.2006.02.018.
Bignozzi, M. C., and F. Sandrolini. 2006. “Tyre rubber waste recycling in self-compacting concrete.” Cem. Concr. Res. 36 (4): 735–739. https://doi.org/10.1016/j.cemconres.2005.12.011.
Błaszczyński, T., and M. Król. 2015. “Usage of green concrete technology in civil engineering.” Procedia Eng. 122 (Jan): 296–301. https://doi.org/10.1016/j.proeng.2015.10.039.
CEN (European Committee for Standardization). 2000. Concrete: Part 1: Specification, performance, production and conformity. EN 206-1. Brussels, Belgium: CEN.
CEN (European Committee for Standardization). 2004. Eurocode 2: Design of concrete structures. 1.1: General rules and rules for buildings. EN 1992-1-1. Brussels, Belgium: CEN.
CEN (European Committee for Standardization). 2006. Ground granulated blast furnace slag for use in concrete, mortar and grout—Part 1: Definitions, specifications and conformity criteria. EN 15167-1. Brussels, Belgium: CEN.
CEN (European Committee for Standardization). 2012. Fly ash for concrete: Part 1: Definition, specifications and conformity criteria. EN 450-1. Brussels, Belgium: CEN.
Davidovits, J. 1976. “Solid phase synthesis of a mineral blockpolymer by low temperature polycondensation of aluminosilicate polymers.” In Proc., IUPAC Int. Symp. on Macromolecules. Stockholm, Sweden: KTH Royal Institute of Technology.
Davidovits, J. 1991. “Geopolymers: Inorganic polymeric new materials.” J. Therm. Anal. 37 (8): 1633–1656. https://doi.org/10.1007/BF01912193.
Deb, P. S., P. Nath, and P. K. Sarker. 2014. “The effects of ground granulated blast-furnace slag blending with fly ash and activator content on the workability and strength properties of geopolymer concrete cured at ambient temperature.” Mater. Des. 62 (Oct): 32–39. https://doi.org/10.1016/j.matdes.2014.05.001.
De Vargas, A. S., D. C. C. Dal Molin, A. C. F. Vilela, F. J. Da Silva, B. Pavão, and H. Veit. 2011. “The effects of Na2O/SiO2 molar ratio, curing temperature and age on compressive strength, morphology and microstructure of alkali-activated fly ash-based geopolymers.” Cem. Concr. Compos. 33 (6): 653–660. https://doi.org/10.1016/j.cemconcomp.2011.03.006.
Duxson, P., A. Fernández-Jiménez, J. L. Provis, G. C. Lukey, A. Palomo, and J. S. J. van Deventer. 2007. “Geopolymer technology: the current state of the art.” J. Mater. Sci. 42 (9): 2917–2933. https://doi.org/10.1007/s10853-006-0637-z.
Duxson, P., J. L. Provis, G. C. Lukey, S. W. Mallicoat, W. M. Kriven, and J. S. J. Van Deventer. 2005. “Understanding the relationship between geopolymer composition, microstructure and mechanical properties.” Colloids Surf. A Physicochem. Eng. Asp. 269 (1–3): 47–58. https://doi.org/10.1016/j.colsurfa.2005.06.060.
Eldin, N. N., and A. B. Senouci. 1992. “Engineering properties of rubberized concrete.” Can. J. Civ. Eng. 19 (5): 912–923. https://doi.org/10.1139/l92-103.
Eldin, N. N., and A. B. Senouci. 1993. “Rubber-tire particles as concrete aggregate.” J. Mater. Civ. Eng. 5 (4): 478–496. https://doi.org/10.1061/(ASCE)0899-1561(1993)5:4(478).
Emiroğlu, M., S. Yıldız, O. Keleştemur, and M. H. Keleştemur. 2012. “Bond performance of rubber particles in the self-compacting concrete.” In Proc., 4th Int. Symp. on Bond in Concrete, edited by J. W. Cairns, G. Metelli, and G. A. Plizzari, 779–786. Elazığ, Turkey: Univ. of Fırat.
Fletcher, R. A., K. J. D. MacKenzie, C. L. Nicholson, and S. Shimada. 2005. “The composition range of aluminosilicate geopolymers.” J. Eur. Ceram. Soc. 25 (9): 1471–1477. https://doi.org/10.1016/j.jeurceramsoc.2004.06.001.
Güneyisi, E. 2010. “Fresh properties of self-compacting rubberized concrete incorporated with fly ash.” Mater. Struct. Constr. 43 (8): 1037–1048. https://doi.org/10.1617/s11527-009-9564-1.
Hamidi, R. M., Z. Man, and K. A. Azizli. 2016. “Concentration of NaOH and the effect on the properties of fly ash based geopolymer.” Procedia Eng. 148 (Jan): 189–193. https://doi.org/10.1016/j.proeng.2016.06.568.
Hardjito, D., S. E. Wallah, D. M. J. Sumajouw, and B. V. Rangan. 2004. “On the development of fly ash-based geopolymer concrete.” ACI Mater. J. 101 (6): 467–472. https://www.concrete.org/publications/internationalconcreteabstractsportal.aspx?m=details&ID;=13485.
Hesami, S., I. Salehi Hikouei, and S. A. A. Emadi. 2016. “Mechanical behavior of self-compacting concrete pavements incorporating recycled tire rubber crumb and reinforced with polypropylene fiber.” J. Clean. Prod. 133 (Oct): 228–234. https://doi.org/10.1016/j.jclepro.2016.04.079.
Hua, X., and J. S. J. Van Deventer. 2002. “Geopolymerisation of multiple minerals.” Miner. Eng. 15 (12): 1131–1139. https://doi.org/10.1016/S0892-6875(02)00255-8.
Huntzinger, D. N., and T. D. Eatmon. 2009. “A life-cycle assessment of portland cement manufacturing: comparing the traditional process with alternative technologies.” J. Clean. Prod. 17 (7): 668–675. https://doi.org/10.1016/j.jclepro.2008.04.007.
Ismail, M. K., and A. A. Hassan. 2015. “Influence of mixture composition and type of cementitious materials on enhancing the fresh properties and stability of self-consolidating rubberized concrete.” J. Mater. Civ. Eng. 28 (1): 4015075. https://doi.org/10.1061/(ASCE)MT.1943-5533.0001338.
Issa, C. A., and G. Salem. 2013. “Utilization of recycled crumb rubber as fine aggregates in concrete mix design.” Constr. Build. Mater. 42 (May): 48–52. https://doi.org/10.1016/j.conbuildmat.2012.12.054.
Ivan, D.-L. E., N. Allouche, and V. Saiprasad. 2011. “Mechanical properties of fly-ash-based geopolymer concrete.” ACI Mater. J. 108 (3): 300–306. https://doi.org/10.14359/51682495.
Kan, A., and R. Demirboga. 2009. “A novel material for lightweight concrete production.” Cem. Concr. Compos. 31 (7): 489–495. https://doi.org/10.1016/j.cemconcomp.2009.05.002.
Klieger, P., and J. F. Lamond. 1994. Significance of tests and properties of concrete and concrete-making materials. Philadelphia: ASTM.
Kusbiantoro, A., M. S. Ibrahim, K. Muthusamy, and A. Alias. 2013. “Development of sucrose and citric acid as the natural based admixture for fly Ash based geopolymer.” Procedia Environ. Sci. 17 (Jan): 596–602. https://doi.org/10.1016/j.proenv.2013.02.075.
Law Yim Wan, D., F. Aslani, and G. Ma. 2018. “Lightweight self-compacting concrete incorporating Perlite, Scoria, and Polystyrene aggregates.” J. Mater. Civ. Eng. 30 (8): 04018178. https://doi.org/10.1061/(ASCE)MT.1943-5533.0002350.
Luhar, S., S. Chaudhary, and I. Luhar. 2018. “Thermal resistance of fly ash based rubberized geopolymer concrete.” J. Build. Eng. 19: 420–428. https://doi.org/10.1016/j.jobe.2018.05.025.
Mastali, M., Z. Abdollahnejad, and F. Pacheco-Torgal. 2018. “Carbon dioxide sequestration on fly ash/waste glassalkali-based mortars with recycled aggregates.” In Carbon doxide sequestration in cementitious construction materials, edited by F. Pacheco-Torgal, C. Shi, and A. P. Palomo, 299–348. Amsterdam, Netherlands: Elsevier.
Mountjoy, E., D. Hasthanayake, and T. Freeman. 2015. Stocks and fate of end of life tyres: 2013–14 Study. Canberra, Australia: National Environment Protection Council.
Nath, P., and P. K. Sarker. 2014. “Effect of GGBFS on setting, workability and early strength properties of fly ash geopolymer concrete cured in ambient condition.” Constr. Build. Mater. 66 (Sep): 163–171. https://doi.org/10.1016/j.conbuildmat.2014.05.080.
Nehdi, M., and A. Khan. 2001. “Cementitious composites containing recycled tire rubber: An overview of engineering properties and potential applications.” Cem. Concr. Aggregates 23 (1): 3–10. https://doi.org/10.1520/CCA10519J.
Nematollahi, B., and J. Sanjayan. 2014. “Effect of different superplasticizers and activator combinations on workability and strength of fly ash based geopolymer.” Mater. Des. 57 (May): 667–672. https://doi.org/10.1016/j.matdes.2014.01.064.
Olivia, M., and H. Nikraz. 2012. “Properties of fly ash geopolymer concrete designed by Taguchi method.” Int. J. Hum. Comput. Interact. 36 (Apr): 191–198. https://doi.org/10.1016/j.matdes.2011.10.036.
Ozbay, E., M. Lachemi, and U. K. Sevim. 2011. “Compressive strength, abrasion resistance and energy absorption capacity of rubberized concretes with and without slag.” Mater. Struct. 44 (7): 1297–1307. https://doi.org/10.1617/s11527-010-9701-x.
Palomo, A., M. W. Grutzeck, and M. T. Blanco. 1999. “Alkali-activated fly ashes: a cement for the future.” Cem. Concr. Res. 29 (8): 1323–1329. https://doi.org/10.1016/S0008-8846(98)00243-9.
Pan, Z., J. G. Sanjayan, and B. V. Rangan. 2011. “Fracture properties of geopolymer paste and concrete.” Mag. Concr. Res. 63 (10): 763–771. https://doi.org/10.1680/macr.2011.63.10.763.
Park, Y., A. Abolmaali, Y. H. Kim, and M. Ghahremannejad. 2016. “Compressive strength of fly ash-based geopolymer concrete with crumb rubber partially replacing sand.” Constr. Build. Mater. 118 (Aug): 43–51. https://doi.org/10.1016/j.conbuildmat.2016.05.001.
Rangan, B. V. 2008. Fly ash-based geopolymer concrete. Perth, Australia: Engineering Faculty, Curtin Univ. of Technology.
Reda Taha, M. M., A. El-Dieb, and M. Abd El-Wahab. 2003. “Fracture toughness of concrete incorporating rubber tire particles.” In Proc., Int. Conf. on Performance of Construction Materials, edited by A. El-Dieb, M. M. Reda Taha, and S. L. Lissel, 129–138. Boca Raton, FL: CRC Press.
Rowles, M., and B. O’Connor. 2003. “Chemical optimisation of the compressive strength of aluminosilicate geopolymers synthesised by sodium silicate activation of metakaolinite.” J. Mater. Chem. 13 (5): 1161–1165. https://doi.org/10.1039/b212629j.
Sagoe-Crentsil, K. K., T. Brown, and A. H. Taylor. 2001. “Performance of concrete made with commercially produced coarse recycled concrete aggregate.” Cem. Concr. Res. 31 (5): 707–712. https://doi.org/10.1016/S0008-8846(00)00476-2.
Silva, P. De, K. Sagoe-Crenstil, and V. Sirivivatnanon. 2007. “Kinetics of geopolymerization: role of Al2O3 and SiO2.” Cem. Concr. Res. 37 (4): 512–518. https://doi.org/10.1016/j.cemconres.2007.01.003.
Singh, B., M. Gupta, M. Chauhan, and A. S. Bhattacharyya. 2013. “Light-weight geopolymer concrete with EPS beads.” In Proc., 19th CIB world Building Congress. Brisbane, Australia: Queensland Univ. of Technology.
Singh, B., G. Ishwarya, M. Gupta, and S. K. Bhattacharyya. 2015. “Geopolymer concrete: A review of some recent developments.” Constr. Build. Mater. 85 (Jun): 78–90. https://doi.org/10.1016/j.conbuildmat.2015.03.036.
Sofi, M., J. S. J. van Deventer, P. A. Mendis, and G. C. Lukey. 2007. “Engineering properties of inorganic polymer concretes (IPCs).” Cem. Concr. Res. 37 (2): 251–257. https://doi.org/10.1016/j.cemconres.2006.10.008.
Steveson, M., and K. Sagoe-Crentsil. 2005. “Relationships between composition, structure and strength of inorganic polymers: part I metakaolin-derived inorganic polymers.” J. Mater. Sci. 40 (16): 4247–4259. https://doi.org/10.1007/s10853-005-2794-x.
Tamut, T., R. Prabhu, K. Venkataramana, and S. C. Yaragal. 2014. “Partial replacement of coarse aggregates by expanded polystyrene beads in concrete.” Int. J. Res. Eng. Technol. 3 (2): 238–241. https://doi.org/10.15623/ijret.2014.0302040.
Tang, W., H. Cui, and S. Tahmasbi. 2016. “Fracture properties of polystyrene aggregate concrete after exposure to high temperatures.” Materials (Basel) 9 (8): 630. https://doi.org/10.3390/ma9080630.
Tang, W. C., Y. Lo, and A. Nadeem. 2008. “Mechanical and drying shrinkage properties of structural-graded polystyrene aggregate concrete.” Cem. Concr. Compos. 30 (5): 403–409. https://doi.org/10.1016/j.cemconcomp.2008.01.002.
Tangchirapat, W., R. Buranasing, C. Jaturapitakkul, and P. Chindaprasirt. 2008. “Influence of rice husk-bark ash on mechanical properties of concrete containing high amount of recycled aggregates.” Constr. Build. Mater. 22 (8): 1812–1819. https://doi.org/10.1016/j.conbuildmat.2007.05.004.
Thomas, B. S., and R. C. Gupta. 2015. “Long term behaviour of cement concrete containing discarded tire rubber.” J. Clean. Prod. 102 (Sep): 78–87. https://doi.org/10.1016/j.jclepro.2015.04.072.
Valizadeh, A., F. Aslani, Z. Asif, and M. Roso. 2019. “Development of heavyweight self-compacting concrete and ambient-cured heavyweight geopolymer concrete using magnetite aggregates.” Materials 12 (7): 1035. https://doi.org/10.3390/ma12071035.
Van Jaarsveld, J. G. S., and J. S. J. Van Deventer. 1999. “Effect of the alkali metal activator on the properties of fly ash-based geopolymers.” Ind. Eng. Chem. Res. 38 (10): 3932–3941. https://doi.org/10.1021/ie980804b.
Van Jaarsveld, J. G. S., J. S. J. Van Deventer, and G. C. Lukey. 2002. “The effect of composition and temperature on the properties of fly ash-and kaolinite-based geopolymers.” Chem. Eng. J. 89 (1–3): 63–73. https://doi.org/10.1016/S1385-8947(02)00025-6.
WBCSD, I.E.A. (World Business Council for Sustainable Development, International Energy Agency). 2009. Cement technology roadmap 2009: carbon emissions reductions up to 2050. Geneva: WBCSD, I.E.A.
Wongsa, A., Y. Zaetang, V. Sata, and P. Chindaprasirt. 2016. “Properties of lightweight fly ash geopolymer concrete containing bottom ash as aggregates.” Constr. Build. Mater. 111 (May): 637–643. https://doi.org/10.1016/j.conbuildmat.2016.02.135.
Xu, Y., L. Jiang, J. Xu, and Y. Li. 2012. “Mechanical properties of expanded polystyrene lightweight aggregate concrete and brick.” Constr. Build. Mater. 27 (1): 32–38. https://doi.org/10.1016/j.conbuildmat.2011.08.030.
Zhang, B., K. J. D. MacKenzie, and I. W. M. Brown. 2009. “Crystalline phase formation in metakaolinite geopolymers activated with NaOH and sodium silicate.” J. Mater. Sci. 44 (17): 4668–4676. https://doi.org/10.1007/s10853-009-3715-1.
Information & Authors
Information
Published In
Journal of Materials in Civil Engineering
Volume 32 • Issue 2 • February 2020
Copyright
©2019 American Society of Civil Engineers.
History
Received: May 11, 2019
Accepted: Jul 8, 2019
Published online: Nov 27, 2019
Published in print: Feb 1, 2020
Discussion open until: Apr 27, 2020
Authors
Metrics & Citations
Metrics
Citations
Download citation
If you have the appropriate software installed, you can download article citation data to the citation manager of your choice. Simply select your manager software from the list below and click Download.