Alkali-Activated Phosphorous Slag Performance under Different Curing Conditions: Compressive Strength, Hydration Products, and Microstructure
Publication: Journal of Materials in Civil Engineering
Volume 30, Issue 1
Abstract
In this paper, the impact of curing parameters such as precuring time, curing time, and temperature on compressive strength of mortar with phosphorous-slag cement activated with two different compound activators including and , as well as the microstructure morphology of the hardened mortars, are studied. Furthermore, variance analysis is used to evaluate the effectiveness of each curing parameter. The results show that application of such a combined low-temperature and high-temperature curing regime can effectively improve the quality of the transition zone (porosity and bonding of the cement matrix to aggregate), in addition to the development of more polymeric structures (silicates of -structures) in hydration products. These improvements together result in a threefold increase in the compressive strength compared with environmental curing conditions.
Get full access to this article
View all available purchase options and get full access to this article.
References
Allahverdi, A., and Kani, E. N. (2013). “Use of construction and demolition waste (CDW) for alkali-activated or geopolymer cements.” Handbook of recycled concrete and demolition waste, F. Pacheco-Torgal, J. Labrincha, J. De Brito, V. Tam, and Y. Ding, eds., Woodhead, Cambridge, U.K., 439–475.
Allahverdi, A., and Mahinroosta, M. (2013). “Mechanical activation of chemically activated high phosphorous slag content cement.” Powder Technol., 245(1), 182–188.
Allahverdi, A., Pilehvar, S., and Mahinroosta, M. (2016). “Influence of curing conditions on the mechanical and physical properties of chemically-activated phosphorous slag cement.” Powder Technol., 288(1), 132–139.
Alonso, S., and Palomo, A. (2001). “Alkaline activation of metakaolin and calcium hydroxide mixtures: Influence of temperature, activator concentration and solids ratio.” Mater. Lett., 47(1–2), 55–62.
Altan, E., and Erdogan, S. T. (2012). “Alkali activation of a slag at ambient and elevated temperatures.” Cem. Concr. Compos., 34(2), 131–139.
ASTM. (2013a). “Standard specification for standard sand.” ASTM C778-13, West Conshohocken, PA.
ASTM. (2013b). “Standard test methods for sampling and testing fly ash or natural pozzolans for use in portland-cement concrete.” ASTM C311/C311M-13, West Conshohocken, PA.
ASTM. (2015). “Standard test methods for chemical analysis of hydraulic cement.” ASTM C114-15, West Conshohocken, PA.
Aydın, S., and Baradan, B. (2012). “Mechanical and microstructural properties of heat cured alkali-activated slag mortars.” Mater. Des., 35(1), 374–383.
Bakharev, T. (2005). “Geopolymeric materials prepared using Class F fly ash and elevated temperature curing.” Cem. Concr. Res., 35(6), 1224–1232.
Bakharev, T., Sanjayan, J. G., and Cheng, Y. B. (2000). “Effect of admixtures on properties of alkali-activated slag concrete.” Cem. Concr. Res., 30(9), 1367–1374.
Bonk, F., Schneider, J., Cincotto, M. A., and Panepucci, H. (2003). “Characterization by multinuclear high-resolution NMR of hydration products in activated blast-furnace slag pastes.” J. Am. Ceram. Soc., 86(10), 1712–1719.
Cheng, T. W., and Chiu, J. P. (2003). “Fire-resistant geopolymer produced by granulated blast furnace slag.” Miner. Eng., 16(3), 205–210.
Clayden, N. J., Esposito, S., Aronne, A., and Pernice, P. (1999). “Solid state 27Al NMR and FTIR study of lanthanum aluminosilicate glasses.” J. Non-Cryst. Solids, 258(1–3), 11–19.
Davidovits, J. (1979). “Synthesis of new high temperature geo-polymers for reinforced plastics/composites.” SPE PACTEC 79, Society of Plastic Engineers, Bethel, CT, 151–154.
Ebbing, D. D. (1990). General chemistry, Houghton Mifflin, Boston.
Escalante-Garcia, J. J., Gorokhovsky, A. V., Mendoza, G., and Fuentes, A. F. (2003). “Effect of geothermal waste on strength and microstructure of alkali-activated slag cement mortars.” Cem. Concr. Res., 33(10), 1567–1574.
Ezziane, K., Bougara, A., Kadri, A., Khelafi, H., and Kadri, E. (2007). “Compressive strength of mortar containing natural pozzolan under various curing temperature.” Cem. Concr. Compos., 29(8), 587–593.
Greenwood, N. N., and Earnshaw, A. (1997). Chemistry of the elements, 2nd Ed., Butterworth-Heinemann, Oxford, U.K.
Guo, X., Shi, H., and Dick, W. A. (2010). “Compressive strength and microstructural characteristics of Class C fly ash geopolymer.” Cem. Concr. Compos., 32(2), 142–147.
Habert, G., d’Espinose de Lacaillerie, J. B., and Roussel, N. (2011). “An environmental evaluation of geopolymer based concrete production: Reviewing current research trends.” J. Clean. Prod., 19(11), 1229–1238.
Haha, M. B., Lothenbach, B., Saout, G. L., and Winnefeld, F. (2011a). “Influence of slag chemistry on the hydration of alkali-activated blast-furnace slag. I: Effect of MgO.” Cem. Concr. Res., 41(9), 955–963.
Haha, M. B., Lothenbach, B., Saout, G. L., and Winnefeld, F. (2012). “Influence of slag chemistry on the hydration of alkali-activated blast-furnace slag. II: Effect of .” Cem. Concr. Res., 42(1), 74–83.
Haha, M. B., Saout, G. L., Winnefeld, F., and Lothenbach, B. (2011b). “Influence of activator type on hydration kinetics, hydrate assemblage and microstructural development of alkali activated blast-furnace slags.” Cem. Concr. Res., 41(3), 301–310.
Hubler, M. H., Thomas, J. J., and Jennings, H. M. (2011). “Influence of nucleation seeding on the hydration kinetics and compressive strength of alkali activated slag paste.” Cem. Concr. Res., 41(8), 842–846.
Ireland, C. R. (2010). Experimental statistics for agriculture and horticulture, CABI, Wallingford, Oxfordshire, U.K.
Kutner, M. H., Nachtsheim, C. J., Neter, J., and Li, W. (2005). Applied linear statistical models, McGraw-Hill, New York.
Lee, T.-C., and Li, Z.-S. (2010). “Conditioned MSWI ash-slag-mix as a replacement for cement in cement mortar.” Constr. Build. Mater., 24(6), 970–979.
Li, D., Shen, J., Mao, L., and Wu, X. (2000). “The influence of admixtures on the properties of phosphorous slag cement.” Cem. Concr. Res., 30(7), 1169–1173.
Maghsoodloorad, H., and Allahverdi, A. (2017). “Developing low-cost activators for alkali-activated phosphorus slag-based binders.” J. Mater. Civil Eng., 04017006.
Maghsoodloorad, H., Khaliliamiri, H., Allahverdi, A., Lachemi, M., and Hossain, K. M. A. (2014). “Recycling phosphorus slag as a precursor for alkali-activated binder; impact of type and dosage of activator.” Ceram. Silik., 58(3), 227–236.
Montgomery, D. (2001). Design and analysis of experiments, Wiley, New York.
Najafikani, E., Allahverdi, A., and Provis, J. L. (2012). “Efflorescence control in geopolymer binders based on natural pozzolan.” Cem. Concr. Compos., 34(1), 25–33.
Oh, J. E., Monteiro, P. J. M., Jun, S. S., Choi, S., and Clark, S. M. (2010). “The evolution of strength and crystalline phases for alkali-activated ground blast furnace slag and fly ash-based geopolymers.” Cem. Concr. Res., 40(2), 189–196.
Palacios, M., and Puertas, F. (2006). “Effect of carbonation on alkali-activated slag paste.” J. Am. Ceram. Soc., 89(10), 3211–3221.
Pallagi, A., Tasi, Á., Gácsi, A., Csáti, M., Pálinkó, I., Peintler, G., and Sipos, P. (2012). “The solubility of in extremely concentrated NaOH solutions at 25°C.” Cent. Eur. J. Chem., 10(2), 332–337.
Puertas, F., Palaciosc, M., Gil-Maroto, A., and Vázquez, T. (2009). “Alkali-aggregate behaviour of alkali-activated slag mortars: Effect of aggregate type.” Cem. Concr. Compos., 31(5), 277–284.
Puertas, F., Palaciosc, M., Manzanod, H., Doladod, J. S., Ricof, A., and Rodríguezf, J. (2011). “Model for the C-A-S-H gel formed in alkali-activated slag cements.” J. Eur. Ceram. Soc., 31(12), 2043–2056.
Rashad, A. M., Zeedan, S. R., and Hassan, H. A. (2012). “A preliminary study of autoclaved alkali-activated slag blended with quartz powder.” Constr. Build. Mater., 33(1), 70–77.
Sajedi, F., and Razak, H. A. (2011). “Comparison of different methods for activation of ordinary portland cement-slag mortars.” Constr. Build. Mater., 25(1), 30–38.
Shi, C., Fernandez-Jimenez, A. F., and Palomo, A. (2011). “New cements for the 21st century: The pursuit of an alternative to portland cement.” Cem. Concr. Res., 41(7), 750–763.
Shi, C., Krivenko, P. V., and Roy, D. M. (2006). Alkali-activated cements and concretes, Taylor & Francis, New York.
Shi, C., and Li, Y. (1989). “Investigation on some factors affecting the characteristics of alkali-phosphorus slag cement.” Cem. Concr. Res., 19(4), 527–533.
Shi, C., and Qian, J. (2000). “High performance cementing materials from industrial slags—A review.” Resour. Conserv. Recy., 29(3), 195–207.
Škvára, F. (2007). “Alkali activated materials or geopolymers.” Ceram. Silik., 51(3), 173–177.
Taher, M. A. (2007). “Influence of thermally treated phosphogypsum on the properties of portland slag cement.” Conserv Recycl., 52(1), 28–38.
Torgal, F. P. (2013). Handbook of recycled concrete and demolition waste, Woodhead, Cambridge, U.K.
Torgal, F. P., Castro-Gomes, J. O., and Jalali, S. (2008a). “Alkali-activated binders: A review. 1: Historical background, terminology, reaction mechanisms and hydration products.” Constr. Build. Mater., 22(7), 1305–1314.
Torgal, F. P., Castro-Gomes, J. O., and Jalali, S. (2008b). “Alkali-activated binders: A review. 2: About materials and binders manufacture.” Constr. Build. Mater., 22(7), 1315–1322.
Vogel, W., Kreidl, N., and Barreto, M. L. (2012). Glass chemistry, Springer, Berlin.
Wang, S.-D., Scrivener, K. L., and Pratt, P. L. (1994). “Factors affecting the strength of alkali-activated slag.” Cem. Concr. Res., 24(6), 1033–1043.
Yang, K.-H., Sim, J.-I., and Namc, S.-H. (2010). “Enhancement of reactivity of calcium hydroxide-activated slag mortars by the addition of barium hydroxide.” Constr. Build. Mater., 24(3), 241–251.
Zivica, V. (2007). “Effects of type and dosage of alkaline activator and temperature on the properties of alkali-activated slag mixtures.” Constr. Build. Mater., 21(7), 1463–1469.
Information & Authors
Information
Published In
Copyright
©2017 American Society of Civil Engineers.
History
Received: Feb 11, 2017
Accepted: Jun 8, 2017
Published online: Oct 25, 2017
Published in print: Jan 1, 2018
Discussion open until: Mar 25, 2018
Authors
Metrics & Citations
Metrics
Citations
Download citation
If you have the appropriate software installed, you can download article citation data to the citation manager of your choice. Simply select your manager software from the list below and click Download.