Effects of Fly Ash and Foundry Sand on Performance of Architectural Precast Concrete
Publication: Journal of Materials in Civil Engineering
Volume 24, Issue 7
Abstract
This research was conducted to establish the effects of fly ash and used foundry sand on strength and durability of concrete. Two series (Series 1 and Series 2) of experiments were performed. All concrete mixtures were produced for and at the production plant of an architectural precast concrete products producer. Concrete mixtures produced were used in manufacture of precast concrete panels. Tests were performed with normal and air-entrained fly ash concrete. Concrete test specimens were evaluated for compressive strength, abrasion resistance, salt-scaling resistance, freezing and thawing resistance, and chloride-ion penetration resistance. On the basis of strength and durability evaluations, it was concluded that both nonair and air-entrained concrete mixtures developed in this investigation are appropriate for manufacture of high-quality, high-durability architectural precast concrete using used foundry sand and fly ash.
Get full access to this article
View all available purchase options and get full access to this article.
Acknowledgments
The authors express a deep sense of gratitude to the (UWS/RMDB) Solid Waste Recovery Research Program, Madison, WI, Advance Cast Stone Company, Random Lake, WI, and Neenah Foundry Co., Neenah, WI, for their support for this investigation. Special appreciation is expressed to Ms. Eileen Norby for her interest in this project and monitoring progress and achievements. Special thanks are expressed to Mr. Mayank Gupta for his help in experimental work, data collection, and analysis related to this project. Thanks are also due to the UWM Center for By-Products Utilization staff, especially Joe Bagatta, Parag Chopada, Yoon-Moon Chun, Wayne Johnson, and Zichao Wu, who directly contributed to the success of this project.
A special gratitude is extended to Matt Garny, President, Advance Caststone Company, for directly contributing to the support and success of this project and allowing access to the production facility at Random Lake to carry out this project over many production dates. This paper presents only part of the production and testing data collected at the Advance Caststone Company.
The Center was established in 1988 with a generous grant from the Dairyland Power Cooperative, La Crosse, WI; Madison Gas and Electric Company, Madison, WI; National Minerals Corporation, St. Paul, MN; Northern States Power Company, Eau Claire, WI; We Energies, Milwaukee, WI; Wisconsin Power and Light Company, Madison, WI; and, Wisconsin Public Service Corporation, Green Bay, WI. Their financial support and additional grants and support from Manitowoc Public Utilities, Manitowoc, WI, are gratefully acknowledged.
References
American Foundrymen’s Society (AFS). (1991). “Alternate utilization of foundry waste sand.” Final Rep. of AFS Research, AFS, Chicago.
ASTM. (2003). “Standard test method for scaling resistance of concrete surfaces exposed to deicing chemicals.” C672-03, West Conshohocken, PA.
ASTM. (2004). “Standard test method for materials finer than 75-μm (No. 200) sieve in mineral aggregates by washing.” C117-04, West Conshohocken, PA.
ASTM. (2005a). “Standard test method for abrasion resistance of concrete or mortar surfaces by the rotating-cutter method.” C944-05, West Conshohocken, PA.
ASTM. (2005b). “Standard test method for soundness of aggregates by use of sodium sulfate or magnesium sulfate.” C88-05, West Conshohocken, PA.
ASTM. (2005c). “Standard test method for temperature of freshly mixed hydraulic-cement concrete.” C1064-05, West Conshohocken, PA.
ASTM. (2006). “Standard Test Method for Sieve Analysis of Fine and Coarse Aggregates.” C136-06, West Conshohocken, PA.
ASTM. (2007a). “Standard test method for density, relative density (specific gravity), and absorption of fine aggregate.” C128-07, West Conshohocken, PA.
ASTM. (2007b). “Standard test method for density, relative density (specific gravity), and absorption of coarse aggregate.” C127-07, West Conshohocken, PA.
ASTM. (2008a). “Standard test method for air content of hydraulic cement mortar.” C185-08, West Conshohocken, PA.
ASTM. (2008b). “Standard test method for fineness of hydraulic cement by the 45-μm (No. 325) Sieve.” C430-08, West Conshohocken, PA.
ASTM. (2008c). “Standard test method for resistance of concrete to rapid freezing and thawing.” C666-08, West Conshohocken, PA.
ASTM. (2008d). “Standard test methods for time of setting of hydraulic cement by Vicat needle.” C191-08, West Conshohocken, PA.
ASTM. (2009a). “Standard Test Method for Autoclave Expansion of Hydraulic Cement.” C151-09, West Conshohocken, PA.
ASTM. (2009b). “Standard test method for bulk density (“unit weight”) and voids in aggregate.” C29-09, West Conshohocken, PA.
ASTM. (2009c). “Standard test method for density of hydraulic cement.” C188-09, West Conshohocken, PA.
ASTM. (2010a). “Standard practice for making and curing concrete test specimens in the field.” C31-10, West Conshohocken, PA.
ASTM. (2010b). “Standard test method for air content of freshly mixed concrete by the pressure method.” C231-10, West Conshohocken, PA.
ASTM. (2010c). “Standard test method for clay lumps and friable particles in aggregates.” C142-10, West Conshohocken, PA.
ASTM. (2010d). “Standard test method for density (unit weight), yield, and air content (gravimetric) of concrete.” C138-10, West Conshohocken, PA.
ASTM. (2010e). “Standard test method for slump of hydraulic-cement concrete.” C143-10, West Conshohocken, PA.
ASTM. (2011a). “Standard specification for concrete aggregates.” C33-11, West Conshohocken, PA.
ASTM. (2011b). “Standard specification for Portland cement.” C150-11, West Conshohocken, PA.
ASTM. (2011c). “Standard test method for compressive strength of hydraulic cement mortars [using 2-in. or (50-mm) cube specimens].” C109-11, West Conshohocken, PA.
ASTM. (2011d). “Standard test method for organic impurities in fine aggregates for concrete.” C40-11, West Conshohocken, PA.
ASTM. (2011e). “Standard test methods for fineness of hydraulic cement by air-permeability apparatus.” C204-11, West Conshohocken, PA.
ASTM. (2012a). “Standard specification for coal fly ash and raw or calcined natural pozzolan for use in concrete.” C618-12, West Conshohocken, PA.
ASTM. (2012b). “Standard specification for ready-mixed concrete.” C94-12, West Conshohocken, PA.
ASTM. (2012c). “Standard test method for compressive strength of cylindrical concrete specimens.” C39-12, West Conshohocken, PA.
ASTM. (2012d). “Standard test method for electrical indication of concrete’s ability to resist chloride ion penetration.” C1202-12, West Conshohocken, PA.
Baillod, C. R., Rundman, K. B., Murto, S. L., Talford, D. A., and Coduti, L. A. (1993). Foundry wastes in Michigan:Industrial uses of spent sand, Environmental Engineering Center, Michigan Technological Univ., Houton, MI.
Burnley, T. (1991). “Illinois examines the beneficial reuse of spent foundry sand.” Mod. Cast.MOCAB5, 81(3), 28–29.
Foundry Industry Recycling Starts Today (FIRST). (2004). “Foundry sand facts for civil engineers.” FHWA-IF-04-004, Federal Highway Administration Environmental Protection Agency, Washington, DC.
Harrington, J. (2010). “Foundry sands in embankments and fill.” 〈http://www.rmrc.unh.edu/materials/fs/interstate_94.pdf〉 (Sept. 2010).
Naik, T. R., and Kraus, R. N. (1997). “Development of low-cost concrete utilizing foundry industry by-products.” Rep. No. CBU-1997-21, UWM Center for By-Products Utilization, Univ. of Wisconsin, Milwaukee.
Naik, T. R., Kraus, R. N., Chun, Y. M., Ramme, B. W., and Siddique, R. (2004). “Precast concrete products using industrial by-products.” ACI Mater. J.AMAJEF, 101(3), 199–206.
Naik, T. R., Kraus, R. N., Chun, Y. M., Ramme, B. W., and Singh, S. S. (2003). “Properties of field manufactured cast-concrete products utilizing recycled materials.” J. Mater. Civ. Eng.JMCEE7, 15(4), 400–407.
Naik, T. R., and Patel, V. M. (1992). “Utilization of used foundry sand: Current state of the knowledge.” Rep. CBU-1992-02, UWM Center for By-Products Utilization, Univ. of Wisconsin, Milwaukee.
Naik, T. R., Patel, V. M., Parikh, D. M., and Tharaniyil, M. P. (1992). “Utilization of used foundry sand: Characterization and products testing.” Rep. CBU-1992-20, UWM Center for By-Products Utilization, Univ. of Wisconsin, Milwaukee.
Naik, T. R., Patel, V. M., Parikh, D. M., and Tharaniyil, M. P. (1994). “Utilization of used foundry sand in concrete.” J. Mater. Civ. Eng.JMCEE7, 6(2), 254–263.
Naik, T. R., and Ramme, B. W. (1990). “High early strength fly ash concrete for precast/prestressed products.” PCI J.PCIJEE, 35(6), 72–78.
Naik, T. R., and Singh, S. (1997a). “Flowable slurry containing foundry sand.” J. Mater. Civ. Eng.JMCEE7, 9(2), 93–102.
Naik, T. R., and Singh, S. (1997b). “Influence of source of foundry sand and fly ash on permeability of flowable slurry materials.” J. Geotech. Geoenviron. Eng.JGGEFK, 123(5), 446–452.
Naik, T. R., Singh, S. S., and Hossain, M. M. (1995). “Abrasion resistance of high-strength concrete made with class c fly ash.” ACI Mater. J., 92(6), 649–659.AMAJEF
Naik, T. R., Singh, S. S., and Ramme, B. W. (2001). “Performance and leaching assessment of flowable slurry.” J. Environ. Eng.JOEEDU, 127(4), 359–368.
Naik, T. R., Singh, S., Tharaniyil, M. P., and Wendorf, R. B. (1996). “Application of foundry by-product materials in manufacture of concrete and masonry products.” ACI Mater. J.AMAJEF, 93(1), 41–50.
Information & Authors
Information
Published In
Copyright
© 2012. American Society of Civil Engineers.
History
Received: Apr 19, 2011
Accepted: Nov 23, 2011
Published online: Nov 25, 2011
Published in print: Jul 1, 2012
Authors
Metrics & Citations
Metrics
Citations
Download citation
If you have the appropriate software installed, you can download article citation data to the citation manager of your choice. Simply select your manager software from the list below and click Download.