Durability of GFRP Rebars in Simulated Concrete Solutions under Accelerated Aging Conditions
Publication: Journal of Composites for Construction
Volume 15, Issue 4
Abstract
This paper discusses the potential ingress and effects of simulated concrete pore solution species on glass fiber-reinforced polymer (GFRP) rebars. Knowing that diffusion of moisture into the fiber-matrix interphase in a composite could cause fiber-matrix debonding and that the presence of alkalis at the location of the glass surface would lead to fiber degradation, particular attention was devoted to investigating whether GFRP rebars allow both species to penetrate or allow only water, while blocking the alkalis. To investigate this scenario, GFRP rebars were immersed in five types of simulated concrete pore solutions at elevated temperatures. Penetration of alkalis was assessed using X-ray mapping of backscattered electron images (BEI) and crosschecked by line and point energy dispersive spectroscopy (EDS) techniques. The effects of diffusion at the fiber-matrix interphase were observed by investigating the degradation of constituents at the interphase. Degradation of polymer matrix was assessed by a Fourier transform infrared (FTIR) spectroscopy. Degradation of fiber was investigated by observing highly magnified scanning electron microscopy (SEM) images and point EDS analyses close to the interphase. Debonding of fibers from the matrix was investigated using a SEM technique. Fiber-matrix debonding took place in a few samples, despite the fact that the glass fibers and polymer matrix remained essentially intact and that no penetration of alkalis into the GFRP rebars was observed. This debonding, which occurred only for samples exposed to 75°C, is believed to be caused by hydrolysis of fiber sizing at high temperatures. Finally, this study shows that the vinyl ester (VE) polymer matrix used acts as an effective semipermeable membrane by allowing the penetration of water, while blocking alkali ions.
Get full access to this article
View all available purchase options and get full access to this article.
Acknowledgments
The writers acknowledge the financial support of the Canadian Network of Centers of Excellence on Intelligent Sensing for Innovative Structures (ISIS Canada) and The Natural Sciences and Engineering Research Council of Canada (NSERC).
References
Apicella, A., Migliaresi, C., Nicolais, L., Iaccarino, L., and Roccotelli, S. (1983). “The water aging of unsaturated polyester-based composites: Influence of resin chemical structure.” Composites, 14(4), 387–392.
ASTM. (2007). “Standard guide for preparation of metallographic specimens.” ASTM Standard E3-01, West Conshohocken, PA. 〈http://www.astm.org/DATABASE.CART/HISTORICAL/E3-01R07.htm〉 (Jul. 5, 2011).
Bank, L. C., Barkatt, A., and Gentry, T. R. (1995). “Accelerated test methods to determine the long-term behavior of FRP composite structures: Environmental effects.” J. Reinf. Plast. Compos., 14(6), 559–587.
Bank, L. C., Puterman, M., and Katz, A. (1998). “The effect of material degradation of bond properties of FRP reinforcing bars in concrete.” ACI Mater. J., 95(3), 232–243.
Barkatt, A. (2001). “Issues in predicting long-term environmental degradation of fiber-reinforced plastics.” Environmental effects on engineered materials, R. H. Jones, ed., Marcel Dekker, New York, 419–458.
Benmokrane, B., and Cousin, P. (2005). “University of Sherbrooke GFRP durability study report.” Intelligent Sensing for Innovative Structures (ISIS), Winnipeg, MB, Canada.
Benmokrane, B., Wang, P., Pavate, T., and Robert, M. (2006). “Durability of FRP composites for civil infrastructure applications.” Durability of Materials and Structures in Building and Civil Engineering, C. W. Yu and J. W. Bull, eds., Whittles Publishing, Dunbeath, Scotland.
Bird, R. B., Stewart, W. E., and Lightfoot, E. N. (2007). Transport phenomena,2nd Ed., Wiley, New York.
Canadian Standards Association (CSA). (2006). “Canadian Highway Bridge Design Code.” CSA-S6-06, Rexdale, ON, Canada.
Chen, Y., Davalos, J. F., and Ray, I. (2006). “Durability prediction for GFRP bars using short-term data of accelerated aging tests.” J. Compos. Constr., 10(4), 279–286.
Chen, Y., Davalos, J. F., Ray, I., and Kim, H. Y. (2007). “Accelerated aging tests for evaluations of durability performance of FRP reinforcing bars for concrete structures.” Compos. Struct., 78(1), 101–111.
Chin, J. W., Nguyen, T., and Aouadi, K. (1997). “Effects of environmental exposure on fiber-reinforced plastic-FRP-materials used in construction.” J. Compos. Technol. Res., 19(4), 205–213.
Chin, J. W., Nguyen, T., and Aouadi, K. (1999). “Sorption and diffusion of water, salt water, and concrete pore solution in composite matrices.” J. Appl. Polym. Sci., 71, 483–492.
Chin, J. W., Aouadi, K., Haight, M. R., Hughes, W. L., and Nguyen, T. (2001). “Effects of water, salt solution, and simulated concrete pore solution on the properties of composite matrix resins used in civil engineering applications.” Polymer Composites, 22(2), 282–297.
Chong, K. P. (1998). “Durability of composite materials and structures.” Proc., 1st Int. Conf. on Durability of Fiber-Reinforced Polymer for Construction (CDCC’98), B. Benmodrane and H. Rahman, eds., Dept. of Civil Engineering, Université de Sherbrooke, Sherbrooke, PQ, Canada, 1–12.
Dejke, V., and Tepfers, R. (2001). “Durability and service life prediction of GFRP for concrete reinforcement.” Proc., 5th Int. Conf. on Fiber-Reinforced Plastics for Reinforced Concrete Structures (FRPRCS-5), Vol. 1, Thomas Telford, London, 505–516.
Devalapura, R. K., Greenwod, M. E., Gauchel, J. V., and Humphrey, H. (1998). “Evaluation of GFRP performance using accelerated test methods.” Proc., 1st Int. Conf. on Durability of Fiber-Reinforced Polymer for Construction (CDCC’98), B. Benmodrane and H. Rahman, eds., Dept. of Civil Engineering, Université de Sherbrooke, Sherbrooke, PQ, Canada, 107–116.
Flegler, S. L., Heckman, J. W., Jr., and Klomparens, K. L. (1993). Scanning and transmission electron microscopy: An introduction, Oxford University Press, New York.
GangaRao, H. V. S., and Vijay, P. V. (1997). “Aging of structural composites under varying environmental conditions.” Proc., 3rd Int. Symp. on Non-Metallic (FRP) Reinforcement for Concrete Structures (FRPRCS-3), Japan Concrete Institute, Sapporo, Japan, 91–98.
Goldstein, J., et al. (2003). Scanning electron microscopy and X-ray microanalysis, 3rd Ed., Kluwer Academic/Plenum Publishers, New York.
Greenwood, M. (2002). “Creep-rupture testing to predict long-term performance on durability of fiber reinforced polymer (FRP) composites for construction.” Proc., 2nd Int. Conf. on Durability of Fiber-Reinforced Polymer for Construction (CDCC’02), B. Benmokrane and E. El-Salakawy, eds., Dept. of Civil Engineering, Université de Sherbrooke, Sherbrooke, PQ, Canada, 203–212.
Karbhari, V. M., and Zhang, J. S. (2003). “E-glass/vinylester composites in aqueous environments. I: Experimental results.” Appl. Compos. Mater., 10(1), 19–48.
Karbhari, V. M., et al. (2003). “Durability gap analysis for fiber-reinforced polymer composites in civil infrastructure.” J. Compos. Constr., 7(3), 238–247.
Katsuki, F., and Uomoto, T. (1995). “Prediction of deterioration of FRP rods due to alkali attack in nonmetallic (FRP) reinforcement for concrete structures.” Proc., 2nd Int. RILEM Symp. (FRPRCS-2), L. Taerwe, ed., RILEM, Bagneux, France, 82–89.
Kim, H. Y., Park, Y. H., You, Y. J., and Moon, C. K. (2008). “Short-term durability test for GFRP rods under various environmental conditions.” Compos. Struct., 83(1), 37–47.
Koch, G. H., Brongers, M. P. H., Thomson, N. G., Virmanio, Y. P., and Payer, J. H. (2005). “Cost of corrosion in the United States.” Handbook of environmental degradation of materials, M. Kutz, ed., William Andrew Publishing, Norwich, NY.
Marchand, J., Bentz, D., Samson, E., and Maltais, Y. (2001). “Influence of calcium hydroxide dissolution on the transport properties of hydrated cement systems.” Calcium hydroxide in concrete: Materials science of concrete, Proc., Workshop on the Role of Calcium Hydroxide in Concrete, American Ceramic Society, Westerville, OH, 113–129.
Marom, G., and Broutman, L. J. (1981). “Moisture penetration into composites under external stress.” Polymer Composites, 2(3), 132–136.
Marsden, J. G., and Sterman, S. (1990). “Organofunctional silane coupling agents.” Handbook of adhesives, 3rd Ed., I. Skeist, ed., Van Nostrand Reinhold, New York.
Mufti, A. A., et al. (2005). “Report on studies of GFRP durability in concrete from field bridge demonstration projects.” Proc., 3rd Int. Conf. on Composites in Construction (CCC 2005), P. Hamelin, D. Bigaud, E. Ferrier, and E. Jacqelin, eds., Université Claude Bernard, Lyon, France, 889-895.
Mukherjee, A., and Arwikar, S. I. (2005). “Performance of glass fiber-reinforced polymer reinforcing bars in tropical environments—Part II: Microstructural tests.” ACI Struct. J., 102(6), 816–822.
Murphy, K., Zhang, S., and Karbhari, V. M. (1999). “Effect of concrete based alkaline solutions on short term response of composites.” Proc., 44th Int. Society for the Advancement of Material and Process Engineering (SAMPE) Symposium and Exhibition, L. J. Cohen, J. L. Bauer, and W. E. Davis, eds., SAMPE, Covina, CA, 2222–2230.
Nkurunziza, G., Debaiky, A., Cousin, P., and Benmokrane, B. (2005). “Durability of GFRP bars: A critical review of the literature.” Prog. Struct. Eng. Mater., 7(4), 194–209.
Onofrei, M. (2005). “Durability of GFRP reinforced concrete from field demonstration structures, Final report.” Univ. of Manitoba, Winnipeg, MB, Canada
Porter, M. L., and Barnes, B. A. (1998). “Accelerated aging degradation of glass fiber composites.” Proc., 2nd Int. Conf. on Composites in Infrastructure (ICCI), Vol. 2, Transportation Research Board, Washington, DC, 446–459.
Porter, M. L., Mehus, J., Young, K. A., O’Neil, E. F., and Barnes, B. A. (1997). “Aging for fiber reinforcement in concrete.” Proc., 3rd Int. Symp. on Non-Metallic (FRP) Reinforcement for Concrete Structures (FRPRCS-3), Vol. 2, Japan Concrete Institute, Sapporo, Japan, 59–66.
Pritchard, G. (1999). Reinforced plastics durability, Woodhead, Cambridge, UK.
Pritchard, G., and Speake, S. D. (1987). “The use of water absorption kinetic data to predict laminate property changes.” Composites, 18(3), 227–232.
Robert, M., Cousin, P., and Benmokrane, B. (2009). “Durability of GFRP reinforcing bars embedded in moist concrete.” J. Compos. Constr., 13(2), 66–73.
Schutte, C. L. (1994). “Environmental durability of glass-fiber composites.” Mater. Sci. Eng., R, 13(7), 265–322.
Sen, R., Mullins, G., and Salem, T. (2002). “Durability of -glass/vinylester reinforcement in alkaline solution.” ACI Struct. J., 99(3), 369–375.
Sonawala, S. P., and Spontak, R. J. (1996). “Degradation kinetics of glass-reinforced polymers in chemical environments 1: Aqueous solutions.” J. Mater. Sci., 31(18), 4745–4756.
Swit, G. (2000). “Durability of stressed -glass fiber in alkaline medium.” Recent developments in durability analysis of composite systems, H. Cardon et al., eds., Taylor and Francis, London, 473–476.
Tannous, F. E., and Saadatmanesh, H. (1999). “Durability of AR glass fiber-reinforced plastic bars.” J. Compos. Constr., 3(1), 12–19.
Thomason, J. L., and Dwight, D. W. (2000). “XPS analysis of the coverage and composition of coatings on glass fibers.” J. Adhes. Sci. Technol., 14(5), 745–764.
Tosun, I. (2007). Modeling in transport phenomena: A conceptual approach, 2nd Ed., Elsevier, New York.
Valter, T., and Ralejs, T. (2001). “Durability and service life prediction of GFRP for concrete reinforcement.” Proc., 5th Int. Conf. on Fiber-Reinforced Plastics for Reinforced Concrete Structures (FRPRCS-5), Vol. 1, Thomas Telford, London, 505–514.
Wade, L. G., Jr. (2003). Organic chemistry, 5th Ed., Prentice Hall, Upper Saddle River, NJ.
Wang, P. (2005). “Effect of moisture, temperature, and alkaline on durability of -glass/vinyl ester reinforcing bars.” Ph.D. thesis, Université de Sherbrooke, Sherbrooke, PQ, Canada.
Watt, I. M. (1997). The principles and practice of electron microscopy, 2nd Ed., Cambridge University Press, New York.
Yilmaz, V. T., and Glasser, F. P. (1991). “Reaction of alkali-resistant glass fibers with cement. Part I: Review, assessment, and microscopy.” Glass Technology, 32(3), 91–98.
Zhang, S., and Karbhari, V. M. (1999). “Effects of alkaline environments on the durability of -glass fiber composites for use in civil infrastructure.” Proc., 14th Technical Conf. of the American Society of Composites, Technomic Publishing, Lancaster, PA, 12–20.
Zheng, Q., and Morgan, R. J. (1993). “Synergistic thermal moisture damage mechanisms of epoxies and their carbon fiber composites.” J. Compos. Mater., 27(15), 1465–1478.
Information & Authors
Information
Published In
Journal of Composites for Construction
Volume 15 • Issue 4 • August 2011
Pages: 473 - 481
Copyright
© 2011 American Society of Civil Engineers.
History
Received: Apr 13, 2009
Published online: Sep 1, 2010
Accepted: Sep 2, 2010
Published in print: Aug 1, 2011
Authors
Metrics & Citations
Metrics
Citations
Download citation
If you have the appropriate software installed, you can download article citation data to the citation manager of your choice. Simply select your manager software from the list below and click Download.