Water Treatment Sludge–Calcium Carbide Residue Geopolymers as Nonbearing Masonry Units
Publication: Journal of Materials in Civil Engineering
Volume 29, Issue 9
Abstract
In this research, water treatment sludge (WTS) calcium carbide residue (CCR) geopolymers were evaluated as a sustainable masonry nonbearing unit. The WTS was a by-product from a water treatment plant, whereas CCR was a by-product from an acetylene gas factory in Thailand. Sodium hydroxide solution (NaOH) and sodium silicate solution () were used for the geopolymerization process. The unconfined compressive strength (UCS), water absorption, and durability of WTS-CCR geopolymer were studied in this research. The test results indicate that the optimal liquid alkaline activator (L)/CCR ratios provided the maximum unit weight decrease with CCR contents for all of the ratios evaluated. The optimal L/CCR ratios were found to be 16, 8, 5.33, 4, 3.2, and 2.67 for CCR contents of 5, 10, 15, 20, 25, and 30%, respectively. The ratio of 70:30 was found to give the highest maximum unit weight and UCS among all of the WTS/CCR ratios tested. Three zones of UCS development with CCR content were evident: the active, inert, and deterioration zones. In the active zone, the UCS increased significantly as the CCR content increased, and the maximum UCS was attained at 10% CCR. In the inert zone, the UCS development was gradual. When the CCR content was more than 20% in the deterioration zone, a subsequent strength decrease was observed. The wet–dry (w–d) cycle strength, , depends primarily on the initial soaked strength, . A predictive equation was proposed for the assessment of initial strength to attain the required w–d strengths. Based on the UCS and water absorption requirements, an optimum ingredient consisting of 10% CCR and 70:30 at room temperature curing can be recommended for nonbearing masonry units.
Get full access to this article
View all available purchase options and get full access to this article.
Acknowledgments
The authors are grateful to the Thailand Research Fund under the TRF Senior Research Scholar program Grant No. RTA5980005, Suranaree University of Technology, Rajamangala University of Technology Isan, and the Office of Higher Education Commission under NRU project of Thailand.
References
Arulrajah, A., Disfani, M. M., Suthagaran, V., and Imteaz, M. (2011). “Select chemical and engineering properties of wastewater biosolids.” Waste Manage., 31(12), 2522–2526.
Arulrajah, A., Kua, T-A., Horpibulsuk, S., Phetchuay, C., Suksiripattanapong, C., and Du, Y-J. (2016a). “Strength and microstructure evaluation of recycled glass-fly ash geopolymer as low-carbon masonry units.” Constr. Build. Mater., 114, 400–406.
Arulrajah, A., Mohammadinia, A., Phummiphan, I., Horpibulsuk, S., and Samingthong, W. (2016b). “Stabilization of recycled demolition aggregates by geopolymers comprising calcium carbide, fly ash and slag precursors.” Constr. Build. Mater., 114, 864–873.
ASTM. (2003). “Standard test methods for wetting and drying compacted soil-cement mixtures.” ASTM C599, West Conshohcken, PA.
ASTM. (2007). “Standard test methods for compressive strength of molded soil-cement cylinders.” ASTM C1633, West Conshohcken, PA.
Chindaprasirt, P., De Silva, P., Sagoe-Crenstil, K., and Hanjitsuwan, S. (2012). “Effect of and on the setting and hardening of high calcium fly ash-based geopolymer systems.” J. Mater. Sci., 47(12), 4876–4883.
Donrak, J., Rachan, R., Horpibulsuk, S., Arulrajah, A., and Du, Y. J. (2016). “Improvement of marginal lateritic soil using melamine debris replacement for sustainable engineering fill materials.” J. Cleaner Prod., 134, 515–522.
Du, Y-J., Jiang, N-J., Liu, S-Y., Horpibulsuk, S., and Arulrajah, A. (2015). “Field evaluation of soft highway subgrade soil stabilized with calcium carbide residue.” Soils Found., 56(2), 301–314.
Horpibulsuk, S., Munsrakest, V., Udomchai, A, Chinkulkijniwat, A., and Arulrajah, A. (2014). “Strength of sustainable non-bearing masonry unit manufacturing from calcium carbide residue and fly ash.” Constr. Build. Mater., 71, 210–215.
Horpibulsuk, S., Phetchuay, C., and Chinkulkijniwat, A. (2012). “Soil stabilization by calcium carbide residue and fly ash.” J. Mater. Civ. Eng., 184–193.
Horpibulsuk, S., Suksiripattanapong, C., Samingthong, W., Rachan, R., and Arulrajah, A. (2015). “Durability against wetting–drying cycles of water treatment sludge–fly ash geopolymer and water treatment sludge–cement and silty clay–cement systems.” J. Mater. Civ. Eng., 28(1), 1–9.
Kampala, A., and Horpibulsuk, S. (2013). “Engineering properties of calcium carbide residue stabilized silty clay.” J. Mater. Civ. Eng., 632–644.
Kampala, A., Horpibulsuk, S., Chinkulkijniwat, A., and Shen, S. L. (2013). “Engineering properties of recycled calcium carbide residue stabilized clay as fill and pavement materials.” Constr. Build. Mater., 46, 203–210.
Kampala, A., Horpibulsuk, S., Prongmanee, N., and Chinkulkijniwat, A. (2014). “Influence of wet-dry cycles on compressive strength of calcium carbide residue-fly ash stabilized clay.” J. Mater. Civ. Eng., 633–643.
Khater, H. M. (2012). “Effect of calcium on geopolymerization of aluminosilicate wastes.” J. Mater. Civ. Eng., 92–101.
Neramitkornburi, A., Horpibulsuk, S., Shen, S. L., Chinkulkijniwat, A., Arulrajah, A., and Disfani, M. M. (2015). “Durability against wetting–drying cycles of sustainable lightweight cellular cemented construction material comprising clay and fly ash wastes.” Constr. Build. Mater., 77, 41–49.
Nimwinya, E., Arjharn, W., Horpibulsuk, S., Phoo-ngernkham, T., and Poowancum, A. (2016). “A sustainable calcined water treatment sludge and rice husk ash geopolymer.” J. Cleaner Prod., 119, 128–134.
Phetchuay, C., Horpibulsuk, S., Suksiripattanpong, C., Chinkulkijniwat, A., Arulrajah, A., and Disfani, M. M. (2014). “Calcium carbide residue: Alkaline activator for clay-fly ash geopolymer.” Constr. Build. Mater., 69, 285–294.
Phoo-ngernkham, T., Chindaprasirt, P., Sata, V., and Sinsiri, T. (2013). “High calcium fly ash geopolymer containing diatomite as additive.” Indian J. Eng. Mater. Sci., 20(4), 310–318.
Phoo-ngernkham, T., Sata, V., Hanjitsuwan, S., Ridtirud, C., Hatanaka, S., and Chindaprasirt, P. (2015). “High calcium fly ash geopolymer mortar containing Portland cement for use as repair material.” Constr. Build. Mater., 98, 482–488.
Sales, A., and Souza, F. R. (2015). “Concretes and mortars recycled with water treatment sludge and construction and demolition rubble.” Constr. Build. Mater., 23(6), 2362–2370.
Sengupta, P, Saikia, N., and Borthakur, P. C. (2002). “Bricks from petroleum effluent treatment plant sludge: Properties and environmental characteristics.” J. Environ. Eng., 1090–1094.
Suksiripattanapong, C., Horpibulsuk, S., Boongrasan, S., Udomchai, A., Chinkulkijniwat, A., and Arulrajah, A. (2015a). “Unit weight, strength and microstructure of water treatment sludge-fly ash lightweight cellular geopolymer.” Constr. Build. Mater., 94, 807–816.
Suksiripattanapong, C., Horpibulsuk, S., Chanprasert, P., Sukmak, P., and Arulrajah, A. (2015b). “Compressive strength development in geopolymer masonsy units manufactured from water treatment sludge.” Constr. Build. Mater., 82, 20–30.
Teixeira, S. R., Santos, G. T. A., Souza, A. E., Alessio, P., Souza, S. A., and Souza, N. R. (2011). “The effect of incorporation of a Brazilian water treatment plant sludge on the properties of ceramic materials.” Appl. Clay Sci., 53(4), 561–565.
TIS (Thailand Industrial Standard). (1987). “Standard for hollow non-load bearing concrete mansonry unit.” TIS 57-2530, Bangkok, Thailand.
Zhan, T. L., Zhan, X., Lin, W., Luo, X., and Chen, Y. (2014). “Field and laboratory investigation on geotechnical properties of sewage sludge disposed in a pit at Changan landfill, Chengdu, China.” Eng. Geol., 170, 24–32.
Information & Authors
Information
Published In
Copyright
©2017 American Society of Civil Engineers.
History
Received: Jul 17, 2016
Accepted: Jan 20, 2017
Published ahead of print: Apr 14, 2017
Published online: Apr 15, 2017
Published in print: Sep 1, 2017
Discussion open until: Sep 15, 2017
Authors
Metrics & Citations
Metrics
Citations
Download citation
If you have the appropriate software installed, you can download article citation data to the citation manager of your choice. Simply select your manager software from the list below and click Download.