Accelerated Life Test of Concrete in Chloride Environment
Publication: Journal of Materials in Civil Engineering
Volume 23, Issue 3
Abstract
The accelerated life test of concrete in a chloride environment was carried out with chloride ion migration equipment. The time that elapsed before critical chloride concentration led to reinforcement corrosion was defined in this paper as the service life of concrete. The negative logarithm of chloride ion concentration was linear with the electrochemical potential. The chloride concentration in the anode chamber was an approximate linear relationship and increased with the testing time after a different stage. The service life of concrete in a natural diffusion test could be predicted by the accelerated curve. The results show that the service life of 10 mm concrete cover in the chloride environment is between 11.89 and 12.45 years. The experimental value is in good agreement with the Life-365 prediction.
Get full access to this article
View all available purchase options and get full access to this article.
Acknowledgments
This research was supported through a research grant from the National Natural Science Foundation of China (No. NNSFC50808045) and an open foundation of State Key Laboratory of coastal and offshore engineering, Dalian University of Technology (No. UNSPECIFIEDLP1013).
References
Ahmad, S. (2003). “Reinforcement corrosion in concrete structures, its monitoring and service life prediction—a review.” Cem. Concr. Compos., 25(4–5), 459–471.
Alonso, C., Andrade, C., Castellote, M., and Castro, P. (2000). “Chloride threshold values to depassivate reinforcing bars embedded in a standardized OPC mortar.” Cem. Concr. Res., 30(7), 1047–1055.
Andrade, C. (1993). “Calculation of chloride diffusion coefficients in concrete from ionic migration measurements.” Cem. Concr. Res., 23(3), 724–742.
Ann, K. Y., and Song, H. W. (2007). “Chloride threshold level for corrosion of steel in concrete.” Corros. Sci., 49(11), 4113–4133.
Arya, C., and Newman, J. B. (1990). “An assessment of four methods of determining the free chloride content of concrete.” Mater. Struct., 23(5), 319–330.
Ba, H. J., and Zhang, W. M. (2007). “Accelerated life test and service life prediction of concrete.” J. Chin. Ceram. Soc., 35(2), 242–246 (in Chinese).
Bautista, A., Blanco, G., Velasco, F., and Martínez, M. A. (2007). “Corrosion performance of welded stainless steels reinforcements in simulated pore solutions.” Constr. Build. Mater., 21(6), 1267–1276.
Bentz, E. C. (2003). “Probabilistic modeling of service life for structures subjected to chlorides.” ACI Mater. J., 100(5), 391–397.
Boddy, A., Bentz, E., Thomas, M. D. A., and Hooton, R. D. (1999). “An overview and sensitivity study of a multimechanistic chloride transport model.” Cem. Concr. Res., 29(6), 827–837.
Cabrera, J. G. (1996). “Deterioration of concrete due to reinforcement steel corrosion.” Cem. Concr. Compos., 18(1), 47–59.
Castellote, M., Andrade, C., and Alonso, C. (2001). “Measurement of the steady and non-steady-state chloride diffusion coefficients in a migration test by means of monitoring the conductivity in the anolyte chamber. Comparison with natural diffusion tests.” Cem. Concr. Res., 31(10), 1411–1420.
Clifton, J. R. (1993). “Predicting the service life of concrete.” ACI Mater. J., 90(6), 611–617.
Diamond, S. (1986). “Chloride concentrations in concrete pores solutions resulting from calcium and sodium chloride admixtures.” Cem. Concr. Aggregates, 8(2), 97–102.
Diamond, S. (1989). “ASR-Another look at mechanisms.” Proc., 8th Int. Conf. on Alkali-Aggregate Reaction, Spon Press, London, 83–87.
Francis, G. P., William, Q. M., and Luis, A. E. (2006). “Analysis accelerated life test models and data analysis.” Springer handbook of engineering statistics, Part C: Reliability models and survival, H. Pham, ed., Springer, London, 398–422.
Friedmann, H., Amiri, O., Aït-Mokhtar, A., and Dumargue, P. (2004). “A direct method for determining chloride diffusion coefficient by using migration test.” Cem. Concr. Res., 34(11), 1967–1973.
Glass, G. K. (2003). “Reinforcement corrosion.” Advanced concrete technology set, J. Newman and B. S. Choo, eds., Butterworth-Heinemann, Oxford, 1–27.
Glass, G. K., and Buenfield, N. R. (1997). “The presentation of the chloride threshold level for corrosion of steel in concrete.” Corros. Sci., 39(5), 1001–1013.
Gouda, V. K. (1970). “Corrosion and corrosion inhibition of reinforcing steel, 1: Immersed in alkaline solution.” Br. Corros. J., 5(9), 198–203.
Hausmann, D. A. (1967). “Steel corrosion in concrete: How does it occur?” Mater. Prot., 6(11), 19–23.
Hussain, S. E., Rasheduzzafar, S. E., Al-Mussallam, A., and Al-Gahtani, A. S. (1995). “Factors affecting threshold chloride for reinforcement corrosion in concrete.” Cem. Concr. Res., 25(7), 1543–1555.
Jung, W. Y., Yoon, Y. S., and Sohn, Y. M. (2003). “Predicting the remaining service life of land concrete by steel corrosion.” Cem. Concr. Res., 33(5), 663–677.
Liang, M. T., Wang, K. L., and Liang, C. H. (1999). “Service life prediction of reinforced concrete structures.” Cem. Concr. Res., 29(9), 1411–1418.
Life-365 V2.0.1 Users Manual, 〈http://www.life-365.org〉 (Feb. 3, 2010).
McGrath, P. F., and Hooton, R. D. (1996). “Influence of voltage on chloride diffusion coefficients from chloride migration tests.” Cem. Concr. Res., 26(8), 1239–1244.
Poupard, O., L’Hostis, V., Catinaud, S., and Petre-Lazar, I. (2006). “Corrosion damage diagnosis of a reinforced concrete beam after 40 years natural exposure in marine environment.” Cem. Concr. Res., 36(3), 504–520.
Song, H. W., Shim, H. B., Petcherdchoo, A., and Park, S. K. (2009). “Service life prediction of repaired concrete structures under chloride environment using finite difference method.” Cem. Concr. Compos., 31(2), 120–127.
Thomas, M. (1996). “Chloride thresholds in marine concrete.” Cem. Concr. Res., 26(4), 513–519.
Vidal, T., Castel, A., and François, R. (2007). “Corrosion process and structural performance of a 17 year old reinforced concrete beam stored in chloride environment.” Cem. Concr. Res., 37(11), 1551–1561.
Yonezawa, T., Ashworth, V., and Procter, R. P. M. (1988). “Pore solution composition and chloride effects on the corrosion of steel in concrete.” Corros., 44(7), 489–499.
Zhang, B. L., and Wei, S. S. (1996). “Test data for reinforced concrete structure at sea port of South China after 10 years exposes.” Port Waterw. Eng., (3), 6–13 (in Chinese).
Zhang, J. Y., and Lounis, Z. (2009). “Nonlinear relationships between parameters of simplified diffusion-based model for service life design of concrete structures exposed to chlorides.” Cem. Concr. Compos., 31(8), 591–600.
Information & Authors
Information
Published In
Copyright
© 2011 American Society of Civil Engineers.
History
Received: Jun 23, 2009
Accepted: Sep 23, 2010
Published online: Sep 27, 2010
Published in print: Mar 1, 2011
Authors
Metrics & Citations
Metrics
Citations
Download citation
If you have the appropriate software installed, you can download article citation data to the citation manager of your choice. Simply select your manager software from the list below and click Download.