Repair Mortars Incorporating Multiwalled Carbon Nanotubes: Shrinkage and Sodium Sulfate Attack
Publication: Journal of Materials in Civil Engineering
Volume 29, Issue 12
Abstract
This study investigates the effect of multiwalled carbon nanotubes (MWCNTs) on the shrinkage and expansion caused by sodium sulfate attack in repair mortars; repair mortar behavior in the fresh state and the compressive strength are also measured. Three repair mortars are studied: 0.0% MWCNTs (reference), mortar from two different manufacturers. Shrinkage and sulfate attacks are evaluated according to current standards. The carbon nanotube increases the compressive strength by approximately 19.5% and decreases the fluidity. Shrinkage occurs more intensely in MWCNT-embedded mortars, although results show similar behavior between the two types of MWCNTs. The MWCNTs increase the expansion due to attack by sodium sulfate, indicating that this material may be harmful when the cementitious composite is in contact with these aggressive agents (sodium sulfate).
Get full access to this article
View all available purchase options and get full access to this article.
Acknowledgments
The authors thank the Federal University of Parana (UFPR) and from Araucaria Foundation for the financial support for developing this research. In addition, they are grateful for the award of scholarships sponsored by the National Council for Scientific and Technological Development (CNPq).
References
Al-Akhras, N. M. (2006). “Durability of metakaolin concrete to sulfate attack.” Cem. Concr. Res., 36(9), 1727–1734.
ASTM. (2017). “Standard specification for portland cement.” ASTM C150, West Conshohocken, PA.
Batiston, E. R. (2007). “Exploratory study of the effects of carbon nanotubes in portland cement matrices.” Master dissertation, Federal Univ. of Santa Catarina, Florianopolis, Brazil (in Portuguese).
Brazilian Association of Technical Standards. (1991). “High early strength portland cement—Specification.” NBR 5733/91, Rio de Janeiro, Brazil.
Brazilian Association of Technical Standards. (1997). “Portland cement—Determination of compressive strength.” NBR 7215/97, Rio de Janeiro, Brazil.
Brazilian Association of Technical Standards. (2001). “Portland cement and other powder materials—Determination of specific gravity.” NBR NM 23/01, Rio de Janeiro, Brazil.
Brazilian Association of Technical Standards. (2005a). “Determination of dimensional variation (shrinkage or linear expansion).” NBR 15261/05, Rio de Janeiro, Brazil.
Brazilian Association of Technical Standards. (2005b). “Preparing the mixture and determining the consistency index.” NBR 13276/05, Rio de Janeiro, Brazil.
Brazilian Association of Technical Standards. (2006). “Determination of unit mass and void volume.” NBR NM 45/06, Rio de Janeiro, Brazil.
Brazilian Association of Technical Standards. (2009). “Aggregates for concrete.” NBR 7211/09, Rio de Janeiro, Brazil.
Brazilian Association of Technical Standards. (2010). “Concrete—Procedure for molding and curing of test specimens.” NBR 5738/10, Rio de Janeiro, Brazil.
Brazilian Association of Technical Standards. (2012). “Standard sand for testing cement.” NBR 7214/12, Rio de Janeiro, Brazil.
Brazilian Association of Technical Standards. (2014). “Determination of dimensional variation of portland cement mortar bars exposed to sodium sulfate solution.” NBR 13583/14, Rio de Janeiro, Brazil.
Chaipanich, A., Nochaiya, T., Wongkeo, W., and Torkittikul, P. (2010). “Compressive strength and microstructure of carbon nanotubes-fly ash cement composites.” Mater. Sci. Eng., 527(4), 1063–1067.
Collins, F., Lambert, J., and Duan, W. H. (2012). “The influence of admixtures on the dispersion, workability, and strength of carbon nanotubes-OPC paste mixtures.” Cem. Concr. Compos., 34(2), 201–207.
Grobert, N. (2007). “Carbon nanotubes—Becoming clean.” Mater. Today, 10(1–2), 28–35.
Henche, D. (2013). “High strength cement composite with the addition of carbon nanotubes.” Master dissertation, Federal Univ. of Parana, Curitiba, Brazil (in Portuguese).
Kim, H. K., Nam, I. W., and Lee, H. K. (2014). “Enhanced effect of carbon nanotube on mechanical and electrical properties of cement composites by incorporation of silica fume.” Compos. Struct., 107, 60–69.
Ko, F., et al. (2003). “Electrospinning of continuous carbon nanotubes-filled nanofiber yarns.” Adv. Mater., 15(14), 1161–1165.
Konsta-Gdoutos, M., Metaxa, Z. S., and Shah, S. P. (2010). “Highly dispersed carbon nanotubes reinforced cement based materials.” Cem. Concr. Res., 40(7), 1052–1059.
Li, G. Y., Wang, P. M., and Zhao, X. (2005). “Mechanical behavior and microstructure of cement composites incorporating surface-treated multi-walled carbon nanotubes.” Carbon, 43(6), 1239–1245.
Makar, J., Margeson, J., and Luh, J. (2005). “Carbon nanotubes/cement composites—Early results and potential applications.” Proc., 3rd Int. Conf. on Construction Materials: Performance, Innovations and Structural Implication, Vancouver, BC, Canada, 1–10.
Mamalis, A. G., Vogtlander, L. O. G., and Markopoulos, A. (2004). “Nanotechnology and nanostructured materials: Trends in carbon nanotubes.” Precis. Eng., 28(1), 16–30.
Medeiros, M. H. F., Dranka, F., Mattana, A. J., and Costa, M. R. M. M. (2015). “Portland cement composites with carbon nanotubes (CNT) addition: Properties in freshly state and compressive strength.” ⟨http://www.scielo.br/scielo.php?script=sci_arttext&pid=S1517-70762015000100012&lng=pt&nrm=iso&tlng=pt⟩ (Apr. 10, 2017).
Medeiros-Junior, R. A., and Lima, M. G. (2016). “Electrical resistivity of unsaturated concrete using different types of cement.” Constr. Build. Mater., 107, 11–16.
Medeiros-Junior, R. A., Lima, M. G., Brito, P. C., and Medeiros, M. H. F. (2015). “Chloride penetration into concrete in an offshore platform-analysis of exposure conditions.” Ocean Eng., 103, 78–87.
Meeten, G. H. (2000). “Yield stress of structured fluids measured by squeeze flow.” Rheol. Acta, 39(4), 399–408.
Mehta, P. K., and Monteiro, P. J. M. (2014). Concrete: Structures, properties and materials, 3rd Ed., PINI, Sao Paulo, Brazil.
Melo, V. S. (2009). “Nanotechnology applied to concrete: Effect of physical mixture of carbon nanotubes in portland cement matrices.” Master dissertation, Federal Univ. of Minas Gerais, Belo Horizonte, Brazil (in Portuguese).
Mendoza, O., Sierra, G., and Tobón, J. I. (2013). “Influence of super plasticizer and on the stability of functionalized multi-walled carbon nanotubes dispersions for cement composites applications.” Constr. Build. Mater., 47, 771–778.
Musso, S., Tulliani, J. M., Ferro, G., and Tagliaferro, A. (2009). “Influence of carbon nanotubes structure on the mechanical behavior of cement composites.” Compos. Sci. Technol., 69(11), 1985–1990.
Neville, A. M., and Brooks, J. J. (2013). Concrete technology, 2nd Ed., Bookman, Porto Alegre, Brazil.
Ouyang, W., Chen, J. K., and Jiang, M. Q. (2014). “Evolution of surface hardness of concrete under sulfate attack.” Constr. Build. Mater., 53, 419–424.
Paiva, M. C., Zhou, B., Fernando, K. A. S., Lin, Y., Kennedy, J. M., and Sun, Y. P. (2004). “Mechanical and morphological characterization of polymer-carbon nanocomposites from functionalized carbon nanotubes.” Carbon, 42(14), 2849–2854.
Popov, V. N. (2004). “Carbon nanotubes: Properties and application.” Mater. Sci. Eng., 43(3), 61–102.
Santhanam, M., Cohen, M. D., and Olek, J. (2002). “Mechanism of sulfate attack: A fresh look. Part 1: Summary of experimental results.” Cem. Concr. Res., 32(6), 915–921.
Santhanam, M., Cohen, M. D., and Olek, J. (2003). “Mechanism of sulfate attack: A fresh look. Part 2: Proposed mechanisms.” Cem. Concr. Res., 33(3), 341–346.
Siddique, R., and Mehta, A. (2014). “Effect of carbon nanotubes on properties of cement mortars.” Constr. Build. Mater., 50, 116–129.
Sindu, B. S., Sasmal, S., and Gopinath, S. (2014). “A multi-scale approach for evaluating the mechanical characteristics of carbon nanotube incorporated cementitious composites.” Constr. Build. Mater., 50, 317–327.
Sobolkina, A., et al. (2012). “Dispersion of carbon nanotubes and its influence on the mechanical properties of the cement matrix.” Cem. Concr. Compos., 34(10), 1104–1113.
Wang, B., Guo, Z., Han, Y., and Zhang, T. (2013). “Electromagnetic wave absorbing properties of multi-walled carbon nanotube/cement composites.” Constr. Build. Mater., 46, 98–103.
Xie, X. L., Mai, Y. W., and Zhou, X. P. (2005). “Dispersion and alignment of carbon nanotubes in polymer matrix: A review.” Mater. Sci. Eng., 49(4), 89–112.
Yang, B. X., Shi, J. H., Pramoda, K. P., and Goh, S. H. (2008). “Enhancement of the mechanical properties of polypropylene using polypropylene-grafted multiwalled carbon nanotubes.” Compos. Sci. Technol., 68(12), 2490–2497.
Yu, M. F., Lourie, O., Dyer, M. J., Moloni, K., Kelly, T. F., and Ruoff, R. S. (2000). “Strength and breaking mechanism of multiwalled carbon nanotubes under tensile load.” Science, 287(5453), 637–640.
Information & Authors
Information
Published In
Copyright
©2017 American Society of Civil Engineers.
History
Received: Mar 7, 2016
Accepted: Jun 9, 2017
Published online: Oct 12, 2017
Published in print: Dec 1, 2017
Discussion open until: Mar 12, 2018
Authors
Metrics & Citations
Metrics
Citations
Download citation
If you have the appropriate software installed, you can download article citation data to the citation manager of your choice. Simply select your manager software from the list below and click Download.