Microstructure of a Type G Oil Well Cement-Nanosilica Blend
Publication: Journal of Materials in Civil Engineering
Volume 27, Issue 5
Abstract
Motivated by the need to improve oil well integrity for potential carbon capture and storage through sequestration, nanosilica was hypothesized capable of improving the quality of oil well cement (OWC) in medium and deep oil wells. In this study, OWC was mixed with 1 and 3% nanosilica by weight to produce OWC pastes with water to binder ratio () of 0.45. The specimens were cured under high temperature and pressure, simulating what occurs in oil wells. A method of analysis combining nuclear magnetic resonance (NMR) and nanoindentation is proposed. The results are compared with observations extracted from nanoindentation in which classification of hydration products is based on the elastic modulus of the different categories of calcium silicate hydrate (C-S-H). The results show that the degree of hydration, the degree of reactivity, and silicate polymerization increase under the elevated curing condition compared with the ambient condition. It seems that C-S-H generated by the pozzolanic reaction of nanosilica in OWC paste has not only different composition but also different packing density sensitive to curing conditions.
Get full access to this article
View all available purchase options and get full access to this article.
Acknowledgments
The authors would like to acknowledge KACST support through King Fahd University of Petroleum and Minerals (KFUPM) for funding Project #09-NAN754-04 as part of the National Science, Technology and Innovation Plan. Additional support to the University of New Mexico team by the U.S. National Science Foundation (NSF) Award #1131369 is greatly appreciated. The corresponding author would like to acknowledge a National Research Foundation (NRF) grant funded by the Korean government (MOE) (No. 2013R1A1A2062784).
References
Acker, P. (2001). “Micromechanical analysis of creep and shrinkage mechanisms. Creep, shrinkage and durability mechanics of concrete and other quasi-brittle materials.” Proc., ConCreep-6, Elsevier, New York.
Alizadeh, R., and Beaudoin, J. J. (2011). “Mechanical properties of calcium silicate hydrates.” Mater. Struct., 44(1), 13–28.
Allen, A. A., Thomas, J. J., and Jennings, H. M. (2007). “Composition and density of nanoscale calcium-silicate-hydrate in cement.” Nat. Mater., 6(4), 311–316.
Allen, A. J., and Thomas, J. J. (2007). “Analysis of C-S-H gel and cement paste by small-angle neutron scattering.” Cem. Concr. Res., 37(3), 319–324.
American Petroleum Institute. (2010). “Specifications for cements and materials for well cementing.”, Washington, DC, 52.
Bell, G. M. M., Benstedm, J., Glasser, F. P., Lachowski, E. E., Roberts, D. R., and Taylor, M. J. (1990). “Study of calcium silicate hydrates by solid state high resolution 29Si nuclear magnetic resonance.” Adv. Cem. Res., 3(9), 23–27.
Bentz, D. P., Jensen, O. M., Coats, A. M., and Glasser, F. P. (2000). “Influence of silica fume on diffusivity in cement-based materials I. Experimental and computer modelling studies on cement pastes.” Cem. Concr. Res., 30(6), 953–962.
Cailly, B., Le Thiez, P., Egermann, P., Audibert, A., Vidal-Gilbert, S., and Longaygue, X. (2005). “Geological storage of CO2: A state-of-the-art of injection processes and technologies.” Oil Gas Sci. Tech., 60(3), 517–525.
Choolaei, M., Rashidi, A. M., Ardjmand, M., and Yadegari, A. (2012). “The effect of nanosilica on the physical properties of oil well cement.” Mater. Sci. Eng. A, 538(1), 288–294.
Cong, X., and Kirkpatrick, R. J. (1996). “ MAS NMR study of the structure of calcium silicate hydrate.” Adv. Cem. Based Mater., 3(3–4), 144–156.
Constantinides, G., and Ulm, F.-J. (2007). “The nanogranular nature of C-S-H.” J. Mech. Phys. Solids, 55(1), 64–90.
Constantinides, G., Ulm, F.-J., and Van Vliet, K. (2003). “On the use of nanoindentation for cementitious materials.” Mater. Struct., 36(3), 191–196.
Crow, W., Carey, J. W., Gasda, S., Williams, D. B., and Celia, M. (2010). “Wellbore integrity analysis of a natural producer.” Int. J. Greenhouse Gas Contr., 4(2), 186–197.
Fischer-Cripps, A. C. (2004). Nanoindentation, Springer Science+Business Media, New York.
Foley, E., Kim, J. J., and Reda Taha, M. M. (2012). “Synthesis and nano-mechanical characterization of calcium-silicate-hydrate (C-S-H) made with ratio.” Cem. Concr. Res., 42(9), 1225–1232.
Garcia Lodeiro, I., Macphee, D. E., Palomo, A., and Fernandez-Jimenez, A. (2009). “Effect of alkalis on fresh C-S-H gels. FTIR analysis.” Cem. Concr. Res., 39(3), 147–153.
Grutzeck, M., Benesi, A., and Fanning, B. (1989). “Silicon-29 magic-angle spinning nuclear magnetic resonance study of calcium silicate hydrates.” Am. Ceram. Soc., 72(4), 665–668.
Halim, S. C., Brunner, T. J., Grass, R. N., Bohner, M., and Stark, W. J. (2007). “Preparation of an ultra fast binding cement from calcium silicate-based mixed oxide nanoparticles.” Nanotechnology, 18(39), 1–6.
Jennings, H. M. (2000). “A model for the microstructure of calicum silicate hydrate in cement paste.” Cem. Concr. Res., 30(1), 101–116.
Jennings, H. M., and Tennis, P. D. (1994). “Model for the developing microstructure in portland cement pastes.” J. Am. Ceram. Soc., 77(12), 3161–3172.
Kim, J. J., Fan, T., and Reda Taha, M. M. (2010). “Homogenization model examining the effect of nanosilica on concrete strength and stiffness.” Transportation Research Record 2141, Transportation Research Board, Washington, DC, 28–35.
Korb, J.-P., Monteilhet, L., McDonald, P. J., and Mitchell, J. (2007). “Microstructure and texture of hydrated cement-based materials: A proton field cycling relaxometry approach.” Cem. Concr. Res., 37(3), 295–302.
Land, G., and Stepan, D. (2012). “The influence of nano-silica on the hydration of ordinary portland cement.” J. Mater. Sci., 47(2), 1011–1017.
Larbi, J. A. (1993). “Microstructure of the interfacial zone around aggregate particles in concrete.” Heron, 38(1), 1–69.
Lippmaa, E., Mägi, M., Samoson, A., Engelhardt, G., and Grimmer, A. R. (1980). “Structural studies of silicates by solid-state high-resolution 29Si NMR.” Am. Chem. Soc., 102(15), 4889–4893.
Macomber, R. S. (1998). A complete introduction to modern NMR spectroscopy, Wiley, New York.
Mondal, P., Shah, S. P., and Marks, L. (2007). “A reliable technique to determine the local mechanical properties at the nanoscale for cementitious materials.” Cem. Concr. Res., 37(10), 1440–1444.
Mondal, P., Shah, S. P., Marks, L. D., and Gaitero, J. J. (2010). “Comparative study of the effects of microsilica and nanosilica in concrete.” Transportation Research Record 2141, Transportation Research Board, Washington, DC, 6–9.
Oliver, W., and Pharr, G. (1992). “An improved technique for determining hardness and elastic modulus using load and displacement sensing indentation experiments.” J. Mater. Res., 7(6), 1564–1583.
Patural, L., et al. (2010). “A pulsed field gradient and NMR imaging investigations of the water retention mechanism by cellulose ethers in mortars.” Cem. Concr. Res., 40(9), 1378–1385.
Richardson, I. G. (2004). “Tobermorite/jennite- and tobermorite/calcium hydroxide-based models for the structure of C-S-H: Applicability to hardened pastes of tricalcium silicate, -dicalcium silicate, portland cement, and blends of portland cement with blast-furnace slag, metakaolin, or silica fume.” Cem. Concr. Res., 34(9), 1733–1777.
Sanchez, F., and Sobolev, K. (2010). “Nanotechnology in concrete—A review.” Constr. Build. Mater., 24(11), 2060–2071.
Sanchez de Rojas, M. I., and Frias, M. (1995). “The influence of silica fume on the heat of hydration of portland cement.” Am. Concr. Inst., SP-153, 829–844.
Saoût, G. L., Lécolier, E., Rivereau, A., and Zanni, H. (2006). “Chemical structure of cement aged at normal and elevated temperatures and pressures. Part II: Low permeability class G oilwell cement.” Cem. Concr. Res., 36(3), 428–433.
Scrivener, K., and Kirkpatrick, R. J. (2008). “Innovation in use and research on cementitious material.” Cem. Concr. Res., 38(2), 128–136.
Sorelli, L., Constantinides, G., Ulm, F.-J., and Toutlemonde, F. (2008). “The nano-mechanical signature of ultra high performance concrete by statistical nanoindentation techniques.” Cem. Concr. Res., 38(12), 1447–1456.
Stark, J. (2011). “Recent advances in the field of cement hydration and microstructural analysis.” Cem. Concr. Res., 41(7), 666–678.
Taylor, H. F. W. (1987). “A method for predicting alkali ion concentration in cement pore solutions.” Adv. Cem. Res., 1(1), 5–17.
Tennis, P. D., and Jennings, H. M. (2000). “A model for two types of calcium silicate hydrate in the microstructure of portland cement pastes.” Cem. Concr. Res., 30(6), 855–863.
Thomas, J. J., and Jennings, H. M. (2006). “A colloid interpretation of chemical aging of the C-S-H gel and its effects on the properties of cement paste.” Cem. Concr. Res., 36(1), 30–38.
Ulm, F.-J., et al. (2010). “Does microstructure matter for statistical nanoindentation techniques.” Cem. Concr. Comp., 32(1), 92–99.
Ulm, F.-J., Vandamme, M., Bobko, C., Ortega, J. A., Tai, K., and Ortiz, C. (2007). “Statistical indentation techniques for hydrated nanocomposites: Concrete, bone, shale.” J. Am. Ceram. Soc., 90(9), 2677–2692.
Vandamme, M., and Ulm, F.-J. (2013). “Nanoindentation investigation of creep properties of calcium silicate hydrates.” Cem. Concr. Res., 52, 38–52.
Velez, K., Maximilien, S., Damidot, D., Fantozzi, G., and Sorrentino, F. (2001). “Determination by nanoindentation of elastic modulus and hardness of pure constituents of portland cement clinker.” Cem. Concr. Res., 31(4), 555–561.
Wieker, W., Grimmer, A.-R., Winkler, A., Mägi, M., Tarmak, M., and Lippmaa, E. (1982). “Solid-state high-resolution 29Si NMR spectroscopy of synthetic 14Å, 11and 9Å tobermorites.” Cem. Concr. Res., 12(3), 333–339.
Xu, J., and Yao, W. (2011). “Nano-scratch as a new tool for assessing the nano-tribological behavior of cement composite.” Mater. Struct., 44(9), 1703–1711.
Yajun, J., and Cahyadi, J. H. (2004). “Simulation of silica fume blended cement hydration.” Mater. Struct., 37(6), 397–404.
Young, J. F. (1988). “Investigations of calcium silicate hydrate structure using silicon-29 nuclear magnetic resonance spectroscopy.” J. Am. Ceram. Soc., 71(3), C118–C120.
Yu, P., Kirpatrick, R. J., Poe, B., McMillan, P. F., and Cong, X. (1999). “Structure of calcium silicate hydrate (C-S-H): Near-, mid- and far-infrared spectroscopy.” J. Am. Ceram. Soc., 82(3), 742–748.
Zhu, W., Hughes, J., Bicanic, N., and Pearce, C. (2007). “Nanoindentation mapping of mechanical properties of cement paste and natural rocks.” Mater. Charact., 58(11–12), 1189–1198.
Information & Authors
Information
Published In
Copyright
© 2014 American Society of Civil Engineers.
History
Received: Nov 20, 2013
Accepted: May 7, 2014
Published online: Aug 5, 2014
Discussion open until: Jan 5, 2015
Published in print: May 1, 2015
Authors
Metrics & Citations
Metrics
Citations
Download citation
If you have the appropriate software installed, you can download article citation data to the citation manager of your choice. Simply select your manager software from the list below and click Download.