Crack Propagation-Based Fatigue Life Prediction of Corroded RC Beams Considering Bond Degradation
Publication: Journal of Bridge Engineering
Volume 25, Issue 8
Abstract
Corrosion increases the nominal stress of reinforcing bars and accelerates the fatigue crack propagation. The stress redistribution induced by bond degradation between concrete and rebars makes the fatigue life prediction of reinforced concrete (RC) structures more complicated. This paper proposes a crack propagation-based fatigue life prediction method for corroded RC beams incorporating fatigue damage of concrete, fatigue bond degradation, and pitting corrosion. The fatigue damage of concrete is modeled based on plastic strain analysis. For the fatigue-worsened bond degradation between concrete and corroded rebars, a novel strain-incompatibility analysis method is developed to quantify the slip of reinforcements in concrete. The fatigue crack propagation parameters of rebars and the corrosion pit-induced stress concentration are experimentally obtained. The stress intensity for the fatigue crack at the corrosion pit root is calculated by an asymptotic interpolation method. Then, the fatigue failure analysis of corroded RC beams is performed, where the reinforcement fracture, concrete crush, and bond degradation-induced anchorage failure at beam ends are checked. The proposed method is verified by the test data. The effects of bond degradation and concrete damage on the fatigue life prediction are analyzed and discussed. The proposed method for fatigue life prediction gives a reasonable estimate of the service life of corroded RC beams.
Get full access to this article
View all available purchase options and get full access to this article.
Acknowledgments
The current research is financially supported by the National Natural Science Foundation of China (51778068 and 51508036), the Special Funds for the Construction of Innovative Provinces in Hunan of China (2019RS2035 and 2019SK2171), the Natural Science Foundation for Excellent Young Scholars of Hunan Province (2019JJ30024), the Training Program for Excellent Young Innovators of Changsha (kq1802012), the Key Disciplinary of Civil Engineering of Changsha University of Science and Technology (18ZDXK08), and China Scholarship Council (201808430192). The support is gratefully acknowledged.
References
ACI (American Concrete Institute). 2008. Building code requirements for structural concrete and commentary. ACI 318-08. Farmington Hills, MI: ACI.
Al-Hammoud, R., K. Soudki, and T. H. Topper. 2010. “Bond analysis of corroded reinforced concrete beams under monotonic and fatigue loads.” Cem. Concr. Compos. 32 (3): 194–203. https://doi.org/10.1016/j.cemconcomp.2009.12.001.
Apostolopoulos, C. A., S. Demis, and V. G. Papadakis. 2013. “Chloride-induced corrosion of steel reinforcement—Mechanical performance and pit depth analysis.” Constr. Build. Mater. 38: 139–146. https://doi.org/10.1016/j.conbuildmat.2012.07.087.
Balaguru, P. N. 1981. “Analysis of prestressed concrete beams for fatigue loading.” PCI J. 26 (3): 70–94. https://doi.org/10.15554/pcij.05011981.70.94.
Bastidas-Arteaga, E., P. Bressolette, A. Chateauneuf, and M. Sánchez-Silva. 2009. “Probabilistic lifetime assessment of RC structures under coupled corrosion–fatigue deterioration processes.” Struct. Saf. 31 (1): 84–96. https://doi.org/10.1016/j.strusafe.2008.04.001.
Bhargava, K., A. K. Ghosh, Y. Mori, and S. Ramanujam. 2008. “Suggested empirical models for corrosion-induced bond degradation in reinforced concrete.” J. Struct. Eng. 134 (2): 221–230. https://doi.org/10.1061/(ASCE)0733-9445(2008)134:2(221).
Brena, S. F., M. A. Benouaich, M. E. Kreger, and S. L. Wood. 2005. “Fatigue tests of reinforced concrete beams strengthened using carbon fiber-reinforced polymer composites.” ACI Struct. J. 102 (2): 305–313.
Cairns, J., and R. B. Abdullah. 1996. “Bond strength of black and epoxy-coated reinforcement—A theoretical approach.” ACI Mater. J. 93 (4): 362–369.
Carpinteri, A., A. Spagnoli, and S. Vantadori. 2004. “A fracture mechanics model for a composite beam with multiple reinforcements under cyclic bending.” Int. J. Solids Struct. 41 (20): 5499–5515. https://doi.org/10.1016/j.ijsolstr.2004.04.032.
Cerit, M., K. Genel, and S. Eksi. 2009. “Numerical investigation on stress concentration of corrosion pit.” Eng. Fail. Anal. 16 (7): 2467–2472. https://doi.org/10.1016/j.engfailanal.2009.04.004.
Coronelli, D. 2002. “Corrosion cracking and bond strength modeling for corroded bars in reinforced concrete.” ACI Struct. J. 99 (3): 267–276.
Dai, L., H. Bian, L. Wang, M. Potier-Ferry, and J. Zhang. 2020. “Prestress loss diagnostics in pre-tensioned concrete structures with corrosive cracking.” J. Struct. Eng. 146 (3): 04020013. https://doi.org/10.1061/(ASCE)ST.1943-541X.0002554.
Deng, L., W. Yan, and L. Nie. 2019. “A simple corrosion fatigue design method for bridges considering the coupled corrosion–overloading effect.” Eng. Struct. 178: 309–317. https://doi.org/10.1016/j.engstruct.2018.10.028.
El-Tawil, S., C. Ogunc, A. Okeil, and M. Shahawy. 2001. “Static and fatigue analyses of RC beams strengthened with CFRP laminates.” J. Compos. Constr. 5 (4): 258–267. https://doi.org/10.1061/(ASCE)1090-0268(2001)5:4(258).
Forman, R. G., and V. Shivakumar. 1986. “Growth behavior of surface cracks in the circumferential plane of solid and hollow cylinders.” In Fracture mechanics: Seventeenth volume, edited by J. Underwood, R. Chait, C. Smith, D. Wilhem, W. Andrews, and J. Newman, 59–74. West Conshohocken, PA: ASTM.
Gao, L., and C.-T. T. Hsu. 1998. “Fatigue of concrete under uniaxial compression cyclic loading.” ACI Mater. J. 95 (5): 575–581.
Giuriani, E., G. Plizzari, and C. Schumm. 1991. “Role of stirrups and residual tensile strength of cracked concrete on bond.” J. Struct. Eng. 117 (1): 1–18. https://doi.org/10.1061/(ASCE)0733-9445(1991)117:1(1).
Guo, Z., Y. Ma, L. Wang, and J. Zhang. 2019. “Modelling guidelines for corrosion–fatigue life prediction of concrete bridges: Considering corrosion pit as a notch or crack.” Eng. Fail. Anal. 105: 883–895. https://doi.org/10.1016/j.engfailanal.2019.07.046.
Guo, Z., Y. Ma, L. Wang, J. Zhang, and I. E. Harik. 2020. “Corrosion fatigue crack propagation mechanism of high-strength steel bar in various environments.” J. Mater. Civ. Eng. 32 (6): 04020115. https://doi.org/10.1061/(ASCE)MT.1943-5533.0003165.
Haskett, M., D. J. Oehlers, and M. S. Mohamed Ali. 2008. “Local and global bond characteristics of steel reinforcing bars.” Eng. Struct. 30 (2): 376–383. https://doi.org/10.1016/j.engstruct.2007.04.007.
Holmen, J. O. 1982. “Fatigue of concrete by constant and variable amplitude loading.” Fatigue Concr. Struct. 75: 71–110.
Kashani, M. M., J. Maddocks, and E. A. Dizaj. 2019. “Residual capacity of corroded reinforced concrete bridge components: State-of-the-art review.” J. Bridge Eng. 24 (7): 03119001. https://doi.org/10.1061/(ASCE)BE.1943-5592.0001429.
Li, F., Y. Qu, and J. Wang. 2017. “Bond life degradation of steel strand and concrete under combined corrosion and fatigue.” Eng. Fail. Anal. 80: 186–196. https://doi.org/10.1016/j.engfailanal.2017.06.036.
Lin, H., Y. Zhao, J. Ožbolt, and R. Hans-Wolf. 2017. “The bond behavior between concrete and corroded steel bar under repeated loading.” Eng. Struct. 140: 390–405. https://doi.org/10.1016/j.engstruct.2017.02.067.
Liu, Y., and S. Mahadevan. 2009a. “Fatigue limit prediction of notched components using short crack growth theory and an asymptotic interpolation method.” Eng. Fract. Mech. 76 (15): 2317–2331. https://doi.org/10.1016/j.engfracmech.2008.06.006.
Liu, Y., and S. Mahadevan. 2009b. “Probabilistic fatigue life prediction using an equivalent initial flaw size distribution.” Int. J. Fatigue 31 (3): 476–487. https://doi.org/10.1016/j.ijfatigue.2008.06.005.
Ma, Y., Z. Guo, L. Wang, and J. Zhang. 2020. “Probabilistic life prediction for reinforced concrete structures subjected to seasonal corrosion–fatigue damage.” J. Struct. Eng. 146 (7): 04020117, https://doi.org/10.1061/(ASCE)ST.1943-541X.0002666.
Ma, Y., Z. Guo, L. Wang, and J. Zhang. 2017a. “Experimental investigation of corrosion effect on bond behavior between reinforcing bar and concrete.” Constr. Build. Mater. 152: 240–249. https://doi.org/10.1016/j.conbuildmat.2017.06.169.
Ma, Y., Z. Guo, L. Wang, J. Zhang, and Y. Liu. 2018a. “Effects of stress ratio and banded microstructure on fatigue crack growth behavior of HRB400 steel bar.” J. Mater. Civ. Eng. 30 (3): 04017314. https://doi.org/10.1061/(ASCE)MT.1943-5533.0002193.
Ma, Y., G. Wang, X. Su, L. Wang, and J. Zhang. 2018b. “Experimental and modelling of the flexural performance degradation of corroded RC beams under fatigue load.” Constr. Build. Mater. 191: 994–1003. https://doi.org/10.1016/j.conbuildmat.2018.10.031.
Ma, Y., Q. Wang, Z. Guo, G. Wang, L. Wang, and J. Zhang. 2017b. “Static and fatigue behavior investigation of artificial notched steel reinforcement.” Materials 10 (5): 532. https://doi.org/10.3390/ma10050532.
Ma, Y., Y. Xiang, L. Wang, J. Zhang, and Y. Liu. 2014. “Fatigue life prediction for aging RC beams considering corrosive environments.” Eng. Struct. 79: 211–221. https://doi.org/10.1016/j.engstruct.2014.07.039.
Masoud, S., K. Soudki, and T. Topper. 2005. “Postrepair fatigue performance of FRP-repaired corroded RC beams: Experimental and analytical investigation.” J. Compos. Constr. 9 (5): 441–449. https://doi.org/10.1061/(ASCE)1090-0268(2005)9:5(441).
Sivaprasad, S., S. Tarafder, V. R. Ranganath, M. Tarafder, and K. K. Ray. 2006. “Corrosion fatigue crack growth behaviour of naval steels.” Corros. Sci. 48 (8): 1996–2013. https://doi.org/10.1016/j.corsci.2005.08.005.
Sun, J., Z. Ding, and Q. Huang. 2019. “Corrosion fatigue life prediction for steel bar in concrete based on fatigue crack propagation and equivalent initial flaw size.” Constr. Build. Mater. 195: 208–217. https://doi.org/10.1016/j.conbuildmat.2018.11.056.
Sun, J., Q. Huang, and Y. Ren. 2015. “Performance deterioration of corroded RC beams and reinforcing bars under repeated loading.” Constr. Build. Mater. 96: 404–415. https://doi.org/10.1016/j.conbuildmat.2015.08.066.
Wang, X., and X. Liu. 2004. “Modeling bond strength of corroded reinforcement without stirrups.” Cem. Concr.e Res. 34 (8): 1331–1339. https://doi.org/10.1016/j.cemconres.2003.12.028.
Ye, Z., W. P. Zhang, Y. Hu, and X. L. Gu. 2016. “Experimental study on effects of fatigue loading history on bond behavior between steel bars and concrete.” Key Eng. Mater. 711: 673–680. https://doi.org/10.4028/www.scientific.net/KEM.711.673.
Yi, W.-J., S. K. Kunnath, X. D. Sun, C. J. Shi, and F.-J. Tang. 2010. “Fatigue behavior of reinforced concrete beams with corroded steel reinforcement.” ACI Struct. J. 107 (5): 526–533.
Zanuy, C., P. de la Fuente, and L. Albajar. 2007. “Effect of fatigue degradation of the compression zone of concrete in reinforced concrete sections.” Eng. Struct. 29 (11): 2908–2920. https://doi.org/10.1016/j.engstruct.2007.01.030.
Zhang, W., Z. Ye, X. Gu, X. Liu, and S. Li. 2017. “Assessment of fatigue life for corroded reinforced concrete beams under uniaxial bending.” J. Struct. Eng. 143 (7): 04017048. https://doi.org/10.1061/(ASCE)ST.1943-541X.0001778.
Zhang, X., L. Wang, J. Zhang, and Y. Liu. 2016. “Bond degradation-induced incompatible strain between steel bars and concrete in corroded RC beams.” J. Perform. Constr. Facil. 30 (6): 04016058. https://doi.org/10.1061/(ASCE)CF.1943-5509.0000921.
Zhang, X., W. Zhang, Y. Luo, L. Wang, J. Peng, and J. Zhang. 2020. “Interface shear strength between self-compacting concrete and carbonated concrete.” J. Mater. Civ. Eng. 32 (6): 04020113. https://doi.org/10.1061/(ASCE)MT.1943-5533.0003229.
Zhao, Y., J. Yu, B. Hu, and W. Jin. 2012. “Crack shape and rust distribution in corrosion-induced cracking concrete.” Corros. Sci. 55: 385–393. https://doi.org/10.1016/j.corsci.2011.11.002.
Zhu, W., R. François, and Y. Liu. 2017. “Propagation of corrosion and corrosion patterns of bars embedded in RC beams stored in chloride environment for various periods.” Constr. Build. Mater. 145: 147–156. https://doi.org/10.1016/j.conbuildmat.2017.03.210.
Information & Authors
Information
Published In
Copyright
© 2020 American Society of Civil Engineers.
History
Received: Dec 28, 2019
Accepted: Mar 23, 2020
Published online: May 28, 2020
Published in print: Aug 1, 2020
Discussion open until: Oct 28, 2020
Authors
Metrics & Citations
Metrics
Citations
Download citation
If you have the appropriate software installed, you can download article citation data to the citation manager of your choice. Simply select your manager software from the list below and click Download.