Evaluation of Slag-Blended Alkaline-Activated Palm Oil Fuel Ash Mortar Exposed to the Sulfuric Acid Environment
Publication: Journal of Materials in Civil Engineering
Volume 27, Issue 12
Abstract
The performance of alkaline activated ground slag/ultrafine palm oil fuel ash (AAGU) mortars upon their exposure to 6% of (acid) for 60 days was investigated. The mortars were prepared with of varied concentrations and () activators and then cured at a temperature of 60°C for 24 h. The findings through strength, microstructural examination, and product characterization revealed that sulfuric acid attack could cause the disintegration of microstructure through the removal of the key elements—Ca, Mg, Na and Al—which resulted in the formation of gypsum, expansive shrinkage cracks, and a reduction in strength retention. Maintaining the slag content, concentration of , ratio, and the mixing water content in the range of 20–40 wt.%, 8–10 M, 1.0–2.5, 5–10 wt.% of the pozzolanic materials (PMs), respectively could enhance the resistance of AAGU mortar subjected to sulfuric acid attack.
Get full access to this article
View all available purchase options and get full access to this article.
Acknowledgments
The authors gratefully acknowledge the Universiti Sains Malaysia for providing financial support for this research work through the Research University Grant Scheme (1001/PAWAM/814191). The support from the Centre for Engineering Research, Research Institute, and Project Department of King Fahd University of Petroleum and Minerals, Dhahran, Saudi Arabia are specially acknowledged. Thanks are also due to United Palm Oil Industries and Southern Steel Company for providing the palm oil fuel ash and steel slag, respectively.
References
ACI (American Concrete Institute). (2000). “Ground granulated blast furnace slag as a cementitious constituent in concrete.”, Detroit, MI.
Ahmad, N. M., Megat Johari, M. A., Zeyad, A. M., Tayeh, B. A., and Yusuf, M. O. (2014). “Improving the engineering and fluid transport properties of ultra-high strength concrete utilizing ultrafine palm oil fuel ash.” J. Adv. Concr. Technol., 12(4), 127–137.
Allahverdi, A., and Skvara, F. (2006). “Sulfuric acid attack on hardened paste of geopolymer cements. Part 2: Corrosion mechanism at mild and relatively low concentrations.” Ceram. Silik., 50(1), 1–4.
Allahverdi, A., and Škvara, F. (2005). “Sulfuric acid attack on hardened paste of geopolymer cements. Part 1: Mechanism of corrosion at relatively high concentrations.” Ceram. Silik., 49(4), 225–229.
Antipas, G. S. E., Temleitner, L., Karalis, K., Kohara, S., Pusztai, L., and Xenidis, A. (2012). “A containerless study of short-range order in high-temperature Fe-Si–Al-Ca–Mg-Cr–Cu-Ni oxide systems.” J. Mol. Struct., 1019(1), 151–158.
Awal, A. S. M. A., and Abubakar, S. I. (2011). “Properties of concrete containing high volume palm oil fuel ash: A short-term investigation.” Malaysian J. Civ. Eng., 23(2), 54–66.
Bakharev, T., Sanjayan, J. G., and Cheng, Y. B. (2003). “Resistance of alkali-activated slag concrete to acid attack.” Cem. Concr. Res., 33(10), 1607–1611.
Bakharev, T. (2005). “Resistance of geopolymer materials to acid attack.” Cem. Concr. Res., 35(4), 658–670.
Bilim, C., and Atis, C. D. (2012). “Alkali activation of mortars containing different replacement levels of ground granulated blast furnace slag.” Constr. Build. Mater., 28(1), 708–712.
Breck, D. W. (1974). Zeolite molecular sieves: Structure, chemistry and use, Wiley-Interscience, New York.
Brown, O. R., Yusof, M. B. B. M., Salim, M. R. B., and Ahmed, K. (2011). “Physico-chemical properties of palm oil fuel ash as composite sorbent in kaolin clay landfill liner system.” 1st Conf. on Clean Energy and Technology, CET 2011. IEEE, 269–274.
Buchwald, A., Hilbig, H., and Kaps, C. (2007). “Alkali-activated metakaolin-slag blends—Performance and structure in dependence of their composition.” J. Mater. Sci., 42(9), 3024–3032.
Budiea, A., Hussin, M. W., Muthusamy, K., and Ismail, M. E. (2010). “Performance of high strength POFA concrete in acidic environment.” Concr. Res. Lett., 1(1), 14–18.
Bukharev, T., Sanjayan, J. G., and Cheng, Y. (1999). “Alkaline activation of Australian slag cements.” Cem. Concr. Res., 29(1), 113–120.
Chandara, C., Mohd Azizli, K. A., Ahmad, Z. A., Saiyid Hashim, S. F., and Sakai, E. (2012). “Heat of hydration of blended cement containing treated ground palm oil fuel ash.” Constr. Build. Mater., 27(1), 78–81.
Chi, M., and Huang, R. (2013). “Binding mechanism and properties of alkali activated fly-ash/slag mortars.” Constr. Build. Mater., 40, 291–298.
Fernández-Jiménez, A., García-Lodeiro, I., and Palomo, A. (2007). “Durability of alkali-activated fly ash cementitious materials.” J. Mater. Sci., 42(9), 3055–3065.
Iller, R. K. (1955). The colloid chemistry of silica and silicates, Cornell University Press, Ithaca, NY.
Jaturapitakkul, C., Tangpagasit, J., Songmue, S., and Kiattikomol, K. (2011). “Filler effect and pozzolanic reaction of ground palm oil fuel ash.” Constr. Build. Mater., 25(11), 4287–4293.
Lee, W. K. W., and van Deventer, J. S. J. (2002). “The effects of inorganic salt contamination on the strength and durability of geopolymers.” Colloids Surf. A, 211(2–3), 115–126.
McGannon, H. E. (1971). The making shaping and treating of steel, United States Steel, 9th ed., United State Steel Corporation.
Megat Johari, M. A., Zeyad, A. M., Bunnori, N. M., and Ariffin, K. S. (2012). “Engineering and transport properties of high-strength green concrete containing high volume of ultrafine palm oil fuel ash.” Constr. Build. Mater., 30, 281–288.
Mijarsh, M. J. A., Megat Johari, M. A., and Ahmad, Z. A. (2014). “Synthesis of geopolymer from large amounts of treated palm oil fuel ash: Application of the Taguchi method in investigating the main parameters affecting compressive strength.” Constr. Build. Mater., 52, 473–481.
Pacheco-Togal, F., Castro-Gomes, J., and Jalali, S. (2010). “Durability and environmental performance of alkali-activated tungsten mine waste mud mortars.” J. Mater. Civ. Eng., 897–904.
Puertas, F., Martinez-Ramirez, S., Alonso, S., and Vasquez, T. (2000). “Alkaliactivated fly ash/slag cement: Strength behaviour and hydration products.” Cem. Concr. Res., 30(10), 1625–1632.
Sata, V., Sathonsaowaphak, A., and Chindaprasirt, P. (2012). “Resistance of lignite bottom ash geopolymer mortar to sulfate and sulfuric acid attack.” Cem. Concr. Compos., 34(5), 700–708.
Song, X., Marosszeky, M., Brungs, M., and Chang, Z. (2005). “Response of geopolymer concrete to sulfuric acid attack.” Geopolymer, Green Chemistry and Sustainable Development Solutions: Proc., World Congress Geopolymer, J. Davidovits, ed., Geopolymer Institute, France, 4.
Takata, M., Acocella, J., Tomozawa, M., and Watson, E. B. (1981). “Effect of water content on the electrical conductivity of glass.” J. Am. Ceram. Soc., 64(12), 719–724.
Turner, L. K., and Collins, F. G. (2013). “Carbon dioxide equivalent (-e) emissions: A comparison between geopolymer and OPC cement concrete.” Constr. Build. Mater. 43, 125–130.
Xie, J., and Kayali, O. (2013). “Effect of initial water content and curing moisture conditions on the development of fly ash-based geopolymers in heat and ambient temperature.” Constr. Build. Mater., 67, 20–28.
Yusuf, M. O., Megat Johari, M. A., Ahmad, Z. A., and Maslehuddin, M. (2014a). “Effects of molar ratio on the strength of alkaline activated ground blast furnace slag-ultrafine palm oil fuel ash based concrete.” Mater. Des., 56, 158–164.
Yusuf, M. O., Megat Johari, M. A., Ahmad, Z. A., and Maslehuddin, M. (2014b). “Effects of addition of Al(OH)3 on the strength of alkaline activated ground blast furnace slag-ultrafine palm oil fuel ash (AAGU) based binder.” Constr. Build. Mater., 50, 361–367.
Yusuf, M. O., Megat Johari, M. A., Ahmad, Z. A., and Maslehuddin, M. (2014c). “Evolution of alkaline activated ground blast furnace slag-ultrafine palm oil fuel ash based concrete.” Mater. Des., 55, 387–393.
Yusuf, M. O., Megat Johari, M. A., Ahmad, Z. A., and Maslehuddin, M. (2014d). “Impact of silica modulus on the early strength of alkaline activated ground steel slag/ultrafine palm oil fuel ash concrete.” Mater. Struct., 48(3), 733–741.
Yusuf, M. O., Megat Johari, M. A., Ahmad, Z. A., and Maslehuddin, M. (2014e). “Performance of different grades of palm oil fuel ash and ground slag in the synthesis of alkaline activated mortar.” J. Adv. Concr. Technol., 12(10), 378–387.
Yusuf, M. O., Megat Johari, M. A., Ahmad, Z. A., and Maslehuddin, M. (2014f). “Strength and microstructural performance of nano- gel (NSG) infused alkaline activated ground blast furnace slag-ultrafine palm oil fuel ash (AAGU) based mortar.” Adv. Mater. Res., 856, 280–284.
Yusuf, M. O., Megat Johari, M. A., Ahmad, Z. A., and Maslehuddin, M. (2014g). “Strength and microstructure of alkali-activated binary blended binder containing palm oil fuel ash and ground blast-furnace slag.” Constr. Build. Mater., 52, 504–510.
Yusuf, M. O., Megat Johari, M. A., Ahmad, Z. A., and Mohammed, M. (2014h). “Shrinkage and strength of alkaline activated ground steel slag/ultrafine palm fuel ash pastes and mortars.” Mater. Des., 63, 710–718.
Information & Authors
Information
Published In
Copyright
© 2015 American Society of Civil Engineers.
History
Received: Nov 12, 2014
Accepted: Feb 19, 2015
Published online: May 7, 2015
Discussion open until: Oct 7, 2015
Published in print: Dec 1, 2015
Authors
Metrics & Citations
Metrics
Citations
Download citation
If you have the appropriate software installed, you can download article citation data to the citation manager of your choice. Simply select your manager software from the list below and click Download.