Evaluation of Moisture Susceptibility of Nanoclay-Modified Asphalt Binders through the Surface Science Approach
Publication: Journal of Materials in Civil Engineering
Volume 27, Issue 10
Abstract
Due to an increasing rate of traffic volume and truckloads in recent years, asphalt binders are often modified with synthetic polymers to increase stiffness and sustain excessive heat during hot summer days. However, the cost of polymer-modified binders (PMBs) is significantly higher than unmodified binders. Nanoclays, on the other hand, are relatively inexpensive and naturally abundant, and have favorable intrinsic properties, such as nanoscopic size and high surface area. To this end, the research reported in this paper investigated moisture resistance properties of a commonly used Performance Grade (PG) 64-22 binder modified with different dosages of two selected nanoclays [(1) Cloisite 15 A, and (2) Cloisite 11B]. The state of dispersion of the nanoclay in the binder was examined using a scanning electron microscope and small-angle x-ray diffraction. The morphological analyses of scanning electron microscope scans and inter-gallery distances (-spacing values) of small-angle x-ray diffraction data of the two selected nanoclays are effective in evaluating the state of exfoliated microstructure of nanoclays in asphalt binders. In particular, the small-angle x-ray diffraction data of two of the tested samples [(1) 4% of Cloisite 11B, and (2) 6% of Cloisite 11B] showed fully exfoliated microstructure. Moisture resistance of nanoclay-modified binders was evaluated through the surface free energy (SFE) technique. The adhesive energies and compatibility ratios (CRs) of nanoclay-modified binder and selected aggregate (four acidic and four basic) systems were also evaluated. The total SFE increases when the asphalt binder is modified by nanoclays. When the asphalt binder is modified with nanoclays, the wetting ability decreases. A 4% Cloisite 15 A and a 6% Cloisite 11B (by the weight of the binder) showed the highest adhesive energy in maintaining good wetting ability, with different acidic and basic aggregates. The work-of-adhesion values under dry and wet conditions of nanoclay-modified binders were highly dependent on the nature (acidic or basic) of aggregate. The CR, an indicator of moisture resistance or bond strength in wet conditions, of the nanoclay-modified asphalt binder decreased for all aggregates except for granite, which showed a slight increase of the CR values. Thus, unless modified with an antistripping agent or other additives, nanoclay modified binders are expected to have poorer moisture resistance than the base binder. While maintaining a dosage level of 4% (by weight) nanoclay, Cloisite 15 A, consisting of smaller particle size than Cloisite 11B, is more compatible with different aggregates than Cloisite 11B. At a lower dosage level (2% by weight), Cloisite 11B is more compatible than Cloisite 15 A. Furthermore, the nanoclay technology is expected to be a cost saving approach, which can reduce the cost per metric ton of asphalt binder from 22–33% compared to the polymer-modified binders. Findings of this paper are expected to assist pavement professionals in evaluating moisture resistance of nanoclay-modified asphalt binders through a fundamental science approach.
Get full access to this article
View all available purchase options and get full access to this article.
Acknowledgments
The writers would like to express their sincere appreciation to the University of Oklahoma (UO) Research Council and UO College of Engineering for providing financial support for the research reported in this paper. Thanks to Dr. Zhanping You, from Michigan Technological University for assistance in blending nanoclay with asphalt binder. Special thanks to Dr. Brian P. Grady for assistance in the SAXD experiments. Also, the writers are thankful to Mr. Jackson Autrey, from the University of Oklahoma, for assistance with laboratory testing.
References
Al-Qadi, I. L., Aurangzeb, Q., Carpenter, S. H., Pine, W. J., and Trepanier, J. (2012). “Impact of high RAP contents on structural and performance properties of asphalt mixtures.”, Illinois DOT, Springfield, IL.
Anderson, D. (1996). “Influence of fines on performance of asphalt concrete mixtures.” Proc., Annual Aggregates Symp., Aggregates Foundation for Technology, Research, and Education, Alexandria, VA.
Barick, A. K., and Tripathy, D. K. (2010). “Effect of organoclay on thermal and dynamic mechanical properties of novel thermoplastic polyurethane nanocomposites prepared by melt intercalation technique.” J. Polym. Adv. Technol., 21(12), 835–847.
BBI (Binzhou Best International). (2014). “Activated carbon adsorbent variety and chemical auxiliary agent classification nano activated clay.” 〈http://www.alibaba.com/showroom/nano-clay.html〉 (Nov. 14, 2014).
Bhasin, A., Button, J. W., and Chowdhury, A. (2005). “Evaluation of selected laboratory procedures and development of databases for HMA.”, Texas Transportation Institute, Texas A&M Univ., College Station, TX.
Bhasin, A., and Little, D. (2006). “Characterizing surface properties of aggregates used in hot mix asphalt.”, Aggregates Foundation for Technology, Research, and Education, Alexandria, VA.
Bhasin, A., Little, D., Vasconcelos, K. L., and Masad, E. (2007). “Surface free energy to identify moisture sensitivity of materials for asphalt mixes.”, Transportation Research Board, Washington, DC, 37–45.
Budhala, A., Hossain, Z., Wasiuddin, N. M., Zaman, M., and O’Rear, E. A. (2012). “Effects of an amine anti-stripping agent on moisture susceptibility of Sasobit and Aspha-Min mixes by surface free energy analysis.” J. Test. Eval., 40(1), 1–9.
Cheng, D. X., Little, D. N., Lytton, R. L., and Holste, J. C. (2001). “Surface free energy measurement of aggregates and its application to adhesion and moisture damage of asphalt aggregate systems.” Proc., Annual Aggregates Symp., Aggregates Foundation for Technology, Research, and Education, Alexandria, VA.
Cheng, D. X., Little, D. N., Lytton, R. L., and Holste, J. C. (2002). “Surface free energy measurement of asphalt and its application to predicting fatigue and healing in asphalt mixtures.”, Transportation Research Board, Washington, DC, 44–53.
Gierhart, D. (2011). “Use of WMA and RAP in Oklahoma.”, Lexington, KY.
Hauser, E., and Colombo, U. (1953). “Colloid science of montmorillonites and bentonites.” J. Clays Clay Miner., 2(1), 439–461.
Hossain, Z., Bhudhala, A., Zaman, M. M., O’Rear, E., Cross, S., and Lewis, S. (2009). “Evaluation of the use of warm mix asphalt as a viable paving material in the United States.”, Federal Highway Administration, Washington, DC.
Hossain, Z., Zaman, M., and Saha, M. (2013). “Evaluation of rutting and moisture susceptibility of nanoclay-modified asphalt binders.” Proc., Int. Road Federation (IRF) World Meeting and Exhibition, Geneva, 10–14.
Hossain, Z., Zaman, M., Saha, M. C., and Hawa, T. (2014). “Evaluation of viscosity and rutting properties of nanoclay-modified asphalt binders.” Proc., Geo-Congress on Geo-Characterization and Modeling for Geo-Sustainability, ASCE, Reston, VA, 23–26.
Hussain, F., Hojjati, M., Okamoto, M., and Gorga, R. (2006). “Review article: Polymer-matrix nanocomposites, processing, manufacturing, and application: An overview.” J. Compos. Mater., 40(17), 1511–1575.
IM (Intelligent Materials). (2014). “Nano clay (modified COOH).” 〈http://www.alibaba.com/product-detail/Nano-Clay-Modified-COOH-_143115857.html〉 (Nov. 14, 2014).
Jahromi, S. G., and Ahmadi, N. (2011). “Engineering properties of nanoclay modified asphalt concrete mixtures.” Int. J. Earth Sci. Eng., 4(6), 941–944.
Janczuk, B., and Biae-Piotrowicz, T. (1988). “Components of surface free energy of some clay minerals.” J. Clays Clay Miner., 36(3), 243–248.
Jouany, C. (1991). “Surface free energy components of clay-synthetic humic acid complexes from contact angle measurements.” J. Clays Clay Miner., 39(1), 43–49.
Khattak, M., Khattab, A., and Rizvi, H. (2011). “Mechanistic characteristics of asphalt binder and asphalt matrix modified with nano-fibers.” Proc., Geo-Frontiers, ASCE, Reston, VA, 4812–4822.
Little, D., and Bhasin, A. (2006). “Using surface energy measurements to select materials for asphalt pavement.”, Washington, DC.
Liu, G., Wu, S., van de Ven, M., Molenaar, A., and Besamusca, J. (2010). “Characterization of organic surfactant on montmorillonite nanoclay to be used in bitumen.” J. Mater. Civ. Eng., 794–799.
Nazzal, M., Kaya, S., Gunay, T., and Ahmedzade, P. (2013). “Fundamental characterization of asphalt clay nanocomposites.” J. Nanomech. Micromech., 1–8.
NECEPT (Northeast Center of Excellence for Pavement Technology). (2012). “Superpave system, Northeast Center of Excellence for Pavement Technology.” 〈http://www.superpave.psu.edu/superpave/system.html〉 (Nov. 14, 2014).
NNI (National Nanotechnology Initiative). (2013). “Nanotechnology 101.” 〈http://www.nano.gov〉 (Nov. 14, 2014).
ODOT (Oklahoma DOT). (2012). “Material and testing e-guide, aggregate and stone test data.” 〈http://www.okladot.state.ok.us/materials/materials.htm〉 (Nov. 14, 2014).
ODOT (Oklahoma DOT). (2013). “Oklahoma Department of Transportation monthly asphalt binder price index.” Rep. Prepared for the Asphalt Weekly Monitor, Oklahoma City, OK.
Ratna, D., Manoj, R., Varley, R., Singh, R. R., and Simon, G. (2005). “Clay reinforced epoxy nanocomposites.” Polym. Int., 52(9), 1403–1407.
Ray, S., and Okamoto, M. (2003). “Polymer layered silicate nanocomposites.” Polym. Sci., 28(11), 1539–1641.
Saha, M. C., Kabir, M. E., and Jeelani, S. (2009). “Effect of nanoparticles on mode-I fracture toughness of polyurethane foams.” Polym. Compos., 30(8), 1058–1064.
Saha, M. C., and Nilufar, S. (2010). “Nanoclay reinforced syntactic foams: Flexure and thermal behavior.” Polym. Compos., 31(8), 1309–1494.
Sherman, L. (2004). “Chasing nanocomposites.” 〈http://www.ptonline.com/articles/chasing-nanocomposites〉 (Nov. 14, 2014).
Wasiuddin, N. M., Zaman, M., and O’Rear, E. A. (2010). “Polymeric aggregate treatment using styrene-butadiene rubber (SBR) for moisture-induced damage potential.” Int. J. Pavement Res. Technol., 3(1), 1–9.
Xiao, F., Amirkhanian, A., and Amirkhanian, S. (2011). “Influence of carbon nanoparticles on the rheological characteristics of short-term aged asphalt binders.” J. Mater. Civ. Eng., 423–431.
Yao, H., et al. (2012). “Performance of asphalt binder blended with non-modified and polymer-modified.” Constr. Build. Mater., 35, 159–170.
You, Z., Mills-Beale, J. F., Justin, M., Roy, S., and Odegard, G. M. (2011). “Nanoclay-modified asphalt materials: Preparation and characterization.” Constr. Build. Mater., 25(2), 1072–1078.
Zisman, W. A. (1964). “Relation of the equilibrium contact angle to solid and liquid construction.” Advances of chemistry, American Chemical Society, Washington, DC, 1–51.
Information & Authors
Information
Published In
Copyright
© 2014 American Society of Civil Engineers.
History
Received: Dec 9, 2013
Accepted: Oct 21, 2014
Published online: Dec 9, 2014
Discussion open until: May 9, 2015
Published in print: Oct 1, 2015
Authors
Metrics & Citations
Metrics
Citations
Download citation
If you have the appropriate software installed, you can download article citation data to the citation manager of your choice. Simply select your manager software from the list below and click Download.