Corrosion Performance of Steel Rebars in the Roof of a 65-Year-Old Underground Reinforced Concrete Water-Storage Tank
Publication: Journal of Performance of Constructed Facilities
Volume 34, Issue 4
Abstract
This work deals with the corrosion evaluation of steel rebars in an underground water-storage tank using visual inspection, half-cell potential, and electrochemical impedance spectroscopy (EIS). The studied case has a service life of 65 years. From the inside, red stains were observed on the roof of the tank, and some cracks, as well as spalling of the concrete’s cover, raised suspicion of corrosion damage. Twenty-seven points on the tank’s roof were selected to drill out cores for further investigation. Measurements of the chloride penetration in the roof showed that the bottom part of the roof that was exposed to greater humidity and chloride-laden vapor was at risk of heavy corrosion. EIS studies of the steel rebars at different depths confirmed that those located in the upper part of the roof still have appropriate resistance to corrosion, but the lower ones exhibited a high corrosion rate. As a result, a repair of at least 12 cm in depth of the bottom of the roof and the installation of a proper ventilation system inside the tank were recommended.
Get full access to this article
View all available purchase options and get full access to this article.
Data Availability Statement
All data, models, and code generated or used during the study appear in the published article.
Acknowledgments
This research was partially supported by Mashhad Water and Waste Water Company under research Grant No. 97338119. The support of the Ferdowsi University of Mashhad and Foundation for Science and Technology, Civil Engineering Research and Innovation for Sustainability (CERIS) Research Center, and Instituto Superior Técnico is also acknowledged.
References
ACI (American Concrete Institute). 2008. Guide to durable concrete? ACI 201.2R-08. Farmington Hills, MI: ACI.
Alonso, C., C. Andrade, M. Castellote, and P. Castro. 2000. “Chloride threshold values to depassivate reinforcing bars embedded in a standardized OPC mortar.” Cem. Concr. Res. 30 (7): 1047–1055. https://doi.org/10.1016/S0008-8846(00)00265-9.
Andrade, C., and C. Alonso. 1996. “Corrosion rate monitoring in the laboratory and on-site.” Constr. Build. Mater. 10 (5): 315–328. https://doi.org/10.1016/0950-0618(95)00044-5.
Ann, K. Y., and H.-W. Song. 2007. “Chloride threshold level for corrosion of steel in concrete.” Corros. Sci. 49 (11): 4113–4133. https://doi.org/10.1016/j.corsci.2007.05.007.
ASTM. 2015. Standard test method for corrosion potentials of uncoated reinforcing steel in concrete. ASTM C876. West Conshohocken, PA: ASTM International.
ASTM. 2017. Standard test method for water-soluble chloride in mortar and concrete. ASTM C1218/C1218M. West Conshohocken, PA: ASTM International.
ASTM. 2018. Standard test methods for chemical analysis of hydraulic cement. ASTM C114. West Conshohocken, PA: ASTM International.
ASTM. 2019. Standard test methods and definitions for mechanical testing of steel products. ASTM A370-19e1. West Conshohocken, PA: ASTM International.
Berrocal, C. G., K. Lundgren, and I. Löfgren. 2016. “Corrosion of steel bars embedded in fibre reinforced concrete under chloride attack: State of the art.” Cem. Concr. Res. 80 (Feb): 69–85. https://doi.org/10.1016/j.cemconres.2015.10.006.
Brenna, A., S. Beretta, F. Bolzoni, M. Pedeferri, and M. Ormellese. 2017. “Effects of AC-interference on chloride-induced corrosion of reinforced concrete.” Constr. Build. Mater. 137 (Apr): 76–84. https://doi.org/10.1016/j.conbuildmat.2017.01.087.
Cairns, J., G. A. Plizzari, Y. Du, D. W. Law, and C. J. A. M. J. Franzoni. 2005. “Mechanical properties of corrosion-damaged reinforcement.” ACI Mater. J. 102 (4): 256.
Choi, Y. S., S.-T. Yi, M. Y. Kim, W. Y. Jung, and E. I. Yang. 2014. “Effect of corrosion method of the reinforcing bar on bond characteristics in reinforced concrete specimens.” Constr. Build. Mater. 54 (Mar): 180–189. https://doi.org/10.1016/j.conbuildmat.2013.12.065.
Elsener, B., C. Andrade, J. Gulikers, R. Polder, and M. Raupach. 2003. “Half-cell potential measurements—Potential mapping on reinforced concrete structures.” Mater. Struct. 36 (7): 461–471. https://doi.org/10.1007/BF02481526.
Fang, S., E. S.-S. Lam, and W.-Y. Wong. 2017. “Using alkali-activated slag ferrocement to strengthen corroded reinforced concrete columns.” Mater. Struct. 50 (1): 35. https://doi.org/10.1617/s11527-016-0915-4.
Flitt, H. J., and D. P. Schweinsberg. 2005. “Evaluation of corrosion rate from polarisation curves not exhibiting a Tafel region.” Corros. Sci. 47 (12): 3034–3052. https://doi.org/10.1016/j.corsci.2005.06.014.
Ghorbani, S., I. Taji, J. de Brito, M. Negahban, S. Ghorbani, M. Tavakkolizadeh, and A. Davoodi. 2019. “Mechanical and durability behaviour of concrete with granite waste dust as partial cement replacement under adverse exposure conditions.” Constr. Build. Mater. 194 (Jan): 143–152. https://doi.org/10.1016/j.conbuildmat.2018.11.023.
Ghorbani, S., I. Taji, M. Tavakkolizadeh, A. Davoodi, and J. de Brito. 2018. “Improving corrosion resistance of steel rebars in concrete with marble and granite waste dust as partial cement replacement.” Constr. Build. Mater. 185 (Oct): 110–119. https://doi.org/10.1016/j.conbuildmat.2018.07.066.
González, J. A., C. Andrade, C. Alonso, and S. Feliu. 1995. “Comparison of rates of general corrosion and maximum pitting penetration on concrete embedded steel reinforcement.” Cem. Concr. Res. 25 (2): 257–264. https://doi.org/10.1016/0008-8846(95)00006-2.
Ishii, S. K., and T. H. Boyer. 2011. “Evaluating the secondary effects of magnetic ion exchange: Focus on corrosion potential in the distribution system.” Desalination 274 (1–3): 31–38. https://doi.org/10.1016/j.desal.2011.01.061.
Jazdzewska, A., K. Darowicki, J. Orlikowski, S. Krakowiak, K. Zakowski, M. Gruszka, and J. Banas. 2016. “Critical analysis of laboratory measurements and monitoring system of water-pipe network corrosion-case study.” Case Stud. Constr. Mater. 4 (Jun): 102–107. https://doi.org/10.1016/j.cscm.2016.01.004.
Ji, Y.-S., G. Zhan, Z. Tan, Y. Hu, and F. Gao. 2015. “Process control of reinforcement corrosion in concrete. Part 1: Effect of corrosion products.” Constr. Build. Mater. 79 (Mar): 214–222. https://doi.org/10.1016/j.conbuildmat.2014.12.083.
Liu, M., X. Cheng, X. Li, J. Hu, Y. Pan, and Z. Jin. 2016. “Indoor accelerated corrosion test and marine field test of corrosion-resistant low-alloy steel rebars.” Case Stud. Constr. Mater. 5 (Dec): 87–99. https://doi.org/10.1016/j.cscm.2016.09.005.
Mansfeld, F. 1976. “The polarization resistance technique for measuring corrosion currents.” In Advances in corrosion science and technology, 163–262. Boston: Springer.
Mansfeld, F. 2005. “Tafel slopes and corrosion rates obtained in the pre-Tafel region of polarization curves.” Corros. Sci. 47 (12): 3178–3186. https://doi.org/10.1016/j.corsci.2005.04.012.
McCafferty, E. 2005. “Validation of corrosion rates measured by the Tafel extrapolation method.” Corros. Sci. 47 (12): 3202–3215. https://doi.org/10.1016/j.corsci.2005.05.046.
Mohamed, H. M., and B. Benmokrane. 2014. “Design and performance of reinforced concrete water chlorination tank totally reinforced with GFRP bars: Case study.” J. Compos. Constr. 18 (1): 05013001. https://doi.org/10.1061/(ASCE)CC.1943-5614.0000429.
Mohammed, T. U., and H. Hamada. 2001. “A discussion of the paper ‘Chloride threshold values to depassivate reinforcing bars embedded in a standardized OPC mortar’ by C. Alonso, C. Andrade, M. Castellote, and P. Castro.” Cem. Concr. Res. 31 (5): 835–838. https://doi.org/10.1016/S0008-8846(01)00485-9.
Oh, B. H., S. Y. Jang, and Y. Shin. 2003. Experimental investigation of the threshold chloride concentration for corrosion initiation in reinforced concrete structures.” Mag. Concr. Res. 55 (2): 117–124.
Patil, S., B. Karkare, and S. Goyal. 2014. “Acoustic emission vis-à-vis electrochemical techniques for corrosion monitoring of reinforced concrete element.” Constr. Build. Mater. 68 (Oct): 326–332. https://doi.org/10.1016/j.conbuildmat.2014.06.068.
Pradhan, B. 2014. “Corrosion behavior of steel reinforcement in concrete exposed to composite chloride–sulfate environment.” Constr. Build. Mater. 72 (Dec): 398–410. https://doi.org/10.1016/j.conbuildmat.2014.09.026.
Ribeiro, D., and J. Abrantes. 2016. “Application of electrochemical impedance spectroscopy (EIS) to monitor the corrosion of reinforced concrete: A new approach.” Constr. Build. Mater. 111 (May): 98–104. https://doi.org/10.1016/j.conbuildmat.2016.02.047.
Tahershamsi, M. 2016. Structural effects of reinforcement corrosion in concrete structures. Gothenburg, Sweden: Chalmers Univ. of Technology Gothenburg.
Taji, I., S. Ghorbani, J. de Brito, V. W. Y. Tam, S. Sharifi, A. Davoodi, and M. Tavakkolizadeh. 2019. “Application of statistical analysis to evaluate the corrosion resistance of steel rebars embedded in concrete with marble and granite waste dust.” J. Cleaner Prod. 210 (Feb): 837–846. https://doi.org/10.1016/j.jclepro.2018.11.091.
Trejo, D., C. Halmen, and K. F. Reinschmidt. 2009. Corrosion performance tests for reinforcing steel in concrete: Technical report. College Station, TX: Texas Transportation Institute, Texas A&M Univ. System.
Zhao, Z., and L. Fu. 2018. “The probability distribution of pitting for accelerated corrosion reinforcement.” Case Stud. Constr. Mater. 9 (Dec): e00193. https://doi.org/10.1016/j.cscm.2018.e00193.
Information & Authors
Information
Published In
Copyright
©2020 American Society of Civil Engineers.
History
Received: Apr 10, 2019
Accepted: Mar 5, 2020
Published online: May 26, 2020
Published in print: Aug 1, 2020
Discussion open until: Oct 26, 2020
Authors
Metrics & Citations
Metrics
Citations
Download citation
If you have the appropriate software installed, you can download article citation data to the citation manager of your choice. Simply select your manager software from the list below and click Download.