Effect of Cyclic Loading Deterioration on Concrete Durability: Water Absorption, Freeze-Thaw, and Carbonation
Publication: Journal of Materials in Civil Engineering
Volume 30, Issue 9
Abstract
The effect of cyclic loading deterioration on freeze-thaw and carbonation resistances of concrete were experimentally investigated in this study. A novel loading method was designed, which simultaneously considers both mechanical loading and environmental actions for concrete. It shows that with the increase of cyclic compressive loading, the porosity and water absorption of concrete initially decrease but then increase when the stress is above a threshold level because of the cracking initiation caused by cyclic compression. With the increase of concrete porosity, both dynamic elastic modulus loss and carbonation depth obviously exhibit an increasing trend. On the other hand, under the same stress level, the freeze-thaw and carbonation resistances of high-strength concrete are relatively superior to those of low-strength concrete. Compared with the unloaded concrete, the carbonation depth and dynamic elastic modulus loss after mechanical loading below the stress level threshold are lower. This is probably due to the denser microstructure compacted by the compression. However, if the loading level becomes above the threshold level, both the carbonation depth and dynamic elastic modulus loss dramatically increase, which is due to the cracks initiation and propagation after cyclic loading deterioration. Therefore, the combination of mechanical and environmental actions is more severe than a single environmental action without considering the mechanical loading.
Get full access to this article
View all available purchase options and get full access to this article.
Acknowledgments
The authors gratefully acknowledge the financial supports from the Australian Research Council (DE150101751, IH150100006), Australia and the National Natural Science Foundation of China (51668045, 51408210), China. The constructive comments and suggestions from Professor Surendra P. Shah at Northwestern University, USA, are greatly appreciated.
References
Boukendakdji, O., E. Kadri, and S. Kenai. 2012. “Effects of granulated blast furnace slag and superplasticizer type on the fresh properties and compressive strength of self-compacting concrete.” Cem. Concr. Compos. 34 (4): 583–590. https://doi.org/10.1016/j.cemconcomp.2011.08.013.
Carpinteri, A., and S. Invernizzi. 2001. “Influence of damage on the fractal properties of concrete subjected to pure tension.” Mater. Struct. 34 (244): 605–611. https://doi.org/10.1617/13714.
Castel, A., R. Francois, and G. Arliguie. 1999. “Effect of loading on carbonation penetration in reinforced concrete elements.” Cem. Concr. Res. 29 (4): 561–565. https://doi.org/10.1016/S0008-8846(99)00017-4.
Chen, S. J., W. G. Li, C. K. Ruan, K. Sagoe-Crentsil, and W. H. Duan. 2017. “Pore shape analysis using centrifuge driven metal intrusion: Indication on porosimetry equations, hydration and packing.” Constr. Build. Mater. 154: 95–104. https://doi.org/10.1016/j.conbuildmat.2017.07.190.
Cui, H., W. Tang, W. Liu, Z. Dong, and F. Xing. 2015. “Experimental study on effects of , concentrations on concrete carbonation and diffusion mechanisms.” Constr. Build. Mater. 93: 522–527. https://doi.org/10.1016/j.conbuildmat.2015.06.007.
Gao, Y., L. Cheng, Z. Gao, and S. Guo. 2013. “Effects of different mineral admixtures on carbonation resistance of lightweight aggregate concrete.” Constr. Build. Mater. 43 (6): 506–510. https://doi.org/10.1016/j.conbuildmat.2013.02.038.
GB. 2002. Standard for test method of mechanical properties. [In Chinese.] GB/T 50081-2002. Beijing: China Architecture and Building Press.
GB. 2009. Standard for test method of long-term performance and durability of ordinary concrete. [In Chinese.] GB/T 50082-2009. Beijing: China Architecture and Building Press.
Gonen, T., S. Yazicioglu, and B. Demirel. 2015. “The influence of freezing-thawing cycles on the capillary water absorption and porosity of concrete with mineral admixture.” KSCE J. Civ. Eng. 19 (3): 667–671. https://doi.org/10.1007/s12205-012-0207-7.
Holly, J., D. Hampton, and M. Thomas. 1993. “Modeling relationships between permeability and cement paste pore microstructures.” Cem. Concr. Res. 23 (6): 1317–1330. https://doi.org/10.1016/0008-8846(93)90069-L.
Hooton, R. D. 1993. “Influence of silica fume replacement of cement on physical properties and resistance to sulfate attack, freezing and thawing, and alkali-silica reactivity.” ACI Mater. J. 90 (2): 143–151.
Hussain, S., D. Bhunia, and S. B. Singh. 2017. “Comparative study of accelerated carbonation of plain cement and fly-ash concrete.” J. Build. Eng. 10: 26–31. https://doi.org/10.1016/j.jobe.2017.02.001.
Jin, S., J. Zhang, and B. Huang. 2013. “Fractal analysis of effect of air void on freeze-thaw resistance of concrete.” Constr. Build. Mater. 47: 126–130. https://doi.org/10.1016/j.conbuildmat.2013.04.040.
Kumar, R., and B. Bhattacharjee. 2003. “Porosity, pore size distribution and in situ strength of concrete.” Cem. Concr. Res. 33 (1): 155–164. https://doi.org/10.1016/S0008-8846(02)00942-0.
Lei, B., W. Li, Z. Tang, V. W. Tam, and Z. Sun. 2018. “Durability of recycled aggregate concrete under coupling mechanical loading and freeze-thaw cycle in salt-solution.” Constr. Build. Mater. 163: 840–849. https://doi.org/10.1016/j.conbuildmat.2017.12.194.
Li, B., J. Maoa, T. Nawa, and T. Y. Han. 2017a. “Mesoscopic damage model of concrete subjected to freeze-thaw cycles using mercury intrusion porosimetry and differential scanning calorimetry (MIP-DSC).” Constr. Build. Mater. 147: 79–90. https://doi.org/10.1016/j.conbuildmat.2017.04.136.
Li, G., F. Hu, and Y. Wu. 2011. “Chloride ion penetration in stressed concrete.” J. Mater. Civ. Eng. 23 (8): 1145–1153. https://doi.org/10.1061/(ASCE)MT.1943-5533.0000150.
Li, W. G., Z. Huang, G. Hu, W. H. Duan, and S. P. Shah. 2017b. “Early-age shrinkage development of ultra-high-performance concrete under heat curing treatment.” Constr. Build. Mater. 131: 767–774. https://doi.org/10.1016/j.conbuildmat.2016.11.024.
Li, W. G., C. Long, V. Tam, C. S. Poon, and W. H. Duan. 2017c. “Effects of nano-particles on failure process and microstructural properties of recycled aggregate concrete.” Constr. Build. Mater. 142: 42–50. https://doi.org/10.1016/j.conbuildmat.2017.03.051.
Liu, J. P., C. W. Miao, C. C. Chen, J. Z. Liu, and G. Cui. 2013. “Effect and mechanism of controlled permeable formwork on concrete water adsorption.” Constr. Build. Mater. 39: 129–133. https://doi.org/10.1016/j.conbuildmat.2012.05.005.
Ma, H. Y. 2014. “Mercury intrusion porosimetry in concrete technology: Tips in measurement, pore structure parameter acquisition and application.” J. Porous Mater. 21 (2): 207–215. https://doi.org/10.1007/s10934-013-9765-4.
Ma, H. Y., D. S. Hou, and Z. J. Li. 2015. “Two-scale modeling of transport properties of cement paste: Formation factor, electrical conductivity and chloride diffusivity.” Comput. Mater. Sci. 110: 270–280. https://doi.org/10.1016/j.commatsci.2015.08.048.
Ma, H. Y., D. S. Hou, Y. Y. Lu, and Z. J. Li. 2014. “Two-scale modeling of the capillary network in hydrated cement paste.” Constr. Build. Mater. 64: 11–21. https://doi.org/10.1016/j.conbuildmat.2014.04.005.
Ma, H. Y., and Z. J. Li. 2013. “Realistic pore structure of portland cement paste: Experimental study and numerical simulation.” Comput. Concr. 11 (4): 317–336. https://doi.org/10.12989/cac.2013.11.4.317.
Mohammed, M. K., A. R. Dawson, and N. H. Thom. 2014. “Carbonation of filler typed self-compacting concrete and its impact on the microstructure by utilization of 100% accelerating techniques.” Constr. Build. Mater. 50 (2): 508–516. https://doi.org/10.1016/j.conbuildmat.2013.09.052.
Monteiro, P. J. M., and P. K. Mehta. 2014. Concrete: Microstructure, properties, and materials. 4th ed. New York: McGraw-Hill.
Morandeau, A., M. MThiérya, and P. Dangla. 2014. “Investigation of the carbonation mechanism of CH and C-S-H in terms of kinetics, microstructure changes and moisture properties.” Cem. Concr. Res. 56: 153–170. https://doi.org/10.1016/j.cemconres.2013.11.015.
Mu, R., C. Miao, X. Luo, and W. Sun. 2002. “Interaction between loading, freeze-thaw cycles, and chloride salt attack of concrete with and without steel fiber reinforcement.” Cem. Concr. Res. 32 (7): 1061–1066. https://doi.org/10.1016/S0008-8846(02)00746-9.
Nagala, V. T., and C. L. Page. 1997. “Effects of carbonation on pore structure and diffusional properties of hydrated cement pastes.” Cem. Concr. Res. 27 (7): 995–1007. https://doi.org/10.1016/S0008-8846(97)00102-6.
Pan, H. K., Z. S. Yang, and F. W. Xu. 2016. “Study on concrete structure’s durability considering the interaction of multi-factors.” Constr. Build. Mater. 118: 256–261. https://doi.org/10.1016/j.conbuildmat.2016.05.032.
Rahman, M. K., W. A. Al-Kutti, M. A. Shazali, and M. H. Baluch. 2012. “Simulation of chloride migration in compression-induced damage in concrete.” J. Mater. Civ. Eng. 24 (7): 789–796. https://doi.org/10.1061/(ASCE)MT.1943-5533.0000458.
Ramli, M., A. A. Tabassi, and K. W. Hoe. 2013. “Porosity, pore structure and water absorption of polymer-modified mortars: An experimental study under different curing conditions.” Compos. Part B 55: 221–233. https://doi.org/10.1016/j.compositesb.2013.06.022.
Ruan, S., and C. Unluer. 2017. “Influence of mix design on the carbonation, mechanical properties and microstructure of reactive MgO cement-based concrete.” Cem. Concr. Compos. 80: 104–114. https://doi.org/10.1016/j.cemconcomp.2017.03.004.
Schneider, U., and S. W. Chen. 1998a. “Modeling and empirical formulas for chemical corrosion and stress corrosion of cementitious materials.” Mater. Struct. 31 (10): 662–668. https://doi.org/10.1007/BF02480442.
Schneider, U., and S. W. Chen. 1998b. “The chemomechanical effect and the mechanochemical effect on high-performance concrete subjected to stress corrosion.” Cem. Concr. Res. 28 (4): 509–522. https://doi.org/10.1016/S0008-8846(98)00015-5.
Schneider, U., and S. W. Chen. 2005. “Deterioration of high-performance concrete subjected to attack by the combination of ammonium nitrate solution and flexure stress.” Cem. Concr. Res. 35 (9): 1705–1713. https://doi.org/10.1016/j.cemconres.2004.11.011.
Sicata, E., F. Gong, T. Ueda, and D. Zhang. 2014. “Experimental investigation of the deformational behavior of the interfacial transition zone (ITZ) in concrete during freezing and thawing cycles.” Constr. Build. Mater. 65: 122–131. https://doi.org/10.1016/j.conbuildmat.2014.04.035.
Singh, N., and S. P. Sing. 2016. “Reviewing the carbonation resistance of concrete.” J. Mater. Eng. Struct. 3 (2): 35–57.
Song, H. W., and S. J. Kwon. 2007. “Permeability characteristics of carbonated concrete considering capillary pore structure.” Cem. Concr. Res. 37 (6): 909–915. https://doi.org/10.1016/j.cemconres.2007.03.011.
Sun, W., Y. M. Zhang, H. D. Yan, and R. Mu. 1999. “Damage and damage resistance of high strength concrete under action of load and freeze-thaw cycles.” Cem. Concr. Res. 29 (9): 1519–1523. https://doi.org/10.1016/S0008-8846(99)00097-6.
Wang, W. J., J. Wu, Z. Wang, G. Z. Wu, and A. Y. Yue. 2016. “Chloride diffusion coefficient of recycled aggregate concrete under compressive loading.” Mater. Struct. 49 (11): 4729–4796. https://doi.org/10.1617/s11527-016-0820-x.
Xiao, J. Z., B. Lei, and C. Z. Zhang. 2012. “On carbonation behavior of recycled aggregate concrete.” Sci. China Technol. Sci. 55 (9): 2609–2616. https://doi.org/10.1007/s11431-012-4798-5.
Yao, Y., et al. 2017a. “Test methods to determine durability of concrete under combined environmental actions and mechanical load: Final report of RILEM TC 246-TDC.” Mater. Struct. 50 (2): 123–155. https://doi.org/10.1617/s11527-016-0983-5.
Yao, Y., Z. D. Wang, and L. Wang. 2017b. “Durability of concrete under combined mechanical load and environmental actions: A review.” J. Sustainable Cem. Based Mater. 1 (1–2): 2–15. https://doi.org/10.1080/21650373.2012.732917.
Yu, H., W. Sun, Y. Zhang, L. Guo, and M. Li. 2008. “Durability of concrete subjected to the combined actions of flexural stress, freeze-thaw cycles and bittern solutions.” J. Wuhan Univ. Technol.-Mater. Sci. Ed. 23 (6): 893–900. https://doi.org/10.1007/s11595-007-6893-1.
Information & Authors
Information
Published In
Copyright
©2018 American Society of Civil Engineers.
History
Received: Nov 22, 2017
Accepted: Apr 3, 2018
Published online: Jun 29, 2018
Published in print: Sep 1, 2018
Discussion open until: Nov 29, 2018
Authors
Metrics & Citations
Metrics
Citations
Download citation
If you have the appropriate software installed, you can download article citation data to the citation manager of your choice. Simply select your manager software from the list below and click Download.